测定了销－盘式热压Ｓｉ３Ｎ４／３Ｃｒ２Ｗ８Ｖ钢摩擦副在室温干摩擦磨损条件下的摩擦系数及Ｓｉ３Ｎ４销的磨损系数，对陶瓷销的磨损面进行了ＳＥＭ显微形貌观察，Ｘ射线分析；并探讨了陶瓷销的磨损机理。研究结果表明：Ｓｉ３Ｎ４陶瓷的磨损以微区脆性断裂为主要机理。     

Si_3N_4／3Cr2W8V钢摩擦副滑动摩擦磨损性能

测定了销－盘式热压Ｓｉ３Ｎ４／３Ｃｒ２Ｗ８Ｖ钢摩擦副在室温干摩擦磨损条件下的的摩擦系数及Ｓｉ３Ｎ４销的磨损系数．对陶瓷销的磨损面进行了ＳＥＭ显微形貌观察、Ｘ射线分析；并探讨了陶瓷销的磨损机理．研究结果表明：Ｓｉ３Ｎ４陶瓷的磨损以微区脆性断裂为主要机理．     

电沉积Ni—P—Si3N4复合镀层的摩擦学特性

通过摩擦磨损试验、Ｘ射线衍射分析和电子探针分析等，研究电沉积Ｎｉ－Ｐ－Ｓｉ３Ｎ４复合镀层的摩擦磨损机理及其与结构和力学特性的关系。结果表明，在干摩擦条件下，复合镀层中的Ｓｉ３Ｎ４微粒能有效降低摩擦副之间的粘着脱落和犁沟效应；在油润滑条件下，复合镀层中Ｓｉ３Ｎ４微粒起到支承载荷作用，同时有利于边界润滑膜的形成，避免粘着磨损，复合镀层中Ｓｉ３Ｎ４微粒共析量的增加是提高复合镀层耐磨性的重要因素。     

Si3N4／铸铁在空气和水润滑下的摩擦学特性

在Ｍ－２００环－块磨损试验机上研究了空气、蒸馏水润滑条件下Ｓｉ３Ｎ４／灰铸铁、Ｓｉ３Ｎ４／低铬铸铁（ＤＴ）摩擦副的摩擦磨损，同时与Ｓｉ３Ｎ４／Ｔ８钢摩擦副进行对比，讨论了铸铁中石墨和碳化物对摩擦磨损的影响，结果表明：蒸溜水润滑下，Ｓｉ３Ｎ４／ＨＴ的摩擦系统非常小，Ｓｉ３Ｎ４与ＨＴ的磨损体积也最小，这是由摩擦时Ｓｉ３Ｎ４水解与形成石墨膜共同作用的；而空气润滑下，Ｓｉ３Ｎ４／ＨＴ的摩擦靡损就不具有这种     

蒸馏水润滑下Si3N4—白口铸铁摩擦面上表面膜的分析

在环－块磨损试验机上考察了蒸馏水润滑下Ｓｉ３Ｎ４分别与白口铸铁和碳钢（作对比用）配副的摩擦磨损特性．在ＳＥＭ下观察了白口铸铁磨面表面膜的形成过程，用ＸＰＳ、ＦＴＩＲ和ＸＲＤ分析了表面膜的成分、组成与结构，并对其形成机理进行了探讨．结果表明，Ｓｉ３Ｎ４在水润滑下摩擦时磨面上发生了氧化和水解反应：当Ｓｉ３Ｎ４与白口铸铁配副时，由于铸铁中碳化物的剥落而形成剥落坑，Ｓｉ３Ｎ４磨屑嵌入剥落坑并氧化和水解，其反应产物富集于剥落坑中，脱水聚合后形成硅胶，从而在磨面形成具有一定厚度和面积的含硅胶的表面膜，表面膜的形成保护了陶瓷和铸铁磨面，使其变得很光滑，从而使摩擦系数降至０．０２，并使系统磨损率几乎接近于零；当Ｓｉ３Ｎ４与碳纲配副时，由于碳钢没有能力富集Ｓｉ３Ｎ４的氧化和水解产物，故磨面不能形成有效的表面膜，所以其摩擦系数仍然较高，且系统磨损率亦较大     

针形α—Fe磁粉表面氧化处理研究

采用针形铁黄（α－ＦｅＯＯＨ）还原制备得到针形α－Ｆｅ金属磁粉，然后将其浸入甲苯中，慢速空气氧化制得样品．用透射电子显微镜（ＴＥＭ）观察其表面形貌，采用Ｘ－射线衍射（ＸＲＤ），Ｘ－射线光电子能谱（ＸＰＳ）分析其组成与结构．提出α－Ｆｅ粒子表面双层缺陷氧化膜（内层Ｆｅ３Ｏ４，外层γ－Ｆｅ２Ｏ３）的模型，用热处理的方法证实了它的存在，并得出有序氧化物结构可改善α－Ｆｅ磁粉稳定性的有益结果     

多晶3C-SiC薄层的淀积生长及结构性能分析

采用ＨＦＣＶＤ生长法,以较低生长温度,在Ｓｉ（１１１）衬底上淀积３Ｃ－ＳｉＣ（１１１）薄层。用ＸＲＤ、ＶＡＳＥ、ＸＰＳ等分析手段研究了薄层的结构、光学常数、组分及化学键等性能。ＸＲＤ显示薄层具有明显的择优取向特征。ＶＡＳＥ测量出薄层的折射率为２．６８６,光学常数随深度的变化曲线反映出薄层的多层结构。ＸＰＳ深度剖面曲线表明薄层中Ｓｉ／Ｃ原子比符合ＳｉＣ的理想化学计量比,其能谱证明Ｃ１ｓ与Ｓｉ２ｐ成键形成具有闪锌矿结构的３Ｃ－ＳｉＣ。     

工程陶瓷与石墨化铸铁配副的无润滑滑动磨损

在室温、不润滑的条件下，使用环块试验机进行了Ａｌ２Ｏ３，Ｓｉ３Ｎ４及ＺｒＯ２与球墨铸铁、灰铸铁配副的滑动摩擦磨损试验。发现陶瓷磨损试验。发现陶瓷磨损体积依次增加的顺序是Ａｌ２Ｏ３→ＺｒＯ２→Ｓｉ３Ｎ４；而铸铁无论与何种陶瓷配副，灰铸铁的磨损体积基本大于球墨铸铁。对磨损后陶瓷表面形貌及能谱分析，发现Ａｌ２Ｏ３表面有大量铸铁转移物，使Ａｌ２Ｏ３磨损量在三种陶瓷中为最小。     

F~-离子和Ti~(4+)离子在CaO-Al_2O_3-SiO_2系玻璃晶化时的作用

在ＣａＯ－Ａｌ２Ｏ３－ＳｉＯ２（ＣＡＳ）系玻璃中单独引入Ｆ－离子或Ｔｉ４＋离子,以及同时引入Ｆ－离子和Ｔｉ４＋离子,通过ＤＴＡ（差热分析）、ＸＲＤ（Ｘ－射线衍射）、Ｒａｍａｎ、ＸＰＳ（光电子能谱）和ＳＥＭ（扫描电镜）方法进行了研究。结果表明在ＣＡＳ系玻璃中一部分Ｆ－离子取代非桥氧离子处于玻璃网络内部,另一部分Ｆ－离子处于玻璃网络间隙,Ｆ－离子能促使ＣＡＳ系玻璃分相,在稍高于Ｔｇ的某一温度热处理时,ＣａＦ２晶体首先从玻璃中析出;Ｔｉ４＋离子对玻璃晶化影响不大,在稍高于Ｔｇ的某一温度热处理时,加Ｔｉ４＋离子和不加Ｔｉ４＋离子的玻璃首先析出的晶相均是钙长石（ＣａＡｌ２Ｓｉ２Ｏ８）;在ＣＡＳ系玻璃中同时引入Ｆ－离和Ｔｉ４＋离子时,在稍高于Ｔｇ的某一温度热处理后首先析出的晶体是ＣａＦ２和钙长石（ＣａＡｌ２Ｓｉ２Ｏ８）,Ｆ－离子和Ｔｉ４＋离子混合使用能更好地促进ＣＡＳ系玻璃的晶化。     

丙烯氨氧化催化剂物化性能研究：Ⅱ.催化剂失活前后的结构表征

采用ＸＲＤ，ＩＲ，Ｍｏｂａｕｅｒ ＥＳＲ，ＸＰＳ，ＳＥＭ和孔结构分析等分析测试手段，对比研究了新鲜，失活和再生三种丙烯氨氧化催化剂的体相结构和表面性质。结果表明，新鲜催化剂中各元素以Ｆｅ２（ＭｏＯ４），α－ＣｏＭｏＯ４，ＮｉＭｏＯ４，γ－Ｂｉ２Ｏ３．ＭｏＯ３，α－Ｂｉ２Ｏ３．３ＭｏＯ３，η－ＭｏＯ３，α－Ｂｉ２Ｏ３和β－Ｂｉ２Ｏ３形式存在２；失活催化剂中，部分Ｆｅ２（ＭｏＯ４）３转变为α－Ｆｅ－Ｍ     

氮化硅陶瓷的摩擦磨损特性

采用无压烧结和反应烧结两种方法制备氮化硅陶瓷，利用拴盘式摩擦实验机考察了氮化硅与ＧＣｒ１５球对磨的摩擦损特性，结果表明，虽然氮化硅具有较高的摩擦系数，但磨损率较低，特别是在水和油等介质存在的条件下，氮化硅具有低摩擦和磨损的特性。     

Corrosion-wear behavior of nanocrystalline Fe88Si12 alloy in acid and alkaline solutions

The corrosion?wear behavior of a nanocrystalline Fe88Si12 alloy disc coupled with a Si3N4 ball was investigated in acid (pH 3) and alkaline (pH 9) aqueous solutions. The dry wear was also measured for reference. The average friction coefficient of Fe88Si12 alloy in the pH 9 solution was approximately 0.2, which was lower than those observed for Fe88Si12 alloy in the pH 3 solution and in the case of dry wear. The fluctuation of the friction coefficient of samples subjected to the pH 9 solution also showed similar characteristics. The wear rate in the pH 9 solution slightly increased with increasing applied load. The wear rate was approximately one order of magnitude less than that in the pH 3 solution and was far lower than that in the case of dry wear, especially at high applied load. The wear traces of Fe88Si12 alloy under dif-ferent wear conditions were examined and analyzed by scanning electron microscopy, energy-dispersive X-ray spectroscopy, and X-ray photoelectron spectroscopy. The results indicated that the tribo-chemical reactions that involve oxidation of the worn surface and hydrolysis of the Si3N4 ball in the acid solution were restricted in the pH 9 aqueous solution. Thus, water lubrication can effectively improve the wear resistance of nanocrystalline Fe88Si12 alloy in the pH 9 aqueous solution.     

月桂酸修饰微/纳米二氧化钛及摩擦学性能研究

利用月桂酸对金红石型微/纳米Ti O2进行了有机表面改性.粒子采用了红外光谱(IR)、热分析(TG-DTA)、扫描电镜(SEM)等对表面改性前后的微/纳米Ti O2结构进行了表征.红外光谱、热分析表明月桂酸是以化学键合的方式结合在微/纳米Ti O2表面形成了包覆层.在四球摩擦磨损试验机上考察了产品作为添加剂在石蜡基础油中的抗磨减磨性能.试验结果表明,修饰后的微/纳米粒子具有优良的抗磨、减摩能力,同时分析了减摩机理.     

二烷基二硫代磷酸锌在菜籽油中的摩擦学机理分析

通过四球机磨损试验和对试球磨损表面进行的X射线光电子能谱分析，研究了二烷基二硫代磷酸锌（Zinc dialkyl-dithiophosphate，简称ZDDP）对菜籽油（RO）摩擦学性能的影响、磨斑表面主要元素的化学状态，并探讨了ZDDP在RO中摩擦作用机理。研究结果表明，ZDDP在RO中的最佳添加量为2．0％；ZDDP可以提高RO的极压性和抗磨性；ZDDP在RO中摩擦作用机理为ZDDP热分解，分解的产物在摩擦过程中发生摩擦化学反应，形成了由磷酸盐、硫酸盐、摩擦聚合物等组成的聚合膜；ZDDP还通过对摩擦副表面的改性，摩擦生成的单质态Zn原子沉积在金属表面，形成铁锌固溶体，增强了摩擦表面的抗磨能力。     

油酸修饰铜纳米颗粒的摩擦学性能

在无水乙醇-十六烷基三甲基溴化铵(CTAB)水溶液混合体系中使用液相还原法制备了油酸修饰铜纳米颗粒.使用透射电子显微镜(TEM)对其形貌进行了表征,结果表明:油酸修饰铜纳米颗粒的粒径大小约为20 nm.用FALEX-6型四球试验机考察了其作为润滑油添加剂在液体石蜡中的抗磨减摩性能,结果表明:当添加纳米颗粒的质量分数为0.2%时就能明显降低摩擦系数,当添加纳米颗粒的质量分数为0.4%时摩擦系数下降至最低值,但当进一步增加浓度至1.0%时,摩擦系数开始有较大的增加趋势.用扫描电子显微镜(SEM)对摩擦表面进行观察,结果表明:当添加纳米颗粒的质量分数为0.4%时磨斑直径(WSD)为最小值,抗磨效果最好.     

微晶二氧化硅粉体添加剂的抗磨减摩作用

为研究微晶SiO2粉体添加剂的抗磨减摩作用,采用微晶SiO2矿物粉体作为润滑油添加剂,利用AMSLER摩擦磨损试验机研究45#钢摩擦副在添加剂润滑油润滑下的摩擦学特性.磨损后钢环表面的形貌和成分通过扫描电子显微镜和X射线光电子能谱仪进行分析.结果显示:以微晶SiO2粉体为添加剂润滑时在摩擦副表面形成一层陶瓷保护层.相比基础油,在微晶SiO2添加剂润滑油润滑条件下,摩擦副的接触状态由金属之间的摩擦磨损转化为自修复膜层之间的摩擦磨损.添加剂润滑油较基础油润滑条件下的摩擦系数大.摩擦磨损过程中自修复膜层的形成,隔离了金属摩擦副的直接接触,降低了试样磨损失重,具有良好的耐磨性能.     

MOSi2-淬火45#钢在油润滑下的摩擦学特性

利用M-200型磨损试验机考察了MoSi2-淬火45针仪分析讨论其磨损机理.结果表明:润滑油明显改善了MoSi2材料的摩擦学性能;MoSi2与淬火45#钢对摩在120～150 N载荷范围内表现出较好的摩擦磨损综合性能;其磨损机制主要表现为疲劳磨损、磨粒磨损和轻微粘着磨损.图4,参10.