低碳微合金钢在过冷奥氏体亚稳定区的转变

通过对低碳Mo-Cu-Nb-B系微合金钢进行连续冷却和等温实验,发现低碳Mo-Cu-Nb-B系微合金钢在过冷奥氏体亚稳定区等温,能发生针状铁素体转变.非再结晶区变形奥氏体连续冷却时虽然能得到各类低碳贝氏体组织,但各类组织特别是针状铁素体的份额却不能有效控制.通过分阶段冷却,可以控制得到针状铁素体和板条贝氏复相组织.利用针状组织分割原奥氏体晶粒能细化组织,达到优化高强度低碳微合金钢的力学性能目的.     

含B钒微合金钢的连续冷却相变行为

为开发一种新的低成本高性能含B钒微合金钢和建立其TMCP生产工艺,用MMS-200热力模拟试验机研究了实验钢在连续冷却条件下的相变规律,绘制出实验钢的静态CCT曲线和动态CCT曲线.结果表明:微量的B提高了钒微合金钢过冷奥氏体稳定性,促进了针状铁素体形成,在比较宽的冷却速度范围内能得到贝氏体组织;未变形钢相比于变形钢,在更低的冷却速度甚至0.5℃/s的冷却速度下能得到大部分的贝氏体组织,但两者在5℃/s以上的冷却速度下都得到全部贝氏体组织;变形降低了奥氏体稳定性,促进铁素体转变,含硼钢铁素体转变存在的冷速升高到2℃/s,不含硼钢的其冷速升高到15℃/s;钒微合金钢中B有利于获得高强度的贝氏体组织,冷速5℃/s以上时相变后含硼钢的硬度都高于变形及未变形不含硼钢的硬度.     

弛豫过程对贝氏体组织细化的定量研究

利用热模拟、金相显微术、结合定量统计和TEM技术，研究了微合金钢奥氏体区变形后弛豫不同时间的组织演化及析出情况。实验结果表明：经弛豫工艺处理后，贝氏体、马氏体复合组织得到了有效细化，在850℃变形后等温弛豫60～200s时，细化效果最佳。与此同时，应变诱导析出相亦能有效地钉扎位错，析出相的尺寸小于10nm。     

室温变形对低碳钢中析出物的影响

以一种低碳微合金钢为对象,通过热模拟实验研究了室温变形对最终组织中析出物的分布、尺寸以及成分等的影响.实验用试样的原始组织为铁素体、珠光体加少量贝氏体,采用一种快速加热短时保温的工艺方法探讨室温变形的作用.研究结果表明:室温变形通过影响试样内部的位错密度,不仅有效增加了析出物的弥散程度,还能够在一定程度上降低析出物的尺寸;从试样的组织形貌来看,采用该工艺,室温变形在维持等轴晶的前提下还有效减小了晶粒尺寸;另外,与未施加室温变形的试样比较发现,室温变形能够在一定程度上促进溶解度较大的微合金元素V的析出.     

高碳镀锌钢丝的组织演变及对扭转性能的影响

针对钢丝镀锌后扭转值波动很大的实际问题，本文系统表征分析了钢丝拉拔—热镀锌—扭转生产过程中的微观组织演化.研究结果表明：钢丝的微观组织在生产过程中会发生较大的变化.拉拔和扭转过程中索氏体片会发生扭曲变形使得片层间距减小，渗碳体片发生破碎，小尺寸的渗碳体颗粒发生溶解，钢丝中的位错密度会显著增加；而热镀锌过程使得小尺寸的渗碳体颗粒发生溶解，同时能消除钢丝内部的应力，使得位错密度降低.渗碳体片破碎、渗碳体颗粒溶解、索氏体片层间距、位错密度等因素综合作用，导致了钢丝扭转过程中的性能差异.     

Nb对低碳微合金钢连续冷却相变行为的影响

结合膨胀法和金相观察绘制了无Nb和添加质量分数0042%Nb的实验钢的动态CCT曲线,阐明了Nb对低碳微合金钢相变行为和相变组织的影响规律.结果表明,添加Nb可显著细化铁素体晶粒,抑制铁素体形成,促进贝氏体形成,使CCT曲线移向右下方,缩小铁素体和珠光体相变区,显著扩大贝氏体相变区.此外,添加Nb可显著增强细晶强化、析出强化和相变强化效果,使实验钢维氏硬度显著提高.     

贝氏体组织细化的RPC工艺参数优化

利用热模拟技术研究了不同弛豫-析出-控制相变(RPC)工艺对含Nb,Ti低碳微合金钢最终组织的影响,结合半定量金相统计、电镜观察及EBSD技术分析了弛豫过程晶体缺陷组态与析出变化及相互作用规律.结果表明,经RPC工艺处理后,试验钢组织得到了有效的细化,主要为超细的贝氏体马氏体复合组织,当变形量增加,组织细化效果较好,出现最佳效果的弛豫时间缩短.终轧温度升高,细化效果减弱.从综合效果来看,当工艺参数的选取可以使弛豫析出速度与位错多边形化演变速度相匹配时,细化效果最佳.     

低焊接裂纹敏感性钢焊接接头组织及微观力学性能

采用埋弧自动焊接方法焊接高强度低焊接裂纹敏感性钢板,并对其焊接接头进行显微组织观察、维氏显微硬度和纳米压痕检测.结果表明:粗晶热影响区的显微组织以粗大粒状贝氏体为主,由于该区的精细结构中含有大量纳米级析出相,且位错密度较高,使得该区具有较高的维氏显微硬度和纳米硬度值;焊缝区和细晶热影响区的主要显微组织分别为针状铁素体+...     

亚快速凝固高强度微合金钢再加热和冷却过程中的奥氏体生长和贝氏体转变动力学研究

首先,采用薄带连铸热模拟技术制备了具有亚快速凝固特征的高强微合金钢样品。然后利用共聚焦激光扫描显微镜(CLSM)原位观察了样品在再加热和冷却过程中奥氏体晶粒等温长大过程和后续的贝氏体转变过程。结果表明,亚快速凝固微合金钢中的奥氏体长大过程与再加热温度关系紧密;在高温区(1000℃以上)和低温区(1000℃以下),奥氏体晶粒生长活化能分别为538.0 kJ/mol和693.2 kJ/mol。并据此建立了基于亚快速凝固微合金钢的奥氏体等温长大动力学模型,经过验证,该模型能很好地预测奥氏体晶粒在保温过程的尺寸变化规律。研究还发现,在较低温度下保温时生成的细小且弥散的析出相能够有效地阻碍奥氏体晶粒生长。此外,还原位观察了不同保温温度下（保温时间1800s）的亚快速凝固微合金钢在冷却过程中的贝氏体相变行为。研究了不同形核位置和不同原奥晶粒尺寸对贝氏体板条生长的影响。结果表明,贝氏体板条的生长速率不仅与成核位置有关,而且与原奥尺寸密切相关。     

含Cu-Cr微合金钢650℃回火时第二相析出强化的研究

将含Cu-Cr微合金钢 930℃保温 30min淬火至室温，随后 650℃回火 10min~10h。利用光学显微镜（OM）和透射电子显微镜（TEM）研究不同回火时间条件下，样品中组织演变和第二相析出行为。结果表明：回火过程中组织从马氏体和贝氏体逐渐向针状铁素体和多边形铁素体演变；硬度变化曲线上出现2个二次硬化峰值，分别为回火1h和4h是的硬化峰，前者是V和Mo的碳化物析出强化结果，后者是由富Cu相的析出强化所致，V和Mo的碳化物强化产生的硬度值增量大于富Cu相；Cr的碳化物在回火过程中析出长大速度较快，析出强化能力较弱。     

等温温度对超细贝氏体钢组织演变规律的影响

通过热膨胀试验研究实验钢的等温转变动力学,采用盐浴等温淬火工艺制备超细贝氏体组织,利用扫描电镜、透射电镜和X射线衍射仪定量分析工艺参数对微观组织结构的影响.结果显示:实验钢室温组织由大量超细板条状贝氏体铁素体和板条间分布的薄膜状奥氏体的复相组织构成,210℃等温淬火得到的贝氏体板条间距细化到约60 nm,硬度约为HBW610;实验钢的最终组织特征取决于发生贝氏体转变的等温温度和等温时间,等温温度越低时贝氏体转变完成需要的等温时间越长.     

590MPa级热轧V-N高强车轮钢组织性能控制

对一种低成本V-N微合金化钢进行了控轧控冷实验,探讨了相变机理与析出行为,并系统地研究了其综合力学性能.结果表明,显微组织为多边形铁素体、粒状贝氏体及少量的针状铁素体,纳米尺度V(C,N)析出质点弥散地分布于铁素体或贝氏体铁素体基体内部.抗拉强度615MPa实验钢具有优良的断后延伸率,冷弯性能合格,扩孔率达到95%,满足轮辐用钢的加工要求,低温冲击性能良好.细晶强化、位错强化、析出强化、相变强化为主要强化机制.     

表面温度波动对微合金钢连铸板坯热塑性的影响

由于铸坯表面与二冷辊列夹持辊发生的间断式接触传热,其表面温度存在一定程度的上下波动. 基于J55微合金钢,考虑温度波动的影响,研究了钢在不同热状态下的热塑性. 结果表明,高于850℃时温度波动制度下测得的断面收缩率低于常规恒温制度下的测量值,而等于或低于850℃时情况相反. 分析了两种不同温度制度下测试结果的差异,认为对于微合金钢,存在着略高于所测钢种Ae3温度的某一分界温度,高于该温度时恒温制度下测得的塑性值相比波动制度下塑性值偏高,而低于该温度时则偏低. 这一认识有助于更加合理地制定实际连铸过程的矫直温度.     

等温温度和时间对超级贝氏体钢Fe-0.40C-2.2Mn-1.5Si相变和组织性能的影响

以超级贝氏体钢Fe-0.40C-2.2Mn-1.5Si为对象,通过热模拟试验、扫描电镜、X射线衍射分析和拉伸试验等方法,研究等温转变温度和保温时间对试验钢的贝氏体相变、微观组织和力学性能的影响。结果表明,随着等温转变温度的降低,钢的显微组织中贝氏体形貌从颗粒状贝氏体转变为板条状贝氏体,其强度逐渐提高,但伸长率和强塑积先增大后减小;随着保温时间的增加,钢的抗拉强度逐渐降低,而伸长率和强塑积逐渐增大,因此可通过适当延长相变时间来改善钢的综合力学性能;在350℃下保温90min时,试验钢显微组织中残余奥氏体体积分数最大,且具有最大强塑积。     

In situ measured growth rates of bainite plates in an Fe-C-Mn-Si superbainitic steel

The growth rates of bainite plates in an Fe-C-Mn-Si superbainitie steel were investigated by in situ observation. The lengthening rates of ferrite bainite during both cooling and isothermal holding processes were observed and the growth rates of bainite plates nucleating at grain boundaries, within grains and on preformed bainite were measured. It is indicated that the lengthening rates of bainite plates during the cooling and isothermal processes were different, and that the growth rates of bainite plates nucleating at different types of sites also demon- strated diversity. The bainite plates initiating at [vain boundaries during cooling grew the fastest, while the plates nucleating on preformed bainite did the slowest. However, the growth rate of the bainite plates nucleating at grain boundaries during isothermal transformation de- creased the most, whereas the bainite plates initiating within grains grew the fastest. In addition, the growth rate of ferrite bainite in the study supported the diffusion transformation mechanism of bainite from the viewooint of ~rowth rate.     

Analysis of the formation conditions and characteristics of interphase and random vanadium precipitation in a low-carbon steel during isothermal heat treatment

The characteristics of nanosized precipitates in steels depend on the heat-treatment parameters. The effects of characteristics of vanadium precipitates formed during isothermal heat treatment on the hardness of the ferrite matrix in low-carbon vanadium-alloyed steel were investigated through analysis of transmission electron microscopy images and microhardness measurements. The results show that, during isothermal holding in the temperature range from 675 to 750℃, only interphase precipitation occurs, whereas only random precipitation occurs in the ferrite matrix during holding at 600℃. Furthermore, during isothermal heat treatment between 600 and 675℃, both random and interphase precipitates occurred in the ferrite. Nanoscale vanadium carbides with different atomic ratios of vanadium (V) and carbon (C) were the dominant precipitates in the random and interphase precipitates. The sizes of random precipitation carbides were smaller than those of interphase ones. Also, the sample isothermally heat treated at 650℃ for 900 s exhibited a higher hardness with a narrower hardness distribution.     

不同工艺下Nb-Ti微合金钢组织演变和析出行为

利用Gleeble 3800热模拟实验机、透射电镜和纳米压痕仪器等研究了终冷温度和保温时间对Nb-Ti微合金钢组织、析出行为的影响规律.结果表明:随终冷温度的升高,铁素体晶粒尺寸增大,珠光体增多,贝氏体逐渐减少,维氏显微硬度随终冷温度先升高后降低,当终冷温度为640℃时,实验钢的维氏显微硬度最大;当终冷温度为640℃时,试样中存在排列规则的相间析出和弥散分布的随机析出两种析出形式.当保温时间为0s时,析出物以相间析出和弥散析出为主;当保温时间为100s时,析出物以弥散析出为主.随保温时间增加,实验钢的纳米硬度降低了140MPa.     

In situ observations of austenite grain growth in Fe-C-Mn-Si super bainitic steel

In situ observations of austenite grain growth in Fe-C-Mn-Si super bainitic steel were conducted on a high-temperature laser scanning confocal microscope during continuous heating and subsequent isothermal holding at 850, 1000, and 1100℃ for 30 min. A grain growth model was proposed based on experimental results. It is indicated that the austenite grain size increases with austenitizing temperature and holding time. When the austenitizing temperature is above 1100℃, the austenite grains grow rapidly, and abnormal austenite grains occur. In addition, the effect of heating rate on austenite grain growth was investigated, and the relation between austenite grains and bainite morphology after bainitic transformations was also discussed.     

Nb-Ti微合金化热轧多相钢的组织和性能

通过两阶段控轧和随后的三段冷却,获得了14mm厚的Nb-Ti微合金化热轧多相钢板.利用光学显微镜、扫描电镜、透射电镜、X射线衍射(XRD)、电子背散射衍射(EBSD)和力学性能测试等手段对其组织和性能进行了研究.结果表明,试验钢的显微组织由铁素体、贝氏体和少量马氏体组成;其平均屈服强度为518MPa,抗拉强度为616MPa,延伸率高达41%;组织中大量的铁素体大角度晶界、近似等轴状铁素体晶粒和较小尺寸贝氏体束的存在,大大提高了试验钢的塑性;铁素体和贝氏体组织的细化,细小的(Nb,Ti)C粒子以及铁素体晶粒和贝氏体板条内的位错提高了试验钢的强度.