银纳米粒子与血清白蛋白相互作用的滞后效应

用圆二色光谱,紫外-可见光谱研究银纳米粒子与血清白蛋白的相互作用及其相关效应.拟合计算圆二色光谱数据发现,与银纳米粒子作用后的血清白蛋白中α-螺旋含量减少,而α-折叠、转角和无规卷曲等结构含量增加,其构象在作用后变得更为松散和伸展.通过时间扫描吸收光谱跟踪研究发现,在血清白蛋白与银纳米粒子相互作用的过程中,银纳米粒子的包覆与聚集、血清白蛋白的构象变化具有双重滞后效应.     

纳米Al2O3/PVAc复合材料的制备与表征

用硝酸铝和碳酸铵为原料,以聚乙二醇为分散剂,采用溶胶-凝胶法制备了纳米Al2O3溶胶.用液-液混合分散法将制得的纳米Al2O3溶胶分散于聚醋酸乙烯酯(PVAc)的丙酮溶液中,得到无色透明的纳米Al2O3/PVAc复合溶胶,将溶胶刮涂制膜,得无色透明的Al2O3/PVAc复合膜.用透射电子显微镜和拉曼光谱对复合材料进行了表征.激光粒度分析仪分析表明,Al2O3在PVAc粒径在30～35 nm范围内,平均密度31.2 nm、体积平均27.5 nm、数均25.3 nm .Zeta电位值为-42.5 mV.并对Al2O3/PVAc复合溶胶进行紫外吸收测试,结果显示,与纯PVAc溶液相比,最大吸收峰蓝移10.4 nm,且吸光度增加2.3倍.     

壳聚糖—纳米金自组装葡萄糖生物传感器的研究

利用壳聚糖与纳米金构建一种新型的葡萄糖生物传感器。探究不同浓度的葡萄糖溶液、p H及温度对传感器响应电流的影响。结果表明,此传感器在温度为35.0℃,p H=7.00,葡萄糖质量浓度为0.018~25.7 mg/L范围内有良好的线性,线性I=4.135 6 m+91.787μA,R2=0.997 9,检出限为0.001 2 mg/L。该传感器具有制备简单、方法简便、灵敏度高,能快速检测等优点。     

Structural,morphological, and optical properties of tin(Ⅳ) oxide nanoparticles synthesized using Camellia sinensis extract: a green approach

Tin oxide (SnO2) nanoparticles were cost-effectively synthesized using nontoxic chemicals and green tea (Camellia sinensis) extract via a green synthesis method.The structural properties of the obtained nanoparticles were studied using X-ray diffraction,which indicated that the crystallite size was less than 20 nm.The particle size and morphology of the nanoparticles were analyzed using scanning electron microscopy and transmission electron microscopy.The morphological analysis revealed agglomerated spherical nanoparticles with sizes varying from 5 to 30 nm.The optical properties of the nanoparticles' band gap were characterized using diffuse reflectance spectroscopy.The band gap was found to decrease with increasing annealing temperature.The O vacancy defects were analyzed using photoluminescence spectroscopy.The increase in the crystallite size,decreasing band gap,and the increasing intensities of the UV and visible emission peaks indicated that the green-synthesized SnO2 may play future important roles in catalysis and optoelectronic devices.     

Optical sensing of explosives in wastewater by competitive complexation

A facile strategy for optical sensing of explosives with the assistance of 1,3,5-Triazine-2,4,6-triamine(MEL) in aqueous solution is proposed. Upon exposure to MEL, the electron-sufficient amino group in MEL was prone to form complexes with electron-deficient nitro group in explosives. The interaction could be tuned by the amount of MEL to fully consumed nitro-contained explosives dissolved in wastewater, thus prevented the gold nanoparticles(GNPs) from combining with MEL. In comparison with common detection method, the dose-response curve procedure reported here was in good linear relationship from 0 μM to 80 μM with good correlation factor(R~2= 0.9871), and was satisfactorily agreed with the proposed theoretical model. The detection limit(Lo D) was1.1 μM by spectrometer, 3.0 μM visualized by naked eyes and 21.3 nM by calculation. The procedure described in this study could be finished within a few minutes and showed its effectiveness in explosive detection upright on the gold surface in real wastewater, making this proposed method a powerful tool in several sensing platforms.     

Influences of ultrasonic irradiation on the morphology and structure of nanoporous Co nanoparticles during chemical dealloying

The Co-61.8 wt% Al nanoparticles of 45 nm were prepared by hydrogen plasma-metal reaction (HPMR) method. The nanoparticles display core shell structure with Al13Co4 and CoAl core and aluminum oxide shell (about 2 nm). Under ultrasonic irradiation, nanoporous fcc-Co nanoparticles were produced successfully by chemically dealloying the Co-Al nanoparticles at room temperature, whereas, without ultrasonic irradiation CoAl phase could hardly react with sodium hydroxide solution. At 323 K the Co-Al nanoparticles could be dealloyed to fcc-Co and hcp-Co phases even without ultrasonic irradiation. The surface area of the dealloyed nanoparticles under ultrasonic irradiation was larger than that of the dealloyed sample without ultrasonic irradiation at the same temperature. It is believed that the microjet and shock-wave induced by ultrasonic irradiation give rise to particles size reduction, interparticle collision and surface cleaning, and accelerate the dealloying process and the phase transformation.     

超声乳化法制备纳米Fe3O4磁性颗粒及壳聚糖表面改性

采用超声乳化法制备纳米Fe3O4磁性颗粒,以壳聚糖作为表面活性剂,制备具有生物亲和性的水基Fe3O4磁流体.研究了Fe2+/Fe3+摩尔比、超声时间和表面活性剂用量对磁流体性能的影响.结果表明:当Fe2+/Fe3+摩尔比为1:1·5,滴加氨水时反应温度为70℃时,可制备理想纳米Fe3O4磁性颗粒;超声时间为7·5min左右,质量分数1%的壳聚糖溶液体积占FeO溶液总体积的50%时,有利于壳聚糖分子的包覆,使磁流体具有较高的比饱和磁化强度及稳定性.     

制备特定尺寸的纳米金颗粒方法及性能表征

通过化学还原法制备出不同粒径的纳米金颗粒。利用紫外可见分光光度计和透射电子显微镜对纳米金颗粒的形貌及尺寸进行表征。讨论了还原剂种类、还原剂用量、试剂加入顺序、反应温度等因素对纳米金颗粒稳定性、粒径、形貌和分散性的影响。结果表明：Na3C6H5O7为还原剂制得纳米金颗粒粒径在15-20 nm之间,NaBH4为还原剂制得的...     

CeO2纳米颗粒对A549细胞的保护作用

探讨了CeO2纳米颗粒对体外培养的人肺腺癌细胞A549的生物效应.使用扫描电子显微镜(SEM)对CeO2纳米颗粒进行了表征,采用噻唑蓝比色法测定了不同质量浓度CeO2纳米颗粒悬液对A549细胞活性的影响,对其抗氧化能力进行了检测,并且测定了30 nm CeO2作用24 h后细胞中的超氧化物歧化酶(SOD)和谷胱甘肽(G...     

直写纳米金墨水制备纸基柔性金属图形

将A4打印纸洗净、烘干,用硅氧偶联剂改性,在改性后的纸上用中性笔书写纳米金墨水图形,然后将其放入化学镀溶液中化学镀铜,得到纸基柔性金属图形.X射线衍射分析图谱(XRD)证实了纸张有金属铜镀上.扫描电子显微镜照片(SEM)显示金属铜图形有清晰的界面.X射线光电子能谱分析(XPS)显示改性后的纸的N和Si元素的含量都大幅上升,傅利叶变换红外测试(FTIR)图谱显示硅氧偶联剂改性后,纸的官能团还都存在,说明改性工艺对纸基材未构成破坏.用Scotch胶带方法测试金属和纸张粘附性,发现纸张与金属结合牢固无法分开.还探讨了书写次数与金属图形导电性的关系,发现手写必须达到一定次数才能成功镀上导电性较好的金属图形.