CeO2/ZnO纳米复合粉体的制备及抗紫外线性能研究

以Ce（NO3）3·6H2O和（CH3COO）2 Zn·2H2O为原料,采用超声—沉淀法制备了纳米CeO2,ZnO粉体,CeO2/ZnO纳米复合粉体。研究了不同的铈锌摩尔对复合粉体紫外吸收性能的影响、通过正交实验确定了制备CeO2/ZnO纳米复合粉体的最佳工艺条件,并采用XRD、IR、TG-DTA、UV-Vis以及激光粒度等测试手段对复合粉体进行了表征。结果表明,在最佳工艺条件下制得的CeO2/ZnO纳米复合粉体,属于原子级混合,其紫外吸收性能优于单一粉体。     

微片结构Gd3GaO6：Eu3＋荧光粉的合成及其发光特性

以柠檬酸为燃烧剂,乙二醇为分散剂采用燃烧固相法制备Gd3GaO6：Eu3＋新型荧光粉．利用X线粉末衍射、扫描电镜和荧光光谱分别对热处理后产物的结构、形貌和发光性能进行表征．结果表明：700℃燃烧10min并在1200℃热处理5h即可获得产物Gd3GaO6：Eu3＋,其空间点群为P21（4）,形貌为微米片结构;产物的特征发射峰来自于Eu3＋的5D0→7FJ（J=1,2,3,4）跃迁,其中在616nm处发射最强,为Eu3＋的。5D0→7F2的特征红色发射;宽激发带主要来自于O2-→Eu3＋的荷移跃迁吸收．该产物是一种性能优良的红色荧光粉．     

纳米Bi2O3粉体的制备与性质研究

本文采用均匀沉淀法合成了纳米Bi2O3粉体材料,应用TEM、XRD、XPS对其形貌和结构进行了表征。通过实验研究确定纳米Bi2O3粉体最佳工艺条件：Bi^3＋溶液的浓度为0．125mol·L^-1;DBS作为添加剂,其最佳浓度为0．023mol·L^-1;最佳焙烧温度750℃。     

花状Sr3Al2O6：Eu^2＋晶体的干燥方式与发光性能

为研究稀土发光纳米晶的微观结构和形貌对发光性能的影响,用凝胶-微波干燥法和凝胶-烘箱干燥法制备了花状形貌的Sr3Al2O6晶体．研究了微波干燥和烘箱干燥两种不同的干燥方式对溶胶-凝胶法制备的Sr3Al2O6：Eu^2＋发光粉体粒径、形貌、团聚程度、干燥时间及发光性能等的影响,结果表明采用微波干燥不仅可以大大缩短干燥所需时间,而且有利于减弱Sr3Al2O6：Eu^2＋发光粉料的团聚和团聚程度,制得了颗粒分散均匀、团聚程度低、发光强度高的Sr3Al2O6：Eu^2＋花状形貌粉体．研究了Sr3Al2O6：Eu^2＋发光粉体的新型形貌对发光性能的影响,微波干燥法制备的均匀分散的花状形貌发光粉体发光强度高,余辉时间长达20min．     

醇水法制备纳米氧化镍电极的结构与电化学性能

采用醇水法制备了纳米氧化镍粉体材料并分析了其粉体形成过程,重点研究了热处理温度对氧化镍粉体的相组成、形态以及氧化镍电极电化学性能的影响。结果表明,氧化镍粉体由前驱体Ni2(OH)2CO3·xH2O在270℃附近分解产生;热处理温度对合成粉体的结晶度和比表面积具有显著影响,而粉体的结晶度和比表面积又是影响氧化镍电极电化学性能的重要因素,其中,粉体结晶度的作用占主导地位。当氧化镍粉体热处理温度为250℃时,所制氧化镍电极具有优异的电化学性能,在测试电流密度为5mA/cm2的条件下,其比电容达到1180F/g。     

尖晶石LiMn_2O_4纳米粉体的制备及其电化学性能

采用溶胶-凝胶并结合热处理工艺制备纳米LiMn2O4粉体,利用热重-差热分析,X射线衍射,透射电镜,循环伏安,充放电测试等方法对前驱体的热分解行为、粉体的结构、形貌及电化学性质进行了表征.结果表明:直接以聚丙烯酸(PAA)为螯合剂合成了稳定的溶胶和凝胶, PAA与金属离子摩尔比为0.3:1时,获得凝胶在烧结过程中产生的燃烧热促进了尖晶石LiMn2O4的形成,避免杂相Mn2O3的产生.随着烧结温度的升高,LiMn2O4颗粒粒径逐渐增大,结晶度提高,晶体生长更加完整.其中,750°C烧结8 h获得了由纳米粒子构成、分布均匀、形貌规整、结构稳定的LiMn2O4粉体,首次放电比容量可达135 mAh/g,20次循环后比容量仍有124 mAh/g,具有良好的充放电循环性能以及较高的充放电效率.     

以尿素为沉淀剂制备纳米λ-Al2O3粉体

以尿素、硝酸铝为原料，在回流条件下采用均匀沉淀法制备了纳米级的λ-Al2O3粉体．以XRD、TEM、傅立叶红外吸收光谱(FTIR)等测试手段，对纳米级Al2O3的粉体结构和形貌进行了表征及研究．结果表明，当前驱体加热到1000℃可得到10nm左右的λ-Al2O3，并对均匀沉淀法形成纳米氧化铝的机理进行了探讨．     

纳米Bi_2O_3粉体的制备与性质研究

本文采用均匀沉淀法合成了纳米Bi2O3粉体材料,应用TEM、XRD、XPS对其形貌和结构进行了表征。通过实验研究确定纳米Bi2O3粉体最佳工艺条件:Bi3+溶液的浓度为0.125 mol.L-1;DBS作为添加剂,其最佳浓度为0.023 mol.L-1;最佳焙烧温度750℃。     

纳米(CeO_2)_(0.86)(Sm_2O_3)_(0.14)的形貌控制与表征

以Ce(NO3)3·6H2O和(NH4)2CO3为沉淀源,搀杂稀土氧化物Sm2O2,利用柠檬酸作为络合剂和分散剂,制备出纳米(CeO2)0.86(Sm2O3)0.14.并采用TEM、XRD等方法对其热分解所得纳米(CeO2)0.86(Sm2O3)0.14的形貌及结晶性等进行了表征.结果表明:随着柠檬酸加入量的增加,焙烧生成的纳米(CeO2)0.86 (Sm2O3)0.14颗粒的形貌从纳米线向类球形颗粒变化,所得(CeO2)0.86(Sm2O3)0.14为立方萤石结构,且随焙烧温度的提高,晶化程度增大.     

溶剂热辅助法控制合成ZnO纳米结构及其光学性质研究

用溶剂热方法合成了znC2O4·2H2O纳米棒的中间体,在不同热处理条件下获得ZnO的玉米棒、颗粒片、链结构等不同形貌,从而实现对ZnO的形貌进行控制．室温下．ZnO在250nm的紫外光激发下,在400nm处出现一个近带发射峰．这种发光峰属于ZnO中的缺陷发光．对ZnO的形成机理做出了热重和红外分析,并对ZnO的形成机理提出了一种可能的解释．溶剂热方法获得的ZnC2O4·2H2O纳米棒在高温下分解成ZnO．在退火过程中,中间体会先形成空洞,然后形成带颗粒的纳米棒;但是这种纳米棒开始会粘接在一起形成片状,然后纳米片会卷曲成玉米棒结构,最终玉米棒散掉,形成纳米链．     

Ba 掺杂和烧结温度对 Sr4V2O9：Eu3＋（5％），Ba2＋（x％）光学性质的影响

采用水热和烧结的方法制备系列Sr4 V2 O9：Eu3＋（5％）,Ba2＋（x％）（x＝0,5）粉末样品。用X射线衍射和荧光分光光度计对样品的结构和光学性质进行了研究。研究结果表明Ba掺杂能提高样品的发光强度,而烧结却降低发光强度。随着烧结温度的增加,Eu离子周围的晶格畸变,导致 Eu离子的磁偶极跳跃减弱并消失。     

KSrGd(PO_4)_2︰Eu~(2+),Mn~(2+)红色荧光粉的合成和发光性能

采用改进的高温固相法合成了Eu2+/Mn2+掺杂的KSrGd(PO4)2荧光粉.用X射线粉晶衍射仪和荧光光谱仪对样品进行了表征.结果表明:Eu2+离子和Mn2+离子成功掺入了KSrGd(PO4)2晶格中,基质晶体结构未见明显变化.Eu2+的发射峰位于522 nm,Mn2+的发射峰位于618 nm.通过Eu2+和Mn2+之间的能量传递,KSrGd(PO4)2荧光粉在紫外光激发下发出明亮的红光.     

Structural,morphological, and optical properties of tin(Ⅳ) oxide nanoparticles synthesized using Camellia sinensis extract: a green approach

Tin oxide (SnO2) nanoparticles were cost-effectively synthesized using nontoxic chemicals and green tea (Camellia sinensis) extract via a green synthesis method.The structural properties of the obtained nanoparticles were studied using X-ray diffraction,which indicated that the crystallite size was less than 20 nm.The particle size and morphology of the nanoparticles were analyzed using scanning electron microscopy and transmission electron microscopy.The morphological analysis revealed agglomerated spherical nanoparticles with sizes varying from 5 to 30 nm.The optical properties of the nanoparticles' band gap were characterized using diffuse reflectance spectroscopy.The band gap was found to decrease with increasing annealing temperature.The O vacancy defects were analyzed using photoluminescence spectroscopy.The increase in the crystallite size,decreasing band gap,and the increasing intensities of the UV and visible emission peaks indicated that the green-synthesized SnO2 may play future important roles in catalysis and optoelectronic devices.     

Structural,morphological,and optical properties of tin(Ⅳ) oxide nanoparticles synthesized using Camellia sinensis extract: a green approach

Tin oxide(SnO_2) nanoparticles were cost-effectively synthesized using nontoxic chemicals and green tea(Camellia sinensis) extract via a green synthesis method. The structural properties of the obtained nanoparticles were studied using X-ray diffraction, which indicated that the crystallite size was less than 20 nm. The particle size and morphology of the nanoparticles were analyzed using scanning electron microscopy and transmission electron microscopy. The morphological analysis revealed agglomerated spherical nanoparticles with sizes varying from 5 to 30 nm. The optical properties of the nanoparticles' band gap were characterized using diffuse reflectance spectroscopy. The band gap was found to decrease with increasing annealing temperature. The O vacancy defects were analyzed using photoluminescence spectroscopy. The increase in the crystallite size, decreasing band gap, and the increasing intensities of the UV and visible emission peaks indicated that the green-synthesized SnO_2 may play future important roles in catalysis and optoelectronic devices.     

有序介孔SBA-15紫外光致发光机理研究

用水热法制备出了有序介孔二氧化硅SBA-15,分别在室温下进行了光致发光(PL)和电子顺磁共振(EPR)分析.室温PL谱分析发现了位于3.8 eV的紫外光致发光峰,进一步研究发现,样品在空气中静置十天后,3.8 eV的发光峰强度会增强.通过样品在不同温度下的退火试验分析并结合EPR谱,对这一发光的机理给予了解析,认为可能是介孔二氧化硅SBA-15中的ODC(Ⅱ)(≡Si…Si≡)缺陷与介孔中吸附的水分子反应形成的硅醇基(≡Si—OH)产生的发光.     

Zn基ZnO纳米棒阵列的制备和发光特性

N2H4.H2O水热体系中,在Zn基底上制备出了ZnO纳米棒薄膜。采用X射线衍射(XRD)、场发射扫描电镜(FESEM)及发致发光谱(PL)等分析测试手段,研究了ZnO薄膜的形貌结构和发光特性。结果表明,预处理工艺不同,Zn基底表面状态不同,ZnO薄膜形貌也不同。在经预氧化形核的Zn基底上易于制备ZnO纳米棒薄膜。在单一取向的Zn基面上,易于制备ZnO纳米棒阵列。PL测试分析表明,ZnO纳米棒有强的近带边紫外光发射峰和弱的缺陷发射峰。阵列棒本征发射峰强度最高、缺陷峰最弱,反映了该ZnO纳米棒结晶质量高。     

一维La2O3:Eu纳米纤维的制备及荧光性质

采用高压静电纺丝技术, 经高温焙烧制得掺杂Eu3+的一维六方晶相La2O3纳米纤维。采用扫描电镜(SEM)、X 射线衍射(XRD)、差热-热重分 析(TG DTA)及荧光光谱(PL)等测试手段对纤维的表面形貌、纯度、晶型及荧光性质进行了表征。由扫描电镜照片可以看出所制得的纤维较为均匀,纤维直径分布在370～430?nm之间,经过1?100?℃焙烧后 直径减小至245?nm左右。荧光光谱测试显示出样品具有较好的荧光性质,尤其是Eu3+的f f跃迁激发及电荷转移跃迁引起较强发光。     

Structural,morphological, and optical properties of tin(IV) oxide nanoparticles synthesized using <Emphasis Type="Italic">Camellia sinensis</Emphasis> extract: a green approach

Tin oxide (SnO₂) nanoparticles were cost-effectively synthesized using nontoxic chemicals and green tea (Camellia sinensis) extract via a green synthesis method. The structural properties of the obtained nanoparticles were studied using X-ray diffraction, which indicated that the crystallite size was less than 20 nm. The particle size and morphology of the nanoparticles were analyzed using scanning electron microscopy and transmission electron microscopy. The morphological analysis revealed agglomerated spherical nanoparticles with sizes varying from 5 to 30 nm. The optical properties of the nanoparticles' band gap were characterized using diffuse reflectance spectroscopy. The band gap was found to decrease with increasing annealing temperature. The O vacancy defects were analyzed using photoluminescence spectroscopy. The increase in the crystallite size, decreasing band gap, and the increasing intensities of the UV and visible emission peaks indicated that the green-synthesized SnO₂ may play future important roles in catalysis and optoelectronic devices.     

Violet/blue photoluminescence from CeO_2 thin film

CeO2 is a rare-earth oxide which has a face centered cubic fluorite crystal structure. It has fine chemical stabil-ity and high dielectrics (e = 26). Its lattice constant has closely matched to silicon and the dismatch is about 0.35%. It is always investigated as insulator material in the silicon-on-insulator (SOI) structures, dielectric mate-rial and the buffer layer between the superconductor Yba2Cu3O7 and the Si substrate[1—6]. Recently, the PL of CeO2 was studied by many groups. The…     

两步反应法制备硅基氮氧化物荧光材料SrSi_2O_2N_2:Eu~(2+)及其发光性能研究

本文以硅酸盐相Sr2SiO4:Eu2+为前驱体,采用两步反应法制备了一系列单相的氮氧化物荧光粉Sr1?xSi2O2N2:Eu2+x(0.02?x?0.10),详细探讨了SrSi2O2N2:Eu2+荧光粉的反应机制及发光性能.实验结果显示所有样品能被近紫外光(400 nm)和蓝光(450 nm)激发发射出峰值位于535 nm的黄绿光,在Sr2SiO4:Eu2+体系中Eu2+的最佳掺杂浓度值x为0.05,Eu2+之间的能量传递是电偶极-偶极相互作用,Eu2+之间能量传递临界距离Rc=1.507 nm.此外,本文还对样品的发光强度和热稳定性与某商用YAG黄粉作了分析比较,所有结果表明该系列荧光粉可用于白光LED制造.