电子束辐照制备Fe3O4/PAM磁性核壳微球

在共沉淀法制备Fe3O4纳米磁粉的基础上,以丙烯酰胺（AM）为单体,在水溶液中通过电子束辐照的方法,制备了具有核壳结构的磁性复合微球Fe3O4/PAM.采用XRD、AFM、IR等对样品进行表征.结果表明,制备的磁粉为Fe3O4单相,粒径为8 nm左右,磁性高分子微球Fe3O4/PAM直径约为100 nm,呈球形.分析了单体浓度、磁粉用量、交联剂浓度、辐照剂量等对Fe3O4/PAM微球粒径的影响规律.     

磁性聚苯乙烯微球的合成与表征

采用化学共沉淀法制备Fe3O4纳米粒子,并用聚乙二醇-6000对其表面改性,然后以苯乙烯(St)为单体,过氧化苯甲酰(BPO)为引发剂,采用分散聚合法,制备粒径小,磁含量高的磁性聚苯乙烯微球.X射线衍射(XRD)研究表明,所制备的Fe3O4粒子为面心立方结构.红外光谱测试(FT-IR)表明微球中存在苯乙烯和Fe3O4纳米粒子.透射电镜(TEM)观察表明,所制备的磁性聚苯乙烯微球的粒径约为100 nm.热重(TG)分析得到磁性聚苯乙烯微球磁性物质质量分数为14.5%.振动样品磁强计(VSM)测试结果表明,磁性聚苯乙烯纳米粒子的比饱和磁化强度为14.4 A·m2/kg,具有超顺磁性.     

纳米Fe_3O_4颗粒的制备及磁性能

采用X-ray衍射、高能X-ray衍射、透射电子显微镜及振动样品磁量计等表征手段,研究了不同制备工艺对Fe3O4纳米粒子的平均晶粒尺寸及磁性能的影响.结果表明多元醇方法所制备的Fe3O4粉体平均粒径为32 nm,其饱和磁化强度为6.8×10-3A/m(该值比块体Fe3O4的饱和磁化强度约降低了8%),剩磁Mr=4.2×10-3A/m,矫顽力Hc=1.43×10-2T;通过共沉淀方法得到的Fe3O4粉体平均粒径显著减小为7 nm,但是其饱和磁化强度也明显降低为3.3×10-4A/m,比块体Fe3O4的饱和磁化强度减小约96%,剩磁及矫顽力也下降为零.这是由于小尺寸效应导致出现超顺磁现象,说明Fe...     

环氧基化磁性微球的制备及表征

采用反相聚合包埋技术制备以Fe3O4为磁核,琼脂糖为壳层的琼脂糖磁性微球,用环氧氯丙烷对其进行表面化学修饰后制得环氧基化磁性微球.通过傅里叶变换红外光谱、热重分析和振动样品磁力测定等表征其结构和性质,采用酶联免疫吸附试验检测其对乙肝表面抗原的固定能力.结果表明,环氧基化磁性微球平均粒径为30.3μm,环氧基含量为140.19μmol·g-1,磁含量为50.53%,饱和磁化强度为11.25emu·g-1,对乙肝表面抗原的固定能力明显高于琼脂糖磁性微球,具有良好的单分散性、超顺磁性和生物兼容性,可作为筛选乙肝表面抗原特异性核酸适配体的载体.     

纳米Co粒子的制备及在硅油基磁性液体中的应用

以锌粉和氯化钴为原料，采用化学法制备纳米Co粒子。采用透射电镜考察工艺条件对生成的Co粒子粒径及晶貌的影响。通过对不同粒径Co粒子的筛选，确定了用于制备磁性液体的适宜粒径。纳米Co经表面活性荆改性后与适量的纳米Fe3O4胶粒混合，用过渡液进行复舍包覆，使用超声波振荡和机械分散的方法将其分散于2-甲基硅油中，得到硅油基复合磁性液体。用振动样品磁强计测定样品的饱和磁化强度。研究结果表明：在反应物浓度一定的条件下，Co粒子的晶貌主要由反应温度决定；对Co粒子粒径影响最大的是反应温度，其次是搅拌转速，反应时间对Co粒子粒径的影响不大。Co粒子用作磁性液体基体材料的适宜粒径约为10．88nm，晶貌主要为六面体和棒形。复合磁性液体的饱和磁化强度比Fe3O4磁性液体的饱和磁化强度提高21％以上。     

Dy3+掺杂对Fe3O4纳米粒子磁性能的影响

为提高Fe3O4纳米粒子的磁性能,研究了Dy3 掺杂对Fe3O4纳米粒子宏观磁性及粒径的影响。适量的掺杂可使Fe3O4粒子的粒径增大,饱和磁化强度提高。过量的掺杂不会引起粒径的进一步增大,但会引起饱和磁化强度的下降。在反应温度为55℃,搅拌转速900 r/min,反应时间1.5 h,掺镝量为12.17%的条件下,用化学共沉淀法制备出平均粒径为18.6 nm、饱和磁化强度可达168.73 mT的镝铁氧体粒子。     

PEI修饰磁性Fe3O4纳米粒的制备和表征

 为了制备性能良好的聚乙烯亚胺（PEI）修饰的磁性Fe3O4纳米粒,以及为进一步开展体内外生物学效应分析奠定基础,采用化学共沉淀法制备PEI修饰的磁性Fe3O4纳米粒。PEI-Fe3O4纳米粒的制备包括磁性Fe3O4纳米粒的制备和PEI修饰磁性Fe3O4纳米粒两部分,采用4因素2水平的正交实验对各因素进行优化,得到较佳的制备工艺。反应过程中用过量氨水保持pH值为9.3~9.7,Fe2+与Fe3+的物质的量比为1:1.75,PEI水溶液的质量百分数为20%,反应温度始终保持为85℃,机械搅拌速率为1400r/min。采用傅里叶变换红外光谱仪（FTIR）、透射电子显微镜（TEM）、X射线衍射分析仪（XRD）、振动样品磁强计（VSM）、热重分析仪（TGA）对磁性纳米粒的物化特征进行表征。结果表明,制得的磁性PEI-Fe3O4纳米粒为接近圆形或椭圆形粒子,具尖晶石结构,粒径约9.4nm,磁含量为82.3%,饱和磁化强度为61.962emu/g,矫顽力几乎为0,具超顺磁性,稳定性和分散性良好。     

PLA-PEG/Fe3O4磁性复合微球的制备与性能研究

以油酸钠改性的Fe3O4纳米粒子为磁性内核,聚乳酸一聚乙二醇(PLA-PEG)嵌段共聚物为载体材料,吐温-80(Tween-80)为表面活性剂,采用非溶剂引起相分离的方法,制备了PLA-PEG/Fe3O4磁性复合微球,系统考察了PLA-PEG质量浓度、Fe3O4与PLA-PEG的质量比及搅拌速度等因素对磁性复合微球性能的影响,确定了制备PLA-PEG/Fe3O4磁性复合微球的最佳条件,并利用透射电镜、红外光谱仪、热分析仪、振动样品磁强计和紫外分光光度计,对所得产物的形貌、粒径、化学组成、Fe3O4的质量分数及磁性能进行了表征.     

Co_(0.2)Fe_(2.8)O_4多孔微球的制备及磁性研究

用溶剂热法结合奥斯特瓦尔德熟化过程制备Co0.2Fe2.8O4多孔微球.用X射线衍射仪(XRD)和扫描电子显微镜(SEM)表征样品的结构和形貌,发现所制备的单分散Co0.2Fe2.8O4多孔微球是由许多纳米颗粒组装而成.用振动样品磁强计(VSM)测量样品在不同温度下的磁性,发现其饱和磁化强度随温度升高先保持稳定后快速降低,而矫顽力随温度升高持续减小.     

Co0.2Fe2.8O4多孔微球的制备及磁性研究

用溶剂热法结合奥斯特瓦尔德熟化过程制备Co0.2Fe2.8O4多孔微球.用X射线衍射仪(XRD)和扫描电子显微镜(SEM)表征样品的结构和形貌,发现所制备的单分散Co0.2Fe2.8O4多孔微球是由许多纳米颗粒组装而成.用振动样品磁强计(VSM)测量样品在不同温度下的磁性,发现其饱和磁化强度随温度升高先保持稳定后快速降低,而矫顽力随温度升高持续减小.     

Fe_3O_4@Au核壳结构的制备及在苯乙烯环氧化中的研究

以FeCl3·6H2O为铁源,乙二醇为还原剂,聚乙二醇为表面活性剂,在200℃水热条件下制备平均粒径约为300 nm的介孔Fe3O4.以3-氨丙基三乙氧基硅烷(APTES)为偶联剂对Fe3O4进行改性,室温超声下用柠檬酸钠将Au3+还原为Au0,制备了Fe3O4@Au核壳材料.利用扫描电镜(SEM),N2-吸附-脱附等温线,X射线衍射(XRD),傅里叶变换红外对核壳材料进行表征,结果表明,比表面为95.56 m2/g、孔径为5.67 nm,Fe3O4表面被金均匀涂层,其具有较好的光催化环氧化选择性.     

Synthesis and characterization of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript>@SiO<Subscript>2</Subscript> magnetic composite nanoparticles by a one-pot process

Fe₃O₄@SiO₂ core–shell composite nanoparticles were successfully prepared by a one-pot process. Tetraethyl-orthosilicate was used as a surfactant to synthesize Fe₃O₄@SiO₂ core–shell structures from prepared Fe₃O₄ nanoparticles. The properties of the Fe₃O₄ and Fe₃O₄@SiO₂ composite nanoparticles were studied by X-ray diffraction, transmission electron microscopy, energy dispersive spectroscopy, and Fourier transform infrared spectroscopy. The prepared Fe₃O₄ particles were approximately 12 nm in size, and the thickness of the SiO₂ coating was approximately 4 nm. The magnetic properties were studied by vibrating sample magnetometry. The results show that the maximum saturation magnetization of the Fe₃O₄@SiO₂ powder (34.85 A·m2·kg–1) was markedly lower than that of the Fe₃O₄ powder (79.55 A·m2·kg–1), which demonstrates that Fe₃O₄ was successfully wrapped by SiO₂. The Fe₃O₄@SiO₂ composite nanoparticles have broad prospects in biomedical applications; thus, our next study will apply them in magnetic resonance imaging.     

磁性氧化铁纳米线的制备与表征

通过溶胶-凝胶法在氧化铝模板（AAO）中制备出了磁性Fe_2O_3纳米线阵列,然后去除AAO模板得到磁性Fe_2O_3纳米线。用SEM,TEM,FTIR,EDX,VSM对磁性纳米线的形貌、微结构和磁性能进行表征。SEM和TEM结果显示磁性纳米线的直径约为50～80nm,长度在8～10μm,长径比为120～180;FTIR和EDX结果表明制备的产物是磁性Fe_2O_3纳米线;VSM结果表明磁性氧化铁纳米线阵列存在明显的磁各向异性。此外,采用Zeta电位仪对磁性Fe_2O_3纳米线表面的电性进行了研究,结果表明纳米线表面带正电荷,有利于和动物细胞相结合。     

固定化柱状假丝酵母脂肪酶的制备与催化性能的研究

通过反相悬浮技术制备了含磁性Fe3O4微粒的聚合物微球,利用扫描电子显微镜（SEM）、X射线粉末衍射仪（XRD）、红外光谱（FT-IR）、振动样品磁强计（VSM）和低温N2吸脱附等方法对微球进行了结构性质表征.结果表明,微球中Fe3O4质量分数为5.82%,比饱和磁化强度σs为3.85 emu/g,且具有超顺磁性;其比表面积、平均孔径和孔容分别为123.6 m2/g,13.01 nm和0.50 cm3/g,表面环氧基团含量为0.74 mmol/g.将磁性聚合物微球用于固定柱状假丝酵母脂肪酶,在30℃下用其催化（R,S）-2-溴丙酸甲酯不对称水解反应,产物（R）-2-溴丙酸的对映体过量值eep为17.7%,（S）-2-溴丙酸甲酯的对映体过量值ees为97.0%.固定化酶经5次重复使用,产物（S）-2-溴丙酸甲酯的对映体过量值ees值仍为75.7%,并且固定化酶在磁场的作用下能够快速沉降,与产物分离.     

功能型磁性聚合物微球的制备与表征

以油酸修饰的Fe3O4为磁核,以苯乙烯、丙烯酸为单体,采用细乳液聚合制备了含羧基功能基团的聚(苯乙烯-丙烯酸)共聚物微球.对修饰后的Fe3O4粒子和聚合物微球进行了XRD、FT-IR和TGA表征,并结合振动扫描样品测试(VSM)对修饰效果和磁性能进行分析.采用SEM、TEM对粒子形态进行了表征,并讨论了丙烯酸用量、助稳定剂和Fe3O4用量对粒子形态的影响.结果表明,当丙烯酸、助稳定剂和Fe3O4用量分别为单体总量的10%、8%和15%时,得到的聚合物微球结构规整,但磁性高.     

四氧化三铁磁流体的制备及性能分析

采用化学共沉淀法制备了Fe3O4磁流体。以阴离子表面活性剂油酸钠对磁性颗粒进行包覆,分析了pH值、温度和Fe2+/Fe3+比例等制备条件对Fe3O4磁流体的影响。运用磁天平、粒度测试仪对磁流体的粒径和磁化率进行了测定,并用傅里叶变换红外光谱仪(FT-IR)、透射电子显微镜(TEM)和振动样品磁强计(VSM)等对磁流体进行了表征。实验和分析结果表明,所制备的磁流体具有超顺磁性,粒径约为16 nm,饱和磁化强度在73.8 emu/g以上。     

Fe3O4/SiO2磁性微球的制备研究

报道了Fe3O4/SiO2纳米复合材料的可控合成方法.研究并探讨了乙醇-水体系配比及氨水和硅酸四乙酯的用量对纳米粒子形貌的影响,利用柠檬酸作分散剂,控制反应条件对Fe3O4纳米粒子进行表面修饰改性后,又对其进行SiO2包覆.然后运用X射线衍射仪（XRD）、透射电子显微镜（TEM）、红外（IR）对合成的纳米微粒的粒径、结构进行了表征.实验结果表明,产物为粒径均匀的单分散Fe3O4/SiO2复合纳米粒子,平均粒度约为100 nm.     

用于水处理的磁性Fe3O4纳米微粒研究

采用化学共沉淀法和水热法制备Fe3O4纳米磁性粒子及油酸包覆Fe3O4磁流体。通过实验确定最佳反应条件;用XRD分析Fe3O4粒子的晶体结构;用TEM观察磁流体样品的微观结构;用HPLC研究纳米粒子对左旋氧氟沙星溶液模拟废水超声降解的影响。结果表明产物为反尖晶石结构立方晶系的AB2O4型化合物,平均粒径小于15 nm;磁流体基本上为规则的球形,颗粒均匀,无团聚情况;制得的磁流体样品具有较好的流动性和超顺磁性;Fe3O4纳米粒子对左旋氧氟沙星具有一定的降解性能。     

Fe掺杂对Zn1 xCoxO纳米晶体结构及磁性行为的影响

利用溶胶-凝胶法制备了Fe掺杂Zn1 xCoxO(x=001~002)纳米晶体.通过XRD,TEM和VSM对其结构、晶格参数和磁性进行了表征和分析.所有样品都没有检测到非晶态产物以及Fe,Co团簇等第二相,即Fe掺杂没有改变Zn1 xCoxO晶体的纤锌矿型ZnO结构、晶粒度大小以及室温铁磁性.随着Fe掺杂浓度的提高,饱和磁化强度、剩余磁化强度和矫顽力等磁性参数都有相应的改善.Fe掺杂还引起了交换偏置,并且,该现象随着Fe掺杂浓度的提高而增强;但是,单原子Fe对饱和磁化强度的贡献低于单原子Co对自发磁化强度的贡献,这表明Fe,Co共掺杂ZnO材料与Co掺杂ZnO材料的磁性机制有所不同.     

双水杨醛缩乙二胺铁（Ⅱ）配合物的合成及其晶体结构

设计合成了双水杨醛缩乙二胺（H2salen）及其铁（Ⅱ）配合物Fe（salen）2,并通过X-射线单晶衍射技术测定了其晶体结构。该配合物属正交晶系,Pbca空间群,晶胞参数a=0.7473（3）nm,b=1.3823（5）nm,c=2.6146（9）nm,V=2.7009（16）nm3,Z=8,Dc=1.584 mg.m-3,F（000）=1328,μ=1.122 mm-1。配合物中,中心铁（Ⅱ）离子采取平面四边形配位构型,配体双水杨醛缩乙二胺的2个N原子和2个氧原子与Fe（Ⅱ）离子配位,单核单元之间通过超分子作用构成一维链状结构。