PET／PEN扩链反应共混的研究——结晶与熔融行为

用差示扫描量热法（DSC）研究了PET／PEN扩链反应性共混物体系的热性能,对共混比例、温度和时间对热性能的影响进行了讨论,并进一步考察了序列结构变化和热性能的关系。结果表明,不同比例的PET／PEN都呈现出一个玻璃化温度,即PET、PEN在无定形态是相混溶的;冷结晶温度和熔融温度与共混比例、共混时间、温度等因素密切有关。PET／PEN50／50即使共混短时间,亦不结晶。其他比例共混物随共混时间的增加,冷结晶温度升高,熔点下降,与序列长度变化有关,当序列长度小于7时,冷结晶峰消失。当酯交换大于30％时熔融峰消失。     

聚酯类热致性液晶的合成与其反应性共混的热性能改性

以联苯二氯苄制备的对联苯二甲酰氯和1．6～已二醇为单体合成了热致型主链液晶高分子,并以此液晶高分子与对苯二甲酸乙二醇酯(PET)在少量扩链剂双2-恶唑啉(BOZ)存在下进行反应性共混．探讨了单体摩尔比、反应温度、催化剂等因素对液晶合成的影响．利用红外光谱对对联苯二甲酸和聚酯液晶进行了表征,用DSC对聚酯液晶进行了热分析．研究了对反应性共混条件对共混物热性能的影响．结果表明,BOZ对酯交换的促进作用使玻璃化温度(Tg)升高,延长共混时间和提高共混温度使冷结晶温度(Tcr)升高,溶体结晶温度(Tmc)和熔点(Tm)下降。     

烷基取代的聚噻吩——结构与性质关系

ＤＳＣ数据表明，烷基取代的聚噻吩的吸热转化温度随取代烷基中碳原子数的增加而降低，聚（３－烷基噻吩）（Ｐ１ＡＴＳ）及其与乙烯－醋酸乙烯酯共聚物的共混物的ＵＶ吸收与烷基侧链长度，浓度及温度有关。层奖结构的形成脑矣合物主链的棒－线转化是产生“热色显示”及“溶剂化显色”原因。     

PET/LCP反应性共混酯交换动力学研究

采用1 HNMR对聚对苯二甲酸乙二酯 (PET)与液晶共聚酯 (LCP)在少量扩链剂双 (2 唑啉 )BOZ存在下反应性共混的酯交换动力学进行了研究。设反应性共混的酯交换反应是二级可逆 ,则在 2 70、2 80、2 90℃下的酯交换反应速率常数分别为 1.5 5×10 - 2 、2 .2 0× 10 - 2 、3 .0 1× 10 - 2 (min- 1 ) ,均比不含扩链剂的体系的酯交换速率快 ;取得酯交换的活化能为 84.4(kJ·mol- 1 )较一般的PET/LCP的酯交换反应活化能低 ,这些均表明BOZ的加入对于PET/LCP的酯交换反应具有明显的促进作用。     

聚醚醚酮/聚酯液晶二元和三元增容共混体系的等温结晶动力学及结晶形态

采取熔融共混方法制备了聚醚醚酮（PEEK）和聚酯液晶（TLCP）二元和三元增容共混物， 用DSC和PLM对 共混物的结晶行为和结晶形态进行了研究. 结果表明， TLCP的存在使PEEK的结晶温度和结晶起始温度均略有升高， 增容剂（RCP）的加入延缓了PEEK结晶过程. 等温结晶动力学研究表明， 液晶的加入加快了聚醚醚酮的结晶速度， 但随其含量增加结晶速度降低. 与二元共混物相比， 加入增容剂后对聚醚醚酮的结晶速度基本无影响. 增容后的聚醚醚酮球晶的尺寸下降， 很难看到Maltese十字消光.     

P(3,HB-co-4,HB)/PLA共混物的扩链改性研究

以异佛尔酮二异氰酸酯(IPDI)和亚磷酸三苯酯(TPP)为扩链剂,对聚(3–羟基丁酸酯–co–4–羟基丁酸酯)/聚乳酸[P(3,HB-co-4,HB)/(PLA)]共混物进行扩链改性.采用毛细管流变仪、电子万能试验机、差示扫描量热仪和扫描电子显微镜等研究两种扩链剂及用量对扩链前后共混物的流变性能、力学性能、结晶性能及断面形态的影响.结果表明:两种扩链剂均显著提高了共混物的熔体剪切黏度和两组分间的相容性,IPDI和TPP添加量分别为1.5份和1.0份时,改性效果最明显,共混物断裂伸长率及缺口冲击强度分别提高了34.5%、69.6%和89.6%、81.0%;IPDI扩链体系的拉伸强度提高8.3%,而TPP扩链体系的拉伸强度略有下降,表明IPDI扩链效果优于TPP.     

聚乙二醇共混改性聚羟基丁酸酯的研究

研究了聚乙二醇（PEG）溶液共混改性聚羟基丁酸酯（PHB）。DSC、WAXD及力学性能实验表明，PHB／FEG共混物经溶液成膜后，PHB相和PEG相的非晶相部分是热力学相容的，少量PEG的加入，能提高PHB相的结晶度，降低PHB相的熔融温度，减小球晶尺寸，PHB的脆性和加工温度有一定的改善。     

增容对回收PET/PP共混物的结晶与熔融行为的影响

制备了不同相容剂增容回收PET/PP共混物,用DSC方法研究了相容剂对r-PET结晶与熔融行为的影响,r-PET对PP结晶与熔融行为的影响和相容剂对r-PET/PP共混物结晶与熔融行为的影响,观察到PP结晶温度随着r-PET含量增加而提高,r-PET结晶温度随着PP含量增加而降低,相容剂加入明显降低共混物中r-PET结晶温度,但不同相容剂对共混物中r-PET结晶与熔融行为影响不大,共混物中PP结晶性能与相容剂的大分子链有关。     

PHA/PEDEA聚酯齐聚物的结晶行为

利用热台偏光显微镜（POM）、广角X射线衍射（WAXD）和差示扫描量热仪（DSC）研究了低相对分子质量聚己二酸己二醇酯（PHA）和聚己二酸（乙二醇/一缩二乙二醇）酯（PEDEA）共混物的结晶行为，结果表明，共混物晶形为球晶，随PEDEA含量增加，混合聚酯的结晶速度下降，结晶度降低，晶形不发生变化，结晶动力学研究表明共混物的阿夫拉米指数约为4。     

PET/PC共混物相容性与结晶性能的研究

采用相容剂增容 PET/ PC共混物 ,使共混体系的相容性得到提高 ,并用 DSC方法对共混物进行了测试。结果表明 :随着相容剂用量的增加 ,共混物中 PET的冷结晶温度降低 ,改善了 PET的结晶性能和韧性。     

聚对苯二甲酸乙二醇酯与液晶高分子共混改性

聚对苯二甲酸乙二醇酯（ＰＥＴ）与液晶高分子（ＬＣＰ）挤出共混，注射模塑制得试样。采用示差扫描量热仪、扫描电子显微镜、力学性能测试仪等手段，表征共混物的热行为、形态、结构和力学性能。研究结果表明：在实验范围内，ＰＥＴ与液晶高分子（ＰＥＴ－６０ＰＨＢ）的共混体系，共混物的强度对ＬＣＰ的含量呈曲线变化，ＬＣＰ的质量分数在０～２０％之间，共混物的强度有极大值；ＬＣＰ的质量分数在４０％～６０％之间，共混物的强度有极小值。     

PBT/PET共混体系熔融过程的DSC研究

用共溶解-沉淀法制得的共混物PBT/PET各组分分别结晶,PET的存在对PBT的结晶有抑制作用;熔融共混PBT/PET的DSC图谱与共混时间有关;超过一定时间后只呈现单一的熔融峰,其本质是由于酯交换使共混物变为共聚酯,而非互溶共晶.     

PET/PEN共混物的热分解行为及其动力学

研究了惰性气氛下聚对苯二甲酸乙二酯(PET)/聚对萘二甲酸乙二酯(PEN)共混物的非等温热分解行为及其动力学.研究发现,不同PET/PEN共混物的热降解为一个主要的热分解过程,热分解反应为一级反应.随着共混物中PEN质量分数的增加,共混物的起始分解温度逐渐升高,共混物的热稳定性逐渐提高,而且共混物的热分解反应活化能也逐渐增加,这是由于PEN分子链中萘环的热分解温度比PET中苯环高,因此分子链的热稳定性比PET要高.共混物中萘环的化学组成含量越高,则热稳定性愈高.     

STUDIES ON THE COMPATIBILITY OF PPO MULTI-COMPONENT BLENDS

The compatibility and phase morphology of poly (phenylcne oxide) (PPO) multi-componenet blends with poly (ethylene terephthalate) (PET) and polystyrene (PS) were studied using differentialscanning calorimetry (DSC), dynamic mechanical analysis (DMA) and scanning electron microsopy (SEM) methods. The effect of glycidyl methacrylate-styrene copolymer (GMS), as a compatibilizer, on the morphology of the PPO blends has also been studied in detail. The influence of the moiecular weight of PET and the synergetic effect of the compatibilizers of GMS and phenoxy on the morphology were examined. The DSC and DMA results show that there are two distinct glass transitions correspondinig to PET and PPO existed, however, the Tg of PPO shifts toward lower temperature region due to the addition of GMS and PS. The SEM results reveal that PET component is as dispersed phases in the PPO matrix, part of which is located at the interfaces due to the interaction with GMS while PS is miscible in the PPO matrix. A significant     

乙二醇添加量对聚酯降解产物的影响

采用不同质量分数的乙二醇(EG)醇解聚对苯二甲酸乙二醇酯(PET),并用醇解产物和甲醇进行酯交换反应以制备对苯二甲酸二甲酯(DMT),研究了EG添加量对醇解产物质量分数及DMT产率的影响。采用高效液相色谱(high performance liquid chromatography,HPLC)对醇解产物进行分析,结果表明,不同EG添加量下,醇解产物的主要成分均为对苯二甲酸乙二醇酯(BHET)单体、二聚体及三聚体,且随着EG添加量的减小,BHET质量分数逐步降低,而低聚体的质量分数则逐渐增加。通过红外光谱、差示扫描量热仪及HPLC对酯交换产物进行表征,发现其主要成分为DMT。对DMT的产率进行分析,结果表明,EG添加量对DMT产率的影响较小,并且不同EG添加量下,DMT产率均可达到85%。优选EG与PET的投料比为1∶2,此时DMT产率可达89%,醇解过程中EG质量分数下降到75%。     

PC/PET/EPDM共混体系的相容性

用熔融共混法制备了PC/PET/EPDM共混物,用TBA,DSC,TEM及IR等方法对共混物进行了表征。计算了相互作用参数,讨论了EPDM对PC/PET相容性的影响。结果表明,PC/PET/EPDM共混体系为部分相容体系,EPDM增大了PC/PET的相容性。     

PET/PPO共混物的结晶及熔融行为

本文用扫描量热法(DSC)研究了聚对苯二甲酸乙二脂(PET)与聚2,6—二甲基—1,4—对苯醚(PPO)共混物从熔体及玻璃态的等温结晶动力学以及结晶后试样相应的熔融行为。结果表明,PET及其共混物的等温结晶过程均符合Avrami方程,但Avrami指数n及结晶速率常数K值均与共混物组成及起始结晶状态有密切关系;从熔体结晶的表现活化能△E值要比玻璃态结晶的△E值高,并且受组成影响较明显。非晶的PPO组分在含量较低时能加速PET的结晶,使之达到比纯PET高的结晶度,但含量高达50％时,结晶速率及结晶度均略有下降,这与共混物织态结构改变有关。相同组成的共混物从玻璃态结晶比从熔体结晶所达到的结晶度高,但起始熔融温度低,熔程宽,表明生成较多的不规整的微晶体。     

Crystallization Behavior of Copolymer Poly(ethylene terephth-alate/isophthalate)(IPET)

The non-isothermal crystallization kinetics, isothermal crystallization and the morphology of crystals of the copolymer poly ( ethylene terephthalate/ isophthalate ) (IPET) were studied by DSC and polarized-light microscopy in this paper. DSC results indicate that the glass transition temperature Tg of IPET is slightly lower than that of poly (ethylene terephthalate) (PET), but the melting temperature Tm and the crystallization temperature Tc of PET and IPET have much difference. The difference of Tc between PET and IPET2 is about 7℃, and the difference of Tm between PET and IPET2 is about 16℃. From the kinetics analysis of the crystallization, the crystallization mechanism of all samples is of three-dimension spherulitic growth from instantaneous nuclei and the incorporation of isophthalate (IPA) decreases the crystallization rate of IPET greatly. The isothermal results indicate that the morphologies of PET and IPET crystals are all spherulite, which is in conformity to the results of non-isothermal d     

PC—g—PS增容PPO／PET共混体系的研究

研究了聚苯醚／聚对苯二甲酸乙二醇酯共混体系的热行为，相形态及拉伸行为，结果表明，ＰＰＯ／ＰＥＴ共混物是一个高度不相容的体系，体系中存在分散相相区尺寸很大的两相结构，其宏观力学性能呈特征的脆性断裂，加了聚碳酸酯、聚苯乙烯的辐射接枝共聚物ＰＣ－ｇ－ＰＳ以作为增容剂后，共混物的相容性明显改善，分散相相区尺寸减小，共混物的拉伸行为呈韧性断裂。