聚合物影响Al-MCM-41结构和形貌的研究

利用硝酸铝自行水解产生的弱酸环境为反应介质,使硅源正硅酸乙酯(TEOS)充分水解,随后引入氨水使无机物种聚合,通过水解-聚合两步途径,制备了硅铝介孔分子筛,考察了不同聚合物添加对其分散性及结构的影响.N2吸附-脱附、TEM和XRD表征结果表明:聚乙二醇(PEG)和聚乙烯吡咯烷酮(PVP)的添加有利于提高介孔硅铝分子筛的分散性和介孔结构的有序度.     

介孔分子筛Ti—AIMSU—Y后合成法制备及其催化性能

以介孔分子筛AlMSU-Y为载体,钛酸四丁酯、二氯二茂钛、四氯化钛为钛源,采用合成后嫁接法合成了3种Ti-AlMSU-Y介孔分子筛样品．用傅立叶变换红外光谱（FT-IR）、X射线粉末衍射（XRD）、N2吸附-脱附、固体核磁（MASNMR）、紫外一可见漫反射（UV_vis）和能谱（EDS）进行了表征,并以环己醇氧化反应考察了样品的催化性能．实验结果表明,样品Ti-AlMsU-Y仍保持了基体A1MSu—Y介孔孔道结构,钛原子进入分子筛骨架且以骨架四面体钛的形式存在,同时分子筛中非骨架铝的含量相对减少．在环己醇氧化反应中,骨架四面体Ti和骨架四面体A1存在明显的协同作用,表现出较高的催化活性．3种Ti—AIMSU-Y样品中,以钛酸四丁酯为钛源制得的样品Ti（z）-AIMSU-Y对环己醇的催化活性最好,在80℃反应24h,环己醇转化率为43．1％,环己酮选择性为100％．     

介孔Worm-like孔壁晶化制备微孔-介孔分子筛研究

采用水热孔壁晶化法,以Worm-like介孔分子筛为硅源,十八水合硫酸铝为铝源,制备不同硅铝比微孔-介孔ZSM-5复合分子筛,XRD、FT-IR、N2吸附-脱附、TEM等表征结果证明,用此方法成功制备出一系列微孔-介孔ZSM-5复合分子筛．将一系列复合分子筛用于催化苯酚叔丁基化反应,在反应温度145 ℃、n(苯酚)∶n(叔丁醇)=1∶2.5条件下,硅铝比为15、25的复合分子筛有较强的催化活性,苯酚转化率和2,4-二叔丁基苯酚选择性分别超过90%和42%．     

一种合成大孔径SBA-15介孔分子筛的新方法

通过加入无机盐硝酸铵辅助合成大孔径介孔分子筛SBA-15,用小角X-射线粉末衍射(SAXS)、透射电子显微镜(TEM)、N_2吸附脱附等手段对分子筛进行了表征.结果表明:合成的大孔径分子筛SBA-15具有高度有序的介孔结构,孔径约12 nm,比表面积894 m~2·g~(-1),孔容为2.6 cm~3·g~(-1);不加硝酸铵则不能得到具有高有序度的介孔材料.     

杂原子介孔分子筛MCM-41的合成与表征

制备纯硅的介孔分子筛MCM-41，具有不同Si／Al的Al-MCM-41，以及含有B原子和Ti原子的B-Al-MCM-41和Ti-MCM-41的试样。小角X射线粉末衍射(XRD)分析表明，样品均具有MCM-41的结构特征，N2吸脱附研究表明，样品呈现Ⅳ型吸附等温线，具有孔径分布均一的中孔结构。利用^27Al MAS NMR研究了试样中Al的化学环境。结果表明，随铝含量的增加，四配位骨架铝和六配位骨架外铝同时增多，并且由非骨架四配位铝或骨架扭曲四配位铝所产生的“不可观察铝”也增多。     

中孔分子筛Al/SO_4~(2-)/MCM-41的合成与表征

用Al2(SO4)3对中孔分子筛MCM-41进行改性,制备了中孔分子筛Al/SO24-/MCM-41.采用X射线多晶衍射(XRD)、红外光谱(FT-IR)、N2吸附-脱附和NH3程序升温脱附(NH3-TPD)等测试技术对样品的结构和表面酸性进行了表征.结果表明,用Al2(SO4)3改性中孔分子筛MCM-41,能得到仍保持着六方介孔结构的中孔分子筛Al/SO24-/MCM-41.     

介孔分子筛SBA-15的合成与表征

以三嵌段共聚物P123为模板剂、正硅酸乙酯为硅源,水热合成了介孔分子筛SBA-15,利用N2吸附-脱附、XRD、TEM等手段对其进行了表征,并考察了SiO2/P123摩尔比、反应溶液酸度、共溶剂等因素对其结构的影响.结果表明,随着SiO2/P123摩尔比的增加,介孔分子筛SBA-15的比表面无显著变化,孔径、孔容逐渐减小;随着反应溶液酸度的增强,样品比表面无明显变化,而孔径、孔容则明显变大;不同共溶剂的扩容效果不一,其中三甲苯的效果最佳.     

含Nb介孔Al2O3分子筛的合成及其性质研究

将过渡金属元素Nb嵌入介孔Al2O3中以期改变Al2O3表面酸性。以三嵌段共聚物P123为模板剂,无水AlCl3和草酸铌为前驱物,在乙醇溶剂中采用溶胶-凝胶法合成含Nb介孔Al2O3分子筛,并用X-射线粉末衍射(XRD)、傅里叶变换红外光谱(FT-IR)、低温氮气吸附-脱附等方法对其结构进行表征,采用Hammett指示剂法对其表面酸量、酸强度分布进行表征。结果表明,Nb嵌入介孔Al2O3骨架中,形成Nb-O-Al键,改变了介孔Al2O3分子筛孔径,使表面出现了较强的酸中心,提高了表面酸强度和总酸量。     

以离子液体为模板剂合成Cr-MCM-41及其催化性能

制备离子液体1-十六烷基-3-甲基咪唑四氟硼酸盐([C16mim]BF4),并以此为模板剂合成掺杂Cr的介孔分子筛Cr-MCM-41。采用X线衍射仪(XRD)、N2吸附-脱附仪、透射电子显微镜(TEM)和傅里叶红外光谱仪(FT-IR)对Cr-MCM-41进行表征,并将Cr-MCM-41应用于H2O2氧化乙苯反应中,考察其催化性能。结果表明:合成的分子筛具有介孔结构,随着Cr掺入量的增加出现Cr2O3晶相。当反应温度为60℃、乙苯0.04 mol、H2O20.12mol、Cr-MCM-41-2 0.1 g,反应时间10 h,乙苯转化率达12.40%,选择性达100%。     

气相水解法介孔分子筛MCM-41组装纳米TiO2研究

以水玻璃为硅源,表面活性剂十六烷基三甲基溴化铵为结构模板剂,合成出MCM-41介孔分子筛,并以钛酸丁酯为前驱体,在高温气相炉中进行水解,羟基缩合对介孔分子筛MCM-41进行了纳米TiO2的修饰。XRD、FTIR、N2吸附脱附、SEM表征手段对其结构特征的测试结果表明:纳米TiO2不仅进入介孔分子筛MCM-41介孔孔道,较均匀地修饰了介孔分子筛MCM-41的孔壁,而且使介孔分子筛MCM-41能够保持有序的孔道结构。     

硅或钛取代AlPO-11分子筛的合成及表征

介绍了硅，钛取代A1PO-11分子筛SAPO-11、TAPO-11的合成方法，采用X射线衍射（XRD）、扫描电子显微镜（SEM）、热重-差热、氮气吸脱附等手段对合成的分子筛进行了表征，考察了晶化温度和原料比对分子筛合成的影响。结果表明，硅，钛取代A1PO-11分子筛能生成AEL结构的TAPO-11分子筛；SAPO-11与A1PO-11分子筛表观形貌相差不大，而TAPO-11分子筛表观形貌则与A1PO-11分子筛有很大不同；硅，钛取代后分子筛的孔道半径及其孔容有所改变；3种分子筛都具有较好的热稳定性。     

Ti-M分子筛合成及其性能研究

 以高硅丝光沸石(M分子筛),TiO₂粉和HClO₄为原料,水热晶化法合成Ti-M分子筛.运用FT-IR和UV-vis光谱技术表征合成的Ti-M分子筛样品的物化特性,证明了钛原子进入了M分子筛的骨架位,推测出骨架钛在Ti-M分子筛中的确存在.选择环已酮氨氧化为探针反应,考察了Ti-M对此反应的催化活性,结果表明Ti-M分子筛对环已酮氨氧化具有较好的催化性能.     

SAPO-11构型分子筛的合成及X射线衍射结构分析

以二正丙胺及二异丙胺为模板剂，采用水热法制得了ＳＡＰＯ－１１分子筛对３种不同的合成方法－异丙醇铝法、上清液法和氟离离子法的产物及杂晶情况作了讨论。采用ＸＲＤ多晶结构分析及真空吸附等方法研究了ＳＡＰＯ－１１的骨架结构和孔结构。     

A new microfiltration membrane with three-dimensional reticular architecture for Nano-pollutants removal from wastewater

This research provides a new insight into designing next-generation filtration materials for Nano-pollutants removal from wastewater, and potentially for gas/solid or liquid/solid separation in corrosive environment. Considering the high corrosion and oxidation resistance, Ti–40Al–10Nb–10Cr porous alloy was prepared by powder metallurgy and used as a mechanical support with a pore size of around 10 ?μm. Subsequently, metallic Zn nanoparticles was coated on the Ti–40Al–10Nb–10Cr porous framework by means of chemical vapor deposition, obtaining a novel microfiltration membrane with three-dimensional reticular architecture. Furthermore, the influence of Zn coating on surface morphology, pore feature, and filtration capability of Ti–40Al–10Nb–10Cr porous alloy was investigated. It is of note that the as-prepared microfiltration membrane exhibits an excellent Nano-pollutants filtration efficiency of greater than 99.989% from wastewater. Most importantly, such a three-dimensional reticular architecture provides excellent structural stability, allowing the reutilization of the microfiltration membrane for at least 200 filtration cycles of wastewater treatment.     

电弧离子镀(Ti,Cr)N硬质薄膜的成分、结构与硬度

用Bulat6型电弧离子镀设备在高速钢表面沉积合成(Ti,Cr)N硬质薄膜。通过改变分离靶弧电流的配置来调节薄膜成分，制取了x=0.62-0.83的（TixCr1-x)N薄膜；考察了薄膜的成分、结构与硬度间的相互关系，明确了Cr在TiN基薄膜中使硬度提高的合金强化作用；结合元素周期律中的基本性质和热力学特征，讨论了Ti,Cr两种元素在（Ti,Cr)N薄膜的相结构（fcc)形成与合金强化中的作用。     

Isothermal oxidation behavior and mechanism of a nickel-based superalloy at 1000℃

The oxidation behavior of a nickel-based superalloy at 1000°C in air was investigated through X-ray diffraction, scanning electron microscopy, andenergy-dispersive spectroscopy analysis. A series of oxides, including external oxide scales (Cr2O3, (TiO2 + MnCr2O4)) and internal oxides (Al2O3,TiN), were formed on the surface or sub-surface of the substrate at 1000°C in experimental still air. The oxidation re-sistance of the alloy was dependent on the stability of the surface oxide layer. The continuity and density of the protective Cr2O3 scale were affected by minor alloying elements such as Ti and Mn. The outermost oxide scale was composed of TiO2 rutile and MnCr2O4 spinel, and the growth of TiO2particles was controlled by the outer diffusion of Ti ions through the pre-existing oxide layer. Severe internal oxidation oc-curred beneath the external oxide scale, consuming Al and Ti of the strength phaseγ′ (Ni3(Al,Ti)) and thereby severely deteriorating the sur-face mechanical properties. The depth of the internal oxidation region was approximately 35μm after exposure to experimental air at 1000°C for 80 h.     

Au/Al_2O_3/Al整体型催化剂的研究

采用阳极氧化法制备了Al2O3/Al载体,研究了阳极氧化条件(硫酸浓度、电流密度、氧化时间等)对载体比表面积和孔结构的影响.用这种载体,经过水合或负载CeO2、Fe2O3等助剂对载体的不同处理后,采用浸渍法制备了金负载量为1%的Au/Al2O3/Al、Au/Al2O3-CeO2/Al、Au/Al2O3-Fe2O3/Al催化剂,考察了其CO催化氧化活性.结果表明:阳极氧化条件对载体的表面结构有着显著的影响,同时也明显影响到催化剂的活性;助剂CeO2的加入能明显提高催化剂的活性.     

不同硅铝比的Beta/MCM-41复合分子筛的合成和性能

分别以四乙基氢氧化铵和十六烷基三甲基溴化铵作为微孔相和介孔相的模板,采用两步晶化法制备了4种具有不同硅铝比,含微孔和介孔双模孔结构的Beta/McM-41复合分子筛.采用X射线衍射、N2吸附-脱附对Beta/MCM-41复合分子筛的结构进行了表征,利用吡啶吸附红外光谱(Py-FTIR)以及正庚烷裂解作为探针反应,对不同硅铝比的Beta/MCM-41复合分子筛的酸量和催化性能进行了研究.实验结果表明,随投料硅铝比的增加,复合分子筛介孔相有序性逐渐提高,微孔相的结晶度逐渐减小,酸量降低,正庚烷裂解的转化率明显下降.说明该复合分子筛的性能可随硅铝比的变化进行调变.