磷酸活化法黄麻杆活性炭的制备及表征

以黄麻杆为原料,采用磷酸活化法制备活性炭,通过正交试验探讨了磷酸浓度、活化温度、活化时间对活性炭得率和吸附性能的影响,确立了最佳制备工艺,即：磷酸浓度2mol／L、活化温度400℃、活化时间1h．实验结果表明：在最佳工艺条件下制得的黄麻杆活性炭得率为4,2．93％,碘吸附值为1059．26mg／g,亚甲基蓝吸附值为353．10mg／g,比表面积为1779．4m㎡／g,总孔容为0．960m3／g,平均孔径为2．16nm,呈现出高中孔率结构．     

氯化锌活化棉杆制备活性炭及孔结构表征

研究了以棉花秸秆为原料,采用微波辐射氯化锌法制备活性炭的可行性。利用正交实验探讨了氯化锌加入率、浸渍时间、微波功率及活化时间对产品活性炭得率和吸附性能的影响。得到了微波辐射氯化锌法制备棉秆活性炭的最佳工艺：氯化锌与棉秆比例以1．6：1,浸渍时间24h,微波功率为560W,微波辐射时间为9min。用此工艺条件制得活性炭的亚甲基兰吸附值、碘吸附值、产率分别为1002．92mg／g,12．8mL／0．1g和38．92％;通过电镜扫描和自动物理化学吸附仪对活性炭孔结构进行表征,表明该活性炭的BET比表面积为794．84m^2／g,属中孔发达的活性炭。     

混合碱法甘蔗渣基活性炭的制备工艺研究

采用正交试验方法研究影响混合碱法制备甘蔗渣基活性炭性能的4种工艺因素：活化剂配比、料液比、活化温度及活化时间。结果表明,影响甘蔗渣活性炭吸附性能的工艺因素的强弱秩序为：活化时间、活化温度、活化剂配比、料液比;样品的亚甲基蓝吸附值随着活化温度的升高或活化时间的延长而呈先增后降的变化规律。其最佳工艺为：活化剂配比（KOH：NaOH）7．4：1、料液比1．18：1、浸渍时间24h、活化温度923K、活化时间0．42h。经优化工艺制得的甘蔗渣基活性炭样品的亚甲基蓝吸附值为12．7ml／0．1g,为活性炭国家标准（GB／T13803．4—1999）中一级品的1．4倍。     

油茶壳基活性炭的微波制备及其对U(Ⅵ)的吸附

以油茶壳为原料,氯化锌为活化剂,采用微波活化制备油茶壳基活性炭。通过测定活性炭的碘吸附值,探究了氯化锌活化剂质量浓度、微波辐照时间、活化剂浸渍时间对所制备活性炭吸附性能的影响;并将制得的最优活性炭进行铀吸附实验,通过扫描电镜(scanning electron microscope,SEM)、能谱分析(energy dispersive spectrometer,EDS)、傅里叶红外光谱分析(Fourier transform infrared spectrometer,FTIR)对油茶壳基活性炭进行表征,探讨其吸附铀的机理。实验结果表明:采用700 W的微波功率,当氯化锌活化剂质量浓度为300 g/L,活化剂浸渍时间为24 h,微波辐照时间为90 s时,所制得油茶壳基活性炭碘吸附值为769.9 mg/g;在溶液pH=6、初始铀质量浓度为5 mg/L、油茶壳基活性炭投加量为1 g/L、吸附时间为6 h时,油茶壳基活性炭对铀的吸附率为98.75%,铀的吸附量为4.94 mg/g。油茶壳基活性炭对U(Ⅵ)的吸附是一种以物理吸附、活性炭表面的-COOH、-OH等官能团与铀酰离子的络合作用并存的吸附方式。     

微波法污泥活性炭的制备技术研究*

以城市污水处理厂污泥为原料,研究了氢氧化钾活化-微波加热制备污泥活性炭的工艺条件,考查了固液比、活化剂浓度、浸渍时间和活化时间等因素对活性炭碘吸附值和产率的影响。在单因素试验的基础上采用正交试验,得到试验室条件下微波法制备污泥活性炭的最佳工艺条件,即：固液比1g:1.5mL,氢氧化钾浓度0.40mol.L-1,浸渍时间24h,活化时间420s。此工艺条件下制备的污泥活性炭碘吸附值为537.63 mg.g-1,产率为74.09％。     

石油焦预氧化及多孔碳的制备

以石油焦和含油污泥为原料,在活化剂的作用下共同热解制备多孔活性炭材料。将得到的多孔碳进行碘吸附值、苯吸附值、BET等测定,确定多孔碳的比表面积及孔结构。研究硝酸预处理石油焦对多孔碳性能的影响以及微波功率和微波辐照时间对多孔碳的影响。结果表明:经硝酸氧化处理所得的活性炭吸附性能明显提高;微波功率越高对物料的活化作用越好,经微波活化的活性炭吸附性能越好;在微波功率800 W条件下,比表面积最大为1 396.91m2/g;微波加热时间约30 min可获得明显的催化效果。     

活化剂对活性炭-多孔陶瓷复合材料的吸附特性影响研究

以活性炭硅藻土基多孔陶瓷复合材料为研究对象,分别探讨了KOH、ZnCl2和H3PO4三种活化剂的作用效果.根据样品的碘吸附值、含炭量及比表面积确定最佳的活化条件,并采用扫描电镜观察样品的微观形貌.结果表明,三种活化剂中,ZnCl2的活化效果较好,其最佳添加浓度为20%(质量百分比)、活化温度为800℃、活化时间为90 min,制得的活性炭多孔陶瓷复合材料碘吸附值为212.9 mg.g-1,比表面积为136.2 m2.g-1,炭在活化过程中的得率为47.2%.     

水解木质素制备药用活性炭的研究

以水解木质素为原料,用化学法(ZnCl2为活化剂)制备药用活性炭。研究活化温度、活化时间、料液比(水解木质素与化学药品活化剂溶液的重量比)等对活性炭的得率、硫酸奎宁吸附值和亚甲基蓝吸附值的影响;确定了用水解木质素制备药用活性炭适宜的工艺条件:活化温度为550℃,活化时间为2h,料液比为1∶3.5,ZnCl2溶液浓度为46°Be′(60℃)。结果表明,药用活性炭的得率为50.28%;活性炭的硫酸奎宁吸附值≥120mg/g,亚甲基蓝吸附值180mg/g,pH6.5,铁0.01%,氯化物0.05%,硫酸盐0.05%,灰分2.63%,酸溶物0.6%,水溶性锌盐0.003%,硫化物、重金属(以Pb计)、氰化物、未炭化物均为合格。     

微波辅助制备甜菜渣活性炭

为了使甜菜渣得到更加充分有效的利用,本文探究了以甜菜渣为原料、氯化锌为活化剂、微波辅助制备甜菜渣活性炭的可行性。本文研究了甜菜渣和氯化锌溶液的比例(料液比)、氯化锌浓度、微波功率和辐照时间对活性炭吸附性能和产率的影响,并用氮气等温吸附、红外光谱和扫描电镜分析了最优制备条件下活性炭的比表面积、表面官能团和微观孔结构,得出其制备的最佳工艺条件为:料液比1∶6,氯化锌浓度30%,微波功率700 W和微波时间10 min。相应的活性炭的碘吸附量为1127.57 mg/g,亚甲基蓝吸附量为217.7 mg/g,产率为25.9%,BET比表面积为927.36 m2/g,总孔容为0.39 cm3/g,且表面具有含氧官能团和较好的孔结构。实验结果证实,以甜菜渣为原料、氯化锌为活化剂的微波辅助制备甜菜渣活性炭是可行的,为开发甜菜渣的高附加值产品提供了理论依据。     

富含纳米孔活性炭的制备、表征及其吸附性能研究

以玉米秸秆皮为原材料,在无惰性气体氛围下,以ZnCl2为活化剂制备活性炭.以亚甲基蓝为探针分子,通过正交实验获得最优活性炭的制备工艺.通过扫描电镜对所制最优活性炭的表面形貌进行研究,运用氮气吸附-脱附实验对其比表面积和孔容积进行检测,并考察了吸附时间、吸附温度对其吸附亚甲基蓝性能的影响.扫描电镜观测到自制活性炭表面具有大量纳米孔,氮气吸附-脱附实验结果表明,自制活性炭平均孔径为1.98 nm,比表面积达到934 m2/g,孔结构中以微孔为主.自制活性炭在60 min左右可以达到吸附平衡,并且吸附效果随温度升高变化不大,吸附效果明显优于市售活性炭.     

2-Steps Preparation Activated Carbon from Solidago Canadensis: Carbonized by Electrial heating and Activated by Microwave Radiation

The activated carbon(AC)was prepared from Solidago Canadensis(SC),an alien invasive plant.The plant was firstly carbonized under nitrogen at 400 ℃ for 90 min in an electrical furnace,and then the carbonized product was activated with KOH through microwave radiation.Effects of KOH/C ratio,microwave power,microwave radiation time on the adsorption capacities and yield of AC were evaluated.It indicated that the optimum conditions were KOH/C ratio 2 g/g,microwave power 700 W,and microwave radiation time 6 min.The carbonation process of SC was analyzed by thermogravimetry(TG).The pore structural parameters and surface functional groups of the AC were characterized by nitrogen adsorption-desorption and Fourier Transformed Infrared Spectroscopy(FTIR),respectively.The activation yield,the surface area,the average pore size,and the average micropore size of AC prepared from optimum conditions were 53.75%,1 888 m2/g,0.567 nm,and 0.488 nm,respectively.The adsorption amounts of AC were 302.4 mg/g for methylene blue and 1 470.27 mg/g for iodine.     

酒糟渣活性炭的制备及其表征

以酒糟渣为原料,采用浓酸炭化法,KOH活化法制备了活性炭。考察了活化温度、活化时间、碱炭质量比以及酒糟渣／KOH质量比对活性炭的影响。采用SEM、BET、FT-IR、XRD对其物化性能进行了表征分析。结果表明：在活化温度为800℃、活化时间为3h、碱炭质量比为3：1、酒糟渣／KOH质量比为4：1时制备的活性炭性能最优。该酒糟渣活性炭吸附孔容为0．88248cm3／g,DFT比表面积为3654．9m3／g,碘吸附值为2216．3mg／g,亚甲基蓝吸附值为389．40mL／g。     

核桃壳真空化学活化制备活性炭

采用真空化学活化法,以核桃壳为原料,氯化锌为活化剂制备活性炭,探讨体系压力、活化温度、浸渍比对活性炭比表面积、孔径分布、碘值和亚甲基蓝值以及表面性质的影响。研究结果表明,30 kPa时制备的活性炭其比表面积和总孔体积比常压条件时分别提高了27%和25%;在低压条件下有利于微孔的形成,在高浸渍比的条件下有利于中孔的形成。在体系压力为30 kPa,活化温度为450℃,浸渍比为2.0时,所得活性炭的BET比表面积为1 800 m2/g,总孔体积为1.176 cm3/g,等电点为9.15,碘吸附量为1 050 mg/g,亚甲基蓝吸附量为315 mg/g。     

微波法制备污泥活性炭及其在制药废水处理中的应用

采用微波加热法,以制药厂污泥为原料,氯化锌为活化剂制备污泥活性炭.结果表明,微波功率、辐照时间和氯化锌浓度对污泥活性炭吸附性能具有较大的影响.制备污泥吸附剂的适宜条件为:干污泥与CuSO4质量比为20∶1,ZnCl2浓度为4 mol/L,微波功率为464W,辐照时间为5min.利用该活性炭处理制药废水,脱色率和COD去除率分别达到90.2%和91.6%.     

酚醛树脂基微孔炭的制备及双电层电容特性

以热固性酚醛树脂为原料,采用CO2物理活化法制备双电层电容器,用高比表面积活性炭.由氮气吸附法测定活性炭的比表面积和孔结构,采用循环伏安、交流阻抗和恒电流充放电考察其在3000/KOH水溶液中的电容特性.结果表明,随着活化时间的延长,所得活性炭收率下降,比表面积、总孔孔容和质量比电容则不断增加;具有高比表面积和宽孔径分布的试样APF957质量比电容值最高,电流密度由50 mA/g提高到1000 mA/g时,其放电比电容由211.6 F/g降低到196.5 F/g,容量保持率达到9300/,显示出良好的功率特性.     

微波改性活性炭吸附1,2-二氯乙烷的性能研究

采用微波高温烧结炉分别在600℃,700℃和800℃下对商业活性炭进行改性,利用比表面积及孔径分析仪、Boehm滴定、傅立叶变换红外光谱比较分析活性炭的比表面积和孔结构、表面官能团等物化性质.以1,2-二氯乙烷为吸附质进行固定床吸附实验.研究表明:改性后活性炭表面酸性基团减少,碱性基团随温度升高增多;比表面积、孔容减小,微孔比表面积增加;活性炭对1,2-二氯乙烷的吸附量排序为:AC-800AC-700AC-600AC-0;灰色关联度分析结果表明:改性活性炭的物理结构特性对吸附量的影响大于表面基团;D-R模型和动力学模型拟合结果都表明活性炭对1,2-二氯乙烷的吸附主要为物理吸附.     

微波-磷酸一步法制备油茶果壳基活性炭

为了获得农林废弃物油茶果壳制备活性炭的新方法,以磷酸为活化剂,微波内热方式进行炭化-活化一步法制备油茶果壳基活性炭的研究,考察了原料粒度、浸渍比、磷酸浓度、微波时间、微波功率和浸渍时间对活性炭碘吸附性能的影响,并以自制油茶果壳基活性炭为吸附剂进行了茶油毛油脱色。结果表明,油茶果壳基活性炭制备的适宜条件为:原料粒度0.25～0.38 mm,浸渍比1∶2,磷酸浓度60 wt%,微波时间18 min,微波功率700 W,浸渍时间20 h,在最适宜条件下所得活性炭的比表面积为1 169.69 m2/g,脱色茶油的色泽为罗维朋色号黄(Y)11和红(R)1.0,符合国标油茶籽油GB/T 11765-2003对一级油品的色泽技术要求。研究结果可为油茶主副产业链的综合利用提供理论依据。     

磷酸-硫酸活化法制备木屑活性炭工艺

以林业废弃物杨木屑为原料,采用正交试验法探讨以磷酸为主活化剂,浓硫酸为辅助活化剂,在不同工艺条件下制备活性炭,测定其亚甲基蓝脱色力和碘的吸附值,考虑活化因素对活性炭得率和吸附性能的影响,确定最佳工艺参数.试验结果表明:磷酸-硫酸活化法制备木屑活性炭的最佳工艺条件为浸渍比1∶2.5,浸渍浓度60%,活化时间90 min,活化温度550℃.     

煤基高比表面积活性炭的制备研究

以山西阳泉无烟煤为原料,NaOH为活性剂,采用化学活化法对煤基高比表面积活性炭的制备进行实验分析研究,着重考察了碱炭质量比、活化温度和活化时间对活性炭吸附性能的影响。结果表明,在碱炭比为4、活化温度为800℃、活化时间为1 h的条件下,可以制得比表面积为2 637 m2/g、总孔容为1.36 cm3/g、碘吸附值为2 893 mg/g、亚甲蓝吸附值为476 mg/g的煤基高比表面积活性炭。