木聚糖酶处理对麦秸纤维板吸着等温线的影响

对经木聚糖酶处理和未处理麦秸纤维制成的纤维板吸着特性进行了研究。测定了不同温度和相对湿度条件下,木聚糖酶处理对麦秸纤维板平衡含水率的影响,求得麦秸纤维板的吸着等温线,并且利用GAB模型对麦秸纤维板吸着等温线进行了拟合。结果表明：经过木聚糖酶改性处理麦秸纤维制成的纤维板,在相同环境温度和相对湿度条件下,吸湿和解吸平衡含水率均低于未处理麦秸纤维板;温度和相对湿度对麦秸纤维板的吸着特性有一定影响;采用GAB模型能较好地拟合试验数据,再现麦秸纤维板的吸着等温线。     

大木竹竹材物理性质的研究

以材性优良的毛竹等竹种为参比,研究了丛生竹种大木竹竹材的物理性能.结果表明:大木竹竹材的基本密度为0.618 g/cm3,小于毛竹的基本密度(0.765 g/cm3),而比参比的其他丛生竹密度大或与之相当;大木竹竹材气干体积干缩率为7.7%,吸水饱和体积湿胀率为18.686%,饱湿含水率为77.8%,均大于毛竹材的相应值.     

不同竹龄毛竹材纤维饱和点的测定

以毛竹为研究对象,采用力学法对不同竹龄毛竹的纤维饱和点计算进行了系统研究。结果表明：通过Boltzmann曲线拟合毛竹材力学性能得到的毛竹纤维饱和点较为合理,利 用4种力学性能指标所测得同一竹龄毛竹材纤维饱和点略有差异。纤维饱和点随竹龄的变化规律相同,即从0.5~1.5年生降幅明显,大于1.5年生后趋于稳定。     

平安竹纤维形态变异特征及其成因分析

【目的】阐明矢竹矮秆稳定变异体——平安竹纤维形态学特征并初步阐释其变异机制。【方法】利用石蜡切片及数量统计学方法进行显微观测与数据分析; qRT-PCR分析基因相对表达量; UPLC/GC-MS法测定赤霉素含量。【结果】平安竹竹秆不同部位纤维长度、长宽比及壁腔比显著小于矢竹; 但其宽度与腔径值显著大于矢竹; 而其不同部位纤维壁厚值虽小于矢竹,但差异不显著。平安竹地下茎纤维在长度、长宽比、壁厚及壁腔比上显著小于矢竹,但其宽度与腔径值则显著大于矢竹。形态解剖学分析显示,平安竹地下茎纤维细胞形态变异出现于节间活跃生长阶段。赤霉素及细胞壁与细胞骨架相关基因表达量分析结果表明,赤霉素信号途径在平安竹节间生长起始阶段即受到抑制; 而其细胞壁与细胞骨架相关下游功能基因则在其伸长早期与活跃阶段显著低于矢竹; 赤霉素含量分析也证实各赤霉素含量早在平安竹节间伸长起始阶段就低于矢竹。【结论】赤霉素信号途径受抑导致其下游细胞壁与细胞骨架组织相关基因下调是最终导致平安竹纤维细胞生长异常的原因之一。     

慈竹不同变异类型的纤维形态研究

通过对四川省青神县慈竹不同变异类型的纤维形态指标进行观测,比较分析了不同变异类型纤维形态特征的差异及变异规律,并对其利用价值进行了探讨.结果表明:慈竹6种类型的平均纤维长度都大于1.6 mm,除罗汉慈外均大于毛竹;慈竹、琴丝慈和蛇头慈纤维长度分布的最大频率出现在2.0 ～3.0 mm之间,其余慈竹类型的纤维长度分布最大频率出现在1.0 ～2.0 mm之间.除罗汉慈外,其余慈竹类型的纤维长宽比平均值均大于100,且大于毛竹.慈竹6种类型纤维平均壁腔比在1.77～ 3.96之间,均小于毛竹.在轴向上,慈竹不同类型纤维的长度、宽度、长宽比和腔径的变异规律随交异类型的不同而不同,其纤维壁厚和壁腔比则具有相似的交异规律;在径向上,慈竹不同类型竹壁内侧的纤维长度、腔径均大于外侧纤维,其竹壁内侧的纤维宽度、长宽比、壁厚和壁腔比大多小于外侧.说明除罗汉慈外慈竹其余变异类型的竹材纤维质量均优于毛竹,琴丝慈的竹材纤维质量优于慈竹,其造纸性能最佳.     

模拟干旱处理下毛竹光响应特征分析

【目的】研究毛竹叶绿素含量和光响应参数的变化,比较分析毛竹对干旱胁迫的响应特点,探讨毛竹抗旱生理与适应变化,为毛竹林的水分管理提供理论依据。【方法】以Ⅰ～Ⅲ度毛竹为试验材料,分别测定干旱和对照条件下毛竹叶片光合色素含量和光响应曲线,并计算出其最大净光合速率(P_n,max)、光饱和点(P_LSP)、光补偿点(P_LCP)、暗呼吸速率(R_d)和表观量子效率(η_AQY)等光合参数。【结果】毛竹叶片叶绿素含量在不同竹龄之间差异都不显著,而Ⅱ度竹光合速率显著高于Ⅰ度竹和Ⅲ度竹,Ⅰ度竹和Ⅲ度竹之间光合速率差异不显著; Ⅰ度竹各叶绿素含量在干旱条件下显著低于对照,而Ⅲ度竹各叶绿素含量在干旱和对照间差异不显著,Ⅱ度竹只有类胡萝卜素含量在干旱条件下显著高于对照。各竹龄毛竹叶绿素含量与光合速率变化不一致,干旱处理下Ⅰ度竹和Ⅲ度竹P_n显著高于对照,Ⅱ度竹则无显著差异。【结论】干旱处理提高了Ⅰ度竹和Ⅲ度竹光能利用效率,降低了Ⅱ度竹对光的生态适应能力。     

外源GA3对毛竹实生苗新分蘖竹株秆形与 竹材纤维质量的影响

为探索竹类植物秆形生长机制,研究利用激素调控竹材纤维生长质量,采用不同质量浓度(0、20、40、60 mg/L)赤霉素(GA₃)处理毛竹实生苗,观察并测定处理后新分蘖竹株数量、秆形及竹材纤维质量变化情况。结果表明:毛竹实生苗叶面喷施不同浓度GA₃后,新分蘖竹株秆高、节间长和叶片数量均有极显著增加(P<0.01),20、40和60 mg/L GA₃处理实生苗新分蘖竹株秆高分别比对照(0 mg/L)增长0.56、1.19和1.21倍,平均节长度增加0.49、1.05和1.10倍,叶片数量增加35.61%、48.35%和38.68%; 新分蘖竹株数量、单株节数和地径在处理与对照之间无显著差异。伴随秆形变化,新分蘖竹株竹材纤维质量也有所改变。20、40和60 mg/L GA₃处理,明显增加了新分蘖竹株竹材纤维细胞长度,分别比对照增加13.17%、20.68%和21.46%; 但各处理对竹材纤维细胞的宽度作用不显著,从而使得处理后竹株竹材纤维的长宽比增加,有利于竹材纤维质量提升。另外发现,不同浓度GA₃处理对竹材纤维细胞的壁厚、腔径和纤维组织比量的影响不显著。分析认为,赤霉素处理能显著改善毛竹实生苗新分蘖竹株的竹材纤维质量,但对提高竹材纤维产量无显著作用。     

含水率对落叶松木材材性检测指标的影响

以落叶松为研究对象,利用无损检测技术,研究不同含水率下木材材性检测指标的变化规律。结果表明：在木材含水率未达到临界纤维饱和点时,木材的材性检测指标随含水率的增大急剧下降;在木材含水率大于临界纤维饱和点时,木材的材性检测指标随含水率的增大下降幅度较小。以木材含水率为单一变量,以木材纤维饱和点(30%)为分界点,建立含水率与落叶松木材材性检测指标的理论公式。用实测结果对理论公式进行修正,修正后的结果表明：材性检测指标的实测值与理论值变化趋势一致,用应力波测量仪和微钻阻力仪测定的波阻模量值的实测值与理论值最接近。同时,推导的理论公式可以作为现场测定木材材性指标的依据。     

标准FZ／T73023——2006应用于竹原纤维织物抗菌性的研究

采用最新标准对竹原纤维织物及毛竹竹粉的抑菌率进行了测定.在奎因法和振荡法中,竹原纤维织物对金黄色葡萄球菌(ATCC 6538)的抑菌率分别为50.1%和9.0%,时大肠杆菌(8099)的枊菌率分别为75.1%和26.5%,毛竹竹粉的抑菌率均为0.根据新标准评价竹原纤维织物虽有一定的抑茵性,但无抗菌效果,并且毛竹竹粉无抗菌效果.分析认为竹原纤堆自身不舍有抗菌化学物质,其抑菌性能来源于天然、独特的纤雏结构,属于物理抑菌.     

新到中国专利资料选登

一、竹基高聚物复合板材及其制法和应用将加工成的任何几何形状的竹板材,浸渍于缩合物(如甲醛)等水溶液中,再经固化即成。不翘曲变形,不干裂、发霉、虫蛀,可与任何物质或物体粘合一起,可作木材替代物且性能优于木材。二、一种有竹纤维的人造刨花板生产过程中加入竹质纤维或竹粉纤维,基板静曲强度和抗拉强度达到甚至超过天然木质板,可代替胶木板和塑料板。     

青豆种子等温线及平衡含水率模型

为研究青豆种子的热动力学特性,深入理解青豆吸附过程的水分特性和所需能量变化,利用饱和盐溶液,采用静态称重法测定了青豆种子在20～40,℃和水分活度在0.112～0.946范围的等温线;采用非线性回归方法确定了BET多分子层吸附理论模型的系数,并判定了青豆的吸附与解吸模型的拟合优度;应用Clausius-Clapeyron方程计算了青豆的净等量吸附热.结果表明：吸附与解吸相比存在明显的滞后现象;解吸时单分子层饱和吸附量大于吸附时的数值,随着温度升高青豆的单分子层饱和吸附量下降;吸附层数的变化趋势与单分子层饱和吸附量的相反;在Henderson、修正的Henderson、修正的Chung-Pfost、Halsey、修正的Halsey、修正的Oswin、修正的GAB模型中,Halsey模型拟合优度最佳;净等量吸附热随平衡含水率的增加而减少.     

Adsorption Mechanism of Disperse Dye on Elastic Polyurethane Fibre

In this paper, the adsorption isotherms of two disperse dyes, C.I. Disperse Red 60 and C.I. Disperse orange 76, on two kinds of PU fibers at 90℃ were measured respectively. It was found that these adsorption isotherms followed a dual model, Nernst and Langmuir. Based on the parameters obtained in studying, the relationship between the chemical structure of dyes and their adsorption behaviors was arialyzed. Through the measurement of washing fastness of dyed sample with two dye concentrations, 1% （o.w. f） and 3% （o. w. f）, it was found that the pale shade dyeing possessed better wet-fastness than the dark. This phenomenon confirmed further that the disperse dyes were sorbed on the PU fiber by langmuir sorption and the partition mechanism.     

Comparison between the Direct Dyeing Kinetics of Bamboo and Conventional Viscose Fibers

Two direct dyes were applied to conventional viscose(CV)and bamboo viscose(BV)fibers,which were prepared from bamboo cellulose pulps,and the dyeing kinetics of two fibers were compared.Three kinetic equations,namely Chrastil,Cegarra-Puente,and Vickerstaff,were used to fit the experimental dyeing rate points,showing that the best result was obtained by the Chrastil equation.BV fibers displayed slightly higher dyeing rates and dye adsorption values at initial stages,but a bit lower dye adsorption values at eq...     

油茶籽的吸附等温线及热力学性质

为充分了解油茶籽水分含量与水分活度、温度之间的复杂关系,运用吸附原理,通过静态调整环境湿度法,研究了油茶籽不同温度下的吸附等温线,选择5种常用数学模型进行拟合,并在此基础上分析油茶籽的热力学性质.结果表明,修正Henderson模型的拟合度最高(R2=0.999 9,RMSE=0.007 1),根据该模型获知油茶籽在20,30,40℃下的相对安全水分含量和绝对安全水分含量分别为9.48%与8.00%,8.96%与7.57%,8.51%与7.19%.热力学性质显示,油茶籽的等量吸附热、吸附结合能均随平衡含水率的增加而不断下降,当平衡含水率一定时,吸附结合能随温度的升高而增大.     

INVESTIGATION OF SOFTENING AGENT PREPARATION AND PERFORMANCE OF HANDMADE ECOCOMPOSITES WITH CONIFEROUS WOOD AND BASALT FIBERS

NTRODUCTIONComposites are one of the inevitable trend of material development. Through design of composites, i.e. according to choice of raw materials, control of material component and technology condition, the advantages of all kinds of ingredient in materials were exerted sufficiently each other. Integration performances were therefore presented excellently. At Present it was difficult to recover for many composites. Moreover these disadvantages brought about a series of serious pollut…     

玉米芯活性炭的制备及储气性能

天然气、氢气、二氧化碳等气体的吸附研究在洁净气体代油燃料的强化存储、温室气体减排、大气治理等方面具有重要意义,其重点内容是高效吸附材料的开发．以玉米芯为原料,采用磷酸活化法制备了含有较高中孔比例的活性炭,其比表面积达到1,610,m2/g,孔容为1.72,cm3/g,中孔体积达到1.14,cm3/g,占孔容的66％．测定了H2、N2、CH4和 CO2在该吸附剂上的吸附等温线．在0.4,MPa 时,CO2对 CH4的选择性达到2.76,对 N2的选择性达到7.63,对 H2的选择性达到42.31,具有良好的分离应用前景．测定了水存在条件下甲烷在该活性炭上的吸附等温线,由于孔尺寸有利于甲烷水合物的生成,因此甲烷吸入量较在干燥吸附剂上提高了82％．根据克劳修斯-克拉佩龙方程计算了甲烷水合物的生成焓为-64.37,kJ/mol．     

木材中水分分离热的测定

<正>一、前言 处于干燥过程的含水木材需要外界不断地吸取热量,准确地测定这种热量,对于计算木材干燥的热效率和木质材料的加工有重要意义。由于木材中水和木材的结合状态与木材的含水率有密切的关系,因此测定木材中水份脱离时所吸收的能量,对于研究木材和水的结合状态也有一定的价值。     

稻秸/木材密度纤维板的复合工艺及其性能

分析了稻秸木材复合工艺配比及防水剂的添加量(0.8%、1.2%、1.6%、2.0%)对稻秸木材复合中密度纤维板性能的影响。结果表明:采用稻秸与木材原料分别进行纤维分离,再混合后施胶的复合工艺,当草木配比为1∶1,防水剂加量为1.2%,脲醛树脂胶粘剂的施胶量为12%时,生产出的稻秸/木材中密度纤维板,除吸水厚度膨胀率外,各项性能均能达到中密度纤维板标准要求。     

Packaging Bags with the Function of Micro-environment Modification

Three kinds of packaging bags composited with barrier film and moisture absorbents were designed in order to find out how to create an internal micro-environment with low 02 content and relative humidity （RH）. Peanuts with different moisture contents were filled into packaging bags and stored in an environmental chamber for a certain period of time. An RH recorder was sealed in each bag and the RH inside the bag was recorded. The moisture contents of peanuts before and after storage were measured as well. It is found that peanuts with moisture content of 13 % can reduce 02 content inside the bag by the aerobic respiration, achieving the self modified atmosphere packaging （ MAP ） effect. A micro- environment with lower RH can be created by using super-absorbent fiber （SAF） or mineral bag as the moisture absorbent. The moisture contents of peanuts stored in the bags with SAF and mineral bag as moisture absorbent decreased from 13% to 10.5% and 11.3%, respectively. SAF is a promising material of packaging bags composited with barrier film, in which a low RH and high CO2 content can be created.