氧化镍在γ－Al_2O_3和TiO_2－Al_2O_3上的分散状态研究

采用浸渍法制备了系列ＮｉＯ／γ－Ａｌ２Ｏ３，ＮｉＯ／ＴｉＯ２－Ａｌ２Ｏ３催化剂样品，用ＸＲＤ，ＥＸＡＦＳ等方法对这些样品进行了分析．ＸＲＤ相定量方法测得ＮｉＯ在γ－Ａｌ２Ｏ３载体上的最大分散量为０．０６５ｇＮｉＯ／１００ｍ２Ａｌ２Ｏ３，而ＮｉＯ在ＴｉＯ２－Ａｌ２Ｏ３载体上的最大分散量为０．０８１ｇＮｉＯ／１００ｍ２ＴｉＯ２Ａｌ２Ｏ３。ＥＸＡＦＳ分析结果表明：ＴｉＯ２的引入改变了ＮｉＯ在载体表面上的分散状态．     

NiO／γ—Al2O3体系分散态研究

对不同温度下焙烧的ＮｉＯ／γ－Ａｌ２Ｏ３体系的ＸＲＤ研究表明,ＮｉＯ在γ－Ａｌ２Ｏ３表面分散阈值随温度升高而增加,在低于５５０℃时,呈单层分散状态,而在较高温度时,有一定量的ＮｉＯ进入体相,此时ＮｉＯ／γ－Ａｌ２Ｏ３体系为ＮｉＯ晶相,分散相和体相三相混合体。     

NiO/γ-Al_2O_3体系分散态研究

对不同温度下焙烧的ＮｉＯ／γ－Ａｌ２Ｏ３体系的ＸＲＤ研究表明,ＮｉＯ在γ－Ａｌ２Ｏ３表面分散阈值随温度升高而增加．在低于５５０℃时,呈单层分散状态,而在较高温度时（７００℃以上）,有一定量的ＮｉＯ进入体相,此时ＮｉＯ／γ－Ａｌ２Ｏ３体系为ＮｉＯ晶相、分散相和体相三相混合体     

包镍Al2O3颗粒的获得及其在复合材料制备中的应用

用自制的化学气相沉积装置在Ａｌ２Ｏ３颗粒表面获得了Ｎｉ涂层,并通过负压铸渗工艺获得了Ａｌ２Ｏ３颗粒／耐热钢基复合材料,考察了其高温磨料磨损特性,结果表明：Ｎｉ涂层能显著改善Ａｌ２Ｏ３与耐热钢的湿润性,从而解决了Ａｌ２Ｏ３颗粒在耐热钢液中均匀分散的难题,所得复合材料具有优良的高温磨料磨损抗力。     

用热分析方法研究制备了Ni／Al2O3催化剂过程中的热分…

以Ｎｉ（ＮＯ３）２．６Ｈ２Ｏ为参照物，用热重分析和差热分析方法，通过研究一系列不同Ｎｉ负载量的Ｎｉ（ＮＯ３）２／Ａｌ２Ｏ３的热分解过程发现，无论是在空气气氛还是氮气气氛中，纯Ｎｉ（ＮＯ３）２．６Ｈ２Ｏ的分解均是分五步进行的，其中前四步为脱水，后一步是Ｎｉ（ＮＯ３）２分解为Ｎｉ２Ｏ３．当Ｎｉ（ＮＯ３）２负载于Ａｌ２Ｏ３表面后，其分解情况随载Ｎｉ量的不同而发生变化。与纯Ｎｉ（ＮＯ３）２．６Ｈ２Ｏ相比，     

用热分析方法研究制备Ni/Al_2O_3催化剂过程中的热分解过程

以Ｎｉ（ＮＯ３）２·６Ｈ２Ｏ为参照物，用热重分析和差热分析方法，通过研究一系列不同Ｎｉ负载量的Ｎｉ（ＮＯ３）２／Ａｌ２Ｏ３的热分解过程发现，无论是在空气气氛还是氮气气氛中，纯Ｎｉ（ＮＯ３）２·６Ｈ２Ｏ的分解均是分五步进行的，其中前四步为脱水，后一步是Ｎｉ（ＮＯ３）２分解为Ｎｉ２Ｏ３．当Ｎｉ（ＮＯ３）２负载于Ａｌ２Ｏ３表面后，其分解情况随载Ｎｉ量的不同而发生变化．与纯Ｎｉ（ＮＯ３）２·６Ｈ２Ｏ相比，负载后的样品的脱水变得更为容易了．在最终含Ｎｉ３％的样品上，分解过程仅有两步：第一步是在较低温度下失水，第二步则是Ｎｉ（ＮＯ３）２分解为ＮｉＯ．随着Ｎｉ含量的增高，失水又开始分步，并向Ｎｉ（ＮＯ３）２·６Ｈ２Ｏ的分解靠近．总的说来，Ｎｉ（ＮＯ３）２的分解变得容易了，它能在更低温度下分解，分解产物可能包括Ｎｉ２Ｏ３     

2024铝合金涂覆Ni,Fe和Cu激光表面合金化

研究了２０２４铝合金涂Ｎｉ、Ｆｅ和Ｃｕ激光表面合金化，结果表明，在分别涂有Ｎｉ、Ｆｅ和Ｃｕ的合金层，分析形成了Ｎｉ３Ａｌ，Ｆｅ３Ａｌ，ＦｅＡｌ和Ｃｕ９Ａｌ４等金属间化合物，由于各种金属间化合物的形成，在合金化层与基体之间形成了无孔洞、无夹杂的冶金结合使金表面硬度提高２－３倍。     

Ni-Fe-P/Al_2O_3复合电沉积工艺对Al_2O_3复合量的影响

研究了Ｎｉ－Ｆｅ－Ｐ／Ａｌ２Ｏ３复合电沉积的工艺参数对沉积层中Ａｌ２Ｏ３硬质微粒复合量的影响．结果表明，复合电沉积层中Ａｌ２Ｏ３微粒复合量随镀液中Ａｌ２Ｏ３含量、温度、阴极电流密度以及ＮａＨ２ＰＯ２含量的改变表现出不同的变化趋势．在实验工艺条件下，可获得Ａｌ２Ｏ３硬质微粒均匀弥散分布的复合电沉积层，其中Ａｌ２Ｏ３的最大复合量可达１３．４８％（体积）．     

Ni－LaO_x／r－Al_2O_3催化剂中助剂及载体电子效应的研究

本文用ＤＶ－Ｘ＿α量子化学方法计算了甲烷化催化剂Ｎｉ一ＬａＯ＿ｘ／ｒ－Ａｌ＿２Ｏ＿３中载体及助剂与镍相互作用模型的电子结构，由计算结果发现，缺氧型稀土氧化物（ＬａＯ＿ｘ）是一个好的电子给予体，镍与载体ｒ－Ａｌ＿２Ｏ＿３作用后，电子由镍向载体转移，表面镍处于缺电子状态，稀土氧化物助剂与镍相互作用后，电子向镍转移．由此推断在Ｎｉ／ｒ－Ａｌ＿２Ｏ＿３催化剂中添加稀土氧化物助剂，将使表面镍的缺电子状态得以缓解，表面镍富集电子，从而有利于对吸附的ＣＯ分子的激活．     

Al2O3／W层状复合材料的制备

采用流态成型－离心注浆成型，热压烧结成功地制备了Ａｌ２Ｏ３／Ｗ层状复合材料，研究了Ａｌ２Ｏ３层，金属Ｗ层的厚度对层状复合材料力学性能的影响。结果表明：Ａｌ２Ｏ３层，金属Ｗ层的厚度有关，而且与Ａｌ２Ｏ３／Ｗ层厚比有关。     

喷丸处理对1Cr13钢选择氧化的作用

对1Cr13钢进行了不同时间(5,10,20,40 min)的喷丸处理,研究了喷丸处理对1Cr13钢在800℃空气中的抗高温氧化性能。高温氧化实验及表面形貌观察分析发现,喷丸处理形成了一个晶粒细化层,降低了1Cr13钢发生选择氧化所需的临界含量,氧化增重显著降低,氧化膜剥落也有所改善。喷丸处理促进了1Cr13钢表面形成选择性的保护氧化膜,提高了1Cr13钢的抗高温氧化性能,喷丸处理10~20 min的试样抗高温氧化性能最佳。     

MA-SPS制备超细晶Ti-8Mo-3Fe合金的摩擦磨损性能

以机械合金化+放电等离子烧结(MA-SPS)制备的超细晶Ti-8Mo-3Fe合金为研究对象,研究了合金在模拟体液(SBF)中的摩擦磨损性能,并与放电等离子烧结制备的微米尺寸晶粒的Ti-8Mo-3Fe合金、铸造纯Ti及Ti-6Al-4V(TC4)合金进行了对比.结果表明:采用MA-SPS工艺可制备出高致密度、组织均匀的超细晶Ti-8Mo-3Fe合金,合金由β相及少量α相组成,平均晶粒尺寸为1.5μm,显微硬度为448 HV;在相同摩擦磨损条件下,超细晶Ti-8Mo-3Fe合金的摩损程度明显低于微米晶粒Ti-8Mo-3Fe和铸态的纯Ti及TC4合金,具有最低的磨损体积和较稳定的摩擦系数.超细晶Ti-8Mo-3Fe合金的磨损机制为磨粒磨损,而微米晶粒Ti-8Mo-3Fe和铸态纯Ti及TC4合金的磨损机制为磨粒磨损和黏着磨损并存的混合磨损.     

Isothermal oxidation behavior and mechanism of a nickel-based superalloy at 1000℃

The oxidation behavior of a nickel-based superalloy at 1000°C in air was investigated through X-ray diffraction, scanning electron microscopy, andenergy-dispersive spectroscopy analysis. A series of oxides, including external oxide scales (Cr2O3, (TiO2 + MnCr2O4)) and internal oxides (Al2O3,TiN), were formed on the surface or sub-surface of the substrate at 1000°C in experimental still air. The oxidation re-sistance of the alloy was dependent on the stability of the surface oxide layer. The continuity and density of the protective Cr2O3 scale were affected by minor alloying elements such as Ti and Mn. The outermost oxide scale was composed of TiO2 rutile and MnCr2O4 spinel, and the growth of TiO2particles was controlled by the outer diffusion of Ti ions through the pre-existing oxide layer. Severe internal oxidation oc-curred beneath the external oxide scale, consuming Al and Ti of the strength phaseγ′ (Ni3(Al,Ti)) and thereby severely deteriorating the sur-face mechanical properties. The depth of the internal oxidation region was approximately 35μm after exposure to experimental air at 1000°C for 80 h.     

铸造Fe_3Al合金的高温抗氧化性能研究与应用

通过对铸造Fe3Al合金在800～900℃温度范围内的抗氧化性能研究,表明铸造Fe3Al合金在高温氧化过程中表面形成了致密的氧化层,具有优良的抗氧化性能。采用铸造Fe3Al合金制备的几种产品的使用效果良好,说明在一定条件下替代Cr Ni系耐热钢是可行的。     

铝合金微弧氧化技术

介绍了铝合金的微弧氧化技术的研究现状,阐述了在电解液中高压脉冲电场作用下铝合金表面Ａｌ２Ｏ３陶瓷层于不同时间段的形成条件和生成机理,及与现行铝合金表面处理工艺相经可能应用的领域。     

Al-2.15％Mn合金的组织及摩擦学特性

采用搅拌法制备了Al-2.15 ％Mn合金,对其显微组织、强化机制及摩擦磨损性能进行了试验研究.结果表明:Al-2.15％Mn合金的组织为含Alu Mn4和Al6 Mn的α-Al固溶体;合金中Al6Mn的沉淀强化作用使其硬度较纯Al提高了60％;纯Al的冲击断口形貌为塑性断裂,Al-2.15％Mn合金的冲击断口形貌为准解理断裂;纯Al与Al-2.15％Mn合金在湿摩擦下的磨损量均大于干摩擦的磨损量;湿摩擦的腐蚀一机械磨损作用使磨痕为犁沟和蚀坑,干摩擦中磨屑的成片脱落由机械磨损中的黏着磨损引起;在干摩擦与湿摩擦中,纯Al的摩擦因数均大于Al-2.15％Mn合金的摩擦因数,Al-2.15％Mn合金较纯Al表现出更加优良的耐磨性.     

铝合金直接氧化合成Al／Al2O3研究现状

评述了Al-Mg-Si合金直接氧化合成Al/Al2O3的工艺、组织结构、性能，认为其中问题主要为：熔体表面Al/Al2O3氧化生长的不均匀性及Al/Al2O3复合材料组织中的孔隙给其在结构方面应用带来了限制。归纳了机制研究的显微通道假说、Mg作用模型、Si作用模型及诱发机制，指出了其中有待重视的几方面问题：氧在Al熔体中的扩散和传递过程；熔体表氧化物MgO和MgAl2O4的作用；Al-Mg-Si合金氧化组织中的固－气反应特征；Al-Mg-Si合金中Si的SiO2诱发机制以及它与Mg作用机制之间的关联性。     

SiC_p/Al_2O_(3f) 混杂增强 2024Al 复合材料摩擦磨损性能的研究

研究了２０２４铝合金、ＳｉＣｐ／Ａｌ２Ｏ３ｆ混杂增强２０２４Ａｌ复合材料与汽车刹车材料对磨时的摩擦磨损性能．借助扫描电镜对磨损形貌的观察,分析了材料的磨损机理．在本研究的试验条件下,２０２４铝合金的磨损极为严重,ＳｉＣｐ／Ａｌ２Ｏ３ｆ混杂增强２０２４Ａｌ复合材料的耐磨性能良好．由于ＳｉＣｐ／Ａｌ２Ｏ３ｆ混杂增强２０２４Ａｌ复合材料的密度较低,因而该材料在汽车工业中有广泛的应用前景．     

NiB/Al_2O_3非晶态合金催化剂抗硫性能研究

采用化学还原法制备了非晶态NiB合金及负载型非晶态NiB/Al2 O3合金 ,用浸渍法制备了Ni/Al2 O3催化剂。用ICP、BET、TPD及氢吸附等方法对催化剂进行了表征。以苯加氢为探针反应 ,以CS2 为毒物 ,对各催化剂的催化活性和抗硫性能进行了比较。研究结果表明 ,非晶态合金由于有更高的活性镍面积而表现出更高的催化活性及抗硫性能 ,载体能改善非晶态合金的性能 ,并对毒物有一定的吸附作用。在非晶态合金表面有三种中心 ,CS2 优先中毒高温吸附中心。     

化学镀Fe-Al-P合金初探

利用化学镀方法在铜基片上施镀了Ｆｅ－Ａｌ－Ｐ合金镀层。通过改变金属盐比率ＡｌＣｌ３／（ＡｌＣｌ３＋ＦｅＳＯ４）、金属盐ＡｌＣｌ３和还原剂ＮａＨ２ＰＯ２的浓度等参数,研究了合金镀层的沉积速率,成分,表面形貌及结构的变化规律,得到了最佳镀液配方,发现络合剂和还原剂的选择是提高镀层含Ａｌ量的关键。