Preparation and densification of BaTiO3 nanopowder by sol-gel autoigniting synthesis

Autoigniting synthesis of gel from Ba(NO3)2, TiO(NO3)2 and C6H8O7H2O aqueous solution was investigated at an initial temperature of 600℃ and tetragonal BaTiO3 nanopowder with particle size of 80nm was prepared. It is indicated that the specific surface area of the combustion product before and after calcination is 14.74 m2/g and 12.49 m2/g, respectively. The combustion wave is composed of solid phase reaction zone and gaseous phase flame reaction zone. The combustion flametemperature is 1 123 K derived from thermocouple measurement. The characteristics and densification behavior of the sol-gel autoigniting synthesized BaTiO3 nanopowder were investigated.     

纳米YAG粉体的制备与表征

以Y(NO3)3·6H2O、Al( NO3)3·9H2O、Nd(NO3)3·6H2O、NH4HCO3为原料,以乙醇为分散剂,采用共沉淀法制备Nd:YAG前躯体,将前躯体在不同温度下煅烧得到Nd:YAG粉体.分别采用红外光谱仪(FT-IR)、热重/差热分析仪(TG/DSC)、X射线衍射仪(XRD)、透射电子显微镜(TEM...     

溶胶-水热法制备BaTiO3基PTC超细粉体

采用乙酸钡和钛酸四丁酯为原料,用溶胶沉淀与水热相结合的方法制备钛酸钡基正温度系数(PTC)纳米粉体.通过改变KOH强碱溶液用量调节水热反应的pH值,用X射线衍射分析了不同pH值条件下钛酸钡粉体晶相,确定了钛酸钡晶核稳定存在的条件.采用化学沉淀和溶液滴定方法研究了反应前驱物中Ba(AC)2和Ti(OC4H9)4的摩尔比对生成粉体化学计量比的影响.将Ba(AC)2Ti(OC4H9)4按照摩尔比为1配置的前驱物置于饱和氢氧化钡溶液构成的富钡环境下进行水热反应,获得了符合化学计量比、晶粒尺寸30nm左右的立方相钛酸钡纳米粉.在钛酸钡纯粉制备基础之上,将施主元素Y及受主元素Mn在前驱物制备过程中引入,瓷体实现了半导化,并获得了PTC效应.     

钛酸钡陶瓷粉末的低温燃烧合成

以Ba(NO3)2-TiO2-C6H7O8.H2O为体系,在600℃加热进行低温燃烧合成实验,制得粒度为1．2－1．4μm的四方相BaTiO3陶瓷粉体,结果表明燃烧的均匀程度对燃烧产物的相组成和微观结构有很大的影响,通过热力学分析,提出低温燃烧合成BaTiO3陶瓷粉末的形成机理。     

雾滴微反应器法制备纳米氧化铈粉体

以硝酸铈和碳酸铵为原料,用新技术——雾滴微反应器法制备了纳米氧化铈粉体,并与用传统沉淀法制备的纳米氧化铈粉体进行比较,用TEM方法对制备的粉体进行表征。结果表明:雾滴微反应器法制备的纳米氧化铈粉体比传统沉淀法制备粉体的颗粒尺寸较小,粒径分布窄,分散性好。     

Bi2Fe4O9的制备及光催化性能研究

用Bi(NO3)3.5H2O和Fe(NO3)3.9H2O为基本原料,采用共沉淀法合成了Bi2Fe4O9粉体,用XRD和SEM测试了不同制备条件下得到的Bi2Fe4O9粉体的晶体结构和形貌,XRD结果表明在650℃～750℃直接煅烧2h可得到纯相Bi2Fe4O9粉体,SEM结果表明随着灼烧温度的提高,晶粒的尺寸增加,750℃时晶粒呈片状,UV-Vis分析表明,Bi2Fe4O9在可见光区域有较强的吸收,光催化性能表明,Bi2Fe4O9粉体对甲基橙降解效果较好。     

Gd_2O_3的掺入对BaTiO_3陶瓷的形貌及相变等性能的影响

通过先制备钛酸钡 (BaTiO3 )的纳米粉 ,然后按一定质量比与Gd2 O3 混合 ,烧结成陶瓷。利用XRD、RAMAN技术研究了Gd2 O3 的掺入对BT陶瓷结构的影响。通过SEM、DSC技术分别观察了Gd2 O3 对BT陶瓷颗粒形貌、一级相变的影响。研究表明 :Gd2 O3 主要存在于晶界 ;由于Gd2 O3 引起的应力的作用 ,Gd2 O3 的对BT的振动模式和一级相变产生了一定的影响 ,影响最显著的是对BaTiO3 陶瓷微观颗粒的形状和大小     

二元系的热刺激电流

测量3种不同化学成份的粉料与硅油混合物的热刺激电流。BT粉与硅油的混合物有很明显的热刺激电流（TSC），且显示出粒径存在一定的关系；TiO2粉和AIO3与硅油的混合物在测量温区几乎没有热刺激电流峰。     

BaTiO3微粉的溶胶凝胶制备与表征

采用溶胶凝胶工艺制备ＢａＴｉＯ３超微粉，利用ＸＲＤ技术研究了不同工艺条件下ＢａＴｉＯ３微粉的结晶结构。根据Ｓｃｈｅｒｒｅｒ原理计算了ＢａＴｉＯ３微晶的晶粒尺寸效应。     

钛酸钡纳米粉料的制备及喇曼光谱分析

以硝酸钡Ｂａ（ＮＯ３）２,硬脂酸（ＨＳＴ）,和钛酸四丁脂Ｔｉ（ＯＣ４Ｈ９）４为主要原料,用ＳＡＧ法（硬脂酸溶液胶－凝胶法）制备了钛酸钡纳米粉料,用ＪＯＢＩＮ ＹＶＯＮ公司的Ｕ－１０００喇曼光谱仪测量了不同温度下的喇曼光谱,通过与已指认过的喇曼谱进行比较,对获得的喇曼谱进行了分析。     

Nd(OH)3-Co3O4-Nb2O5纳米复合掺杂和传统复合掺杂BaTiO3基陶瓷性能的对比研究

 制备了Nd(OH)₃,Co₃O₄和Nb₂O₅纳米粒子以及Nd(OH)₃-Co₃O₄-Nb₂O₅纳米复合掺杂和传统复合掺杂BaTiO₃基陶瓷,研究了掺杂剂的粒径对BaTiO₃基陶瓷的微观形貌和介电性能的影响,并对纳米掺杂和传统掺杂BaTiO₃基陶瓷的性能进行了比较.结果表明,掺杂剂的粒度对BaTiO₃基介电陶瓷的微观形貌和介电性能有较明显的影响,特别是纳米复合氧化物掺杂能够促进烧结中晶粒"芯-壳"结构的形成,能有效地抑制晶粒长大并形成细晶结构,从而显著地降低烧结温度,提高介电常数、降低介电损耗,改善BaTiO₃基陶瓷的温度稳定性.     

Eu（bpy）2（NO3）3（H2O）2/Nafion修饰于金电极上的电化学发光性质研究（英文）

本文合成了铕-联吡啶的二元配合物Eu(bpy)2(NO3)3(H2O)2,用元素分析、红外及紫外光谱对配合物进行了表征.采用循环伏安法,研究了用Nafion将Eu(bpy)2(NO3)3(H2O)2修饰于金电极上的电化学发光行为.讨论了介质、pH对该体系电化学发光性质的影响,推测了Eu(bpy)2(NO3)3(H2O)2电化学发光的机理.结果表明:在没有共反应试剂存在的条件下,Eu(bpy)2(NO3)3(H2O)2在pH 8.0的硼砂缓冲溶液中可以产生较强的电化学发光,其发光体可能为Eu*(bpy)2(NO3)3(H2O)2.     

微波-水热合成钛酸钡粉体及其表征

以钛酸丁酯和氯化钡为钛钡源,氢氧化钠为沉淀剂,采用微波和水热二者联用的方法合成钛酸钡。利用X射线衍射仪(XRD)、扫描电镜(SEM)、傅里叶变换红外光谱仪(FTIR)对合成的钛酸钡粉体进行表征测试。     

掺杂La_2O_3的CuW电触头的组织及电性能

采用液-固掺杂工艺将La(NO3)3与WO3混合,经干燥、La(NO3)3裂解和WO3还原等工艺制备含有La2O3的稀土W粉,采用粉末冶金-熔渗法制备含有La2O3的CuW电触头;研究了保温时间对La(NO3)3裂解的影响以及La2O3对CuW电触头性能的影响. 结果表明:用液-固混料法制备的稀土W粉,La2O3分布均匀,粉末粒度较细;La(NO3)3裂解粉末的颗粒随着保温时间的延长而长大;掺杂La2O3的CuW触头耐电弧烧蚀性能有显著的提高.     

ZnO and MnO2 Doped PbTiO3 Ceramics Prepared by Sol-gel Method

ZnO and MnO2-doped PbTiO3 nanometer powders have been prepared by using titanium butoxide (Ti(OC4H9)4) and lead acetate (Pb(Ac)2.3H2O) as starting materials, acetic acid (HAc) and methanol (CH3OH) as catalyst and solvent, respectively, and Zn(Ac)2 and Mn(NO3)2 as dopants. High density and crack-free PbTiO3 ceramics were obtained. Electrical measurement indicates that the ceramics has lower dielectric constant, dielectric loss, and especially low surrounding moisture effect.     

ZnO and MnO2 Doped PbTiO3 Ceramics Prepared by Sol-gel Method

ZnO and MnO2-doped PbTiO3 nanometer powders have been prepared by using titanium butoxide (Ti(OC4H9)4) and lead acetate (Pb(Ac)2.3H2O) as starting materials, acetic acid (HAc) and methanol (CH3OH) as catalyst and solvent, respectively, and Zn(Ac)2 and Mn(NO3)2 as dopants. High density and crack-free PbTiO3 ceramics were obtained. Electrical measurement indicates that the ceramics has lower dielectric constant, dielectric loss, and especially low surrounding moisture effect.     

Eu(bpy)_2(NO_3)_3(H_2O)_2/Nafion修饰于金电极上的电化学发光性质研究(英文)

本文合成了铕-联吡啶的二元配合物Eu(bpy)2(NO3)3(H2O)2,用元素分析、红外及紫外光谱对配合物进行了表征.采用循环伏安法,研究了用Nafion将Eu(bpy)2(NO3)3(H2O)2修饰于金电极上的电化学发光行为.讨论了介质、pH对该体系电化学发光性质的影响,推测了Eu(bpy)2(NO3)3(H2O)2电化学发光的机理.结果表明:在没有共反应试剂存在的条件下,Eu(bpy)2(NO3)3(H2O)2在pH 8.0的硼砂缓冲溶液中可以产生较强的电化学发光,其发光体可能为Eu*(bpy)2(NO3)3(H2O)2.     

三元轻稀土硝酸盐水溶液的等压研究

以NaCl和CaCl2水溶液为参考溶液,在298 15K条件下,利用等压法研究了三元轻稀土硝酸盐水溶液{H2O+La(NO3)3+Pr(NO3)3},{H2O+La(NO3)3+Nd(NO3)3}和{H2O+Pr(NO3)3+Nd(NO3)3}及其二元亚系La(NO3)3(aq),Pr(NO3)3(aq)和Nd(NO3)3(aq)溶液的热力学性质·结果表明,在实验误差范围内(≤0 0010),它们的热力学行为符合偏理想溶液模型及Zdanovskii规则·     

pH值和煅烧温度对莫来石生成的影响

以溶胶凝胶法为基础,采用正硅酸乙酯(C8H20O4Si)、硝酸铝(Al(NO3)3·9H2O)为主要原料,借助X射线衍射仪进行检测,系统研究了pH值、煅烧温度对生成3∶2型莫来石以及生成过程的影响。结果表明：莫来石凝胶介于单相凝胶和双相凝胶的混合尺度,pH值在4~10范围内均可生成莫来石,煅烧温度为1175 ℃时出现明显的莫来石化;pH=4时,不利于无定形硅的转化;在pH值为5~9范围、煅烧温度1200 ℃时完全莫来石化,且生成的莫来石结晶度总体变小,晶胞参数上下波动。莫来石的生成经历了无定形硅和铝的氧化物到铝硅尖晶石再到莫来石的过程。     

Ba_(1-x)Sr_xTiO_3·yLa_2O_3固溶体的合成、结构与性能

用化学掺杂方法合成了Ｂａ１－ｘＳｒｘＴｉＯ３和Ｂａ０９Ｓｒ０１ＴｉＯ３·ｙＬａ２Ｏ３（０≤ｘ≤１,０≤ｙ≤０３）系列固溶体超细粉末。ＸＲＤ证实,当ｘ＝１,ｙ＝０时,为四方晶系ＢａＴｉＯ３纯相,当０＜ｘ＜１,０＜ｙ≤０３时,得到一系列完全互溶固溶体,结果符合Ｖｅｇａｒｄ定律。ＳＥＭ观察粒子为球形,大小均匀,粒度０２～０３μｍ,制陶实验发现,钛酸钡经化学掺杂后,室温介电常数显著提高,当ｘ＝０１,ｙ＝００２时,ε可达３００００,比ＢａＴｉＯ３纯相的室温介电常数提高２０倍。