为了减少粘胶长丝纺织经编缺压组织的布面疵点，改善纺织条件，提高布面质量，对以250D粘胶长丝纺织“龙花”的主要工艺参数进行了正交试验，经筛选，确定了最优工艺条件：经编机牵拉密度为28个线圈／ cm,经编机转速为280r/min，整经机加油量为0.215%,整经机单纱张力为0.275N，整经机转速为280r/min。     

亚麻籽胶为壁材制备沙棘油微胶囊研究

本文采用喷雾干燥法制备沙棘籽油为芯材、亚麻籽胶为壁材的微胶囊,并以微胶囊化效率和含油率为考察指标,考察了制备工艺.结果表明,最佳喷雾干燥工艺条件：进风温度为180℃,出风温度为80℃,雾化器转速24000r/min,进料速度为40.21mL/min.在此工艺条件下沙棘籽油的微胶囊化效率为87.12%,含油率为45.09%.     

Study on preparation of lycium oil microcapsule using flaxseed gum as wall material

本文采用喷雾干燥法制备沙棘籽油为芯材、亚麻籽胶为壁材的微胶囊,并以微胶囊化效率和含油率为考察指标,考察了制备工艺.结果表明,最佳喷雾干燥工艺条件：进风温度为180℃,出风温度为80℃,雾化器转速24000r/min,进料速度为40.21mL/min.在此工艺条件下沙棘籽油的微胶囊化效率为87.12%,含油率为45.09%.     

3D打印UV与ABS材料仿生表面摩擦学性能

对在干摩擦条件下仿生表面对摩擦副的作用机理与影响规律进行了研究.实验以光敏树脂(UV)和丙烯腈-苯乙烯-丁二烯(ABS)2种高分子材料为样品,利用3D打印技术分别加工出具有仿生表面与光滑表面的试样.干摩擦条件下,在摩擦磨损试验机上进行球-面摩擦磨损实验,测量UV与ABS的摩擦系数与磨损量,并用激光共聚焦显微镜与体视荧光显微镜观察磨损表面.研究结果表明:载荷与转速的改变会引起摩擦系数与磨损量的变化.UV仿生表面在3 N载荷与200 r/min转速、5 N载荷与200 r/min转速和3 N载荷与400 r/min转速工况下平均摩擦系数分别为0.534、0.598和0.642;在5 N载荷下相较3 N磨损量提高了40.0%,在400 r/min转速下相较200 r/min磨损量提高了185.5%.ABS仿生表面在3 N载荷与200 r/min转速、5 N载荷与200 r/min转速和3 N载荷与400 r/min转速工况下平均摩擦系数分别为0.336、0.346和0.378;在5 N载荷下相较3 N磨损量提高了2.69%,在400 r/min转速下相较200 r/min磨损量提高了12.5%.UV样品为粘着磨损,而ABS样品黏着磨损为主,伴随有磨粒磨损.     

磷酸盐缓冲液法提取茶叶多酚氧化酶的工艺研究

采用磷酸盐缓冲液提取法,研究了从茶鲜叶中提取多酚氧化酶的最佳工艺条件.结果表明,茶鲜叶多酚氧化酶提取的最佳工艺条件为pH 6.4,料液比(茶叶g∶缓冲液mL)为1∶1,离心转速为9000 r/min,离心时间35 min.     

Al3+改性膨润土负载壳聚糖对活性艳橙的吸附研究

探讨了Al3+改性膨润土负载壳聚糖复合吸附剂的制备及用其吸附处理活性艳橙的工艺条件.研究结果表明:膨润土在Al3+为10.0g.L、搅拌2 h的改性条件下吸附性能和过滤性能显著提高;当负载量为0.03g/g、复合吸附剂质量为5.0 g/L在最佳条件下即pH为6、温度为25℃、转速为150 r/min恒温振荡45 min...     

解钾硅酸盐细菌培养基及培养条件的研究

以所筛选的硅酸盐细菌RM 0 1菌株为材料 ,对所需的培养基和培养条件进行了研究分析 .在选择的适宜培养基中 (TR复合培养基 ) ,对培养基pH值、培养温度、摇床转速及摇瓶装液量等影响因素进行了正交实验 .结果表明 ,在pH为 7、温度 36℃、转速 2 2 0r/min、装液量 5 0mL时 ;硅酸盐细菌菌量可达 10 .6× 10 8个 /mL     

红霉素摇瓶发酵控制条件的优化

文章讨论摇瓶发酵控制条件对红霉素发酵水平的影响。通过单因素和正交实验优化,最佳发酵条件为A1B2C2D2:前期发酵、中期和后期发酵三阶段发酵温度分别为31℃、33℃、29℃,发酵起始pH值为6.7,摇床转速控制为:0～48 h为220 r/min,48～96 h为300 r/min,96～144 h为220 r/min,144～168 h为150 r/min。优化后菌株UL5的发酵水平比优化前提高15.54%。     

旋转抽油杆柱扭转振动固有频率分析

在对旋转抽油杆柱的扭转振动分析的基础上 ,给出了各阶扭转振动固有特性参数的计算式 .实例计算结果表明 :螺杆泵采油系统在 70 0～ 1 80 0 m的正常下泵深度时 ,常用的单级和二级抽油杆柱的前五阶扭转振动固有频率在 2 6～ 6 0 8r/min,覆盖了螺杆泵采油系统的工作转速区 (6 5～3 5 0 r/min) ,这完全不同于有杆泵采油系统 .指出 :在选定螺杆泵采油系统的工作转速时 ,应将杆柱的前五阶扭转振动固有频率对应的转速作为约束条件 ,以避开该转速范围 ;对于级次杆柱的高阶固有频率 ,由于其频率相对单级杆柱的增减幅值在 2 .1 %～ 5 .2 %之间 ,可近似按单级杆柱考虑 .文中提供的数据可以直接指导螺杆泵采油系统的杆柱组合与系统转速的匹配     

硼酸镧钙晶体的提拉法生长研究

首次采用提拉法生长La2 CaB10 O19晶体 .配制不同摩尔比的CaB4O7和LaB3 O6原料进行晶体生长 ,发现CaB4O7∶LaB3 O6在 1 .3∶2～ 1∶1范围内都能获得La2 CaB10 O19的单晶 .研究了晶体生长工艺 ,在CaB4O7∶LaB3 O6=1 .3∶2时获得 1 4mm× 2 5mm的透明单晶 .生长过程中靠近液面温度梯度为 30℃ /cm～ 6 0℃ /cm ,晶体转速为 1 0r/min～ 2 5r/min ,提拉速度不大于 1mm/h .在不同次的生长中 ,所获得的晶体表现发育完好的 {0 0 1 }板面 .     

混纤丝经编新产品的研制

介绍了在经编针织中 ,利用新型纺织材料混纤丝研制新品的过程 .从原料选择、设备改造 ,组织结构设计等方面进行阐述 ,分析了生产中应注意的技术要点 ,展望了该产品广阔的市场前景 .     

Effect of Knitting Process on Elastic Property of Polyethylene Terephthalate (PET)/Polybutylene Terephthalate (PBT) Warp Knitted Fabric

This study investigated the elastic elongation and elastic recovery of the elastic warp knitted fabric made of polyethylene terephthalate( PET) and polybutylene terephthalate( PBT)filament. The effect of knitting parameter on the elasticity of PBT /PET warp knitted fabric was analyzed. The increase of drawing density( from 16 to 26 courses per centimeter( CPC)) on machine resulted in the decrease of elongation at the weft direction. But,the elongation at the warp direction fluctuated as drawing density increasing. The yarn run-in speed influenced the elongation of PET /PBT warp knitted fabric as well. When the yarn run-in speed of GB1( front bar) was kept a constant,the increase of GB2( back bar) yarn run-in speed caused the gradual enhancement of the elastic elongation at the warp direction,but the different trends of the elastic elongation at the weft direction. When yarn run-in speed of GB2 was kept a constant,the increase of GB1 yarn run-in speed enlarged the elastic warp elongation from 104.16 to 124.97 mm,while the weft elongation decreased from 110.34 to 98.03 mm.Eventually yarn run-in speeds of GB1 and GB2 were retained at1 360 and 1 170 mm / rack respectively under 20 CPC drawing density. It could not only balance the two directions of elongation but also reach the highest elongation at both directions( 126. 32 and115.88 mm) under 100 N tension. These results provide a better understanding of characteristics of PET / PBT warp knitted fabric,and its elastic elongation and recovery behavior for development and effective applications.     

OWL程序设计与多梳栉经编织物花型计算机辅助设计

为了适应多梳栉拉舌尔经编机向现代高速、工艺先进和计算机控制的方向发展,满足市场对经编产品小批量、多品种的要求,国内外在多梳栉经编织物计算机辅助设计方面都做了大量的工作,而国内的设计研究尚显不足.从多梳栉经编织物计算机辅助花型设计的特殊性出发,选用了一种面向对象程序设计——OWL程序设计,将二者有机地结合起来所做的研究工作.     

经编双轴向织物用作涂层基布的性能优势

分别对经编双轴向织物和机织物增强材料的涂层产品进行拉伸和撕裂试验，研究了经编双轴向织物用作涂层基布时的一些性能优势：优异的拉伸性能和抗撕裂性能；较高的纱线强力利用率等等。     

单梳经平织物增强复合材料拉伸性能试验研究

在拉舍尔舌针经编机上编织了6种玻璃纤维单梳经平织物,采用手糊工艺将其与不饱和聚酯树脂复合.在万能材料试验机上测试了单梳经平织物增强复合材料试样的拉伸性能,并对其纵向、横向与斜向应力-应变曲线、弹性模量、断裂强度等进行了分析.结果表明,单梳经平织物增强复合材料的拉伸性能具有明显的正交各向异性特征;织物结构参数的变化,导致了线圈形态、延展线的长度和取向等的差异,使复合材料的拉伸性能不同.     

OPTIMAL SETTING-UP OF KNITTING ELEMENTS AND ITS EFFECT ON TENSION VARIATION

The dynamic yarn tension variations during knitting cycle are very difficult to control and be-come one of barriers to knitting on modern warp knitting machine.Examination of experimentaldata and theoretical analysis show that the relative position of spring rail to knitting elements suchas needle,guide as well as their displacement has noticeable effect on tension variation so that theknitting condition can be much improved by rearrangement of the knitting elements and theirmovement within a knitting cycle.     

双控式电子送经装置的研究

在修正了对积极式送经装置功能要求的基础上，设计了双控式电子送经装置方案。将纱线、织物，准备工序和织机等四方面的参数输入计算机并模拟出一个满足织造工艺要求的织轴转速曲线，为该装置的研制奠定了坚实的基础。模拟运行结果，双控式电子送经机构能按照织造规律主动送出所需经纱，改变了现有机构的模索式送经，可有效地消除送经织疵，为数以万计的织机改造和新机设计提供了一条途径。     

经编灯箱布的生产工艺

柔性经编灯箱布产品具有机械强度好、透光适量均匀、印刷后色彩鲜艳夺目、使用方便、气候适应性强以及使用寿命长等特点,在广告媒体中已得到大量应用.文中从原料选用、整经要求、编织工艺直至后整理等对经编灯箱布产品的生产工艺流程进行了系统的论述,对后整理中涂层、贴合两种工艺与参数控制分别作了说明;并简要讨论了编织时布边衬纬纱易出现松弛、后整理贴合牢度不高的问题.     

DETERMINATION OF AN ANALYTICAL DEPENDENCE DESCRIBING THE PROCESS OF TENSION OSCILLATION DURING THE WORK OF A WARP KNITTING MACHINE

The analytanl repnsedtfon of the osciliation of tension in the proass of fabric meking on a warp knitting machine is ddsiled, basis on funCtion approxfortion by Fourie row.     

纱线捻度对针织面料服用性能的影响分析

实验以纬平针组织为研究对象,采用24tex纯棉纱线为原料,科学地选取具有一定代表性的纱线捻度值进行加捻实验,通过KH-868／KR-838型针织横机编织形成相应织物。对由不同纱线捻度值形成的针织物进行服用性能测试,包括透气性、悬垂性、起毛起球性、拉伸断裂性能,以分析不同的纱线捻度对针织面料服用舒适性能产生的重要影响。实验得出,对于S捻的24tex纯棉并捻纱线,纱线捻度值在4r／10cm时,织物的力学性能、透气性、柔软性和悬垂性等均达到较理想水平。