能级统计与纳米金属小粒子的磁化率

作者考虑到纳米金属小粒子电子能级分离的特点以及电子数奇偶性的影响，采用能级统计的方法在正则系综中数值计算了纳米金属小粒子的磁化率，并对其在高低温时的特点作了讨论．     

Influence of nano-MgO particle size on bactericidal action against Bacillus subtilis var. niger

Nano-MgO has been widely used as a functionalmaterial in various areas[1,2]. Recently, it was reported[3]that MgO had good bactericidal performance due to theformation of O?2 anions at its surface in aqueous solution.It was shown by the research work of Stoimenov et al.[4]that nano-MgO exhibits high bactericidal activity againstbacteria, spores and viruses after adsorbing halogen gasbecause of its large surface area, abundance of crystal de-fects and positively-charged particles which can r…     

纳米无机磁性聚合物复合膜的制备技术

综述了国内外纳米无机磁性聚合物复合膜的制备技术。模板合成法制备条件温和,所得纳米粒子大小和形状容易控制、粒子排列更加有序,产品具有特殊的优异性能。     

纳米铜对酚醛树脂及摩擦材料性能的影响

采用原位同生法成功地制备了纳米铜改性酚醛树脂.利用X射线衍射分析和透射电子显微镜对所制备的树脂进行了表征,结果显示酚醛树脂中的纳米铜粒子分散良好,粒径为10～40nm.通过热重分析、冲击试验和摩擦试验,分别研究了纳米铜对酚醛树脂及摩擦材料性能的影响,结果表明:随纳米铜含量的增加,酚醛树脂的初始分解温度和半分解温度先升高后降低,在其质量分数为7%时分别达到最大值;随纳米铜含量的增加,摩擦材料的冲击强度先增大后下降,在其质量分数为5%时达到最大值;纳米铜可改善摩擦材料的摩擦磨损性能,尤其在高温下可使摩擦材料的热衰退明显减轻,磨损率显著下降.     

Fe3O4纳米颗粒的制备及其导电性和磁性

实验通过化学共沉淀法,得到了亲水性磁性纳米Fe3O4,反复清洗过滤、晾干,得到磁性纳米Fe3O4颗粒,并分别对不同实验条件得到的实验产物进行分析,当反应物以1 moL亚铁离子∶2 moL铁离子∶8 moL氢氧根离子的比例进行反应时,得到的Fe3O4纳米颗粒的导电性和磁性最佳.     

AlN和Al2O3纳米颗粒增强铜基复合材料

用粉末冶金法制备了Cu/AlN和Cu/Al2O3两种复合材料,研究了两种纳米颗粒含量对复合材料性能的影响和复合材料的软化温度,并探讨了相关机理,比较了AlN和Al2O3纳米颗粒的增强效果.结果表明,在烧结过程中,弥散分布在铜基体中的AlN和Al2O3纳米颗粒细化了晶粒;随着复合材料中AlN和Al2O3质量分数的增加,材料的密度和导电性都呈下降趋势,而硬度出现极大值;两种复合材料的软化温度均达到700℃,远远高于纯铜的软化温度(150℃),从而提高了材料的热稳定性;综合各种因素考虑,AlN纳米颗粒对铜基体的增强效果要优于Al2O3纳米颗粒.     

含油金刚石纳米制冷剂的核态池沸腾换热特性

研究了含油金刚石纳米制冷剂（即由制冷剂R113、润滑油VG68和金刚石纳米颗粒组成的纳米流体）的核态池沸腾换热特性,分析了金刚石纳米颗粒对含油制冷剂核态池沸腾换热的影响.实验中饱和压力为101.3 kPa;热流密度为10~80 kW/m2;纳米油(纳米颗粒和润滑油的混合物)的质量分数为0~5%;在纳米油中金刚石纳米颗粒的质量分数为0~15%.实验结果表明：金刚石纳米颗粒增强了含油制冷剂的池沸腾换热,在测试工况下换热系数最大可增加63.4%,并且增加幅度随纳米油中纳米颗粒质量分数的增加而增加,随纳米油质量分数的降低而增加.开发了含油纳米制冷剂池沸腾换热关联式,关联式预测值与94%的实验数据偏差在±20%以内.     

Subcooled boiling of nano-particle suspensions on Pt wires

An experimental investigation is conducted to explore the subcooled boiling characteristics of nano-particle suspensions on Pt wires. Some phenomena are observed for the boiling of water-SiO2 nano-particle suspensions on Pt wires. The experiments show that there exist not any evident differences for boiling of pure water and of nano-particle suspensions at high heat fluxes. However, bubble overlap phenomenon can be easily found for nano-particle suspensions at low heat fluxes, which probably results from the increase of the attracter force between bubbles and of the bubble mass.     

超声震荡与电场对冰升华法制备NaNO2纳米粒子的影响

将常规冰升华产物NaNO₂纳米粒子在乙醇分散剂中超声震荡, 使小晶粒重新组合, 形成更稳定的方形聚集体, 并在冰升华过程中, 施加一个0.5 kV/cm的垂直电场. 结果表明, 电场导致一部分NaNO₂纳米晶超过6 nm, 表现为相互分离的状态. 这是由于电场使NaNO₂纳米晶粒沿电场方向被极化, 而同向极化使相邻晶粒间存在一个斥力, 从而导致离散的NaNO₂纳米晶粒形成.      

ISG工艺合成SrTiO_3纳米粒子薄膜

采用 ISG工艺 ,在氧化铝陶瓷基片上合成 Sr Ti O3陶瓷薄膜 ,研究了溶胶性能和溶胶 -凝胶的晶化过程 ,分析了薄膜的形成及结构 .结果表明 ,Sr O- Ti O2 复合氧化物系统由凝胶向结晶相的转变过程中 ,无简单氧化物等中间相生成 ,经 40 0～ 80 0℃ ,0 .5 h,可生成结晶度较好的单一的立方 Sr Ti O3相 .Sr Ti O3陶瓷薄膜晶粒为 1 0 nm左右 .