高铬铸铁-钢双金属缸套热处理研究

要使高铬铸铁－钢双金属缸套具有优良的性能，关键在于适宜的热处理工艺，对热 处理工艺参数进行了一系列实验表明：在９４０～９７０℃淬火；２００～２２０℃回火； ７２０℃退火，双全属缸套的性能最好。     

Fe73．5 Cu1 Nb3 Si13．5 B9纳米晶合金的软磁特性

自1988年，Yoshizawa等人首先发现并命名为Finemet的铁基纳米晶合金后，该材料以其优异的软磁性能引起人们广泛的研究兴趣．本文对国内外研究文献进行综述，主要包括Fe73．5 Cu1 Nb3 Si13．5 B9纳米晶合金的制备及合成技术，微观结构特征，软磁特性等．     

Solid-Liquid State Bonding of Si3N4 Ceramics with Ceramic-Modified Brazing Alloy

Solid-liquid state bonding of Si3N4 ceramics with TiN-modified Ag-Cu-Ti brazing alloy was used to enhance joint strength. The effects of the TiN particles on the microstructures, interfacial reactions, and room-temperature properties of the joints were investigated. The results show that the TiN particles are generally well dispersed in the Ag-Cu eutectic base and the interface between them is both clean and compact. Changes in the TiN volume fractions from 0 to 20% exert no noticeable effect on the interfacial reaction between Ag-Cu-Ti and the substrates. Other bonding parameters being constant, the TiN volume fraction in the filler material plays a key role in the joint properties. For TiN volume fractions below 20%, the joints are reinforced, especially joints with 5% and 20% TiN. The average shearing strength of joints with 5% TiN is 200.8 MPa, 30% higher than that of joints with no TiN (154.1 MPa). However, for TiN volumes fractions above 20%, the joint strengths decrease.     

K6合金铸造叶片质量分析

应用金相显微镜和扫描电镜以及Ｘ射线能谱分析了Ｋ６合金铸造叶片的质量问题。结果表明：Ｋ６合金铸造叶片报废的主要原因在于非金属夹杂物在浇注成型时混入合金叶片中造成的，因此需要严格控制Ｋ６母合金质量和选择合理的重熔浇注工艺参数。     

Fe—C合金组织图填写与组织相对量计算

本文研究了Fe—C合金组织图的填写方法及组织组成物相对量的计算方法,提出了“过河搭桥”与“逆推顺算”法的概念,为解决这一问题提供了一种新的途径。     

微量Sc对2197铝锂合金组织和力学性能的影响

研究了微量Sc对Al-Li-Cu系2197合金的显微组织和拉伸性能的影响.采用拉伸试验和透射电镜等方法对样品进行了力学性能测试和微观组织分析.研究结果表明,δ'(Al3Li),θ'(Al2Cu)和T1(Al2CuLi)相仍为含Sc 2197合金的主要强化相;添加微量Sc使合金析出初生和次生Al3Sc颗粒,时效过程中δ'相依附在Al3Sc颗粒上析出、长大,形成Al3Li/Al3Sc复合沉淀相,但这2种颗粒的存在并未明显提高热处理可强化的2197合金的强度和塑性.