一步水解氧化法制备纳米级Mn3O4

以低成本的硫酸锰为原料,采用一步水解氧化法,以弱碱氨水为反应介质,成功制备出γ型Mn3O4.利用乙醇和其他有机相的协同作用解决了产品粒度与分散性的关系,得到粒度小、二次粒子分散较好、纯度高的γ型Mn3O4.最后探讨了其制备高性能软磁铁氧体的可能性.     

添加剂作用下纳米四氧化三铁的制备及性能研究

采用空气氧化法,在可见光作用下制备纳米Fe3O4,探讨羟基化合物单一添加剂、乙醇和EDTA双组分添加剂对Fe3O4粒径及分散性的影响,并对其性能进行分析.结果表明:加入乙醇、乙二醇和聚乙二醇600添加剂,Fe3O4的晶粒度均减小;随乙醇添加剂的增加,所得Fe3O4的晶粒度减小;EDTA的加入也有利于纳米Fe3O4晶粒度的减小;乙醇和EDTA双组分共同添加时可得到分散性较好、晶粒度为10.1 nm的均匀纳米Fe3O4,其在乙醇溶液中的分散稳定性较好.不同晶粒度(36.6~10.1 nm)纳米Fe3O4分别呈现出铁磁性、超顺磁性特征.     

磁性Fe3O4明胶复合纳米粒子的制备与表征

用化学共沉淀法制备磁性Fe3O4纳米粒子,然后用异丙醇为凝聚剂采用单凝聚法制备磁性Fe3O4明胶复合纳米粒子。考察了明胶浓度与异丙醇的体积以及Fe3O4含量对粒径分布及性能的关系。采用透射电子显微镜和Zetasizer粒度分析仪测量磁性明胶复合纳米粒子的平均粒径,X射线衍射仪和红外光谱以及热重及差热分析进行结构和热稳定分析。结果表明磁性Fe3O4明胶复合纳米粒子中的Fe3O4纳米粒子被明胶所包覆,而且粒径很小,具有良好的热稳定性。     

溶剂热法制备纳米Fe3O4粉体

通过溶剂热法,以FeOOH作为前驱体,以油酸作为表面活性剂,以十八烯为溶剂,制备了纳米Fe3O4颗粒,研究了油酸和FeCl3用量、反应时间对纳米Fe3O4粒子的大小以及分散性的影响.结果显示,FeCl3用量的增加和反应时间的延长均可使Fe3O4粒子粒径增大,油酸用量的增加会导致Fe3O4粒子粒径先减小再增大.利用XRD、TEM等手段对所制备颗粒的结构、形貌进行了表征,结果表明,所制备的纳米Fe3O4粒子属于反尖晶石结构.FeCl3用量为0.003mol,油酸用量为13.5mL时(即Fe3+/油酸约为1/15),在230℃反应12h得到结晶度较高,分散性良好,平均粒径比较小的纳米Fe3O4粒子.     

导向药物用纳米Fe3O4磁性粒子的制备及表征

采用化学共沉淀法先生成Fe3O4微粒,再将其分散于含有表面活性剂的水中的方法制备了纳米级Fe3O4磁性粒子.通过双层表面活性剂包覆可使Fe3O4磁性粒子稳定分散于水中而不聚集.在反应溶液pH值为11～12,温度为60℃及油酸钠为第1层表面活性剂,十二烷基苯磺酸钠为第2层表面活性剂的条件下制备了粒径为36nm的Fe3O4磁性粒子.实验结果表明:反应溶液pH值和表面活性剂是影响Fe3O4磁性粒子稳定性、粒径和饱和磁化强度的主要因素;利用XRD和IR证实了Fe3O4磁性粒子中存在Fe3O4和表面活性剂结构.所制备的纳米级Fe3O4磁性粒子可用作导向药物的磁载体.     

水热法制备Fe_3O_4磁性纳米粒子

通过改进实验工艺,调节前驱体配比,采用水热法制备Fe3O4磁性纳米粒子,有效克服了Fe3O4粒子制备过程中普遍存在的氧化问题;并利用XRD、SEM以及TEM测试分析磁粒子的组成和结构,证实所制得的磁粒子为纯相Fe3O4纳米粒子;利用激光粒度分析仪表征分析,得出本实验产物大部分为纳米级粒子,粒径较窄;由交流梯度磁强计测得产物的磁化曲线,可确定产物有较理想的超顺磁性 .     

Fe3O4/SiO2磁性微球的制备研究

报道了Fe3O4/SiO2纳米复合材料的可控合成方法.研究并探讨了乙醇-水体系配比及氨水和硅酸四乙酯的用量对纳米粒子形貌的影响,利用柠檬酸作分散剂,控制反应条件对Fe3O4纳米粒子进行表面修饰改性后,又对其进行SiO2包覆.然后运用X射线衍射仪（XRD）、透射电子显微镜（TEM）、红外（IR）对合成的纳米微粒的粒径、结构进行了表征.实验结果表明,产物为粒径均匀的单分散Fe3O4/SiO2复合纳米粒子,平均粒度约为100 nm.     

室温固相法合成纳米FeOOH及Fe2O3

首次报道了通过室温固相反应法,以FeCl3@6H2O和KOH为原料合成纳米FeOOH,将FeOOH分别在400、600、800℃焙烧2 h,即可得到纳米Fe2O3.通过对产物进行TGA-DTA、XRD、IR、TEM和BET表征,结果表明,FeOOH及无定形Fe2O3粒径均在10 nm左右,而α-Fe2O3的粒径为50nm.室温固相法合成纳米FeOOH及Fe2O3操作简单、转化率高、污染少,制备的产物具有粒径小,粒度分布均匀,无团聚现象,比表面较大等优点.对此反应的反应机理进行了初步探讨.     

纳米Fe3O4磁流体的制备及表征

采用化学沉淀法制备纳米Fe3O4颗粒,并以聚乙二醇为改性剂,蒸馏水为载液,制备出固体质量分数为10%的纳米Fe3O4磁流体.用XRD研究Fe3O4纳米粒子的结晶情况;用FT-IR研究聚乙二醇改性前后Fe3O4粒子表面官能团的变化;用TEM研究Fe3O4颗粒的粒径大小及改性情况;用VSM研究Fe3O4粒子的磁性能.结果表明,制备的纳米Fe3O4为立方晶型,平均粒径在15 nm左右,聚乙二醇物理吸附在Fe3O4表面,Fe3O4颗粒几乎没有磁滞,具有超顺磁性.     

丝素蛋白/改性Fe3O4纳米粒子复合材料的制备

文章采用共沉淀法制备Fe3O4纳米粒子,分别用油酸钠、聚乙二醇对纳米粒子改性.超声下用乙醇分散改性纳米粒子,再与丝素蛋白溶液形成凝胶,制备出丝素蛋白/磁性纳米粒子复合材料.采用红外光谱仪、透射电镜、振动样品磁强计等对产物进行表征.结果表明,复合产物的铁氧特征吸收峰出现在583 cm-1处,透射电镜显示改性后的纳米粒子较均匀地分布到丝素蛋白溶液中,并表现出较好的磁性.油酸钠较聚乙二醇(PEG)改性Fe3O4纳米粒子的效果更好.     

壳聚糖/Fe3O4复合纳米颗粒的制备

以柠檬酸为改性剂,制备水基Fe3O4磁性纳米粒子,基于静电自组装作用,使壳聚糖分子在水溶液中包覆Fe3O4纳米晶粒,获得壳聚糖/Fe3O4复合纳米颗粒液溶胶。扫描电子显微镜（SEM）分析结果表明,复合纳米颗粒平均粒径为49.0 nm,标准差为11.0 nm。X射线衍射（XRD）和红外光谱（FT-IR）分析结果表明,复合纳米颗粒由壳聚糖分子和Fe3O4晶体粒子构成。     

Synthesis and characterization of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript>@SiO<Subscript>2</Subscript> magnetic composite nanoparticles by a one-pot process

Fe₃O₄@SiO₂ core–shell composite nanoparticles were successfully prepared by a one-pot process. Tetraethyl-orthosilicate was used as a surfactant to synthesize Fe₃O₄@SiO₂ core–shell structures from prepared Fe₃O₄ nanoparticles. The properties of the Fe₃O₄ and Fe₃O₄@SiO₂ composite nanoparticles were studied by X-ray diffraction, transmission electron microscopy, energy dispersive spectroscopy, and Fourier transform infrared spectroscopy. The prepared Fe₃O₄ particles were approximately 12 nm in size, and the thickness of the SiO₂ coating was approximately 4 nm. The magnetic properties were studied by vibrating sample magnetometry. The results show that the maximum saturation magnetization of the Fe₃O₄@SiO₂ powder (34.85 A·m2·kg–1) was markedly lower than that of the Fe₃O₄ powder (79.55 A·m2·kg–1), which demonstrates that Fe₃O₄ was successfully wrapped by SiO₂. The Fe₃O₄@SiO₂ composite nanoparticles have broad prospects in biomedical applications; thus, our next study will apply them in magnetic resonance imaging.     

Bi2Fe4O9的制备及光催化性能研究

用Bi(NO3)3.5H2O和Fe(NO3)3.9H2O为基本原料,采用共沉淀法合成了Bi2Fe4O9粉体,用XRD和SEM测试了不同制备条件下得到的Bi2Fe4O9粉体的晶体结构和形貌,XRD结果表明在650℃～750℃直接煅烧2h可得到纯相Bi2Fe4O9粉体,SEM结果表明随着灼烧温度的提高,晶粒的尺寸增加,750℃时晶粒呈片状,UV-Vis分析表明,Bi2Fe4O9在可见光区域有较强的吸收,光催化性能表明,Bi2Fe4O9粉体对甲基橙降解效果较好。     

聚吡咯-Fe3O4纳米复合材料的制备与表征及性能

用共沉淀方法制备出平均粒径在10 nm左右的Fe3O4纳米粒子,然后在阳离子表面活性剂的引导下采用原位化学氧化聚合法,合成出聚吡咯-Fe3O4纳米复合材料.同时对此纳米复合材料的结构和性能进行了研究.结果表明Fe3O4纳米粒子和聚吡咯之间存在着一定的相互作用,从而有利于吡咯单体在Fe3O4纳米粒子的表面发生聚合反应,进而Fe3O4纳米粒子被聚吡咯所包覆.聚吡咯/Fe3O4纳米复合材料同时具有导电性和磁性,其导电性随着Fe3O4纳米粒子含量的增加先增大后减小,磁性则始终随着Fe3O4纳米粒子含量的增加而增大.     

Fe3O4@SiO2磁性纳米粒子的制备及表征

用多元醇还原法制备出平均粒径为6.0 nm的Fe3O4磁性纳米粒子,并用盐酸溶液(1 mol/L)对其进行酸化处理,然后利用反相微乳液法,在Op-10/正丁醇/环己烷/浓氨水反相微乳体系中制备出Fe3O4@SiO2磁性纳米复合粒子.利用X射线衍射(XRD)仪,透射电子显微镜(TEM),傅立叶-红外光谱仪(FT-IR)和...     

羧基磁流体制备和牛血清白蛋白表面修饰

 磁性纳米粒已被用作肿瘤磁感应热疗的介质，目前常用纳米Fe3O4，其经典制备方法是化学共沉淀法，得到具有超顺磁性的纳米Fe3O4粒径约为10～15nm。本文采用改进的化学共沉淀法制备聚丙烯酸（PAA）修饰的羧基纳米Fe3O4，通过EDC、NHS活化法偶联模型蛋白牛血清白蛋白（BSA），用BCA定量分析磁粒对BSA的偶联效率，并进一步偶联荧光标记的抗体，观察偶联效果。结果表明，改进的化学共沉淀法制备的羧基纳米粒粒径约10nm，水相分散性良好；定量分析和光学观察结果均显示，采用EDC、NHS活化法能使蛋白质与羧基化磁性颗粒稳定结合。本研究为靶向磁性纳米粒的制备提供一种新方法。     

磁性聚苯乙烯(Fe_3O_4/PS)微球合成的影响因素分析

以共沉淀法制备的Fe3O4纳米颗粒作为磁核,用聚乙二醇(PEG)为分散剂,过氧化苯甲酰(BPO)为引发剂,苯乙烯为单体,在乙醇/水混合溶剂中,采用分散聚合法制备出聚苯乙烯磁性高分子微球.研究聚合温度、Fe3O4用量、引发剂用量、分散剂用量以及乙醇/水比例等反应条件对聚合物磁性微球粒径和磁性能的影响,找出的最佳工艺参数为:单体用量为15 mL,Fe3O4用量为0.5 g,引发剂与单体的质量比为10∶1 000,醇水体积比为45/50,分散剂PEG用量为25 g,最佳反应温度为75℃.     

Fe_3O_4@C纳米材料制备及其药物缓释性能

以乙酰丙酮铁和蔗糖为原料,碳酸钠作为沉淀剂,采用溶剂热法制备磁性Fe3O4@C纳米材料.用X射线衍射仪（XRD）和扫描电子显微镜（SEM）对磁性Fe3O4@C纳米材料的组成、形貌及尺寸进行表征,并探究了磁性Fe3O4@C纳米材料对氯霉素的吸附性能及对卡那霉素的缓释性能.研究结果表明,该纳米材料具有良好的药物吸附及缓释性能.     

表面巯基化Fe3O4纳米粒子的一步合成及表征

以FeCl3为铁源,在生物小分子L-半胱氨酸(L-Cys)、水和丙三醇的混合体系中,采用溶剂热法一步合成L-Cys包覆的Fe3O4复合纳米粒子Fe3O4/L-Cys.通过粉末X射线衍射(XRD)、红外光谱(IR)、热重-差热分析(TG-DTA)等表征Fe3O4/L-Cys复合纳米粒子的晶体结构;采用Zeta电位测量和酸...