磁性Fe3O4明胶复合纳米粒子的制备与表征

用化学共沉淀法制备磁性Fe3O4纳米粒子,然后用异丙醇为凝聚剂采用单凝聚法制备磁性Fe3O4明胶复合纳米粒子。考察了明胶浓度与异丙醇的体积以及Fe3O4含量对粒径分布及性能的关系。采用透射电子显微镜和Zetasizer粒度分析仪测量磁性明胶复合纳米粒子的平均粒径,X射线衍射仪和红外光谱以及热重及差热分析进行结构和热稳定分析。结果表明磁性Fe3O4明胶复合纳米粒子中的Fe3O4纳米粒子被明胶所包覆,而且粒径很小,具有良好的热稳定性。     

磁性荧光Fe3O4@APTES-RB复合材料的合成及性能表征

磁性-荧光双功能复合纳米材料同时具有磁性和发光特性,因其在生物医学领域具有潜在的广泛应用,引起了人们的广泛关注.采用3-氨丙基三乙氧基硅烷(APTES)对共沉淀法制备的Fe3O4纳米粒子表面进行修饰,获得氨基化的磁性纳米粒子,然后通过共价法将罗丹明B(RB)结合到其表面,获得分散性和荧光信号均得到改善的磁性/荧光复合纳米粒子.利用荧光光谱仪、透射电子显微镜(TEM)、傅里叶变换红外光谱仪(FTIR)、热重分析仪、X-射线衍射仪(XRD)和振动样品磁强计(VSM)对合成的粒子进行了表征.结果表明,氨基化的Fe3O4纳米粒子和Fe3O4-荧光纳米复合材料粒径基本相同,粒径为6～10 nm;Fe3O4-荧光纳米复合材料的饱和磁化强度为38.1 A.m2/kg,室温下呈现超顺磁性,具有较强的荧光信号.这种新型的磁性荧光纳米复合材料将会在生物医学领域具有广阔的应用前景.     

单畴晶纳米四氧化三铁粒子的制备及其在磁共振成像中的应用

采用共沉淀法制备了包覆油酸钠的超顺磁性纳米Fe3O4粒子,主要研究了搅拌强度、加料方式、温度、料液浓度等因素对Fe3O4粒径的影响。对包覆油酸钠的纳米Fe3O4粒子采用葡聚糖进行表面处理后制备成靶向复合纳米粒子,考察了复合粒子的特异性浓聚效果。结果表明:在转速为7 000r/min的高速剪切机里,当温度为70℃,FeCl2的浓度为0.1mol/L时,所制备的单层包覆油酸钠的纳米Fe3O4粒子平均粒径为8nm,为单畴晶并具有超顺磁性。靶向纳米复合Fe3O4粒子可以特异性聚集于肿瘤部位,浓聚效果是生理盐水的2.13倍。     

PLA-PEG/Fe3O4磁性复合微球的制备与性能研究

以油酸钠改性的Fe3O4纳米粒子为磁性内核,聚乳酸一聚乙二醇(PLA-PEG)嵌段共聚物为载体材料,吐温-80(Tween-80)为表面活性剂,采用非溶剂引起相分离的方法,制备了PLA-PEG/Fe3O4磁性复合微球,系统考察了PLA-PEG质量浓度、Fe3O4与PLA-PEG的质量比及搅拌速度等因素对磁性复合微球性能的影响,确定了制备PLA-PEG/Fe3O4磁性复合微球的最佳条件,并利用透射电镜、红外光谱仪、热分析仪、振动样品磁强计和紫外分光光度计,对所得产物的形貌、粒径、化学组成、Fe3O4的质量分数及磁性能进行了表征.     

壳聚糖/Fe3O4复合纳米颗粒的制备

以柠檬酸为改性剂,制备水基Fe3O4磁性纳米粒子,基于静电自组装作用,使壳聚糖分子在水溶液中包覆Fe3O4纳米晶粒,获得壳聚糖/Fe3O4复合纳米颗粒液溶胶。扫描电子显微镜（SEM）分析结果表明,复合纳米颗粒平均粒径为49.0 nm,标准差为11.0 nm。X射线衍射（XRD）和红外光谱（FT-IR）分析结果表明,复合纳米颗粒由壳聚糖分子和Fe3O4晶体粒子构成。     

四氧化三铁纳米粒子的简易合成法及其性能

以尿素铁配合物([Fe(CON2H4)6](NO3)3)为前躯体,采用溶剂热法和直接热分解法制备Fe3O4纳米粒子,并对两种制备方法进行了比较.用XRD、N2吸附-解吸、磁性测定和透射电镜等手段对制得的样品进行表征.结果表明,制备方法和制备条件对产物性能的影响较大;用溶剂热法制备的Fe3O4纳米粒子的晶粒较小,具有超顺磁性;用直接热分解法制备的Fe3O4纳米粒子的晶粒较大,具有强磁性.     

Fe2O3纳米粒子复合纤维素膜降解有机染料亚甲基蓝

合成Fe2O3纳米粒子复合纤维素膜.采用XRD、TEM和磁力线等多种方法对Fe2O3纳米粒子复合纤维素膜的结构和性能进行表征,并研究Fe2O3纳米粒子复合纤维素膜对亚甲基蓝的降解作用.结果表明：当溶液中H2SO4加量为25.8mol/L、H2O2加量为2.4mol/L时,用5g/L的复合纤维素膜对1.4×10-5 mol/L的亚甲基蓝溶液进行降解,25min内降解率达到100%.     

磁性PLA-Fe3O4复合微球制备及其对茜素红的脱除研究

采用化学共沉淀法制备了纳米级Fe3O4磁性粒子,以油酸钠改性后的磁性Fe3O4粒子作为模板,以一次性聚乳酸(PLA)饭盒作为聚乳酸原料,采用溶剂扩散法制备了磁性PLA-Fe3O4复合微球.利用扫描电镜、红外光谱仪及热重分析仪对所得产物的形貌、组成和含量进行了表征.以茜素红(AR)模拟染料废水,探讨了磁性PLA-Fe3O4复合微球对染料茜素红的脱除效率,研究了吸附时间,磁性PLA-Fe3O4复合微球的用量,溶液的pH及溶液的初始浓度等因素对茜素红脱除效率的影响.结果表明:磁性PLA-Fe3O4复合微球的用量为25mg、pH为4.3、吸附时间为2h、溶液起始浓度为19mg/L时吸附率可达90%以上.     

丝素蛋白/改性Fe3O4纳米粒子复合材料的制备

文章采用共沉淀法制备Fe3O4纳米粒子,分别用油酸钠、聚乙二醇对纳米粒子改性.超声下用乙醇分散改性纳米粒子,再与丝素蛋白溶液形成凝胶,制备出丝素蛋白/磁性纳米粒子复合材料.采用红外光谱仪、透射电镜、振动样品磁强计等对产物进行表征.结果表明,复合产物的铁氧特征吸收峰出现在583 cm-1处,透射电镜显示改性后的纳米粒子较均匀地分布到丝素蛋白溶液中,并表现出较好的磁性.油酸钠较聚乙二醇(PEG)改性Fe3O4纳米粒子的效果更好.     

Fe2O3/油酸纳米复合粒子的结构及性能表征

采用油酸作为包覆剂，在油／水两相体系中制备Fe2O3／油酸纳米复合粒子，并用XRD、FTIR、XPS、TG—DIA和纳米粒度分布仪对所制得的纳米复合粒子进行了结构表征。结果表明，Fe2O3／油酸纳米复合粒子是非晶态、窄粒度分布的，其粒径在12nm左右。Fe2O3／油酸纳米复合粒子具有憎水亲油性，能在甲苯、环己烷等有机溶剂中很好地分散。FTIR和XPS证明Fe2O3与油酸之间发生了化学键合。将Fe2O3／油酸纳米复合粒子按不同比例加入高氯酸铵(AP)中，并对样品进行差热分析，发现Fe2O3／油酸纳米复合粒子能使AP的高温分解峰温明显降低，且比例越大，高温分解峰温的降低的也越多。     

纳米Fe3O4磁流体的制备及表征

采用化学沉淀法制备纳米Fe3O4颗粒,并以聚乙二醇为改性剂,蒸馏水为载液,制备出固体质量分数为10%的纳米Fe3O4磁流体.用XRD研究Fe3O4纳米粒子的结晶情况;用FT-IR研究聚乙二醇改性前后Fe3O4粒子表面官能团的变化;用TEM研究Fe3O4颗粒的粒径大小及改性情况;用VSM研究Fe3O4粒子的磁性能.结果表明,制备的纳米Fe3O4为立方晶型,平均粒径在15 nm左右,聚乙二醇物理吸附在Fe3O4表面,Fe3O4颗粒几乎没有磁滞,具有超顺磁性.     

Synthesis and characterization of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript>@SiO<Subscript>2</Subscript> magnetic composite nanoparticles by a one-pot process

Fe₃O₄@SiO₂ core–shell composite nanoparticles were successfully prepared by a one-pot process. Tetraethyl-orthosilicate was used as a surfactant to synthesize Fe₃O₄@SiO₂ core–shell structures from prepared Fe₃O₄ nanoparticles. The properties of the Fe₃O₄ and Fe₃O₄@SiO₂ composite nanoparticles were studied by X-ray diffraction, transmission electron microscopy, energy dispersive spectroscopy, and Fourier transform infrared spectroscopy. The prepared Fe₃O₄ particles were approximately 12 nm in size, and the thickness of the SiO₂ coating was approximately 4 nm. The magnetic properties were studied by vibrating sample magnetometry. The results show that the maximum saturation magnetization of the Fe₃O₄@SiO₂ powder (34.85 A·m2·kg–1) was markedly lower than that of the Fe₃O₄ powder (79.55 A·m2·kg–1), which demonstrates that Fe₃O₄ was successfully wrapped by SiO₂. The Fe₃O₄@SiO₂ composite nanoparticles have broad prospects in biomedical applications; thus, our next study will apply them in magnetic resonance imaging.     

磁性纳米Fe_3O_4与Fe_3O_4/TiO_2复合材料的制备

用共沉淀法制备了纳米Fe3O4.TEM及XRD的测定结果表明制备了尖晶石型纳米Fe3O4,VSM结果显示样品具有超顺磁性.在此基础上采用均匀沉淀法制备了Fe3O4/TiO2复合材料,XRD和UV-Vis结果表明制备出双层封闭结构的复合粒子的光吸收带发生了较大幅度的红移,并进入可见光区,同时吸收光强度也明显增大,这对开发日光型催化剂是十分有利的.     

聚吡咯-Fe3O4纳米复合材料的制备与表征及性能

用共沉淀方法制备出平均粒径在10 nm左右的Fe3O4纳米粒子,然后在阳离子表面活性剂的引导下采用原位化学氧化聚合法,合成出聚吡咯-Fe3O4纳米复合材料.同时对此纳米复合材料的结构和性能进行了研究.结果表明Fe3O4纳米粒子和聚吡咯之间存在着一定的相互作用,从而有利于吡咯单体在Fe3O4纳米粒子的表面发生聚合反应,进而Fe3O4纳米粒子被聚吡咯所包覆.聚吡咯/Fe3O4纳米复合材料同时具有导电性和磁性,其导电性随着Fe3O4纳米粒子含量的增加先增大后减小,磁性则始终随着Fe3O4纳米粒子含量的增加而增大.     

超声乳化法制备纳米Fe3O4磁性颗粒及壳聚糖表面改性

采用超声乳化法制备纳米Fe3O4磁性颗粒,以壳聚糖作为表面活性剂,制备具有生物亲和性的水基Fe3O4磁流体.研究了Fe2+/Fe3+摩尔比、超声时间和表面活性剂用量对磁流体性能的影响.结果表明:当Fe2+/Fe3+摩尔比为1:1·5,滴加氨水时反应温度为70℃时,可制备理想纳米Fe3O4磁性颗粒;超声时间为7·5min左右,质量分数1%的壳聚糖溶液体积占FeO溶液总体积的50%时,有利于壳聚糖分子的包覆,使磁流体具有较高的比饱和磁化强度及稳定性.     

Fe_3O_4@SiO_2@PGA磁性吸附材料的制备与表征

首先以共沉淀法制备了磁性纳米颗粒Fe_3O_4并在表面包覆SiO_2,制得Fe_3O_4@SiO_2磁性纳米颗粒.然后由PBLG水解制得PGA为共聚组分,过硫酸铵为引发剂,EGDMA为交联剂,使用自由基共聚制备交联共聚物,同时加入Fe_3O_4@SiO_2纳米颗粒,制备得到Fe_3O_4@SiO_2@PGA磁性纳米粒子.通过核磁(~1H-NMR),红外(FT-IR),X-射线衍射(XRD),动态光散射(DLS)和透射电镜(TEM)等一系列手段对磁性纳米粒子的结构和形貌进行了表征,初步证明了制备的样品具有稳定的结构和良好的磁性.     

反相乳液聚合制备阿霉素磁性抗癌毫微粒

以阿霉素为模型药物,Fe3O4为磁核,乙烯吡咯烷酮(NVP)为载体,通过反相乳液聚合法制备了阿霉素磁性抗癌毫微粒,并对影响阿霉素磁性毫微粒大小及粒径分布的因素进行了考察.环境扫描电镜表明,最佳制备条件下制得的毫微粒外观光滑,大小均匀;激光光散射测定表明该产物平均粒径为500 nm,粒径分布系数0.23,呈单分散分布;红外光谱测试证明本实验所制备的毫微粒是由阿霉素、Fe3O4和聚乙烯吡咯烷酮共同组成.     

PEI修饰磁性Fe3O4纳米粒的制备和表征

 为了制备性能良好的聚乙烯亚胺（PEI）修饰的磁性Fe3O4纳米粒,以及为进一步开展体内外生物学效应分析奠定基础,采用化学共沉淀法制备PEI修饰的磁性Fe3O4纳米粒。PEI-Fe3O4纳米粒的制备包括磁性Fe3O4纳米粒的制备和PEI修饰磁性Fe3O4纳米粒两部分,采用4因素2水平的正交实验对各因素进行优化,得到较佳的制备工艺。反应过程中用过量氨水保持pH值为9.3~9.7,Fe2+与Fe3+的物质的量比为1:1.75,PEI水溶液的质量百分数为20%,反应温度始终保持为85℃,机械搅拌速率为1400r/min。采用傅里叶变换红外光谱仪（FTIR）、透射电子显微镜（TEM）、X射线衍射分析仪（XRD）、振动样品磁强计（VSM）、热重分析仪（TGA）对磁性纳米粒的物化特征进行表征。结果表明,制得的磁性PEI-Fe3O4纳米粒为接近圆形或椭圆形粒子,具尖晶石结构,粒径约9.4nm,磁含量为82.3%,饱和磁化强度为61.962emu/g,矫顽力几乎为0,具超顺磁性,稳定性和分散性良好。     

功能型磁性聚合物微球的制备与表征