炭/炭复合材料的摩擦磨损性能

选取由CVD预增密至一定密度,再进行树脂浸渍/炭化补充增密至1.85 g/cm3的炭/炭复合材料作摩擦环试样.测试了该试样在一系列刹车速度时的摩擦磨损性能,并对其摩擦面及磨屑进行了SEM观察,对摩擦面进行显微喇曼光谱分析.研究结果表明炭/炭复合材料的摩擦磨损性能随刹车速度的变化而发生显著变化,在10 m/s时出现最高峰,在25 m/s出现亚高峰;磨损量随刹车速度的增加而增加,而氧化磨损在刹车速度为25 m/s时开始大量产生,在28 m/s时达最大值.其摩擦表面形貌、结构及磨屑亦有较大差别.刹车速度从5 m/s升至20 m/s时,摩擦面石墨化度降低,石墨结构向无定型碳结构转变,但在高速时石墨化度反而升高,无定型碳结构又向石墨结构转变.     

纤维体积分数对炭/炭复合材料摩擦磨损性能的影响

通过化学气相沉积法将纤维体积分数分别为23%,30%和40%的3种炭纤雏针刺毡预制件增密至1.50 g·cm-3,再浸渍树脂进一步增密至1.80 g·cm-3,进行热处理后制成炭/炭复合材料,观察3种试样的金相显微结构,测试3种试样在不同刹车压力下的摩擦磨损性能;采用扫描电子显微镜对其磨损表面进行观察.研究结果表明:对于热解炭为非典型粗糙层结构的炭/炭复合材料,纤维体积分数增大,其摩擦曲线相对较平稳,磨损量较大;当纤维体积分数超过30%后,磨损量显著增加;在相同的刹车压力下,纤维体积分数对摩擦因数无显著影响.刹车压力低时试样的摩擦因数比刹车压力高时的摩擦因数大;作为摩擦炭/炭复合材料,纤维体积分数为30%左右较适宜.     

不同刹车压力下C/C复合材料的摩擦磨损性能

研究了粗糙层和光滑层2种不同热解炭与树脂炭混合基体炭/炭复合材料在不同制动压力下的摩擦磨损性能,且对摩擦表面与磨屑进行了SEM观察和分析,并采用X射线衍射与激光喇曼光谱测定了在不同刹车压力下摩擦表面的石墨化度.研究结果表明:C/C复合材料的摩擦因数由摩擦表面所形成的摩擦膜所决定,随着刹车压力的增大,摩擦膜更完整平滑,摩擦因数呈降低趋势,磨损则随刹车压力的增大而呈增大趋势;粗糙层结构C/C复合材料即使在高制动压力下,仍能具有较高的摩擦因数,显示出优良的高压摩擦性能;高压下摩擦表面会发生应力石墨化作用,这是高压下摩擦因数下降的原因之一.     

热解炭结构对炭/炭复合材料摩擦磨损性能的影响

通过控制化学气相沉积工艺条件,得到粗糙层、光滑层、过渡结构、各向同性等几种具有不同微观结构的热解炭.通过金相观察、石墨化度、摩擦磨损性能的测试,得出:热解炭的微观结构对炭/炭复合材料的摩擦磨损性能有较大影响;制动过程中形成的薄膜使摩擦因数降低;粗糙层结构的炭/炭复合材料石墨化程度高,摩擦因数高,线型平稳,且随着压力的增加,其力矩上升明显,是一种优良的摩擦材料;光滑层结构的炭/炭复合材料石墨化度低,摩擦因数低,磨损小.     

炭/炭复合材料熔融渗Si研究

为了改善航空刹车副用炭/炭复合材料的摩擦磨损性能,对A,B 2种试样进行了渗Si处理.在试样A的摩擦磨损试验中,其线性磨损由原来的42 μm/次降低到17.56 μm/次,摩擦因数较稳定,均为0.36,并且摩擦磨损曲线的线型较好;试样B渗Si后也比渗Si前的摩擦磨损曲线线型好,同时解决了摩擦时的振动问题,但随试样中所生成SiC含量的增加,其摩擦因数由0.40→0.34→0.30降低,静盘线性磨损量由2.0→21.21→69.33 μm增加,对应的动盘线性磨损量也由1.4→23.12→52.85 μm增加.并从摩擦磨损的机理上进行了分析.实验结果表明,摩擦磨损性能一方面受A,B 2种试样的结构性能影响;另一方面是由渗Si后所生成SiC的性能和不同结构决定的.     

不同能载水平下C/C复合材料的摩擦特性

对具有粗糙层热解炭结构的针刺毡C/C复合材料在MM 1000型摩擦试验机上模拟某飞机正常着陆、超载着陆和中止起飞3种不同的能载水平进行摩擦磨损性能试验,并对磨损表面和磨屑进行扫描电镜观察.结果表明:C/C复合材料在不同能载水平下均具有高达0.31～0.32的摩擦因数,刹车力矩曲线均较平稳,磨损随能载水平的增加而增大;样件的磨损表面在正常着陆条件下形成较光滑、完整、连续的磨屑层,随着能载水平的增加,形成粗糙的磨屑层,在极高的能载水平(中止起飞条件)下又形成光滑的磨屑层;而样件的磨屑尺寸随能载水平的增加而急剧减小.表明该C/C复合材料具有极好的摩擦制动性能,尤其是在大能载水平下,摩擦性能更加优良,适用作飞机刹车材料.     

刹车速度对RMI-C/C-SiC复合材料摩擦磨损行为的影响

以针刺整体炭毡为坯体,采用化学气相浸渗法（CVI）增密制备C/C多孔体,然后采用熔硅浸渗C/C多孔体制备C/C-SiC复合材料。在MM-1000摩擦磨损试验机上测试该材料在不同刹车速度下的摩擦磨损行为,分别用金相显微镜和扫描电子显微镜观察摩擦表面及磨屑形貌。结果表明：复合材料摩擦因数随刹车速度的增加先升高后降低最后趋于稳定;在速度为2 500 r/min时,摩擦因数达到0.52;磨损量随刹车速度的提高而降低,在速度为1 000 r/min时,线性磨损量为最大值21.3μm/（面·次）;当刹车速度小于4 000 r/min时,摩擦磨损机理为很严重的磨粒磨损,当速度大于4 000 r/min时,摩擦磨损机理以粘着磨损和氧化磨损为主。     

湿式C/C制动材料的摩擦特性及其数值模拟

利用多元耦合场CVI工艺将炭毡增密至1.58 g/cm3,再进行树脂浸渍/炭化增密至1.85 g/cm3制备C/C复合材料。测试由其制成的摩擦实验环的湿式摩擦磨损性能,并利用软件建立的有限元模型对2 500 r/min及1.5 MPa时摩擦实验环的温度场分布进行模拟。结果表明:该湿式摩擦材料的摩擦因数在0.07~0.13间波动,当初始转速恒定时,摩擦因数随刹车压力的增大而减小;当刹车压力恒定时,摩擦因数先增大后减小。建立了C/C复合材料湿式制动过程模型,通过模拟获得了制动盘的各个部位温度场在本模拟研究中呈岛形分布,最高温度出现在0.875 s,这为制动材料的设计提供了参考。     

制动条件对Cu基闸片材料摩擦磨损性能的影响

采用粉末冶金工艺制得Cu基摩擦材料。利用MM1000-Ⅱ型摩擦磨损试验机对材料进行性能测试,用扫描电镜观察磨痕并分析磨损机理。分析结果表明:一定制动压力条件下,随着制动速度的增加,摩擦因数和磨损率均呈现先增大后减小的趋势。制动速度为250~300 km/h时,材料的制动性能最好。在不同的制动速度条件下,材料摩擦因数的稳定因数均保持在较大值,材料表面状态较为稳定。一定制动速度条件下,随着制动压力的增加,摩擦因数先增大后减小,磨损率逐步增大并趋于稳定;0.4 MPa时摩擦因数达到最大值0.35,此时材料的制动性能最好。     

铜基粉末冶金摩擦材料的湿式摩擦性能

采用粉末冶金方法制备铜基湿式摩擦材料,利用金相技术分析材料表面的微观结构,并用MM-1000摩擦试验机研究制动条件对动摩擦因数影响的变化规律。研究结果表明：添加短切炭纤维增强的材料能有效提高材料的能量许用负荷和摩擦因数;摩擦副的制动速度为1500r／min和2500r／min时,摩擦因数随制动压力的增加而减小;摩擦副的制动速度为3500r／min时,摩擦因数随制动压力的增大呈现先降低而后增大的趋势;当制动压力为1．0MPa和1．5MPa时,摩擦因数随制动速度的提高而缓慢减小;当制动压力为2．0MPa和2．5MPa时,摩擦因数随制动速度的增加呈现先减小而后急剧增大的趋势。     

Friction and Wear Behaviors of C/C-Si C Composites under Water Lubricated Conditions

C/C-SiC composites have the potentiality to be applied in shield pumps of nuclear reactors as the bearing material because of their low density, good mechanical properties and excellent tribological properties. The C/C-SiC composites are fabricated via reactive melt infiltration(RMI) using silicon liquid infiltrated in C/C matrix composites. Friction and wear behaviors of C/C-SiC composites under water lubricated conditions are investigated using the block-on-ring test at room temperature, and compared with those of the resin graphite which is used as the bearing material in shield pumps at present. In addition, friction and wear mechanisms of C/C-SiC composites under water lubricated conditions have been discussed. Results show that tensile strengths of C/C-SiC composites are 150-210 MPa, and compressive strengths are 403-536 MPa. Friction and wear behaviors of C/C-SiC composites are closely related to the load and the speed. The time to reach a stable friction status decreases with the increase of the speed. Though the friction coefficient of C/C-SiC composites under water lubricated conditions is slightly higher than that of graphite, the wear rate of C/C-SiC composites is much lower, which suggests that the C/C-SiC composites can sustain a longer life during operation.     

离心铸造高铅锡青铜合金摩擦磨损性能研究

采用离心铸造方法制备了高铅锡青铜(ZCu Pb22Sn1.5)合金,研究了载荷和摩擦速度对其摩擦磨损性能的影响及摩擦磨损机理.研究发现:在0.05 m/s摩擦速度下,随着载荷的增加,高铅锡青铜合金摩擦系数减小,磨损率增加,当载荷增加到120 N后,摩擦系数趋于稳定;在100 N载荷下,随着摩擦速度的增加,摩擦系数逐渐减小,磨损率增加,摩擦速度增加到0.10 m/s以后,摩擦系数迅速减小,到0.20 m/s以后摩擦系数趋于稳定;当继续增加载荷和摩擦速度时,由于铅润滑膜的破坏而增加了磨损率.在摩擦磨损过程中容易在摩擦表面形成软质铅润滑膜从而起到耐磨作用.     

盘式制动器铜基摩擦片摩擦制动特性的实验研究

为了研究盘式制动器铜基摩擦片与制动盘的摩擦制动特性,分析了盘式制动器制动原理。通过对铜基摩擦片的摩擦特性进行实验,探讨了不同制动速度以及制动压力下摩擦系数和磨损率的变化规律。研究结果表明:制动压力为30 N时,摩擦系数随时间逐渐增大并趋于稳定,稳定后的平均值为0.46;磨损率随制动压力增加而增加,随制动速度的增加而减小;此外,制动压力为30 N、制动速度为80 mm/min时,达到实验中的最佳制动效果。     

蠕墨铸铁在铁道车辆制动系统的应用

在分析车辆制动器摩擦温度场的基础上 ,研究了蠕墨铸铁在铁道车辆制动系统的使用性能。研究结果表明 :在车辆制动器服役条件下 ,摩擦速度与接触压力的提高 ,摩擦副的摩擦系数显著降低 ,而磨损率显著增加 ;在所研究的不同石墨形态的铸铁中 ,蠕墨铸铁不但具有低而稳定的磨损率 ,而且具有高而稳定的制动性能 ,是制造车辆制动器部件的合理选材。     

C/SiC复合材料摩擦性能及储油性能分析

复合材料因性能独特而备受关注,但其自身结构复杂且受到诸多因素的影响,因而对其摩擦学性能的研究仍有待进一步加强。为了对比不同摩擦配副对C/SiC复合材料摩擦性能及储油性能的影响,以C/SiC复合材料为研究对象,运用销盘摩擦学试验方法,研究了C/SiC复合材料与45#钢以及C/SiC复合材料与ZrO₂材料摩擦配副的摩擦学性能,采用三维形貌仪等仪器对C/SiC复合材料摩擦后的表面进行表征分析,研究其摩擦后的表面质量及其储油性能。结果表明,C/SiC复合材料与45#钢磨损剧烈,摩擦后表面储油性能严重下降;其与ZrO₂对磨则摩擦系数较低,磨损量较小,摩擦后的表面仍保持了较好的承载性能及储油性能,是一种良好的摩擦配副。研究结果为拓展C/SiC复合材料的应用及揭示其摩擦学特性提供了有力支撑。     

不同载荷和对偶下C/C-Cu复合材料的摩擦磨损性能

以炭纤维针刺整体毡为预制体,用化学气相渗透（CVI）、浸渍/炭化（I/C）的方法制备密度和基体炭不同的C/C多孔坯体,采用真空熔渗将铜合金液渗入C/C坯体中制备C/C-Cu复合材料,研究试验条件对复合材料摩擦磨损性能影响。研究结果表明：随着时间的延长,C/C-Cu复合材料摩擦因数趋于稳定;随着载荷的增加,摩擦因数和体积磨损先增后减,当载荷为80 N时达到最大值;试样摩擦因数和体积磨损与对偶件有关,当采用硬度较高的40Cr钢为对偶件时,试样摩擦因数随着时间的延长而增加并趋于稳定,且磨损量最大;当采用硬度低的黄铜和紫铜为对偶件时,试样摩擦因数随着时间变化不大,与紫铜对偶时的磨损量最小;C/C-Cu复合材料的磨损机制主要为磨料磨损、粘着磨损,采用40Cr钢作对偶时氧化磨损加大。     

氯化胆碱作为润滑剂研究

研究了氯化胆碱在钢-钢摩擦副表面上不同速度不同载荷条件下的润滑特性.在利痕试验机和销盘式摩擦磨损试验机上测定不同速度不同载荷条件下的摩擦系数,分析其润滑特性;通过测试摩擦副表面粗糙度、润滑剂吸附力,研究其润滑机理;结果表明,用氯化胆碱作为润滑剂,钢-钢摩擦副之间能出现低的摩擦系数,但在摩擦一段时间之后,润滑剂会失去,摩...     

非平衡磁控溅射CrTiAlN镀层摩擦学性能分析

为探讨CrTiAlN镀层高硬度、低磨损机理,应用UDP850/4镀层设备,在高速钢和单晶硅基体上制备了CrTiAlN复合镀层,并测试了其力学性能和摩擦学性能,采用XRD、SEM、TEM等手段对镀层微观组织结构进行了分析.结果表明:在75 V负偏压下沉积的镀层具有显微硬度高、摩擦系数小,磨损率低,膜/基结合和韧性良好;镀层由CrN、TiN、AlN、Cr2N和Ti2N等纳米晶组成;纳米晶粒弥散于非晶的结构是硬度增强的机理;良好的膜基结合、韧性好和低摩擦系数是镀层具有低磨损的原因.