油润滑下WSi2/MoSi2复合材料的摩擦学性能

运用M 200型摩擦磨损试验机测定了WSi2/MoSi2复合材料与45#钢配副油润滑时的摩擦学性能,采用扫描电子显微镜分析了其磨损机理.结果表明:油润滑可明显改善WSi2/MoSi2复合材料的摩擦学性能,在80～120N时材料具有较好的摩擦磨损综合性能;在油润滑下,WSi2/MoSi2复合材料的磨损机理表现为点蚀磨损和磨粒磨损,偶件45#钢的损失主要归因于磨粒的切削作用.图6,参13.     

碳纤维/石墨-铜基自润滑耐磨复合涂层的摩擦学性能

为提高45~#钢的摩擦学性能,采用热压烧结技术,在45~#钢表面制备了以Ni为中间连接层的铜基自润滑耐磨复合涂层。采用扫描电镜和能谱仪对涂层表面及截面的微结构进行了分析;采用球-盘式摩擦磨损试验机与GCr15球配副,在不同载荷和速度下,研究了铜基自润滑耐磨复合涂层和基体的干摩擦学性能,并分析了磨损机理。结果表明:在所有试验条件下,含4wt%碳纤维和2wt%石墨样品的摩擦系数和磨损率均比45~#钢低,且在15 N载荷、500 r/min转速下显示出最优的摩擦学性能。     

减振材料的摩擦磨损特性及影响因素

对部分新的和常用的货车摩擦减振器材料进行了比较系统的摩擦磨损试验,分析了7组不同配副材料的摩擦磨损性能及其影响因素.结果表明,T10与针状铸铁、高分子复合材料及少合金ADI球铁/ADI球铁配副的摩擦系数均小于45钢与ADI球铁配副;试验的所有摩擦副的重量磨损量均比传统的45钢与ADI摩擦副的磨损量小,T10与高分子复合材料配对的摩擦副磨损量最小;影响摩擦副摩擦磨损特性的主要因素有摩擦速率、摩擦表面的状况、材料的导热和蓄热能力及摩擦副材料的相溶性等.     

含BaSO_4钴基自润滑复合材料的制备及高温摩擦学性能

采用热压烧结技术制备3种含不同BaSO_4质量分数的钴基自润滑复合材料,研究其在室温到1 000℃范围内的摩擦学性能。在载荷为15 N、滑动速度为0.19 m/s的条件下,采用球-盘式高温摩擦试验机与Si_3N_4陶瓷球配副研究复合材料的高温摩擦学性能。采用X线衍射仪和扫描电镜等分析复合材料的物相成分和摩擦表面形貌。研究结果表明:随着BaSO_4质量分数的增加,复合材料的硬度和密度逐渐降低。从室温到800℃,复合材料的摩擦因数逐渐降低,这是由于随着温度的上升,复合材料的摩擦表面逐渐形成了由铬酸盐、钼酸盐和氧化物等组成的润滑膜,使得复合材料在高温条件下具有了较优良的减摩耐磨性能。在3种钴基复合材料中,含10%BaSO4的钴基自润滑复合材料在400～800℃范围内的摩擦学性能较好。     

磁场强度对叠层复合材料摩擦学性能的影响

采用叠装-粘接工艺制备了不同润滑剂含量的钢-聚合物叠层复合材料,以GCr15钢球为摩擦配副,在球-盘摩擦试验机上考察叠层复合材料在不同磁场强度下的摩擦学性能.摩擦实验结果发现:随着磁场强度增大,不含润滑剂的叠层复合材料(S0)的摩擦系数和磨损率均发生显著降低;含润滑剂的叠层复合材料(S4)的摩擦系数和磨损率先缓慢降低后增大.用扫描电子显微镜(SEM)和能谱仪(EDS)观察磨损表面形貌和元素分布,分析其磨损机理表明:细小磨屑被磁场吸附在接触表面并形成了滚珠效应,显著改善了S0的磨粒磨损和粘着磨损;在摩擦热和涡流热作用下,润滑剂迁移到硅钢表面并形成转移膜,使得S4具有良好的润滑性能;在无磁场时S4的聚合物表面发生疲劳剥落,在磁场作用下聚合物以塑性流动和粘着磨损为主.     

纳米SiO2填充UHMWPE/PTFE/纳米MMT复合材料的摩擦磨损行为

通过热压成型工艺制备纳米SiO2和纳米蒙脱土(MMT)及聚四氟乙烯(PTFE)复合填充超高分子量聚乙烯(UHMWPE)复合材料,采用销-盘式摩擦磨损试验机考察复合材料在干摩擦条件下与45#钢配副时的摩擦磨损行为,用扫描电子显微镜观察复合材料的磨损表面形貌.结果表明:当PTFE和MMT的填充质量分数均保持6%,填充质量分...     

基于离散元研究石墨对铜基石墨复合材料摩擦磨损性能的影响

文章利用离散元二维颗粒流程序(PFC2D)建立铜基石墨复合材料和45#钢摩擦副数值模型,基于环-块滑动接触方式,研究摩擦过程中摩擦界面动态变化规律及石墨粒径和体积分数对复合材料摩擦磨损性能的影响。结果表明：复合材料和45#钢摩擦过程中,在摩擦表面逐渐形成石墨润滑层,使得摩擦副的接触由金属与金属接触逐渐转变为石墨与金属接触;随着时步数增加,材料摩擦系数整体下降并达到稳定;石墨粒径增加,摩擦系数增大,磨损量先减少后增多,石墨粒径为18μm时,磨损量最少为1.65×10^-8 m³;石墨体积分数增多,材料摩擦系数降低,磨损量先减少后增多,石墨体积分数为12%时,磨损量最少为1.61×10^-8 m³。     

石墨相氮化碳表面包覆改善锂离子电池正极材料LiCoO2电化学性能的研究

通过简单的固相法和液相法,分别制备出石墨相氮化碳（g-C₃N₄）表面改性的商品化LiCoO₂复合材料,采用扫描电子显微镜观察改性后的材料,发现g-C₃N₄都均匀地包裹在LiCoO₂表面。两种g-C₃N₄-LiCoO₂复合材料被用作锂离子电池的正极材料,电化学测试结果显示,固相法制得的g-C₃N₄-LiCoO₂复合材料在0.2 C的倍率下充放电测试,首次比容量达167 mA·h·g^-1,循环80次后,比容量仍达132 mA·h·g^-1,高于未经g-C₃N₄包裹的纯LiCoO₂（98 mA·h·g^-1）;液相法制得的Y-C₃N₄-LiCoO₂复合材料循环稳定性明显优于同类材料,循环80次后容量保持率均在95%以上。试验证实,g-C₃N₄表面改性的策略具有一定的实用价值,改性后,材料优异的电化学性能归因于g-C₃N₄的包裹处理,这不仅增强了固体电解质界面（SEI）的稳定性,也抑制了锂离子嵌入/脱出电极材料时引起LiCoO₂体积的变化。     

镍/聚四氟乙烯复合材料摩擦诱导磁化的研究

文章利用多功能环境可控摩擦磨损试验机,研究了具有不同镍含量的聚四氟乙烯(PTFE)基复合材料和45号钢干摩擦时的摩擦诱导磁化以及摩擦学性能,考查了镍含量对摩擦诱导磁化和摩擦学性能的影响。研究结果表明:含有镍颗粒的PTFE基复合材料在摩擦过程中能够产生摩擦诱导磁化现象,且摩擦诱导磁化的磁感应强度与镍含量有关;随着镍含量的增加,Ni/PTFE复合材料摩擦诱导磁感应强度逐渐增大,摩擦系数几乎不变,磨损量先逐步减小后迅速增大;摩擦诱导磁化作用在一定程度上对促进转移膜的生成有利,从而有利于改善摩擦学性能。     

Fe_xSi_y改性C/C-SiC制动材料的制备及其性能

以针刺整体炭毡为预制体,采用化学气相渗透法(CVI)增密制备C/C多孔体,采用反应熔体浸渗法(RMI),将Fe与Si同时熔渗进C/C坯体中制备FexSiy改性C/C-SiC复合材料。研究FexSiy改性C/C-SiC复合材料的组织结构、力学性能和摩擦磨损性能。研究结果表明:硅铁化合物被SiC基体包围填充于C/C坯体孔隙中;FexSiy改性C/C-SiC复合材料的弯曲强度为189.65 MPa,垂直和平行摩擦面的压缩性能分别为296.93 MPa和201.32 MPa;分别采用30Cr钢和自身材料作对偶时,FexSiy改性C/C-SiC复合材料的平均摩擦因数均为0.24左右,线磨损均小于3.5μm.面-1.次-1,但与铬钢对摩静系数明显增大,而与自身对摩制动曲线出现明显翘尾现象,其摩擦磨损过程是由磨粒磨损、黏着磨损和氧化磨损相互作用的结果。     

MOSi2-淬火45#钢在油润滑下的摩擦学特性

利用M-200型磨损试验机考察了MoSi2-淬火45针仪分析讨论其磨损机理.结果表明:润滑油明显改善了MoSi2材料的摩擦学性能;MoSi2与淬火45#钢对摩在120～150 N载荷范围内表现出较好的摩擦磨损综合性能;其磨损机制主要表现为疲劳磨损、磨粒磨损和轻微粘着磨损.图4,参10.     

SiC颗粒填充单体浇铸尼龙的摩擦学性能

为了研究 Si C颗粒作为填料对单体浇铸尼龙 (MC尼龙 )的摩擦磨损性能的影响 ,选用两种材料在 MM- 2 0 0摩擦磨损试验机上进行了试验研究 ,并借助于扫描电镜观察了磨损形貌 ,探讨了磨损机理。研究结果表明 ,在干摩擦条件下 ,Si C颗粒填充 MC尼龙的摩擦学性能与载荷和滑动速度的乘积 (Pv)值的大小有关 ,复合材料的摩擦因数比纯尼龙的大 ,当 Pv值较低时 ,复合材料的耐磨性能比纯尼龙好 ,其磨损机理主要是磨粒磨损和粘着磨损 ;当 Pv值较高时 ,复合材料的耐磨性能不如纯尼龙 ,其磨损机理主要是疲劳剥落 ,并有磨粒磨损和粘着磨损。在水润滑条件下 ,Si C颗粒填充 MC尼龙表现出较好的耐磨性能 ,其摩擦学性能受 Pv值的影响小 ,磨损机理主要是磨粒磨损     

仿生凹坑与纳米碳化硅/镍基复合镀层耦合表面的磨损性能

为了探讨凹坑形态与纳米碳化硅/镍基复合镀层耦合表面的磨损性能,采用激光技术和电沉积技术制备了由凹坑形态和纳米碳化硅/镍基复合镀层构成的仿生耦合表面,并进行了摩擦和磨损试验。结果表明,仿生耦合表面的磨损性能高于单纯复合镀层的磨损性能;随着磨损载荷的增加和磨损时间的延长,试样表面磨损机制由以塑性磨损为主逐渐转变成以粘着磨损、磨粒磨损为主的磨损机制。     

压缩机动涡旋表面磷化膜层的磨损性能

采用AMSLER摩擦磨损试验机,模拟压缩机上支撑与动涡旋摩擦副,对灰铸铁表面磷化膜层摩擦副在不同条件下的摩擦磨损性能进行了研究,采用扫描电子显微镜(SEM)观测摩擦磨损表面形貌.试验结果表明:磷化工艺可以有效降低灰铸铁与磷化膜层之间的摩擦系数;在摩擦磨损过程中,磷化膜避免了金属表面的直接接触,降低了摩擦副之间的黏着.磷化试样在高速和低速条件下的抗咬合性能均优于未磷化试样.     

Effect of different atmospheres on dry friction behavior of steel sliding against brass at high speed

The atmosphere components have an influence on tribological behaviors of tribo-pairs. Through changing the atmosphere component, the effect of atmosphere component on the tribological behaviors of CrNiMo steel against brass at high sliding velocity was investigated. The wear test was carried out on a high-speed friction and wear test rig whose test atmosphere could be controlled. The tests were performed at four sliding velocities （30, 40, 50, 60 m/s）, one contact pressure （1.33 MPa） and two atmosphere components （N2 or O2）. The morphologies of the worn surfaces of various pins were observed with a scanning electron microscope. The chemical compositions of the surfaces and subsurfaces for steels were determined with an energy dispersion spectroscopy. The results showed that the wear rate of the steel pins were low all the time with the sliding velocity increasing in oxygen atmosphere, and that the wear rate of the steel pin in nitrogen atmosphere was higher than that of the steel pin in oxygen atmosphere. It was found that the thin and compact oxidation layer formed on the worn surface of the steel in oxygen atmosphere played a key role in wear resistance. However, the wear rate of the steel pin increased rapidly with the sliding velocity increasing in nitrogen atmosphere, which was attributed to the thick and loose surface layer formed on the worn surface of the steel.     

刷镀电压对镍镀层摩擦磨损性能的影响

为研究刷镀电压对镍镀层摩擦磨损性能的影响,分别在不同刷镀电压下,采用快速镍刷镀方法在45~#钢表面制备工作层.在球-盘摩擦磨损试验机上,以Cr12钢球为摩擦配副进行油润滑条件下的摩擦磨损试验,通过磨损失重、油液的光谱和铁谱分析、摩擦系数、磨损表面形貌研究了不同镍镀层的摩擦磨损性能.结果表明:不同刷镀电压下制备的镍镀层的摩擦磨损性能存在较大差异.刷镀电压过低(8V)或过高(22V)时,镍镀层耐磨性能均下降;当刷镀电压为14V时,镍镀层的摩擦磨损性能最佳;镍镀层磨损机制以磨粒磨损和黏着磨损为主.     

MPTS/MPTES复合自组装薄膜的制备及摩擦磨损特性分析

采用分子自组装技术,在单晶硅表面制备3-巯丙基三甲氧基硅烷(MPTS)、3-甲基丙烯酰氧丙基三甲氧基硅烷(MPTES)薄膜以及MPTS/MPTES复合自组装薄膜,利用原子力显微镜（AFM）、X射线光电子能谱仪（XPS）及接触角测定仪对MPTS/MPTES复合薄膜的结构进行分析,并采用DF PM型动/静摩擦系数精密测定仪评价其摩擦磨损性能.结果表明,与MPTS薄膜和MPTES薄膜相比,MPTS/MPTES复合薄膜具有优异的疏水性和摩擦磨损性能,其原因在于MPTS/MPTES复合薄膜的分子体积较大并具有可移动性和特殊的柔韧性,其基底附近呈现出类似于固体紧密排列的结构并具有一定的刚性和承载能力.     

Tribological behaviors of some polymeric materials in sea water

Ocean tribology, a new research field of tribology, is being established and developing. The investigation on the tribology in sea water has important significance to ocean exploitation. In this paper, the tribological behaviors of UHMWPE, PTFE as well as Ekonol/PTFE, graphite/PTFE and CF/PTFE sliding against GCr15 steel and Ni-Cr-WC alloy in sea water were investigated, and compared with those in pure water. Results show that the main factors that affect the tribological behaviors of five polymeric materials in sea water are the corrosive effect and lubricating effect of sea water. When polymeric materials sliding against GCr15 in sea water, owing to serious corrosion of counterface by sea water, the surface roughness of the counterface increases largely. As a result, the lubricating effect of medium decreases sharply and the plowing effect of counterface increases greatly. So the friction coefficients and wear rates of five materials sliding against GCr15 in sea water are much larger than those under other conditions. Such wear model, depending on the corrosion of counterface by medium, can be called indirect corrosive wear. Under other three conditions, owing to the more superior lubricating effect of sea water than pure water and the better wettability of Ni-Cr-WC than GCr15, the friction coefficients and wear rates of five materials increase in the following order： sliding against Ni-Cr-WC in sea water 〈 sliding against Ni-Cr-WC in pure water 〈 sliding against GCr15 in pure water. Moreover, compared with other materials, CF/PTFE is the one with more superior plowing and wear resistance in pure and sea water, which is a potential frictional material well suitable for pure and sea water lubrication.     

基于原位反应制备CuO/PPS复合涂层的热性能和摩擦学性能

利用原位反应方法在PPS涂料中掺杂CuO,通过浸涂制备了CuO/PPS复合涂层.利用热重分析仪测试了涂层的热性能,选用销盘式磨损实验机测试了涂层的摩擦学性能,采用SEM观察分析了磨损表面,并在此基础上探讨了磨损机理.研究结果表明,涂层表面平整光洁,复合涂层热稳定性较PPS树脂有所提高,热分解温度提高;CuO的加入使PP...