光辐射对丙烯酸聚氨酯涂层防腐保护性能的影响

以氙灯为光源,对丙烯酸聚氨酯涂层/碳钢体系进行人工加速老化实验,用傅里叶变换红外光谱仪(FTIR)、光学显微镜和光泽仪对老化的涂层进行分析表征,用盐雾实验测试涂层老化后的防腐性能,初步探讨了光辐射对涂层保护性能的影响.结果表明,不同老化周期的体系在盐雾实验后,表面涂层的保护状态均基本完好,但膜下金属腐蚀程度随老化时间的增加而加剧.其原因是:光辐射使涂层中C—N键断裂,且随老化时间的延长,涂层表面粗糙程度增加,光泽度下降;涂层化学结构及表面状态的变化加速了腐蚀介质在涂层中的渗透,从而导致膜下金属腐蚀加重.     

人工加速老化对聚脲涂料防护性能的影响

针对聚脲涂料防腐涂层进行紫外加速老化实验,采用光泽度计、扫描电子显微镜(SEM)以及傅里叶变换红外光谱仪(FTIR)分析并结合电化学阻抗谱(EIS)图谱,研究涂层的老化行为.结果表明:涂层的老化分为前期、中期和后期三阶段,涂层表面在老化中期变色较大.涂层的表面、断面SEM及EIS测试显示涂层中的微气泡阻止了涂层的老化裂纹向基体发展,涂层仍保持较好的防护性能.     

有机涂层室内加速实验的对比

研究了丙烯酸聚氨酯清漆涂层在荧光紫外UVA辐照/凝露和氙灯辐照/雨淋两种加速实验程序下的物理、化学性能和防护屏障性与暴露时间的关系.结果表明:氙灯辐照/雨淋对涂层的膜厚损失、失光率的影响程度略大于同周期UVA加速的效果;而黄色指数及不同暴露周期的完整涂层的低频阻抗模值与暴露时间的关系则与FTIR反映的羰基指数的变化规律较为一致,显示UVA加速涂层老化的效果大于同周期氙灯加速效果.且在两种加速条件下,完整涂层的低频阻抗模值均与暴露时间呈指数规律衰减,表现出较好的时间函数关系;说明EIS的低频阻抗模值与UV光辐射产生的涂层性能的变化有一定的相关性,并很好地反映其防护屏障性,可作为有效的监测参量用于建立室内外老化实验的相关性,预测光老化涂层的防护寿命.     

丙烯酸聚氨酯涂层的紫外老化行为

针对丙烯酸聚氨酯防腐涂层进行紫外加速老化实验,采用光泽度、色差检测以及SEM、FTIR分析,结合交流阻抗谱法(EIS),研究丙烯酸聚氨酯涂层的紫外老化行为.结果表明:用光泽度表征涂层光降解程度更灵敏;由接触角及色差等变化规律可将丙烯酸聚氨酯涂层紫外老化分为前期(慢速光老化)、中期(快速光老化)和后期(慢速光老化)三阶段.对涂层进行表面化学分析认为丙烯酸聚氨酯的紫外光降解主要是O—CH键及C—N键断裂导致的;涂层表面形貌和性能与EIS结果对比分析显示丙烯酸聚氨酯涂层发生明显降解之前防护性能已经明显下降.     

丙烯酸聚氨酯涂层耐老化性能指标的数学模型

通过丙烯酸聚氨酯涂层室内氙灯加速老化实验,结合光泽度、色差检测和微观形貌分析,探究了丙烯酸聚氨酯涂层耐老化性能指标随加速老化实验时间的变化规律,初步建立了涂层耐老化性能指标随加速实验时间的数学模型.研究结果表明:涂层光泽度、失光率随加速实验时间近似呈类指数函数模型变化;涂层色差随加速实验时间近似呈类幂函数模型变化.通过拟合各性能指标的数学模型得出了涂层耐老化性能指标与加速实验时间之间的数学关系式,相关系数均在0.99以上,具有较好的相关性.     

铝板表面锆化陶瓷膜的结构及性能

采用锆化工艺在铝板表面制备了陶瓷膜,用扫描电镜和能谱仪分析了陶瓷膜的组织形貌和元素成分,用电化学法研究了陶瓷膜的耐蚀性能,用附着力测定仪测试了陶瓷膜的涂装附着力性能以及用中性盐雾实验研究了涂层体系的耐盐雾性能.结果表明:铝板表面的陶瓷膜为无色的纳米膜层,主要由Zr,Si和Al的氧化物组成;锆化陶瓷膜的的耐电化学腐蚀性能优异,与环氧树脂漆或聚氨酯漆的附着力均为1级;整个涂层体系可通过600 h的中性盐雾实验.锆化陶瓷膜可以用作铝板的漆前打底膜,有望替代污染较重的磷化处理工艺.     

镁合金微弧氧化-涂装体系的研究

提出了一种镁合金/微弧氧化膜/有机涂层的镁合金防护体系.在以硅酸钠为主的复合溶液中,利用双向对称脉冲电压在阴、阳极镁合金表面同时微弧电沉积陶瓷膜.利用盐雾实验比较了以镁合金微弧氧化膜为基底并涂覆环氧底漆和聚胺脂丙烯酸面漆的试样与镁合金/微弧氧化膜/有机硅、镁合金/微弧氧化膜/溶胶凝胶涂装试样的耐蚀性,并利用盐雾实验与交流阻抗谱相结合跟踪对比分析了镁合金/有机涂层、镁合金/铬酸盐转化膜/有机涂层、镁合金/微弧氧化膜/有机涂层的屏蔽性能.结果表明:采用溶胶凝胶、有机硅和有机涂层对微弧氧化膜进行涂装的方法均可进一步提高镁合金的耐蚀性,其中镁合金/微弧氧化膜/有机涂层试样可承受480h以上的中性盐雾实验,且其介质屏蔽性能优于镁合金/有机涂层和传统的镁合金/铬酸盐转化膜/有机涂层防护体系.     

H_2O_2对涂层老化行为影响研究

采用光泽度、色差检测及SEM分析,研究H_2O_2对涂层加速老化行为。考察了H_2O_2浓度、辐照强度和辐照时间对涂层失效特征的影响。实验结果表明,涂层的失光率和黄变系数随着H_2O_2浓度、辐照强度和辐照时间的增加而呈上升趋势。开展了紫外加速老化、氙灯加速老化和H_2O_2+氙灯加速老化三种老化实验,并探讨他们之间的相关性。结果表明,H_2O_2+氙灯加速老化效果强于其它两种老化方法,基于紫外加速老化方法的加速因子为30,基于氙灯加速老化方法的加速因子为80。     

三元乙丙橡胶的人工气候老化

利用氙灯人工气候箱对三元乙丙橡胶(EPDM)进行人工气候老化实验,采用X射线光电子能谱(XPS)、扫描电子显微镜(SEM)、电子万能试验机和色度计研究了人工气候老化对EPDM化学结构、表面形貌、力学性能和颜色的影响. 结果表明:在氙灯人工气候环境中老化90d后,EPDM表面生成一层厚度约2μm的氧化膜,其组成包括有C-O-C/C-OH、CO和O-CO;交联密度随老化时间的变化基本呈线性增加;随老化时间的延长,试样表面粗糙度增加,有孔洞和微裂纹生成,拉伸强度、撕裂强度和硬度增加,EPDM试样表面变红变黄,亮度增加.     

Al_2O_3对激光熔覆镍基涂层腐蚀性的影响

为研究不同Al2O3含量对激光熔覆镍基涂层耐腐蚀性能的影响.将基体与不同Al2O3含量的Al2O3/Ni熔覆层界面进行对比试验,利用SSX-500型扫描电镜对合金熔覆层的组织形貌进行观察,采用电化学腐蚀实验和盐雾实验对涂层的腐蚀性进行测试,结果表明,在镍基自熔合金粉末中加入Al2O3后,熔覆层的显微组织得到了细化.当Al2O3含量为40%时,致钝电流密度和维钝电流密度最小,钝化区范围最大;盐雾实验中涂层单位面积增重为1.15mg/mm2,较不加Al2 O3的Ni60合金涂层降低了约48.5%,耐蚀性能得到了显著提高.     

Microstructure and corrosion resistance of Fe/Mo composite amorphous coatings prepared by air plasma spraying

Fe/Mo composite coatings were prepared by air plasma spraying (APS) using Fe-based and Mo-based amorphous and nanocrystalline mixed powders. Microstructural studies show that the composite coatings present a layered structure with low porosity due to adding the self-bonded Mo-based alloy. Corrosion behaviors of the composite coatings, the Fe-based coatings and the Mo-based coatings were investigated by electrochemical measurements and salt spray tests. Electrochemical results show that the composite coatings exhibit a lower polarization current density and higher corrosion potentials than the Fe-based coating when tested in 3.5wt% NaCl solutions, indicating superior corrosion resistance compared with the Fe-based coating. Also with the increase in addition of the Mo-based alloy, a raised corrosion resistance, inferred by an increase in corrosion potential and a decrease in polarization current density, can be found. The results of salt spray tests again show that the corrosion resistance is enhanced by adding the Mo-based alloy, which helps to reduce the porosity of the composite coatings and enhance the stability of the passive films.     

复配抗紫外光老化剂对改善沥青光老化性能的影响

采用紫外光耐候实验箱加速老化系统模拟沥青自然环境下紫外光老化,通过对沥青光老化前后针入度、软化点和延度性能的测试以及FTIR（Fourier Transform Infrared）红外光谱检测,对比分析了复配抗紫外光老化剂对提高沥青抗紫外光老化性能的影响,并对其机理进行了分析,研究结果显示,在一定的老化环境下,添加抗紫外光老化剂的沥青试样老化后与基质沥青老化后相比,针入度增加,软化点减小,延度增加,其抗老化性能有显著提高;添加复配添加剂质量百分比为5％A＋1.5％B的沥青试样,三大性能指标变化百分比较大且羰基特征吸收峰减弱,改善沥青的抗光老化性能较好。     

光照对Q450NQR1耐候钢在干湿交替下腐蚀行为的影响

采用腐蚀质量损失、扫描电子显微镜、X射线衍射仪、线性极化等测试手段,研究无光照、半光照及全光照三种实验条件对Q450NQR1耐候钢在干湿交替条件下腐蚀行为的影响规律.结果表明:光照对实验钢干湿交替腐蚀过程影响显著.实验钢在腐蚀前期(48h)腐蚀速率大小依次为半光照、无光照和全光照,腐蚀中后期(72 ～96h)腐蚀速率由大到小依次为半光照、全光照和无光照.腐蚀宏观形貌有明显差别,无光照时试样腐蚀产物呈淤泥状分布整个表面,有光照条件时腐蚀产物则呈颗粒状分布,但全光照条件时腐蚀产物颗粒更细且孔隙更小.另外,三种条件下腐蚀产物物相组成一致,但含量有所不同.线性极化测试得出96h极化电阻由大到小依次为无光照、全光照和半光照,这一结果与通过腐蚀失重得出的腐蚀速率结果一致.     

热浸Zn-Ti合金镀层的显微组织与耐蚀性能

为了抑制热镀锌过程中因含硅活性钢引起的镀层超厚生长,本文采用在纯锌浴中加Ti的方法,研究了0.09%Si钢在含低于0.1%Ti的几种锌浴中热浸镀获得的组织,并采用盐雾腐蚀,电化学极化以及X射线光电子能谱等方法,研究了Zn和Zn-Ti镀层的耐蚀性能。结果表明,随着锌浴中Ti含量的增加,Ti对ζ相生长的抑制作用增强,合金层厚度逐渐减薄,Ti能有效地抑制含硅活性钢镀层的超厚生长。当Ti含量大于0.05%时,镀层中出现Γ2粒子。Zn-Ti合金镀层在5%NaCl溶液中发生自发腐蚀的倾向小于Zn镀层,其极化电阻增大,腐蚀电流密度减小,耐蚀性能提高。Zn-Ti镀层表面形成的氧化膜由ZnO 和TiO2组成。锌钛合金镀层的耐腐蚀性能优于纯锌镀层是由于在镀层表面形成了更加稳定的TiO2膜。     

时效处理对7085铝合金锻件组织和腐蚀性能的影响

采用慢应变速率拉伸试验、剥落腐蚀试验、极化曲线及透射电镜等分析方法,研究时效处理对7085铝合金锻件腐蚀性能的影响.研究结果表明:与T6时效合金相比,合金经T74时效的抗应力腐蚀和抗剥落腐蚀性能提高但强度显著降低;经RRA时效处理,合金保持了较高强度的同时,应力腐蚀性能敏感性降低,抗剥落腐蚀性能提高;在腐蚀溶液中,极化曲线测试也表现出同样的趋势:合金经过RRA时效处理,形成粗大且不连续的晶界析出相是提高腐蚀性能的主要原因.     

钛钢复合板表面结构及与有机涂层的结合性能

利用高能喷涂技术制备钛钢复合板,喷钛涂层中将不可避免会产生孔隙和裂纹,这将降低钛钢复合板的性能,为此采用几类市售有机涂料以及实验室自制的纳米改性丙烯酸涂料对喷钛涂层进行封孔处理.利用扫描电镜分析了喷钛涂层的表面结构以及与有机涂层的结合形貌,同时通过电化学测试和盐雾试验对比了不同有机涂层/钛钢复合板的耐腐蚀性能.结果表明,采用纳米TiO2,SiO2改性的丙烯酸涂料更适合用作喷钛涂层的封闭涂料,能够与喷钛涂层起协同作用共同保护底材.     

三元乙丙橡胶老化与气候关联性及老化程度全国分布预测

利用三元乙丙橡胶( EPDM)在我国11个典型大气站点暴晒3年的老化数据及气候环境数据,基于对EPDM老化行为分析以及气候环境对EPDM作用机制,探究EPDM老化与气候因子之间的关联性。通过因子分析与逼近理想解排序法,将多个老化指标转化为综合老化值;由灰色关联度分析,得到影响EPDM老化的关键气候因子为辐照度、湿度、温度和降雨;通过BP人工神经网络,建立EPDM综合老化值与气候因子间关联模型。利用我国97个地市级城市气象数据,预测EPDM在未试验地区综合老化值,可视化得到EPDM在我国的老化分布图。图形表明,EPDM在我国西部地区,新疆南部、云南南端、广东南部、海南、台湾等地区老化程度较严重。