电子束辐照制备Fe3O4/PAM磁性核壳微球

在共沉淀法制备Fe3O4纳米磁粉的基础上,以丙烯酰胺（AM）为单体,在水溶液中通过电子束辐照的方法,制备了具有核壳结构的磁性复合微球Fe3O4/PAM.采用XRD、AFM、IR等对样品进行表征.结果表明,制备的磁粉为Fe3O4单相,粒径为8 nm左右,磁性高分子微球Fe3O4/PAM直径约为100 nm,呈球形.分析了单体浓度、磁粉用量、交联剂浓度、辐照剂量等对Fe3O4/PAM微球粒径的影响规律.     

阴离子聚电解质保护的金纳米粒子的制备及表征

采用NaBH4作为还原剂还原HAuCl4的方法,将阴离子聚电解质即聚丙烯酸(PAA)作为保护剂,成功制备了稳定性非常好的小粒径金纳米粒子．分别采用紫外-可见-近红外光谱仪(UV-vis-NIR)、透射电子显微镜(TEM)、光电子能谱仪(XPS)、X射线衍射仪(XRD)和电化学等实验方法对所制备样品进行表征．实验结果表明,合成体系的pH和所用阴离子聚电解质聚合物链的空间位阻对金纳米粒子的稳定性起着非常重要的作用．     

壳聚糖修饰的金纳米复合粒子的制备与表征

用半胱氨酸做稳定剂,壳聚糖做修饰剂,通过NaBH4还原HAuCl4制备了稳定的金/壳聚糖复合纳米粒子(Au/CS),并研究了反应物配比对金纳米粒子性能的影响.通过紫外-可见、红外、X射线衍射及透射电镜对其结构进行了表征.结果表明,当反应物选择合适的配比时可以合成性能良好的金纳米粒子.     

高强度物理-化学混杂双网络水凝胶的制备及性质

以聚乙烯醇（polyvinyl alcohol, PVA）和丙烯酰胺（acrylamide, AM）为原料, 采用“一锅煮”及紫外辐照结合冷冻 解冻两步聚合法制备聚乙烯醇/聚丙烯酰胺(PVA/PAM)混杂双网络水凝胶, 并对水凝胶的力学性能、 溶胀性能、 失水性能以及自愈合性进行测试和分析. 结果表明, PVA/PAM混杂双网络水凝胶具有较高的力学强度, 其拉伸强度为428 kPa, 失水速率和单网络水凝胶相比较慢, 具有一定的自愈合性.     

ZnO/PAM复合纳米粒子的制备与表征

运用沉淀法和反相乳液聚合法制备出具有较强荧光强度的氧化锌/聚丙烯酰胺复合纳米粒子。在包含有氧化锌纳米粒子的油包水反相乳液体系中,由过硫酸钾引发、以丙烯酰胺作为单体进行反相乳液聚合,聚合产物将氧化锌包覆并形成氧化锌/聚丙烯酰胺复合纳米粒子。对复合物煅烧后的得到氧化物粉末进行X射线衍射分析,对复合纳米粒子进行透射电子显微镜分析、动态光散射分析、荧光显微镜分析。获得的氧化锌/聚丙烯酰胺复合纳米粒子形状近似为球形,直径范围约为100-300nm之间,并且能够发出较强的绿色荧光。     

of ZnO/PAM Nano-Composite Particles

运用沉淀法和反相乳液聚合法制备出具有较强荧光强度的氧化锌/聚丙烯酰胺复合纳米粒子。在包含有氧化锌纳米粒子的油包水反相乳液体系中,由过硫酸钾引发、以丙烯酰胺作为单体进行反相乳液聚合,聚合产物将氧化锌包覆并形成氧化锌/聚丙烯酰胺复合纳米粒子。对复合物煅烧后的得到氧化物粉末进行X射线衍射分析,对复合纳米粒子进行透射电子显微镜分析、动态光散射分析、荧光显微镜分析。获得的氧化锌/聚丙烯酰胺复合纳米粒子形状近似为球形,直径范围约为100-300nm之间,并且能够发出较强的绿色荧光。     

金纳米粒子的制备与表征

以4.5 G PAMAM(4.5代聚酰胺-胺型)树状大分子为保护剂,利用微波法还原HAuCl4溶液制备金纳米粒子。考察了在同一照射条件下,4.5 G PAMAM与HAuCl4不同物质的量比对金纳米粒子大小及形状的影响。利用紫外可见分光光度计、透射电子显微镜以及X射线衍射分析对其进行了表征。结果表明,照射时间相同时,以30 s为例,当4.5 G PAMAM与HAuCl4物质的量比为5时,得到的金纳米粒子最小;随着4.5 G PAMAM与HAuCl4物质的量比值的减小,金纳米粒子变大,且发生了不同程度的聚集。     

新型Au@C壳核结构光催化剂的制备及其性能研究

通过水热合成法成功制备了新型纳米复合物Au@C,并通过TEM,XRD等对其进行了表征.从TEM图像可以看出金纳米复合物为球型壳核结构,其中Au核大小约为30～50 nm,UV-Vis图谱表明Au@C新型纳米复合物在紫外可见光谱中500～800 nm的可见光范围内有明显的吸收峰.该催化材料在模拟太阳光下对降解染料罗丹明B有很好的光催化活性,这可归因于Au纳米粒子的表面等离子体共振效应.     

Au纳米晶在单晶硅(110)表面上的分形生长

利用水溶液法制备了Au纳米粒子水溶胶, 透射电镜观察, Au纳米粒子的平均粒径 为29 nm. 将此溶胶滴至干净的单晶硅(110)表面上, Au纳米粒子自组装形成分形结构. 通 过控制温度, 所得的分形结构表现出不同的形貌特点. 利用光学显微镜观察Au纳米粒子 的聚集分形生长过程, 用原子力显微镜对分形结构的表面形貌进行表征, 讨论了分形生 长机理.     

金银合金纳米粒子的制备

以柠檬酸钠为稳定剂,利用硼氢化钠还原AgNO3和HAuCl4混合溶液制备了Au-Ag合金纳米粒子,UV-Vis光谱谱图只观察到一个位于纯银和纯金之间的表面等离子体共振峰,且该表面等离子体共振峰的最大吸收波长与合金中Au的摩尔分数成线性关系.TEM结果表明:Au-Ag合金纳米粒子的粒径大约为43 nm,且颜色均一,没有明...     

UV光引发丙烯酰胺反相微乳液聚合研究

采用光引发聚合技术，选取合适的光引发剂进行丙烯酰胺（AM）反相微乳液聚合。用UV光引发AM／水／白油／（Span80＋OP-10）体系聚合，所得聚合物粘均相对分子质量可达10^6.考察了光引发剂类型及质量分数、单体质量分数、乳化剂质量分数和聚合时间等对聚合反应的影响，得到了光引发合成聚合物的较优工艺条件。通过红外光谱法鉴定出所得聚合物为聚丙烯酰胺（PAM）。     

单分散水性硫普罗宁包覆金纳米粒子可控制备

利用紫外-可见光谱（UV-vis）、X衍射（X-ray Diffraction,XRD）和透射电子显微镜（Transmission Electron Microscope,TEM）等研究小尺寸水溶性金纳米粒子的可控制备.在乙酸和甲醇（体积比为1：6）的混合系统中,通过NaBH4对三水氯金酸还原,将硫普罗宁分子包覆到金纳米粒子表面,得到尺寸可控、稳定的硫普罗宁包覆的金纳米粒子水溶胶.通过控制金与硫普罗宁的摩尔比（Au/S比）,金纳米粒子的尺寸能够在2~8nm范围内得到有效控制.本文中,当Au/S比分别为1：3,1：1和3：1时,所合成的金纳米粒子的尺寸分别为（2.8±0.3）,（4.0±0.3）,（6.1±0.4）nm.     

表面修饰的金纳米粒子的制作及表征

通过硼氢化钠NaBH4还原金氯酸HAuCl4，成功地制作了羧酸酯表面修饰的金纳米粒子，并用丁二酸硫醇作为硫醇配体稳定剂，抑制了纳米粒子的进一步生长，这种方法有效地把粒径控制在纳米范围内并且粒径分布范围小，只需通过一次反应就可大量地制得1－20nm、具有量子效应的纳米料，用X射线衍射仪、透射式电子显微镜和隧道扫描显微镜对这些粒子进行了检测，证实了大量的粒子都是面心立方结构，硫醇配体在金粒子在表面由化学吸附形成一层单分子膜，隧道扫描显微镜观察到了这一层单分子膜。     

光引发丙烯酰胺沉淀聚合研究

以丙酮/水为溶剂，采用紫外光（UV）引发丙烯酰胺（AM）沉淀聚合，考察了聚合反应的特征以及溶剂、初始单体浓度、引发剂浓度、表面入射光强、液层厚度等参数对聚合物分子量的影响。结果表明，紫外光引发丙烯酰胺沉淀聚合过程中单体转化率和聚合物分子量都随反应时间的延长而增加，光照80min时，单体转化率可达90％以上。所得聚合物分子量为10⁵～10⁶，提高单体浓度可使聚合物分子量增加，增加引发剂浓度和提高光强导致聚合物分子量降低，液层厚度对聚合物的分子量影响不大。所得聚合物粒子粒径约为200～300nm左右，粒径分布较为均匀，溶剂组成对聚合物粒子相貌影响较大，增加水含量可使粒子粒经变大但分散性变差。     

Investigation on composite Au/TiO_2 nanoparticles (Ⅰ)——Synthesis and characterization

Nanometer sized Au/TiO\-2 particles were synthesized by irradiation of a HAuCl\-4 solution containing colloidal TiO\-2 with light of wavelength (λ)>330 nm. The absorption maximum attributed to the surface plasmon band of gold was observed at 540 nm, a red shift of about 20 nm from the position in aqueous solution. The Au clusters are situated on the surface of TiO\-2 in terms of microcrystallite, which was confirmed by HRTEM, EDS and XRD. The electronic interfaction between the metal and the suport was discussed.     

LLDPE/TiO2 nanocomposites produced from different crystallite sizes of TiO2 via in situ polymerization

Nano-TiO2 particles with a range of crystallite sizes were synthesized by a conventional sol-gel method,and then used as nanoparticle substrates in the synthesis of LLDPE/TiO2 nanocomposites via in situ polymerization of ethylene/1-hexene with zirconocene/MMAO catalyst.It was found that the size of the nano-TiO2 crystallite nanoparticles can influence the catalytic activity in the polymerization system.The larger nano-TiO2 crystallites provided better catalytic activity in the polymerization system due to more space for monomer attack.In addition,by thermo-gravimetric analysis,it can be seen that the larger nano-TiO2 crystallites also exhibited lower interaction with available MMAO.Consequently,the MMAO reacted more efficiently with the zirconocene catalyst during the activation process,and enhanced polymerization catalysis.All the polymer nanocomposites products did not have well defined melting temperature indicating non-crystalline polymers.This is due to the high amount of hexene incorporation(based on 13C NMR).The difference in crystallite sizes of the nano-TiO2 also affected how 1-hexene became incorporated into the polymer nanocomposites.The smaller crystallite size of nano-TiO2 allowed greater 1-hexene incorporation due to depression of the reactivity of the ethylene.The contribution of this work helps develop a better understanding of the role of nano-TiO2 in the catalytic activity of the polymerization system and in the microstructure of the polymer composite product.However,this study only considers work on the laboratory scale,so for commercial application of these results,it is necessary to scale up the polymerization process.It is only at this stage,that other physical properties,such as the mechanical properties of these materials can be sensibly determined.     

聚吡咯-Fe3O4纳米复合材料的制备与表征及性能

用共沉淀方法制备出平均粒径在10 nm左右的Fe3O4纳米粒子,然后在阳离子表面活性剂的引导下采用原位化学氧化聚合法,合成出聚吡咯-Fe3O4纳米复合材料.同时对此纳米复合材料的结构和性能进行了研究.结果表明Fe3O4纳米粒子和聚吡咯之间存在着一定的相互作用,从而有利于吡咯单体在Fe3O4纳米粒子的表面发生聚合反应,进而Fe3O4纳米粒子被聚吡咯所包覆.聚吡咯/Fe3O4纳米复合材料同时具有导电性和磁性,其导电性随着Fe3O4纳米粒子含量的增加先增大后减小,磁性则始终随着Fe3O4纳米粒子含量的增加而增大.     

水/Span85-Tween60/环己烷微乳液及纳米复合微粒制备

以紫外／可见光分光光度计为检测手段,研究确定了水／Ｓｐａｎ８５－Ｔｗｅｅｎ６０／环己烷反相微乳液体系的适宜条件如乳化剂含量、ＨＬＢ值和溶水量值;进而在其中进行丙烯酰胺（ＡＭ）聚合反应和ＡｇＣ１、ＺｎＳ沉淀反应,制备了ＡｇＣ１／ＰＡＭ、ＺｎＳ／ＰＡＭ纳米复合微粒,并采用航向电镜（ＴＥＭ）观察了给米微粒的形貌。     

电荷稳定分散聚合制备光活性聚苯乙烯微球

采用苯乙烯磺酸钠电荷稳定分散聚合体系,在甲醇/水混合溶剂中,通过后滴加功能单体4-烯丙氧基-2-羟基苯甲酮（BP-OH）,制备出表面带有二苯甲酮光引发基团的聚苯乙烯（PS）微球。研究了功能单体BP-OH的补加时间及总反应时间对微球形貌及功能基团结合量的影响,并将所制备的功能性PS微球在紫外光辐照下引发荧光单体7-甲基丙烯酰氧乙基-4-甲基香豆素（MCMA）反应;并通过场发射扫描电子显微镜（FESEM）、傅里叶变换红外光谱（FT-IR）、紫外可见光谱（UV-Vis）及荧光显微镜（FM）对微球进行测试表征。结果表明,所制备的微球具有光引发活性。     

连续还原法制备Au/Fe3O4纳米复合粒子

采用共沉淀法制备20～40nm的Fe₃O₄颗粒。在Fe₃O₄悬浮液中分别利用柠檬酸钠单独作为还原剂、四羟甲基氯化磷（THPC）和抗坏血酸共同作为还原剂还原HAuCl₄,生成10～90nm的Au纳米颗粒,形成Au/Fe₃O₄复合颗粒。通过透射电子显微镜和紫外分光光度计对Au/Fe₃O₄进行表征,研究还原剂种类对Au/Fe₃O₄粒径、形貌和分散性的影响,结果表明：柠檬酸钠为还原剂时,生成Au纳米颗粒的反应主要在Fe₃O₄纳米颗粒表面进行,Au纳米颗粒的负载量随柠檬酸钠用量增加而减少,粒径在28.08～77.71nm之间;THPC和抗坏血酸共同作为还原剂时,先在Fe₃O₄ 纳米颗粒表面生成THPC-Au,加入抗坏血酸后生成Au纳米颗粒,粒径在71.44～153.2nm之间。