Fe离子掺杂对La0．67Ca0．33Mn1-xFe2O3体系晶体结构、输运性质的影响

采用固相反应法制备了La0．67Ca0．33Mn1-xFe2O3（0≤x≤0．2）系列样品．实验研究了Fe离子掺杂稀土锰氧化物La0．67Ca0．33MnO3的电输运性质、微观结构和导电机制．结果表明：样品高温下导电遵从Mott变程跳跃机制;相同温度下烧结的样品,体系电阻率急剧增加,绝缘-金属转变温度T1M向低温方向移动．相同Fe替代含量的样品,在1200℃、1250℃、1300℃3个不同烧结温度下,晶格常数c变化不大,晶格常数a、b和晶胞体积随着烧结温度的升高而减小,晶体颗粒和体系电阻率随着烧结温度的升高而增大,绝缘一金属转变温度T1M向高温方向移动．     

钐掺杂氧化锌陶瓷的晶体结构和电磁特性

以ZnO,Sm2O3粉体为原料,采用常压固相烧结法,通过优化烧结工艺,制备出平整、组织均匀、致密的Zn1-xSmxO(x=0.01,0.02,0.03,0.04,0.05)陶瓷样品.多晶X射线衍射分析结果表明:当Sm2O3的掺杂量x≥0.04时,过量或堆积的Sm与ZnO结合生成了锌钐尖晶石相ZnSm2O4.特别研究了样品Zn0.97Sm0.03O的表面形貌与成型压力之间的关系和晶粒尺寸、相对密度、电阻率随烧结温度的变化关系.结果表明:成型压力为5 MPa时样品缺陷最少,当烧结温度为1 300℃时,用四探针测试仪测得样品电阻率的最小值为4.78×10-2Ω.cm,用阿基米德排水法测得样品的相对密度超过95%;用振动样品磁强计(VSM)测量陶瓷样品磁化强度与磁场强度之间的关系,表明样品在室温下均呈现顺磁行为.     

ZnO半导体粉体制备工艺与电阻率的关系

采用固相合成法制备了氧化铝掺杂的氧化锌半导体粉体,通过X-射线衍射分析,探讨了掺杂量、煅烧温度和保温时间对粉体导电性能的影响.实验发现:Al2O3的掺杂量高于0.5%(摩尔比)时,会生成ZnAl2O4尖晶石相,降低ZnO的电导率;在一定的温度和保温时间下,才能保证有足够的Al3 进入ZnO的晶格,从而获得电阻率比较低的ZnO半导体粉体;温度过高和保温时间过长都会导致Al2O3与ZnO反应生成尖晶石,减少Al3 对Zn2 的置换率,并对电子产生散射,从而导致ZnO半导体粉体的电阻率升高;当Al2O3掺杂量为ZnO的0.5%(摩尔比)时,在1300℃下保温3h所得到的ZnO粉体的电阻率为18kΩ.cm.     

烧结温度对Co掺杂ZnO稀磁半导体性能的影响

通过溶胶—凝胶法制备了Co掺杂ZnO稀磁半导体纳米颗粒,利用X射线衍射仪、透射电子显微镜和振动样品磁强计等测试手段对Co掺杂ZnO稀磁半导体样品进行了结构和磁性表征.结果表明,随着烧结温度的升高,样品的固溶度逐渐增加.当样品的烧结温度为800℃时,样品为单相的ZnO结构.磁性测试结果表明,Co掺杂ZnO稀磁半导体在室温下具有铁磁性.     

掺杂Fe对SrBi2Nb2O9介电性质的影响

报道了掺杂Fe可使SrBi2Nb2O9介电和铁电性能得以改善而且可降低陶瓷的烧结温度．采用传统的烧结工艺制备了陶瓷样品，XRD和SEM分析表明SBFN仍具有层状钙钛矿结构，掺杂Fe导致SrBi2Nb2O9陶瓷样品的烧结温度降低约100℃．居里温度从406℃升高到453℃，并且介电常数在居里温度下从1150升高到1409．居里温度和居里温度下介电常数提高都表明自发极化增强，该现象归因于较小Fe^3 掺杂扩大了正离子的“rattling空间”．     

Fe离子掺杂对La_(0.67)Ca_(0.33)Mn_(1-x)Fe_xO_3体系晶体结构、输运性质的影响

采用固相反应法制备了La0.67Ca0.33Mn1-xFexO3(0 x 0.2)系列样品.实验研究了Fe离子掺杂稀土锰氧化物La0.67Ca0.33MnO3的电输运性质、微观结构和导电机制.结果表明:样品高温下导电遵从Mott变程跳跃机制;相同温度下烧结的样品,体系电阻率急剧增加,绝缘—金属转变温度TIM向低温方向移动.相同Fe替代含量的样品,在1200℃、1250℃、1300℃3个不同烧结温度下,晶格常数c变化不大,晶格常数a、b和晶胞体积随着烧结温度的升高而减小,晶体颗粒和体系电阻率随着烧结温度的升高而增大,绝缘—金属转变温度TIM向高温方向移动.     

高能球磨法制备Mg_4Nb_2O_9微波介质陶瓷及其表征

采用高能球磨法制备粉体.粉体球磨60 h后在900℃保温3 h预烧合成Mg4Nb2O9纯相,研究了由高能球磨所得粉体制备的Mg4Nb2O9陶瓷的相结构、显微组织和微波介电性能随烧结温度的变化关系.X射线衍射检测Mg4Nb2O9陶瓷在1 150～1 200℃烧结过程中有微量的MgNb2O6和Mg5Nb4O15杂相产生,烧结温度高于1 200℃时,样品为Mg4Nb20g纯相;样品收缩率和密度随烧结温度的增大而增加,在1 200℃趋于饱和,分别为13.6和4.22 g/cm3(相对密度96.42%);样品的气孔含量随烧结温度增大降低,晶粒尺寸随烧结温度增大而增大,介电常数和品质因数随烧结温度的增大而增加;1 200℃烧结的样品具有高的致密度、清晰的显微组织,平均晶粒尺寸为3.5 μm,微波介电性能εr=12.6,Q·f=133164 GHz,τ=-56.69×10-6/℃.实验结果表明.高能球磨有效促进球磨后粉体在900℃低温合成Mg4Nb2O9纯相;并降低Mg4Nb2O9陶瓷的烧结温度到1 200℃,改善了陶瓷的谐振频率温度系数,有望成为新一代中温烧结微波介质材料.     

Nb~(5+)的低温掺杂对La_(0.67)Sr_(0.33)MnO_3结构、磁性和电性的影响

将Nb2O5掺杂到用溶胶一凝胶法制备的La0.67>Sr0.33MnO3(LSMO)微粉中,XRD结果表明:随掺杂量的增多,样品中出现相分离,其一为具有菱方结构的钙钛矿材料,另一相为LaNbO4.随Nb掺入量的增多,TP单调下降而Tc没有明显变化,说明低温烧结减弱了B位替代效应.在x=0.07的样品中得到最大电阻率为23.7 Ωcm,比LSMO高三个数量级,这主要是尺寸效应所决定.     

Al_2O_3掺杂ZnO线性电阻的性能及其显微组织

通过高能球磨法,分别在1 250,1 300,1 350℃下制备了掺杂量为3.5%,4.0%,4.5%,5.0%的Al2O3掺ZnO线性电阻,通过扫描电镜和X射线衍射对其显微组织和相成分进行了分析,探讨了不同Al2O3掺杂量和不同烧结温度对ZnO线性电阻的线性性能和介电性能的影响.结果表明:掺杂A12O3的ZnO线性电阻主晶相为ZnO,并伴随有少量锌尖晶石相生成.在烧结温度为1 350℃,Al2O3掺杂摩尔分数为3.5%时,线性电阻性能最优,其非线性系数为1.00.另外,随A12O3掺杂量增大,ZnO线性电阻的介电常数变化不大,而烧结温度对陶瓷的介电常数有较为明显的影响.     

V2O5和Li2CO3共掺杂对Mg4Nb2O9陶瓷烧结行为及微波介电性能的影响

采用固相法，制备了Mg4Nb2O9（MN）微波介质陶瓷，研究了V2O5和Li2CO3共掺杂对MgaNb2O9陶瓷烧结行为、相结构、显微结构和微波介电性能的影响．结果表明，采用1．5％V2O5和1．5％Li2CO3共掺杂，能够将Mg4Nb2O9（135O℃）陶瓷的烧结温度降至925℃，且有助于Mg4Nb2O9单相的形成．3．0％（V2O5，Li2CO3）共掺杂样品在925℃空气中烧结5h可获得良好的微波介电性能（介电常数为13．7，品质因数为77975GHz）．     

ZnO和Nb2O5共掺杂钛酸锶钡陶瓷的结构及其介电性能研究

采用固相反应法制备了ZnO、Nb 2 O 5共掺杂Ba 0.2 Sr 0.8 TiO 3陶瓷材料,并用X射线衍射（XRD）和介电谱方法,分别对系列陶瓷样品的结构和复介电常数进行了测量.结果表明：1）Zn2＋、Nb5＋进入Ba 0.2 Sr 0.8 TiO 3晶格后仍然为钙钛矿型固溶体;2）Nb 2 O 5会使得材料的低温弥散相变过程转变为弛豫相变过程,并在300～360K区域内会出现新的弛豫过程;3）掺入一定量的ZnO后Nb2O5掺入降低了Ba 0.2 Sr 0.8 TiO 3陶瓷材料的介电常数,增大了其介电损耗.     

高介、低损耗Ba(Ti,Zr)O_3基电容器陶瓷的研究

采用正交设计实验法研究了配方对Ba(Ti,Zr)O3(BTZ)基电容器陶瓷介电性能的影响 ,得到了影响BTZ基陶瓷介电性能的主次因素 ,各因素水平影响其性能的趋势 对介电常数而言 ,主次影响因素的顺序为Nb2 O5、BaZrO3/BaTiO3、ZnO、CeO2 ;对介质损耗而言 ,主次影响因素的顺序为Nb2 O5、ZnO、CeO2 、BaZrO3/BaTiO3 同时得到了介电常数最大的配方和介质损耗最小的配方 通过正交设计实验得到了综合性能最佳的BTZ基陶瓷 ,它具有高介 (ε)≥1 32 0 0低损耗 (tanδ) <60× 1 0 - 4 和高耐压 (大于 5MV/m) 探讨了各组分对BTZ基陶瓷介电性能影响机理 ,为研制高介、低损耗、高耐压电容器陶瓷提供依据     

The development of Bi Fe O3-based ceramics

The multiferroic properties of Bi Fe O3-based ceramics were improved through optimizing their sintering method and doping with certain rare earth elements in pure Bi Fe O3. Some methods, especially liquid-phase sintering method has largely decreased the densities of oxygen vacancies and Fe2in Bi Fe O3-based ceramics, and thus their resistivity became high enough to measure the saturated polarization and the large piezoelectric d33 coefficient under the high electric field of [150 k V/cm. Besides,multiferroic properties were improved through the rare earth elements’ doping in pure Bi Fe O3. Magnetization commonly increases with the proportional increase of Nd,La, Sm and Dy contents up to ＊30 %, while ferroelectric phase can transform to paraelectric phase at a certain proportion. An improved magnetoelectric coupling was often observed at ferroelectric phase with a relatively large proportion. Besides, an enhanced piezoelectric coefficient is expected in Bi Fe O3-based ceramics with morphotropic phase boundaries as they are already observed in thin epitaxial Bi Fe O3 films.     

烧结温度对PSBN铁电陶瓷介电性能的影响

用普通的电子陶瓷工艺制备了ＰｂＯ－ＳｒＯ－ＢａＯ－Ｎｂ２Ｏ５（ＰＳＢＮ）系统民陶瓷，研究了ＰＳＢＮ系统铁电陶瓷的介电性能与烧结温度的关系，ＸＲＤ分析表明：ＰＳＢＮ系统铁电陶瓷的主晶相是Ｐｂ０．７Ｂａ０．３Ｎｂ２Ｏ６（ＰＢＮ）、Ｓｒ０．５Ｂａ０．５Ｎｂ２Ｏ６（ＳＢＮ）和Ｂａ０．２７Ｓｒ０．７５Ｎｂ２Ｏ５．７８（ＢＳＮ），将这一复杂的化学系统看作三元系固熔体，其中ＰＢＮ、ＳＢＮ和ＢＳＮ各相比例随烧结温     

添加BaO-B2O3-SiO2玻璃对Sr0.3BaO0.7Nb2O6陶瓷烧结和介电性能的影响

以分析纯的BaCO3,SrCO3,Nb2O5,H38O3和SiO2粉末为原料,采用传统的固相合成法制备添加50BaO-4082O3-10SiO2玻璃(物质的量比)的Sro.3Ba0.7Nb2O6(即SBN70)陶瓷.采用X线衍射仪(XRD)、扫描电子显微镜(SEM)和阻抗分析仪研究添加玻璃对SBN70陶瓷的烧结和介电性能的影响.研究结果表明;随着玻璃含量的增加,陶瓷样品的相对密度先增大后减小;当玻璃含量为5%(质量分数,下同)时,样品的密度达到最大值;添加玻璃降低了陶瓷的烧结温度,于1 250℃时添加5%玻璃的SBN70陶瓷已烧结致密,陶瓷的平均晶粒尺寸约2 μm,晶粒呈短柱状结构;当玻璃含量增大时,晶粒尺寸呈增大趋势;当玻璃添加量≤5%时,样品仍为单相四方钨青铜结构;当含量为10%时,出现了第二相SrB4O7;随着玻璃含量的增加,SBN70衍射峰的位置先移向低角度后移向高角度,而居里温度T0逐渐降低,从195℃下降到25℃左右;随玻璃含量的增加,最大介电常数εmax呈先减小后增大的变化趋势,而介电损耗tan δ则随玻璃含量的增大而减小;添加玻璃的SBN70陶瓷具有弥散相变特性,其弥散系数γ随添加玻璃含量的增加而增大.     

BaCu(B2O5)的合成及其对CLST陶瓷烧结性能的影响

分别采用固相反应法和共沉淀结合固相反应法合成了BaCu(B2O5)粉体,并研究了所合成BaCu(B2O5)粉体对CLST陶瓷的烧结性能的影响规律.结果表明:以BaO、CuO和B2O3为原料,BaO和B2O3先反应生成BaB2O4,进一步与CuO反应生成BaCu(B2O5).适当延长煅烧时间,有利于BaCu(B2O5)的...     

Ca(Sm0.5Nb0.5)O3介质陶瓷的微波烧结

通过改变微波烧结温度和保温时间,优化Ca( Sm0.5 Nb0.5) O3 (CSN)陶瓷的微波烧结工艺,用X线衍射仪(XRD)、扫描电镜(SEM)和微波网络分析仪等对试样进行表征.从相组成、显微结构及微波介电性能等方面对微波烧结试样与常规烧结试样进行对比分析.结果表明:微波烧结可大幅降低CSN的烧结温度,促进试样的致密化,其物相组成和传统烧结试样无明显差别;微波烧结还可以改善CSN陶瓷的微波介电性能,在1 375℃微波烧结30 min可获得优异的微波介电性能,介电常数(εr)=20.08,品质因数(Q×f)=37.03 THz,谐振频率温度系数(Tf)=-10.2×10-6℃-1.     

ZnO压敏陶瓷次晶界及其对陶瓷性能的作用

研究了在烧结过程中，烧结温度与等温烧结时间对ＺｎＯ晶粒中次晶界的影响及次晶界对ＺｎＯ压敏陶瓷电性能的作用，结果发现随烧结温度升高、等温烧结时间延长，次晶界趋于消失，次晶界的存在将增大ＺｎＯ晶粒的电阻率、削弱ＺｎＯ压敏陶瓷的脉冲能量吸收能力。     

单斜相SrAl2Si2O8陶瓷的烧结及其对Sr的固化

Monoclinic SrAl₂Si₂O₈ ceramics for Sr immobilization were prepared by a liquid-phase sintering method. The sintering temperature, mineral phase composition, microstructure, flexural strength, bulk density, and Sr ion leaching characteristics of the SrAl₂Si₂O₈ ceramics were investigated. A crystalline monoclinic SrAl₂Si₂O₈ phase formed through liquid-phase sintering at 1223 K. The introduction of four flux agents (B₂O₃, CaO·2B₂O₃, SrO·2B₂O₃, and BaO·2B₂O₃) to the SrAl₂Si₂O₈ ceramics not only reduced the densification temperature and decreased the volatilization of Sr during high-temperature sintering but also impacted the mechanical properties of the ceramics. Product consistency tests showed that the leaching concentration of Sr ions in the sample with flux agent B₂O₃ was the lowest, whereas that of Sr ions in the sample with flux agent BaO·2B₂O₃ was the highest. These results show that the leaching concentration of Sr ions depends largely on the amorphous phase in the ceramics. Meanwhile, the formation of mineral analog ceramics containing Sr is an important factor to improve Sr immobilization.     

织构化Sr_(0.4)Ba_(0.6)Nb_2O_6陶瓷的工艺研究

以熔盐法合成的各向异性的棒状铌酸锶钡陶瓷粉体为模板粉体,采用流延成型工艺,制备出织构化的铌酸锶钡陶瓷,研究了模板添加量及烧结温度与织构化陶瓷微观组织结构间的关系。实验结果表明:使用流延成型工艺可以制备晶粒定向排列的铌酸锶钡陶瓷,随着模板添加量的增加,陶瓷的织构化程度变大。在本实验的条件下,在1375℃烧结3h,模板加入量为30%时,铌酸锶钡陶瓷的织构化程度达到57%。