316L不锈钢扩散焊接工艺与接头性能的研究

针对不同焊接工艺参数的316L不锈钢扩散焊接头,进行了室温和 550℃短时拉伸强度试验,采用金相、XRD分析接头区域的微观结构和相组成。实验结果表明：随着保温时间的延长,接头焊合率和延伸率逐渐提高;接头强度随焊接温度的提高呈“V”字形变化。接头高温强度约为常温强度的 50%,在评价扩散焊接质量时,应将接头强度与经过相同扩散焊接工艺处理的母材强度相比较。     

超高强度钢焊接接头断裂行为预测

测试了D406A钢母材和热影响区表面裂纹断裂韧度,比较了母材与热影响区断裂韧度概率分布,分析了非匹配对接头断裂韧性的影响.根据局部法由母材表面裂纹试样的断裂韧度值,得出威布尔形状参数和尺度参数,再根据该参量对热影响区表面裂纹试样的断裂行为进行了定量预测,预测结果与试验结果吻合很好,表明局部法能很好地描述超高强度钢焊接接头的断裂行为.     

数控机床故障分析与可靠性评价技术的研究

针对传统数控机床可靠性建模时只考虑故障间隔时间而忽略故障性质的现象，提出兼顾机械故障和电气故障的混合威布尔分布模型，进而提高模型准确度.利用最大似然法来确定混合威布尔分布模型参数，用皮尔逊相关系数来确定数控机床各故障时间之间的关系.并通过K-S方法对模型进行检验， 最后确定其符合混合威布尔分布，并运用可靠性评定方法得出数控机床的平均无故障时间.     

AISI304/低碳钢真空扩散焊接头组织和性能

采用真空扩散焊接方法连接AISI304奥氏体不锈钢和低碳钢异种材料.在焊接温度和焊接压力恒定的条件下,研究焊接时间对ASTM304/低碳钢异种材料扩散焊接头组织和性能的影响.研究结果表明:在焊接温度850℃,焊接压力10 MPa,焊接时间60 min条件下AISI304奥氏体不锈钢/低碳钢异种材料实现了良好的扩散结合,其强度和韧性均超过低碳钢母材水平.接头抗拉强度达到440 MPa,拉伸断裂发生在低碳钢一侧.在扩散焊高温环境下,界面附近有碳化物偏析现象,析出相为脆硬的Cr23C6,脆硬相的出现导致界面韧性下降,延长焊接时间可有效避免有害化合物Cr23C6的析出,冲击韧性达到120.5 J/cm2,冲击断口在低碳钢一侧.     

异种钢焊接接头高温力学性能的研究

为提高电站锅炉过热器铁素体－奥氏体异种钢焊接接头的高温蠕变断裂强度和延长服役寿命，设计了用专用镍基填充材料焊接的不锈钢－镍基焊缝－耐热钢三元组合接头。通过对不同焊缝接头的高温持久性能试验及用ＳＥＭ和ＥＰＭＡ对焊缝界面组织变化的对比分析，认为在高温低应力条件下接头早期失效的主要原因是熔合区及热影响区碳、铬等元素迁移和碳化物聚集所引起的蠕变断裂。组合接头的设计方案对改善接头应力分布，阻碍碳扩散和提高接头蠕变强度具有显著效果     

多个威布尔分布形状参数的检验

一、引言在第二类型截尾样本的情况下,[1]文对于多个威布尔分布总体的形状参数的检验,提出了一个仅依赖于形状参数的极大似然估计的统计量,并用Monte-Carlor方法给出了统计量分布的分位点值。由于威布尔分布参数的极大似然估计,一般需要用电子计算机来计算,所以使用时有一定的困难。本文用极值分布参数的最好线性无偏估计来获得威布尔分布参数的估计量(参考[2]),并据此构造出适当的统计量     

威布尔分布参数的精确确定方法

本指出了现行确定威布尔分布参数方法的缺陷；说明了精神确定威布尔分布参数的方法和一组数据服从其分布的条件，并可用于求所有能直线化的三参数问题。     

高温水环境下温度对316 L不锈钢应力腐蚀开裂的影响

在高温水环境中,采用慢应变速率拉伸实验方法研究了温度对316 L不锈钢应力腐蚀开裂的影响规律,并通过扫描电镜(SEM)对试样断口形貌进行分析. 结果表明:在高温水环境中,温度为200～345 ℃时316 L不锈钢具有应力腐蚀开裂敏感性;材料脆性指标随温度升高而增大,应力腐蚀开裂敏感性增强,断口分析与之吻合;250 ℃是316 L不锈钢发生应力腐蚀开裂的敏感温度,断口边缘形貌呈现明显脆性断裂特征.     

失效率局部成比例的伽玛分布和威布尔分布顺序统计量的随机比较

在独立情形下伽玛分布和威布尔分布顺序统计量的随机比较基础上,给出了随机变量以一般随机序局部大于和局部依序列条件递增的概念.讨论失效率函数局部成比例这种非独立条件下的伽玛分布和威布尔分布的顺序统计量的随机比较,得出当形状参数不变、尺度参数占优条件下二元最小顺序统计量的随机关系.此外,基于这种情形,得出威布尔分布顺序统计量是局部依序列条件递增的.     

寿命分布检验和参数估计的线性回归法及微机实现

本文介绍了一种用线性回归原理来检验产品寿命分布类型和估计特征量的方法及其自动实现寿命试验数据处理的通用计算机程序。此程序所涉及的分布函数有指数分布、双参数威布尔分布、三参数威布尔分布、正态分布、对数正态分布等五种,并具有自动判别最佳分布的功能。     

新的非比例加载低周疲劳寿命估算方法

利用对 316L不锈钢多轴非比例加载低周疲劳的试验结果 ,对现有的多轴低周疲劳寿命估算方法进行了讨论 ,基于 316L不锈钢非比例加载低周疲劳的微观机理 ,选择最大剪应变以及应变路径的非比例度作为损伤参量 ,建立了基于临界面方法的新的非比例加载低周疲劳寿命估算公式 ,利用新的非比例加载低周疲劳寿命估算公式对寿命的预测结果表明 :新的寿命估算公式对剪切型破坏的 316L与 316LN不锈钢及拉伸型破坏的 30 4不锈钢非比例加载低周疲劳寿命预言能力比现有的临界面方法精确 .     

AISI316L奥氏体不锈钢在摸拟人体组织液中腐蚀疲劳裂纹萌生的初步研究

AISI316L奥氏体不锈钢是较常用的金属植入材料之一.但在临床应用中,由它制成的植入物特别是全髋关节,常因腐蚀疲劳破断而失效.本文对316L不锈钢在Hank’s溶液中的腐蚀疲劳裂纹萌生机理进行了初步研究.结果发现,在Hank’s溶液中,自然钝化的316L不锈钢在稳定钝化态下,裂纹的萌生是由交变应力引起的微观塑性变形和Hank’s溶液交互作用的结果;在有点蚀产生的非钝化态下,裂纹的萌生是点蚀和腐蚀疲劳相叠加的结果.316L不锈钢经离子氮化表面处理后,提高了在Hank’s溶液中的抗点蚀能力,但在外加腐蚀电位的苛刻条件下,困氮化层发生晶间腐蚀和脱落而加速了裂纹的萌生     

Production of 316L stainless steel implant materials by powder metallurgy and investigation of their wear properties

In this study,the mechanical and wear properties of AISI 316L stainless steel implant materials,produced by powder metallurgy(P/M),were investigated.AISI 316L stainless steel powder was cold-pressed with 800 MPa of pressure and then sintered at 1200,1250 and 1300°C for 30 min as three sample groups.The microstructure,and mechanical and wear properties of the resulting steels were investigated.Light optical and scanning electron microscopiese were used to characterize the microstructure of the steels.Room temperature mechanical properties of the steels were determined by hardness measurements and impact tests.Wear was determined using the pin-on-disc wear test,and the results were evaluated according to weight loss.The results indicate that the sintering temperature,time and atmosphere are important parameters that affect the porous ratio of materials produced by P/M.Sintering at high temperature can eliminate small pores and make the residual pores spherical.The wear tests showed that the wear of the AISI 316L stainless steel implants changed depending on the sintering temperature and load.Spherical pores in the samples increase the wear resistance.Moreover,decreasing the porosity ratio of these materials improves all of their mechanical properties.     

Microstructures and mechanical properties of dissimilar Nd:YAG laser weldments of AISI4340 and AISI316L steels

This paper presents studies on the microstructure and mechanical properties of AISI 316L stainless steel and AISI 4340 low-alloy steel joints formed by the Nd:YAG laser welding process. The weld microstructures and heat affected zones (HAZs) were investigated. Austenitic microstructures were observed in all of the samples. The sizes of the HAZs changed when the heat input was varied, and the 316L sides exhibited a larger HAZ. The cooling rates were calculated by measuring the solidification dendrite arm spacing. It is shown that high cooling rates lead to an austenitic microstructure. Tensile tests were carried out, and the results revealed the tensile properties of both the base metals and the weldments. The hardness test results agreed well with the tensile test results.     

液固流动相中不锈钢耐颗粒冲刷腐蚀性能研究

采用自制的旋转冲刷腐蚀失重装置，研究了湿法磷酸中固体颗粒的性质，如固含量，粒径等环境参数对不锈钢316L和904L冲刷腐蚀速率的影响，并在扫描电镜下观察了不锈钢腐蚀的形貌，试验结果表明，CaSO4结晶颗粒固含量质量分数由10％增加到50％时，冲刷腐蚀速率有所增大，316L不锈钢主要以腐蚀为主，且表现为晶间腐蚀，当浆体中含有SiO2固体颗粒时，液相腐蚀性得到降低，虽然不锈钢904L耐液相腐蚀性能优良，但耐冲刷（磨损）性能较差，尤其当SiO2粒径增大时，冲刷腐蚀速率明显增大。     

316L不锈钢应力腐蚀研究进展

316L不锈钢具备良好的力学性能、焊接性能、耐蚀性能，被广泛应用于化工管道、船舶及核电等领域。因其应用环境复杂，316L不锈钢在特定介质环境和拉应力的协同作用下，易发生应力腐蚀开裂，导致严重事故。概述了316L不锈钢应力腐蚀裂纹萌生及扩展的规律，总结了其应力腐蚀的阳极溶解和氢致开裂两种微观主导机制的特点。在此基础上，针对介质环境、材料、表面应力状态3个影响因素，综述了近年来通过调节介质环境的pH、溶液浓度、引入压应力、优化微观结构及涂层工艺等方面，改善316L不锈钢应力腐蚀性能的研究进展。最后，基于316L不锈钢面临的应力腐蚀问题，从应力腐蚀机制和防护措施两方面展望了316L不锈钢应力腐蚀的研究热点和方向。     

316L和316LN不锈钢在高温高盐溶液中钝化膜的性能研究

利用电化学及扫描电子显微镜（SEM）对316L与316LN两种不锈钢在高温高盐环境中的耐蚀性能进行了对比研究,利用Mott-Schottky曲线研究了两种材料的钝化膜半导体特征,借助X射线光电子能谱（XPS）研究了316LN不锈钢的钝化膜结构以及N元素在钝化膜中的分布状态。结果表明：在高温高盐环境中,两种材料形成的钝化膜都为n型半导体;316LN不锈钢形成的钝化膜耐点蚀性能更好,其钝化膜内缺陷浓度更低,N元素会在钝化膜中富集。最后利用点缺陷原理对316LN钝化膜的耐蚀机理进行了研究。     

醋酸介质中T-403塔不锈钢填料腐蚀机理研究

某化工厂PTA装置氧化单元系统中铁离子含量增高，已影响到氧化反应效果，严重威胁稳定生产，分析认为铁离子主要来自T-403溶剂回收塔316L不锈钢填料的腐蚀．利用扫描电镜、电子探针、金相显微镜等现代物理和化学分析检测手段，观察了从T-403塔取出填料的微观形貌，测试分析了所用填料的主要化学成分及元素分布，对比了未使用和已腐蚀填料的金相显微结构、力学性能变化，研究分析了不锈钢填料的腐蚀机理．实验结果表明：不锈钢填料发生了严重的局部腐蚀，腐蚀形态为晶间腐蚀和小孔腐蚀．填料发生腐蚀后，强度和硬度明显降低．测试分析结果证明，贫铬导致晶间腐蚀，Br以及不锈钢钝化膜局部破损造成蚀孔．原填料质量存在问题，不锈钢填料的含碳量未达到超低碳316L不锈钢的标准．     

Properties of passive film formed on 316L/2205 stainless steel by Mott-Schottky theory and constant current polarization method

Semiconductor properties of the passive films formed on 316L and 2205 stainless steel were studied by Electrochemical Impedance Spectroscopy(EIS) in the high-temperature acetic acid.The results showed that the corrosion resistance of 2205 was higher than that of 316L,and the passive films formed on 316L and 2205 stainless steel showed p-type and n-type semiconductor behavior,respectively.Destruction and self-repairing of passive films were studied by using the constant current polarization method.The result...     

渗钛合金层对316L不锈钢晶间腐蚀性能的影响

采用等离子表面合金化技术在316L不锈钢表面进行渗钛处理,对渗层的结构及其晶间腐蚀性能进行了分析,结果表明,在温度为1000℃、保温时间为3.5h的渗钛条件下形成了表面改性合金层。在不锈钢10%草酸浸蚀试验中,316L不锈钢基体呈现七类凹坑组织Ⅱ晶间腐蚀;而渗钛合金层几乎没有发生晶间腐蚀,显著提高了316L不锈钢的耐晶间腐蚀性能。