Effects of sphere size on the microstructure and mechanical properties of ductile iron–steel hollow sphere syntactic foams

The effects of sphere size on the microstructural and mechanical properties of ductile iron–steel hollow sphere (DI–SHS) syntactic foams were investigated in this study. The SHSs were manufactured by fluidized-bed coating via the Fe-based commercial powder–binder suspension onto expanded polystyrene spheres (EPSs). Afterwards, the DI–SHS syntactic foams were produced via a sand-mold casting process. The microstructures of specimens were investigated by optical microscopy, scanning electron microscopy (SEM), and energy- dispersive X-ray spectroscopy (EDS). The microscopic evaluations of specimens reveal distinct regions composed of the DI matrix, SHS shells, and compatible interface. As a result, the microstructures and graphite morphologies of the DI matrix depend on sphere size. When the sphere size decreases, the area fractions of cementite and graphite phases are observed to increase and decrease, respectively. Compression tests were subsequently conducted at ambient temperature on the DI–SHS syntactic foams. The results reveal that the compression behavior of the syntactic foams is enhanced with increasing sphere size. Furthermore, the compressed specimens demonstrate that microcracks start and grow from the interface region.     

Fabrication of Fe–TiC–Al2O3 composites on the surface of steel using a TiO2–Al–C–Fe combustion reaction induced by gas tungsten arc cladding

The aim of the present study was to fabricate Fe–TiC–Al₂O₃ composites on the surface of medium carbon steel. For this purpose, TiO₂–3C and 3TiO₂–4Al–3C–xFe (0 ≤ x ≤ 4.6 by mole) mixtures were pre-placed on the surface of a medium carbon steel plate. The mixtures and substrate were then melted using a gas tungsten arc cladding process. The results show that the martensite forms in the layer produced by the TiO₂–3C mixture. However, ferrite–Fe₃C–TiC phases are the main phases in the microstructure of the clad layer produced by the 3TiO₂–4Al–3C mixture. The addition of Fe to the TiO₂–4Al–3C reactants with the content from 0 to 20wt% increases the volume fraction of particles, and a composite containing approximately 9vol% TiC and Al₂O₃ particles forms. This composite substantially improves the substrate hardness. The mechanism by which Fe particles enhance the TiC + Al₂O₃ volume fraction in the composite is determined.     

Synthesis and characterization of carbon-coated cobalt ferrite nanoparticles

Cobalt ferrite nanoparticles (CFNPs) were prepared via a reverse micelle method. The CFNPs were subsequently coated with carbon shells by means of thermal chemical vapor deposition (TCVD). In this process, acetylene gas (C₂H₂) was used as a carbon source and the coating was carried out for 1, 2, or 3 h at 750°C. The Ar/C₂H₂ ratio was 10:1. Heating during the TCVD process resulted in a NP core size that approached 30 nm; the thickness of the shell was less than 10 nm. The composition, structure, and morphology of the fabricated composites were characterized using X-ray diffraction, simultaneous thermal analysis, transmission electron microscopy, high-resolution transmission electron microscopy, and selected-area diffraction. A vibrating sample magnetometer was used to survey the samples’ magnetic properties. The deposited carbon shell substantially affected the growth and magnetic properties of the CFNPs. Micro-Raman spectroscopy was used to study the carbon coating and revealed that the deposited carbon comprised graphite, multiwalled carbon nanotubes, and diamond- like carbon. With an increase in coating time, the intensity ratio between the amorphous and ordered peaks in the Raman spectra decreased, which indicated an increase in crystallite size.     

Experimental investigation and adaptive neural fuzzy inference system prediction of copper recovery from flotation tailings by acid leaching in a batch agitated tank

The potential of copper recovery from flotation tailings was experimentally investigated using a laboratory-mixing tank. The experiments were performed with solid weight percentages of 30 wt%, 35 wt%, 40 wt% and 45 wt% in water. The measurements revealed that adding sulfuric acid all at once to the tank rapidly increased the efficiency of the leaching process, which was attributed to the rapid change in the acid concentration. The rate of iron dissolution from tailings was less than when the acid was added gradually. The sample with 40 wt% solid is recommended as an appropriate feed for the recovery of copper. The adaptive neural fuzzy system(ANFIS) was also used to predict the copper recovery from flotation tailings. The back-propagation algorithm and least squares method were applied for the training of ANFIS. The validation data was also applied to evaluate the performance of these models. Simulation results revealed that the testing results from these models were in good agreement with the experimental data.     

Mechanochemical leaching of chalcopyrite concentrate by sulfuric acid

This study aimed to introduce a new cost-effective methodology for increasing the leaching efficiency of chalcopyrite concentrates at ambient temperature and pressure. Mechanical activation was employed during the leaching (mechanochemical leaching) of chalcopyrite concentrates in a sulfuric acid medium at room temperature and atmospheric pressure. High energy ball milling process was used during the leaching to provide the mechanochemical leaching condition, and atomic absorption spectroscopy and cyclic voltammetry were used to determine the leaching behavior of chalcopyrite. Moreover, X-ray diffraction and scanning electron microscopy were used to characterize the chalcopyrite powder before and after leaching. The results demonstrated that mechanochemical leaching was effective; the extraction of copper increased significantly and continuously. Although the leaching efficiency of chalcopyrite was very low at ambient temperature, the percentages of copper dissolved in the presence of hydrogen peroxide (H₂O₂) and ferric sulfate (Fe₂(SO₄)₃) after 20 h of mechanochemical leaching reached 28% and 33%, respectively. Given the efficiency of the developed method and the facts that it does not require the use of an autoclave and can be conducted at room temperature and atmospheric pressure, it represents an economical and easy-to-use method for the leaching industry.     

Effects of copper content on the shell characteristics of hollow steel spheres manufactured using an advanced powder metallurgy technique

Metallic hollow spheres are used as base materials in the manufacture of hollow sphere structures and metallic foams. In this study, steel hollow spheres were successfully manufactured using an advanced powder metallurgy technique. The spheres’ shells were characterized by optical microscopy in conjunction with microstructural image analysis software, scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and X-ray diffraction (XRD). The microscopic evaluations revealed that the shells consist of sintered iron powder, sintered copper powder, sodium silicate, and porosity regions. In addition, the effects of copper content on various parameters such as shell defects, microcracks, thickness, and porosities were investigated. The results indicated that increasing the copper content results in decreases in the surface fraction of shell porosities and the number of microcracks and an increase in shell thickness.