K_(0.5)Na_(0.5)NbO_3纳米管阵列的制备及其电学性能研究

以乙醇铌、乙酸钾和乙酸钠为原料,乙二醇甲醚为溶剂,采用溶胶-凝胶(Sol-Gel)氧化铝(AAO)模板法制备K0.5Na0.5NbO3(KNN)纳米管阵列,并采用X射线衍射、扫描电子显微镜和透射电子显微镜表征KNN纳米管的物相、形貌和微观结构.研究表明,在700℃退火处理可获得结晶性较好,具有单斜钙钛矿结构的KNN多晶纳米管阵列.单根纳米管的外径约为200 nm,管壁厚约为20 nm.采用压电力显微镜(PFM)对单根KNN纳米管的压电性能进行表征,结果显示所制备的KNN纳米管具有明显的压电性能.     

TiO2纳米管的水热法合成研究

采用水热法合成了外径约为15 nm、壁厚约为1 nm的TiO2纳米管.通过采用TEM,XRD,TG-DSC等分析手段,对在不同工艺条件下获得的产物进行了表征,并对其光催化活性进行评价.研究结果表明,反应时间和反应温度对样品的结构和光催化活性有较大影响;TiO2纳米管的形成机理可能是氧化钛颗粒在强碱的作用下形成具有层状结构的碱金属钛盐,随着反应的进行逐渐卷曲而形成纳米管,这种自发的卷曲可能是由于弹性形变等多种因素的共同作用下以降低能量使其结构更稳定所致.经过酸处理以后可以得到含有H2TiO3组分的纳米管,该纳米管在300℃热处理后,H2TiO3受热分解转化为锐钛矿型的TiO2.     

电子束诱导原位制备银纳米环

本文报道了一种电子束诱导原位制备银纳米环的有效方法.使用溶胶-凝胶的方法,以分散Ag+的二氧化钛溶胶为前驱体,通过浸渍-提拉法和相应的热处理工艺制备出二氧化钛和银的复合薄膜.以扫描电镜聚焦的电子束为辐射源,在Ag/TiO2的复合薄膜表面原位观察到了银纳米环的形成过程.纳米环内径为100~280 nm,外径为120~300 nm.     

在AAO模板上用溶胶—凝胶法制备TiO_2纳米管阵列

用二次阳极氧化法在草酸电解液中制备出有序多孔阳极氧化铝(AAO)模板,采用溶胶-凝胶法在负压辅助条件下用钛酸四丁脂Ti(OC_4H_9)_4为TiO_2前驱体溶胶浸渍AAO模板,450℃下热处理制备长度和孔径可控的TiO_2纳米管的阵列结构.剥离去除模板后,用FE-SEM、XRD对产物形貌、晶型进行表征和分析.结果表明,制备的TiO_2纳米管长约3μm,外径130 nm,内径100 nm,与AAO模板的孔径相当,且单根TiO_2纳米管分散性较好,管与管之间无团聚,说明负压辅助可提高TiO_2纳米管的连续性.XRD分析显示,TiO_2纳米管呈锐钛矿相晶型.     

Bi3．15Nd0．85Ti3O12纳米管阵列的制备与微结构表征

采用溶胶-凝胶法,在孔径为100nm的阳极氧化铝模板中制备了Bi3．15Nd0．85Ti3O12（BN（IT）纳米管阵列．通过XRD、SEM、TEM、HRTEM、SAED和Raman光谱测试手段对纳米管阵列的物相、微结构和声子振动特性进行了表征．研究表明,所合成BNdT纳米管为钙钛矿相多晶结构,纳米管外径约为100nm,管壁厚约10nm,长度达几个微米．Raman光谱分析表明,Nd离子部分取代了类钙钛矿层中A位的Bi离子．     

水杨酸掺杂聚苯胺纳米管的合成机理及表征

采用化学氧化法制备水杨酸掺杂聚苯胺纳米管,获得约15℃下制备聚苯胺纳米管的反应条件.表征产物的结构与性能,并讨论聚苯胺纳米管的形成机制.结果表明:当水杨酸与苯胺物质的量比为0.06时,合成了管长大于1μm,外径约150nm,内径约为30nm的圆型孔腔聚苯胺纳米管.随着水杨酸和苯胺物质的量比减少,产物由一维结构的纳米纤维和纳米管向二维结构的纳米片转变,这种转变可归因于反应体系中水杨酸与苯胺盐在水溶液中形成球型胶束的能力.该聚苯胺纳米管室温下电导率为8.66×10-2 S/cm,并显示出良好的电化学活性.     

纳米管阵列光催化降解TVOC的速率数学模型

基于菲克定律和质量守恒原理,建立了TVOC分子在纳米管内的质量传递方程,推导出了纳米管阵列(TNAs)的TVOC降解速率数学模型,模型表明:随着管长的增加,降解速率增加;存在最佳管径使降解速率达到最大.采用管径为60 nm、75 nm、90 nm,管长为1.1μm和2.3μm的TiO2纳米管,对初始浓度约为10 mg/m3的TVOC气体进行了光催化降解实验,估计了模型中的参数,同时计算出了相应实验条件下纳米管内TVOC降解速率的模型值.对比分析模型结果与实验结果,表明:TVOC初始浓度一定时,TVOC的降解速率与纳米管的总表面积正相关;TVOC降解速率的数学模型简单可靠.该模型为光催化反应中光催化纳米管尺寸的选择提供了理论依据.     

阳极氧化TiO_2纳米管阵列的制备与表征

采用阳极氧化法,分别选用HF和NH4F两种电解质,对纯钛进行阳极氧化处理制备TiO_2纳米管阵列。选用扫描电子显微镜、透射电子显微镜、能谱及X-射线衍射对纳米管的形貌、化学成分和物相结构进行表征和分析。结果表明:在HF体系中,随着氧化时间的增加,纳米管整齐度增加,同时管径也增大,当氧化时间为20 min时,管内径约60 nm,壁厚约10 nm;而纯钛片厚度的变化对纳米管的形貌没有明显的影响。在NH_4F体系中,加热使纳米管的内径增加,壁厚变薄,内径达到130 nm,壁厚约7 nm,这是由于加热使氧化反应速率增加,加快了纳米管的形成速率。EDS检测的Ti和O的原子数的比例接近1∶2。XRD图谱表明,在450℃热处理后的纳米管的物相结构为锐钛矿,由此可见,阳极氧化制备的纳米管阵列为二氧化钛纳米管。     

CoFe_2O_4纳米管的合成与表征

利用阳极氧化铝模板,用化学方法合成了CoFe2O4纳米管.X射线衍射结果表明,纳米管由无择优取向的、立方尖晶石结构的多晶CoFe2O4构成.电子显微镜显示,纳米管管径约300 nm,管壁厚度约100 nm,由约30 nm的CoFe2O4颗粒组成.进一步的磁性测量表明,纳米管阵列无明显的各向异性,其矫顽力约1 kOe,磁滞回线的方形度约0.37.     

柱状纳米羟基磷灰石的制备和结构表征

以P2O5,Ca(NO3)2.4H2O为原料,无水乙醇为溶剂,通过调节pH值控制凝胶的形成,利用溶胶-凝胶/水热法制备柱状纳米羟基磷灰石(HAP).通过XRD、FTIR、电镜(TEM、SEM)等检测手段,对凝胶燃烧产物和经水热处理后的粉体相组成、形貌进行分析,探讨HAP晶体形成的原因.结果表明,利用溶胶-凝胶经低温燃烧后形成主晶相为纳米级的HAP,形状以柱状为主,经水热处理后,可得高纯度的HAP柱状晶体(100 nm×1800 nm),杂以少量粒状纳米粒子(30 nm×60 nm).     

碳纳米管的化学镀银及SEM研究

通过对碳纳米管进行金属包覆,制备一维纳米复合材料,利用化学镀方法在碳纳米管表面得到完整均匀的银镀层。研究表明,镀层质量与表面处理,反应速率和反应时间密切相关。     

Decoration of activated carbon nanotubes by assembling nano-silver

A facile solution processed strategy of synthesizing nano silver assembled on carbon nanotubes (CNTs) at room temperature was put forward. Activated carbon nanotubes were used as precursors for preparing silver-decorated nanotubes. The nature of the decorated nanotubes was studied using transmission electron microscopy (TEM), scanning electron microscopy (SEM), and energy-dispersive X-ray spectroscopy (EDX). The inert surfaces of carbon nanotubes were activated by introducing catalytic nuclei via an oxidation-sensitization-activation approach. Activated carbon nanotubes catalyzed the metal deposition specifically onto their surfaces upon immersion in electroless plating baths. The method produced nanotubes decorated with silver. The extent of silver decoration was found to be dependent on fabrication conditions. Dense nano silver assembled on nanotube surfaces could be obtained by keeping a low reaction rate in the solution phase. The results here show that this method is an efficient and simple means of achieving carbon nanotubes being assembled by nano metal.     

外加电场下碳纳米管的稳定性分析

基于Tersoff势,采用分子动力学方法研究了外加电场下碳纳米管的稳定性,并对不同半径及手性的碳纳米管进行了对比分析。结果表明:随着直径的增加,当作用于碳纳米管上的电场力表现为拉伸作用时,碳纳米管拉伸断裂的临界电场强度也随之增大,而当作用于碳纳米管上的电场力表现为压缩作用时,屈曲临界电场强度随着直径的增加而不断减小,但两种情况在直径2.0 nm以后都达到一个稳定的值。     

NiO/TiO2纳米管阵列异质结电极的制备及光电化学性能

采用阳极氧化方法在金属钛表面制备TiO2纳米管阵列,管内径为60~90 nm,壁厚约为15 nm,长度为600 nm,通过化学镀Ni并结合空气中热处理过程,在TiO2表面生长出NiO纳米颗粒层,厚度约为200 nm,颗粒尺寸为20~40 nm,获得异质结型NiO/TiO2纳米管阵列复合电极.结果表明,在100 mW/c...     

TiO_2纳米管制备及其在染料敏化太阳能电池中的应用

采用强碱水热法由钛粉和NaOH溶液水热反应合成二氧化钛纳米管,并用透射电子显微镜(TEM)、扫描电子显微镜(SEM)、X-射线电子衍射(XRD)等表征手段对反应产物进行表征,该方法制备的二氧化钛纳米管长度为200～300 nm,管径为20～25 nm.采用丝网印刷技术将二氧化钛纳米管粉末印制在掺杂氟的SnO2导电玻璃(FTO)上,并进行热处理.随后,将印制了薄膜的FTO导电玻璃浸泡在染料中,浸泡一段时间后,将其与导电面涂了铂的FTO导电玻璃组装成染料敏化太阳能电池,并对电池性能进行测试.在模拟太阳光照射下,该电池的填充因子为0.43,短路电流为0.48 mA,断路电压为0.35 V,光电转换效率为0.07%.     

细胞色素C在纳米银线阵列传感器上的电化学研究

在自制的多孔阳极氧化铝模板辅助下,用直流电解法在玻碳电极表面成功生长了大面积的纳米银线阵列。高分辨扫描电镜照片显示,银纳米线阵列均匀有序,单根纳米线的直径约40 nm,这与所用氧化铝模板的平均孔径(40 nm)相当吻合。将银纳米线阵列传感器用于细胞色素C的电化学研究,灵敏度大大提高,检测限达到0.1 mg/mL。     

多孔钛片上二氧化钛纳米管束的制备与表征

在氢氟酸电解液中采用阳极氧化法在多孔钛片上制备了二氧化钛纳米管束.考察了电压对二氧化钛氧化层形貌及温度对二氧化钛晶型的影响.制备的二氧化钛纳米管形貌,晶型及光催化性能分别采用SEM,XRD和光催化还原Pd2+沉积钯膜实验表征.SEM结果表明,最佳阳极氧化电压为30 V.在此电压下制备的二氧化钛纳米管长约为300 nm, 管径约为40 nm, 壁厚约为20 nm.XRD结果显示, 773 K退火后,二氧化钛为锐钛矿型;873 K退火后二氧化钛主要为锐钛矿型,含有2.99% 的金红石相;973 K退火后二氧     

Simultaneously inducing synthesis of semiconductor CdS nanotubes and nanospheres through living bio-membrane bi-template

Group II-VI semiconductors, because of its wider band width and nonlinear optical properties, have al- ready shown vital applications in fluorescence probe, sensors, solar battery, photoelectrocatalysis, photoelec- tricity devices, laser light-emitting di…     

碳纳米管高温热形变的研究

使用分子动力学方法对单壁碳纳米管高温下的结构进行了计算机模拟 .对直径为 1.35nm、长度为 2 .34nm、拓扑结构为扶手椅形式 (10× 10 )的单壁碳纳米管进行了分子动力学模拟 ,模拟结果表明 ,碳纳米管开头端由于能量弛豫过程 ,直径比内部略大 ,在温度逐渐升高之后 ,构成纳米管的碳原子逐渐偏离晶格位置 ,碳纳米管至少在 30 0 0K之下结构是稳定的 .     

银纳米粒子的制备及表征

利用乙二醇在高温下的还原特性,在溶剂热条件下制备了银纳米粒子,产品经XRD和TEM表征,所制备的银纳米具有面心立方相的多晶结构,平均粒径在50nm左右.