A STUDY OF HIGH LOFT NONWOVEN FABRICS USING POWDER BONDING TECHNOLOGY

In this paper, two types of high loft nonwoven fabrics have been constructed in the laboratory apparatus made by ourselves with different binders (polyamide and polyethylene powder) and varying binder contents (10%, 20%, 30% and 40%). The tensile and compression properties of these nonwoven fabrics were tested. It was found that one can reduce powder binder content to increase loft and softness of nonwoven fabrics, but it has to sacrifice its tensile strength. Adhesion force between binder and single fibre was also explored. The experiments showed that the adhesion force at the interface between binder and fibre depends on the fibre variety, the fibre surface morphology, heating temperature and heating time etc..     

高膨松性非织造布的加工方法和产品性能的分析比较

本文对三利,不同粘合加固纤维网方法(乳液喷洒法,双组分低熔点纤维和热熔粉末粘合法)所制得的高膨松非织造布的性能进行了测试,并对各生产过程特点和产品性能逆行了比较。在高膨松性非织造布的体积密度范围内,有空气对流传热机理存在。导热系数随体积密度增加而降低,在单位面积重量相同条件下,膨松度高的非织造布。织物表现厚度大,虽然导热系数高,但织物传热量较低,其绝热保暖性好。     

粘合剂粒径对非织造布性能的影响

探讨了粘合剂粒径对非织造布力学性能的影响。实验表明,随着粒径变细,非织造布的拉伸强度和弯曲模量呈非线性增加。分析认为由细旦纤维制成的非织造布可具有较高的拉伸强度和较低的抗弯模量,这些概念也适用于热熔纤维粘合和热轧非织造布。     

非织造布粘结剂含量和粘弹性模型参数的关系

对同一纤维网制成的不同粉末粘结荆含量非织造布的研究表明：简易三元件模型的参数和欧林模型的参数随着其粘结荆含量变化呈一定规律变化，且欧林模型的时间修正常数不变。根据模型的拟舍参数计算和讨论证明了应用力学模型可以检验非织造布加工中纤维网粘结程度的优劣。用MATLAB语言编写整套程序。     

非织造布力学性能的模拟用其应用探讨

对不同粉末粘结剂含量非织造布的研究表明:线性和非线性的简易三元件模型均能较好地描述非织造布的拉伸性能和应力松弛性能。根据模型的拟合参数计算和讨论提出了应用力学模型可以检验非织造布加工中纤维网粘结程度优劣的可能性。     

不同工艺对木棉/ES非织造材料保暖性能的影响

采用正交试验法对木棉/ES非织造材料的成型工艺参数进行研究,探讨了纤维质量配比、成型温度和成型时间对非织造材料保暖性能的影响程度和显著性.结果表明：木棉/ES非织造材料的成型时间对其保暖性能影响最大,其次是纤维质量配比,成型温度影响最小;获得木棉/ES非织造材料最优保暖性的工艺条件为成型时间10 min,m（木棉）∶m（ES）=30∶70,成型温度120℃.     

射流喷网非织造布工艺技术的研究

本文研究了最新的非织造布加固技术——射流喷网工艺,其基本原理与针刺加固相似,采用高压水针替代机械针刺,纤网在水流直接和反弹的双重作用下,纤维缠结加固。实验表明:预水刺时,各注射器的水压能量须逐个提高,纤维的缠结效果好,并提出了原料、速度、压力、温度等关健技术参数。纤网定量降低,注射器数量增加,涤纶射流非织造布机械性能比棉纤维的好,纤维种类和强力对非织造布性能有较大的影响。随着纤网定量的增加,断裂强度,撕破强度和顶破强度增加。漂白棉射流非织造布手感比涤纶纤维差,射流法非织造布的撕裂强度曲线呈锯齿形。     

金属镀膜复合絮片织物的保暖性能

本文研究了金属镀膜复合絮片（简称金属棉）织物在服装系统内的隔热保暖特性,探索并分析了金属棉织物复合层的不同配置、结构、针刺方向和体积重量、空气隔层,风速等条件对保暖效果的影响;提出了较为理想的结构配置、服饰设计的注意方向和使用条件场所的建议等。     

胶乳粘合非织造布物理-机械性能及其影响因素分析

本文用二次回归旋转设计方法研究了纤维网重、含胶量、针刺密度对胶乳粘合非织造布的主要物理-机械性能的影响:利用导出的回归方程,确定了上述影响因素的控制范围。在这个范围内,可使胶乳粘合非织造布物理-机械性能达到最佳值,实际结果验证了回归方程的可靠性,因而可使最佳因素控制范围应用到实际的非织造生产中。     

INVESTIGATION OF PARAMETERS OF NONWOVEN FILTER USED IN WHITE CELLS REMOVING

This paper is concerned with the relation between the parameters of nonwoven filter and removing of white cells. Melt-blown polypropylene nonwovens are used as filtration materials of white cells filter. According to the combination of different fiber diameter, different product density and different weight, optimized combination of parameters of nonwoven filter with more effective removing of white cells is obtained. The result is that removing of white cells is 96.90 percent; recovery of red cells is 92.27 percent.     

热轧非织造布粘合结构的形成

本文分析了热轧法非织造布的粘合结构形成机理及其工艺条件,研究了工艺参数变化对产品强力和粘合结构形态的影响,提出了由复合相构成的非织造布物理结构模型。分析结果对于调整热轧生产工艺和提高非织造布质量具有一定意义。     

Investigation of Atmospheric Plasma Discharge and Its Application to Surface Modification of Textile Materials

In this paper, an improved quasi-stable atmospheric pressure dielectric barrier discharge （DBD） plasma source is achieved after carefully controlled discharge voltage and current, discharge power, working gas, treatment period, and gap between the electrodes. This plasma source has been used to modify the surface of Polybutylene Terephthalate （PBT） melt-blown nonwovens and Polyester （PET） fabrics, and the various influences on surface modification and the aging effect of treated polymeric materials have been systematically investigated. In addition, the method of spectrum analysis is also used for diagnosing plasma paramneters such as electron temperature. Experimental results indicate that both the wettablity and permeation of treated PBT melt-blown nonwovens and dyeing ability of treated PET fabrics are certainly improved.     

粉末型非织造布用粘合剂的开发及其性能

本文为开发非织造布用粉末型粘合剂对热塑性聚烯烃进行了接枝改性的分子设计和试验研究,试验结果表明:在一定量的接枝助剂和引发剂条件下,可用马来酸酐对聚烯烃高聚物进行共聚接枝,制得的粉末状改性聚烯烃聚合物具有熔点低,粘合力强的优点,可以作为粉末型非织造布的粘合剂。     

非织造布组分配比微波检测法的研究

本文利用微波检测技术对非织造布的组分配比进行了测试研究。非织造布由不同配比的双组分(ES)纤维和蚕丝下脚料经混和,开松,梳理成网,并加热,熔融粘合而成。测试结果表明:微波谐振腔传感器检测电流示值与非织造布的配比关系曲线呈指数方程形式,指数值与组分配比呈良好的线性相关,同时,检测电流示值与非织造布强力也有一定程度的相关。     

聚乙烯醇复合凝胶的强度与界面强度研究

为了提高物理交联聚乙烯醇(PVA)水凝胶的强度,制备了PVA无纺布复合水凝胶. 当基体凝胶PVA质量分数为10%、无纺布体积分数为15%时,复合水凝胶的拉伸强度为5.90MPa;随着基体凝胶PVA质量分数和无纺布体积分数的提高,复合凝胶的强度提高;当基体凝胶PVA质量分数为15%、无纺布体积分数为25%时,复合水凝胶的拉伸强度为10.90MPa. 利用A系数研究了不同PVA质量分数以及无纺布体积分数的复合水凝胶中基体与无纺布的界面作用,在无纺布体积分数相同时,界面强度随PVA质量分数的提高而增大;在基体凝胶PVA质量分数相同时,无纺布体积分数较低的复合凝胶的界面强度较大. 复合水凝胶的结晶度低于纯水凝胶的结晶度.     

粉末粘结非织造布拉伸强度的理论模型

采用临界区思想推出了粉末粘结非织造布拉伸强度的理论估计模型。并根据模型需要对纤维从粘结纤维网中的平均抽拔力进行实测,进而对模型参数进行估计,最终实现对强度的估算。通过对比,发现强度的理论估计值和实测值与粉末含量的关系具有相同的趋势。由于理论的假设,使理论值与实测值之间存在差异,但它们之间存在着良好的线性关系。     

基于激光散射强度测量非织造布面密度的实验研究

应用光技术测量原理研究了非织造布的激光散射强度与面密度的关系,并应用计算机程序控制非织造布激光散射强度测定系统测定和分析了3种加工方法的非织造布试样。结果表明:非织造布面密度与激光散射强度之间存在十分密切的关系,这里所述的方法具有无放射性和易于采用计算机测量的优点,可用于薄型非织造布面密度的测量。     

热熔粘合聚丙烯熔喷非织造布的结构与性能

本文采用了广角X光衍射、差示扫描量热法、扫描电子显微镜技术,对热熔粘合聚丙烯熔喷非织造布的结构和形态进行研究。讨论了粘合温度对非织造布的几何尺寸和机械性能的影响。结果表明,球晶是熔喷聚丙烯纤维的主要结构形式。在不同的热粘合条件下,球晶的结晶变体中可以出现α晶,或是拟六方酝晶,以及两者的混合形式。粘合温度对纤维的结晶度和晶粒尺寸,及非织造布的热收缩和厚度具有较大的影响。热粘合温度在软化点出现非织造布强度峰值。     

树脂粘结剂含量对汽车摩擦材料性能的影响

选定国产改性酚醛树脂作为汽车摩擦材料树脂粘结剂基体,研究了不同树脂含量对材料机械性能和摩擦磨损性能的影响,并通过ＳＥＭ 和ＥＤＡＸ表观分析来确定摩擦材料中树脂粘结剂的最佳含量．研究结果表明：在所选定的６ ％ ～１４％ 树脂含量（质量分数）范围内,材料的冲击强度都能满足使用要求．树脂含量在１４％ 及其以上时,材料高温热衰退严重,导致摩擦因数下降,高温磨损加剧,磨损量上升;在树脂含量过高或过低时,材料将因粘结剂量过少或树脂高温分解导致粘结力下降,使增强纤维存在拔出现象,导致摩擦因数不稳定,材料磨损加剧．综合各项性能,得出：摩擦材料中基体树脂用量不宜太多,其含量以８％ ～１２ ％ 为佳,其中以８％ 为最佳．该结论在桑塔纳轿车无石棉盘式刹车片的研制中得到验证     

黄麻纤维农用非织造地膜的制备工艺研究

以黄麻、聚丙烯、ES纤维为原料,通过针刺和热轧工艺加固,制得黄麻农用非织造地膜.探讨工艺过程中的针刺密度、热轧时间、热轧压力、热轧温度等工艺参数对最终产品性能的影响,并通过正交设计寻找最优的工艺方案.