果胶/壳聚糖抗菌膜结构及性能分析

采用溶液共混法制备了不同质量比例的果胶/壳聚糖复合膜,用IR、XRD表征其结构,并测试了复合膜的溶胀度、水蒸气透过率、透光率、体外降解和抗菌性等性能.结果表明:果胶和壳聚糖分子间有很好的相容性并发生了一定的相互作用;当二者质量比例为1:1时,复合膜的水蒸气透过率最低、透气性较小,溶胀度达到487%,并且能够保持良好的体外降解性和抗菌性.     

pH响应型医用抗菌水凝胶人工血管材料

基于互穿网络结构的聚乙烯醇/聚丙烯酰胺水凝胶，运用抗菌肽制备了一种pH响应型抗菌水凝胶人工血管材料。试验结果表明，该水凝胶表面光滑、微孔结构均匀，力学性能优良且具有低体积溶胀性。体外细胞毒性试验和抗菌试验结果表明，该水凝胶在生理状态下不具备杀菌性能和细胞毒性，而在低pH值环境下对大肠埃希菌与金黄色葡萄球菌都具有明显的杀菌作用。研究结果为进一步开发响应型抗菌水凝胶人工血管提供了理论和试验依据。     

壳聚糖/SiO_2复合膜的制备及性能研究

以廉价的工业硅溶胶为SiO2纳米粒子,使其与壳聚糖的醋酸溶液共混,得到壳聚糖/SiO2复合膜(简称复合膜).研究了复合膜在干态和湿态下的力学性能,在波长200～800nm范围内的透光率,在水中的溶胀率,复合膜内SiO2微粒的形貌及其与壳聚糖的相互作用.结果表明:随着膜内SiO2质量分数增加,复合膜的溶胀率从65.88%降到45.65%.复合膜在干态和湿态下的拉伸强度、伸长率等力学性能呈现先增加到最大值,然后又降低的变化趋势.复合膜中SiO2质量分数为14.07%,其干态膜的力学性能较佳,拉伸强度和断裂伸长率分别为58.09MPa和20.74%.当复合膜中SiO2质量分数为30.30%时,湿态膜的力学性能最佳,其拉伸强度为35.83MPa,断裂伸长率为114.76%.SiO2通过与壳聚糖形成强的相互作用而被均匀分散在复合膜内,该复合膜具有良好的生物相容性和耐水性能,可作为一种潜在的生物分离功能膜.     

用NBR／PVC共混胶制备耐寒制品的配方研究

讨论了NBR/PVC共混胶与BR并用、相容剂、硫化体系、补强体系和增塑体系对配方硫化胶低温耐寒性能、耐油性和相关力学性能的影响,研制出了具有优良耐寒性能和力学性能的耐寒制品配方。该配方硫化胶的脆性温度可以达到-44℃,压缩耐寒系数在-20℃和-30℃下分别达到了0.78和0.33,耐油溶胀度达23.3%。     

oxi-HA/oxi-CMC/PAH水凝胶的制备及性能

以聚丙烯酰肼(PAH)为交联剂,通过席夫碱反应制备了系列氧化透明质酸/氧化羧甲基纤维素/聚丙烯酰肼(oxi-HA/oxi-CMC/PAH)水凝胶,并对水凝胶的溶胀率、降解行为、流变学性能、体外药物释放行为及冻干水凝胶的微观形貌进行了研究。结果表明,oxi-HA6/oxi-CMC6/PAH3水凝胶具有较合适的流变学性能、较高的溶胀率、较好的稳定性和一定的药物缓释能力;药物模型牛血清蛋白(BSA)的体外释放通过扩散机制、溶胀机制和降解机制控制。在37℃pH值7.4的磷酸盐缓冲溶液(PBS)中,oxi-HA6/oxi-CMC6/PAH3水凝胶5 h溶胀率达到16,20 d降解率约为51%,载药水凝胶中BSA的7 d累积释放率约为86%,可应用于药物传输和细胞封装等领域。     

基于Diels-Alder反应的可注射缓释水凝胶的制备及其理化性质

本研究旨在通过药物-聚合物偶联物模型和Diels-Alder点击反应制备一种可注射缓释水凝胶。将葛根素与透明质酸通过酰胺键连接得到葛根素-透明质酸偶联物(PUE-HA),将PUE-HA和四臂马来酰亚胺聚乙二醇(4-arm-PEG-MAL)通过Diels-Alder点击反应交联制备了可注射缓释水凝胶(PUE-HA-PEG),并考察了三种不同呋喃(Furan)与马来酰亚胺基(MI)比例对所得水凝胶的胶凝时间、形貌、溶胀度、降解度、葛根素体外释放、水凝胶力学性能以及水凝胶生物相容性等理化性质的影响。与1Furan/1MI和1Furan/2MI水凝胶相比，1Furan/4MI的水凝胶胶凝时间可缩短至1 min。随着MI比例的增加，水凝胶具有更低的降解速率(21 d降解率低于60%),更好的力学性能，缓释释药作用更加明显。实验结果表明，Furan/MI的比例对可注射缓释水凝胶的理化性质具有重大影响。     

魔芋胶的流变性研究

对魔芋胶的流变性进行了研究.结果表明:浓度、剪切力、溶解温度、加热时间、pH值、冻融等变化与魔芋胶的粘度有较大关系;魔芋胶溶液具有较高的粘度,当浓度达到1%时,其粘度为428mPa/s;魔芋胶溶液为"非牛顿流体";加热时间与温度对魔芋胶粘度影响较大;魔芋胶溶液在酸性和碱性条件下都较为稳定;冻融处理后魔芋胶粘度下降.魔芋胶与黄原胶、卡拉胶有强烈的协效性,与皂荚胶的协效性较低.     

离子液体?聚乙烯醇复合质子交换膜的制备及其性能

离子液体1-(2-氰乙基)-3-苄基咪唑硫酸氢盐([cebzim]HSO4)与聚乙烯醇(PVA)通过溶液浇铸法制备离子液体复合膜[cebzim]HSO4/PVA.采用FT-IR、XRD、TGA及SEM对所制备离子液体复合膜的结构和形貌进行表征.同时研究了离子液体含量对[cebzim]HSO4/PVA复合膜的耐水性能、溶胀性能、电导率及机械性能的影响.实验结果表明:随着离子液体含量的增加,[cebzim]HSO4/PVA复合膜的吸水率、溶胀率、电导率增加,机械性能下降.综合考虑,当离子液体质量分数为50%时,[cebzim]HSO4/PVA复合膜的性能最优.     

聚N-异丙基丙烯酰胺/壳聚糖温敏性敷料——自剥离伤口敷料的制备及性能研究

通过自由基聚合法以单体N-异丙基丙烯酰胺(NIPAAm)和壳聚糖(CS)为原料反应制得聚N-异丙基丙烯酰胺/壳聚糖(PNIPAAm/CS)多孔温敏复合膜。用扫描电子显微镜(SEM)、傅立叶红外光谱(FTIR)、差热分析(DSC)和溶胀率等研究手段对复合膜的理化性能进行表征。研究结果表明:复合膜仍保持其良好的温度敏感性;膜结构随CS含量增加而变得规则,孔径变小,机械性能增强,同时相转变温度略有下降;复合膜内两相间分布比较均匀,未出现相分离;PNIPAAm与CS两相间存在一定的键合作用,主要是CS的羟基和氨基与PNIPAAm中的酰胺基之间形成了氢键结合,这些作用对复合膜的力学性能有一定增强作用。研究还发现,PNIPAAm含量对膜的吸水率和力学性能亦有一定影响。     

降解黄原胶与降解魔芋胶形成的凝胶体系的流变性

以降解黄原胶与降解魔芋胶为主要原料,将两者在一定条件下共混制得不同的凝胶体系,考察了共混比例、总胶浓度、共混时间、盐离子浓度对凝胶体系流变特性的影响,并研究了该凝胶体系的本构方程。结果表明:降解黄原胶与降解魔芋胶凝胶体系具有剪切变稀特性,其本构方程为非线性共转Jeffreys模型,模型计算值与实验值吻合良好。     

Preparation and characterization of chitosan/carboxymethylated konjac glucomannan blend films

In order to improve the mechanical and water swelling properties of the chitosan (CS) film, a series of transparent films were prepared by blending 2% (weight) chitosan acetic acid solution with 1.5% (weight) carboxymethylated konjac glucomannan (CMKGM) aqueous solution according to predetermined ratio and drying at 30°C. The morphological structure, miscibility, thermal stability, mechanical properies, and swelling capacity of the blend films were studied by infrared (IR), X-ray diffraction (XRD), differential thermal analysis (DTA), scanning electron micrograph (SEM), and measurements of the mechanical properties and swelling properties. The results demonstrated that there was strong interaction and good miscibility between CS and CMKGM resulted from intermolecular hydrogen bonding and electrostatic force. The mechanical properties in dry state and wet state, thermostability, and water swelling properties of the blend films were obviously improved. The best values of the tensile strength in the dry and wet state achieved 89 MPa and 49 MPa, respectively, when the CMKGM content was 30% (weight). The CS/ CMKGM blend films provided promising biomedical applications. Foundation item: Supported by the National Science Foundation of China (No.29977014). Biography: Zheng hua (1965-), male, Associate professor, research direction: renewable resource chemistry.     

SBR/PAANa遇水膨胀橡胶的力学及膨胀性能研究

研究了SBR/PAANa混炼型遇水膨胀橡胶的力学及遇水膨胀性性能.结果表明,PAANa含量越高,SBR/PAANa膨胀性能和压缩永久变形性越高,但拉伸强度逐渐降低;相对于在去离子水中,增加金属离子浓度或者金属离子电荷都会使SBR/PAANa膨胀性能下降.     

含氮纽结魔芋葡甘露聚糖分子链凝胶结构拓扑分析

以魔芋葡甘聚糖分子链和氨基的相互作用为基础,运用分子动力学模拟魔芋葡甘聚糖分子和KGM纽结作用位点,结合红外光谱图,从理论上分析含氮魔芋葡甘聚糖凝胶的高强度性,结果表明含氮魔芋葡甘聚糖凝胶的高强度性是因为氮与魔芋葡甘聚糖通过偶合反应形成了可以相对滑动的"8"字型交联环,由拓扑分析得到,KGM由平凡纽结变换成"8"字型纽结后Schultz指数与修正Schultz指数变小,加强了分子之间作用力,得到了高强度不可逆凝胶.KGM"8"字型纽结的形成有利于魔芋葡甘聚糖凝胶的机械强度和稳定性的提高.     

KGM-AM-（DMAEA-EB）三元接枝共聚物的性能研究

以魔芋粉、丙烯酰胺和季铵盐等为原料,经接枝共聚合成了魔芋粉一丙烯酰胺一季铵盐类树脂。讨论了引发剂、丙烯酰胺、魔芋粉等的用量,反应时间和温度等因素对树脂溶胀性能的影响。结果表明反应温度为55-65℃,反应时间为4h,反应单体质量比为1：1,引发剂用量为0.5％（占单体总质量）,单体与KGM质量比为4：1下制得树脂的溶胀度可达到最大值149.85g／g。     

烯类单体与丁腈橡胶直接共混制备吸水膨胀橡胶

用水溶性烯类单体与丁腈橡胶直接共混制备吸水膨胀橡胶ＷＳＲ（ｗａｔｅｒ－ｓｗｅｌｉｎｇｒｕｂｂｅｒ）,并对ＷＳＲ的亚微观形态、吸水膨胀特性、力学性能和浸水稳定性进行了研究。ＴＥＭ研究证明,水溶性单体与橡胶共混可制得亲水组分在橡胶相中分散均匀的ＷＳＲ;烯类单体的聚合反应活性越高,所制得的ＷＳＲ的吸水膨胀率越高;其由丙烯酸钠与橡胶共混制得的ＷＳＲ力学性能和耐久性与高吸水树脂／橡胶共混型ＷＳＲ相似     

红外辐照对魔芋葡甘聚糖膜力学性能的影响

以魔芋葡甘聚糖(KGM)粉末为研究对象,分别以分子量、水分含量的内在性质和红外辐照温度、时间、强度外部条件为参考因子,考察其与KGM溶胶成膜后力学性能的相关性,并通过扫描电镜分析,观察膜截面的微观形貌.实验结果表明:经红外处理,KGM膜力学性能的下降百分比与分子量呈明显线性正相关,与水分含量呈负相关;较高辐照温度、光强度和较长辐照时间显著破坏膜的力学性能;膜截面的有序完整片层破坏成碎裂小块和多孔结构.合理选择高品质KGM,控制红外辐照条件,可改善KGM膜的力学性能.     

枸杞果冻加工工艺研究

以枸杞汁、白砂糖为主要原料,研究枸杞果冻的加工工艺及最佳配方.通过正交试验确定复合凝胶剂(卡拉胶、魔芋胶)的配比、胶剂的添加量、白砂糖添加量、枸杞汁添加量、柠檬酸添加量对果冻产品品质的影响.实验结果表明:卡拉胶、魔芋胶的配比为7∶3,总胶粉添加量为0.9%,添加白砂糖15%,枸杞汁20%和0.12%柠檬酸,水浴85℃,杀菌15min,得到淡红色、口感爽滑、酸甜可口的枸杞果冻,具有浓郁的枸杞风味.     

魔芋葡甘聚糖降解产物对肌原纤维蛋白的冷冻保护作用

采用酸降解、β-葡聚糖酶水解、纤维素酶水解、辐照降解、微波辅助H2O25种方式降解魔芋葡甘聚糖.以草鱼肌原纤维蛋白为研究对象,比较了不同魔芋葡甘聚糖降解产物对冻藏过程中肌原纤维蛋白的冷冻保护效果,并对不同降解产物的冰点进行测定.实验结果表明：魔芋葡甘聚糖降解产物能有效地抑制草鱼肌原纤维蛋白在冻藏过程中的蛋白质变性,其中β-葡聚糖酶水解、纤维素酶水解和辐照降解的魔芋葡甘聚糖添加量为0.5%,抗冻效果略优于商用抗冻剂.同时,魔芋葡甘聚糖降解产物作为冷冻保护剂能降低水分子的冰点和融化热焓值.     

增塑剂对壳聚糖-小檗碱复合膜物理和抗菌性能的影响

研究了工业无毒增塑剂柠檬酸三乙酯、乙酰柠檬酸三乙酯、柠檬酸三丁酯和乙酰柠檬酸三丁酯在可食性膜中添加的可能性，及其对可食性膜机械性能的影响。通过正交试验确定在60℃下，壳聚糖与甘油质量比为8∶5（即壳聚糖0.02g/mL，甘油0.0125g/mL），增塑剂体积分数在0.75%时，该膜的机械性能最佳。抑菌圈法检测表明柠檬酸三丁酯的添加不影响膜对桃褐腐病菌（Monilinia fructicola）的抑制作用。膜包裹法处理实体桃，结果表明室温下放置10d，膜包裹法处理的桃果实日失重率达到30%以上，腐烂指数近60%，而对照组日失重率达到40%相似文献   

高红外透过性UHMWPE/锦纶复合微孔织物的制备

将超高相对分子质量聚乙烯(ultrahigh relative molecular weight polyethylene,UHMWPE)溶解后与锦纶6网格布热压复合,采用热致相分离法制得UHMWPE/锦纶复合微孔织物。研究了UHMWPE相对分子质量和质量分数对复合织物厚度、水通量、透气率和水蒸气透过率的影响,并研究了复合织物对紫外光、可见光及红外光的透过性能,计算了复合织物对人体发射红外波段范围内的红外透过率。研究结果表明,采用UHMWPE相对分子质量为100万或400万,质量分数为5%~10%时,其与锦纶6网格布复合形成的微孔织物在波长7~14μm内的加权平均红外透过率达95%以上,且均具有较好的透气性、透湿性和满足服用织物需要的力学性能,同时,该复合织物对紫外光和可见光均有较好的遮蔽性能,可用作凉爽织物。