铕的配合物的电致发光性质研究

本文以二苯甲酰丙酮（DBM）,三氟噻吩丙酮（TTA）为第一配体,以4,4′-二甲酸正丁酯-2,2′-联吡啶（dctbpy）,合成了两种铕的三元配合物Eu（DBM）3dctbpy,Eu（TTA）3dctbpy,以铕配合物掺杂在PVK中所构成的膜作为发光层,以ITO为阳极,Mg：Ag合金为阴极,AlQ为电子传输层,BCP为空穴阻挡层制备了电致发光器件.实现了铕的特征红色荧光发射,,测定了器件的电致发光性能;讨论了此掺杂体系中能量传递机制.     

深蓝色OLED材料均三嗪衍生物的合成与表征

简要本文合成了三种均三嗪衍生物TPTPA、TITPA和TCTPA，并利用其在电学和光学特性，将其作为发光/电子传输层材料制作有机电致发光器件(OLEDs). 其中，TCTPA具有比TPTPA和TITPA更高的荧光量子产率(PL). 从TPTPA到TCTPA其最低未占据轨道能级(LUMO)逐渐减少，这说明了TCTPA由于其共轭结构的增大，具有更高的电子迁移率. 以TCTPA作为发光/电子传输层的无掺杂OLED器件，在20V时亮度达到最大值2 612 cd/m2，其最大亮度效率和最大功率效率分别为1.72 cd/A 和1.35 lm/W. 将Ir(PPy)3、PVK、PBD等化合物，分别掺杂到以TCTPA为发光/电子传输层的OLED器件中，均展示出比无掺杂器件更高的亮度及效率.     

罗丹明B掺杂ZnQ2的电致发光器件及其性能研究

将8-羟基喹啉锌(ZnQ₂)和8-羟基喹啉铝(AlQ₃)的发光性能进行比较,筛选出ZnQ₂作为掺杂发光层主体材料,与荧光染料罗丹明B(RhB)共掺杂,采用真空热蒸镀法制备有机电致发光器件(OLEDs).掺杂不同浓度RhB可以获得不同波长的光发射,得到不同的发光色调.通过对溶液态荧光光谱和器件发光光谱等特性的测量与分析,探讨了器件的能量转移及发光机理.     

掺杂浓度对四苯基卟啉掺杂电致发光器件的发光性能影响研究

以8-羟基喹啉铝(Alq3)为主体发光材料,四苯基卟啉(TPP)为掺杂染料,制备了5种不同摩尔掺杂浓度(0．5％、1．0％、1．5％、2．0％、2．5％)的掺杂电致发光器件,考察了掺杂浓度对其器件的电致发光光谱、色度、亮度和发光效率的影响;并结合掺杂器件的发光机理,对实验结果进行了分析和讨论     

单一白色发光层的OLED制备与发光性能研究

研制了两种类型单一白色发光层的有机电致发光器件(OLED),即小分子Zn(BTZ)2的掺杂型器件：ITO／PVK：TPD／Zn(BTZ)2：Rubrene／Al和聚合物LPPP的混合型器件：ITO／混合型发光层／Al,获得了较高的器件亮度和发光效率,且色坐标均非常接近于白色等能点,进而对上述器件的发光和电学性能进行了初步研究。     

ZnS:TmF3薄膜电致发光特性的研究

为了提高蓝色薄膜电致发光器件(TFEL)的发光亮度,自行配制了氟化铥(TmF3),并制备了以ZnS:TmF3为发光层的薄膜电致发光器件,研究了TmF3的掺杂浓度对ZnS:TmF3 发光器件发光特性的影响.实验结果显示,当掺杂浓度为1.2%mol时,发光亮度最强.     

DCM染料掺杂对有机电致发光磁效应的影响

制备了DCM染料掺杂的有机电致发光器件ITO/NPB/Alq3： DCM/Alq3/ LiF/Al, 研究了15 K-R.T.（室温）温度范围内, 器件的电致发光随磁场的变化关系（即电致发光的磁效应）. 发现电致发光的磁效应由低场（0≤B≤40 mT）效应和高场（B≥ 40 mT）效应两部分组成. 室温下, 对于未掺杂的参考器件, 发光在低场部分随磁场的增加迅速增强, 高场部分随磁场的增加缓慢并逐渐趋于饱和. 而对于掺杂器件, 尽管发光在低场部分随磁场也迅速增强, 但高场部分却在低场增加的基础上出现下降. 器件的注入电流越大, 发光在高场下降越明显. 低温下（T ≤150 K）, 尽管未掺杂器件电致发光的磁效应的高场部分也出现减弱趋势, 但掺杂样品的高场部分受温度的影响要远弱于未掺杂样品的结果. 基于掺杂引起的能级陷阱效应, 通过讨论外磁场作用下的三重态激子淬灭过程, 我们对实验结果进行了定性解释.     

高效率的白光有机电致发光器件

为了提高白光有机电致发光器件的发光效率和光谱稳定性,采用染料掺杂的方法,制备了多层结构白光有机电致发光器件。通过参数优化实现了非常好的白光发射,并表现出良好的光谱稳定性。器件的开启电压为5.1V,发光亮度达到10800cd／m^2,最大电流效率和功率效率分别是10.4cd／A和3.5lm／W。     

有机掺杂红色发光二极管的特性研究

研究了不同掺杂浓度掺杂Alq3：DCM体系有机发光二极管的电致发光（EL）特性，根据实验结果，指出器件的EL发射峰值跟作为受体的DCM在给体Alq3中的掺杂浓度有关，应用Forster能量传递理论对其机理进行了解释。     

9,9’-bianthrancene为发光层的蓝色OLED的研究

报导了蓝色有机电致发光材料9,9'-联二蒽(9,9'-bianthracene,简称BA)作为发光层,研制了结构为ITO/PVK:TPD/BA/Alq3/Al的蓝色有机发光器件.对该器件的发光及电学性能进行了研究.启亮电压约为12 V,在24 V外加电压下亮度达到最大值2 433 cd/m2.     

铽（Ⅲ）配合物的纳米导电高分子结构及荧光性质的研究

以聚乙烯咔唑（PVK）为基质,分别采用直接掺杂法和原位复合法制备了含稀土铽（Ⅲ）配合物的纳米发光薄膜,并且对膜层的荧光光谱、紫外吸收光谱、透射电镜和原子力显微镜进行了研究,实验结果表明：当稀土配合物被复合到导电高分子PVK中,铽配合物是以纳米的尺寸分散在聚合物基质中,两种方法获得的薄膜都发出了铽离子的特征荧光。     

Photoconductivity of fullerene derivatives

Two fullerene derivatives (compounds 1 and 2) have been synthesized. Their redox properties have been measured by cyclic voltammetry. The photoconductivities of poly(N_vinylcarbazo_le) (PVK) doped with fullerene and with their derivatives have been studied to explore the possible relationship between the reductibility of fullerenes and the photoconductivity of fullerenes_doped PVK. The charge generation efficiencies of PVK doped with fullerene and with its derivatives have changed remarkably: the diversity of charge generation efficiency is obvious in different doping systems. The result indicates that there is charge transfer between fullerenes and PVK.     

Pure and stable white organic light-emitting device with an ultra-thin layer

Due to high brightness, low viewing angle, low driving voltage and short response time, organic light-emitting display is appraised as one of the most promising flat displays in the near future. Full-color technology is the bottle neck for industrializati…     

White organic light-emitting devices using Zn（BTZ）2 doped with Rubrene as emitting layer

Zn(BTZ)2 was synthesized from the complex reaction between zinc acetate dihydrate and 2-(2-hydroxyphenyl) benzothiazolate. Then Zn(BTZ)2 was used as main light-emitting material doped with different amounts of fluorescent dye Rubrene and fabricated a series of white organic light emitting devices. The configurations were as follows: ITO/PVK:TPD/Zn(BTZ)2:Rubrene/Al. The doping concentration of Rubrene in Zn(BTZ)2 was 1.2%, 0.12%, 0.08% and 0.05%, respectively. According to the EL spectra and CIE coordinates of the above devices, the optimum doping concentration (0.05%, weight percent) had been determined. The steady and bright white light emitting of the device with 0.05% doping concentration had been obtained, and the white emission covered a wide range of driving voltage (10--22.5 V). The CIE coordinates were (x=0.341, y=0.334) at the driving voltage of 20 V, which was very close to the equi-energy point (x=0.333, y=0.333), and the corresponding luminance and external quantum efficiency were 4048 Cd/m^2 and 0.63% (4.05 Cd/A), respectively. Lastly, we also discussed the emitting mechanisms of the material and the devices.     

Cu3(BTC)2提高聚二甲基硅氧烷/聚醚酰亚胺复合膜气体分离性能成因的研究

将金属有机骨架化合物Cu₃(BTC)₂填充到聚二甲基硅氧烷中，制备聚二甲基硅氧烷/聚醚酰亚胺改性复合膜，用于气体分离的研究。考察了操作温度和压力对CO₂、CH₄、O₂和N₂在改性复合膜中的渗透系数、扩散系数、溶解度系数和分离系数的影响。结果表明，填充Cu₃(BTC)₂可降低气体的渗透活化能、扩散活化能和膜的压缩效应，进而提高气体的扩散性能和渗透性能；Cu₃(BTC)₂改性复合膜在低温条件下可得到较高的渗透性能和分离性能，较高压力可在不降低膜分离性能的基础上提高其渗透性能。     

微波烧结法制备Fe2O3掺杂0.55PNN-0.45PZT压电陶瓷及性能

 微波烧结是一种新型、高效的陶瓷烧结工艺,具有升温速度快、节能省时、改善微观结构以及降低烧结温度等特点.本文采用微波烧结工艺制备了Fe₂O₃掺杂的0.55Pb(Ni_1/3Nb_2/3)O₃-0.45Pb(Zr_0.3Ti_0.7)O₃(简写为0.55PNN-0.45PZT)压电陶瓷,烧结温度为1200℃、保温时间为2h.利用X射线衍射(X-ray Diffraction,XRD)、扫描电子显微镜(Scanning Electron Microscope, SEM)、阻抗分析仪及铁电分析仪等测试表征方法,研究了Fe₂O₃掺杂对陶瓷的结构、介电以及压电性能的影响.结果表明,所有陶瓷样品均为钙钛矿结构,随着Fe₂O₃掺杂量的增加,压电和介电性能呈先增加后减小趋势.当Fe₂O₃掺杂量为0.8%(质量分数)时,陶瓷达到最优电学性能：压电常数(d₃₃)、平面机电耦合系数(k_p)、相对介电常数(ε_r)和介电损耗(tanδ)分别为d₃₃=520pC/N,k_p=0.51,ε_r=4768,tanδ=0.026.     

Electroluminescent property of tetrakis(phenyl)porphyrin carbonyl ruthenium(Ⅱ)

Luminescent tetrakis(phenyl)porphyrin carbonyl ruthenium (Ⅱ) (RuTPPCO) complex was employed as a doped emitting material to fabricate red organic electroluminescent (EL) devices. The EL device structure was [ITO/copper phthalocyanine (Cu-Pc) (15.0 nm)/N,N′-di(α-naphthyl)-N,N′-diphenyl-(1,1′-biphenyl)-4, 4′-diamine (NPB)(60.0 nm)/tris(8-hydroxyquinolinato)aluminum (Alq3):RuTPPCO (50.0 nm)/LiF (1.0 nm)/Al (200.0 nm)]. The codeposited films of Alq3:RuTPPCO were utilized as the emitting layer to construct EL devices. Experimental results showed that energy transfer from Alq3 to RuTPPCO occurred in the codeposited films. The EL property of the codeposited Alq3:RuTPPCO films with different RuTPPCO concentrations was described. For the EL device with the RuTPPCO concentration of 15% by weight, deep red electroluminescence at 656 nm with the maximum EL efficiency of 0.32 cd/A was achieved.     

Co2(CO)8红外光谱及羰基钴氢催化活性的理论研究

在B3LYP/6-31G*水平上对Co₂(CO)₈红外光谱及烯烃氢甲酰化催化反应的催化活性中间体HCo(CO)₄和HCo(CO)₃的结构进行了优化及相关计算,结果表明：(1) Co₂(CO)₈的两种稳定构象态分别具有C_2v和D_3d对称性,计算所得的结构数据与实验 值具有极好的一致性。C_2v对称性的Co₂(CO)₈比D_3d对称性的Co₂(CO)₈的能量低28.80kJ/mol; (2) C_2v对称性的Co₂(CO)₈的红外吸收峰的计算结果 与实验值极为接近;(3) 催化反应的活性中间体HCo(CO)4和HCo(CO)3的稳定构象 态分别具有C_3v和C_2v对称性,其中HCo(CO)₃比HCo(CO)₄具有更高的催化活性;(4) 催化反应中乙烯与HCo(CO)3形成了相对稳定的π配合物,该配合物中π配键的键能约为100.80kJ/mol。     

掺杂聚合物对有机电致发光二极管的影响

利用甩胶方法在导电玻璃上分别制得单一的聚烷基噻吩并在其中掺杂不同量的聚乙烯咔唑的有机发光层，再用真空蒸发方法将铝沉积在这些有机层上作为发光二极管的负极。选择合适的掺杂比，电致发光二极管在电压为５Ｖ、电流密度为３０ｍＡ／ｃｍ＾２时就有光输出。这一结果表明，掺杂具有空穴特性的聚乙烯咔唑对增强短烷基侧链的聚烷基噻吩电致发光强度是一种有效的方法。     

一种叠层结构绿光有机电致发光器件

制备了叠层结构的绿光有机电致发光器件,采用电荷生成层将两个发光单元串接起来,各个发光单元之间互不影响,由两个发光单元分别发出的光叠加,得到高效率的绿光发射.