TiO_2/Ce_(0.45)Zr_(0.45)Mn_(0.05)La_(0.05)O_X光催化降解气相苯

采用等孔体积浸渍法经500℃焙烧得到了负载型光催化剂TiO2/Ce0.45Zr0.45Mn0.05La0.05OX,以气相苯模拟室内挥发性气体,在静态反应装置中考察该催化剂对气相苯的光催化降解性能,结果表明,TiO2负载在TiO2/Ce0.45Zr0.45Mn0.05La0.05OX上能显著提高对苯的光催化降解性能,TiO2/Ce0.45Zr0.45Mn0.05La0.05OX上苯降解率是纯TiO2上的2.8倍.XRD结果显示没有检测到TiO2的衍射峰.TiO2结合能向低值移动、负载型光催化剂在紫外-可见区吸收增强、表面氧物种增多和晶格缺陷增多可能是该催化剂能显著提高光催化活性和延长寿命的重要原因.     

TiO2/Ce0.45Zr0.45Mn0.05La0.05OX光催化降解气相苯

采用等孔体积浸渍法经500℃焙烧得到了负载型光催化剂TiO2／Ce0．45Zr0．45Mn0．05La0．05Ox以气相苯模拟室内挥发性气体,在静态反应装置中考察该催化剂对气相苯的光催化降解性能,结果表明,TiO2负载在TiO2／Ce0．45Zr0．45Mn0．05La0．05O上能显著提高对苯的光催化降解性能,TiO2／Ce0．45Zr0．45Mn0．05La0．05Ox上苯降解率是纯TiO2上的2．8倍．XRD结果显示没有检测到TiO2的衍射峰．TiO2结合能向低值移动、负载型光催化剂在紫外一可见区吸收增强、表面氧物种增多和晶格缺陷增多可能是该催化剂能显著提高光催化活性和延长寿命的重要原因．     

纳米Bi_2O_3/TiO_2光催化剂的制备及光催化活性评价

在超声波作用下采用水解法制备Bi2O3/TiO2复合光催化剂,以紫外灯为光源,对有机染料进行光催化降解实验,考察Bi2O3/TiO2的光催化性能.结果表明:Bi2O3与TiO2复合拓宽了催化剂对光的吸收范围,提高了TiO2的光催化活性,掺杂量(Bi2O3)为0.25%(w)复合光催化剂催化活性最高.考察了催化剂投加量、染料初始浓度、溶液pH值等因素对罗丹明B降解效果的影响,降解反应遵从假一级动力学模型,测得反应速率常数为0.0574min-1.     

掺钇纳米TiO2的制备及其光催化降解性能

以价廉易得的TiCl4为原料,采用低温水解法制备出掺钇纳米TiO2光催化剂,进行了XRD分析,研究了掺钇纳米TiO2对甲基橙的光催化降解性能,结果显示:掺钇阻碍了晶粒生长,抑制了TiO2由锐钛矿向金红石晶型的转变,使粒径减小,光催化降解能力增强.实验条件下,掺钇纳米TiO2光催化剂降解甲基橙的最佳投加量为2.0g/L.     

掺铁二氧化钛光催化剂的制备及催化性能

以钛酸四丁酯和Fe（NO3）3.9H2O为原料,在室温下制备得到TiO2和掺铁TiO2光催化剂粉体;以紫外灯为光源,甲基橙溶液为目标降解物,在紫外-可见分光光度计上对其光催化活性进行了研究。实验结果表明：掺杂Fe3＋的TiO2光催化剂比纯TiO2具有更好的催化活性,在Fe3＋掺入量为0.05%,催化剂加入量为2g,紫外光照时间为3h时,掺铁TiO2光催化剂可达到83%的光催化降解效率。     

TiO2的微波辐射Sol-Gel法制备及其光催化性能

采用微波辐射Sol-Gel法在石英砂表面制备负载型TiO2光催化剂，考察不同加热方式。微波功率以及微波加热温度对溶胶质量的影响，微波加热反应制备的溶胶粒子平均粒径小于常规加热反应制备得到的溶胶粒子，微波加热反应适宜条件是微波功率600W，反应温度为90℃、以苯酚为光催化降解研究对象，考察了两种方式制备的负载型TiO2光催化剂的催化性能，实验结果表明微波辐射Sol-Gel法制备的负载型TiO2光催化剂光催化性能也优于常规Sol-Gel法制备的负载型TiO2光催化剂。     

石墨烯杂化钛酸管复合光催化剂的制备与表征

以化学法还原的石墨烯和纳米TiO2为原料,采用水热法制备出一系列具有良好可见光活性的石墨烯 钛酸管复合光催化剂,并研究石墨烯含量和水热温度对其光催化性能的影响.结果表明：当石墨烯质量分数为5%时,复合光催化剂的催化活性最佳;采用较低水热温度制备出的复合光催化剂具有更大的比表面积和更优异的催化性能,其比表面积为一般石墨烯 TiO2复合光催化剂的10倍;在可见光照射条件下,其降解罗丹明 B的速率常数可达8.76×10-2 min-1,远高于文献报道的TiO2类光催化剂降解的速率常数;其可见光活性来源于石墨烯的敏化作用.     

Pt/TiO2催化剂上苯的光催化降解

以TiO2、Pt TiO2为光催化剂,光催化降解苯为模型反应,比较了两者的光催化活性,并利用在线气相色谱及原位红外考察了反应中间物及产物分布.结果表明铂的负载有利于反应中间产物的进一步降解,从而提高光催化降解效率.     

高活性光催化剂TiO2粉体的制备条件研究

以钛酸四异丙酯为前驱体，采用溶胶-凝胶法和超声波照射法制备了高活性TiO2粉体光催化剂．考察了超声处理、冰乙酸用量、异丙醇用量、陈化时间等对TiO2粉体的光催化活性的影响．染料活性艳红（X-3B）的降解实验表明：钛酸四异丙酯在超声波照射下、在纯水中水解、冰乙酸用量为10ml、陈化36h制得的TiO2粉体的光催化活性最高，比商品P25TiO2光催化剂的活性高1．4倍．     

铁掺杂纳米TiO2的可见光催化性能

为了提高纳米TiO2催化剂的光催化氧化性能,采用溶胶-凝胶法,以酞酸丁酯为原料制备铁掺杂纳米TiO2光催化剂(Fe-TiO2).分别采用X射线衍射和紫外-可见光漫反射对其晶相和光催化活性进行表征.以偶氮结构的弱酸性染料溶液为目标降解物,研究在可见光照射下Fe-TiO2的光催化性能.结果表明,Fe-TiO2光催化剂的晶相为单一锐钛矿相,粒径为17.7nm;吸收边带红移至500nm,禁带宽度减小到2.48eV.在可见光下光催化反应180min,Fe-TiO2光催化剂对弱酸性染料的降解率达99.86%.     

钒氮共掺杂TiO2降解亚甲基蓝影响因素的研究

用溶胶-凝胶法制备钒氮共掺杂TiO2光催化剂,以亚甲基蓝的降解率为评价指标,考察钒氮共掺杂TiO2光催化降解亚甲基蓝的影响因素.结果表明,钒氮共掺杂能显著提高TiO2的光催化活性;在本实验条件下,钒氮添加量(与Ti的摩尔比)分别为0.1%、10%的TiO2于600℃焙烧、投入量为3g/L、溶液pH值为4~7、超声振荡30min、光照催化氧化处理4h的条件对处理低浓度亚甲基蓝溶液效果最好.     

Ag/TiO2光催化剂的表面性能表征

采用光催化还原法将 Ag沉积于 Ti O2 膜表面制备出负载型 Ag/Ti O2 光催化剂 ,通过 SEM、EDS检测出 Ti O2 表面上 A g元素的存在 ,由 TEM显示 Ag颗粒分散的均匀性 ,XPS图谱证实了 Ag是按光催化还原反应机理以单质形式存在 ,对低浓度甲基橙溶液光催化降解结果表明 ,沉积的单质 Ag对 Ti O2 光催化剂的降解活性有很大的提高作用。     

Photocatalytic oxidation of gaseous benzene over nanosized TiO2 prepared by solvothermal method

Nanosized TiO2 particles were prepared by solvothermal method using tetrabutyl titanate as precursor,ethanol and water as solvents,and a facile immobilization method of nanosized TiO2 particles on woven glass fabric was developed. The samples obtained under various preparation conditions were charac-terized by means of thermo gravimetric analysis(TG) and differential scanning calorimetry(DSC) ,X-ray diffraction(XRD) ,transmission electron microscopy(TEM) ,high resolution-transmission electron mi-croscopy(HR-TEM) ,and Brunauer-Emmett-Teller(BET) . The results show that the cube-shape of TiO2 prepared by solvothermal method has good crystallinity of(101) surface,higher thermal stability and large specific surface area. Scanning electron microscopy(SEM) images confirmed that the immobi-lized TiO2 film was uniformly distributed and clung to the substrate firmly. The photocatalytic activity of the catalysts was tested using photocatalytic oxidation of gaseous benzene. The results show that the TiO2 calcined after solvothermal treatment suffers from lower specific surface area,and hence de-creases its photocatalytic activity. The photocatalytic activities of the TiO2 by solvothermal treatment with or without calcination in degradation 400 mg/m3 benzene are 3.7 and 4.1 times as high as catalyst without solvothermal treatment,respectively.     

双N源合成N-TiO_2可见光催化剂及其性能研究

以氨水和草酸铵为双N源,用原位沉淀技术制备了高活性N修饰TiO2可见光催化剂.通过N2吸脱附等温线、XRD、UV-Vis、XPS和IR波谱等技术对催化剂结构和光谱性质进行了系统表征.同时以亚甲基蓝水溶液的可见光降解为模型反应对催化剂的活性进行了评价.结果表明:由双N源合成的N-TiO2催化剂,氨水和草酸铵的协同作用有利于N进入TiO2晶格,其活性要高于单N源及后修饰的N-TiO2催化剂.     

CNTs/TiO_2复合物的水热法合成及其光催化性能

利用水热法制备了高活性碳纳米管(CNTs)/Ti O2光催化剂,采用XRD,IR,SEM和UV等手段表征了其结构及表面组成,并以偶氮类染料EBPV为目标物评价了该催化剂在可见光下的光催化效果。结果表明:CNTs/Ti O2复合物为锐钛矿型,粒子为球状和类球状;与Ti O2相比,CNTs/Ti O2复合物吸收峰移至可见光区;在实验条件下其对目标物的可见光催化降解效率达95%以上。实验表明,在水溶液中EBPV的光催化降解过程服从准一级动力学方程。9次循环利用后,CNTs/Ti O2复合物的光催化活性降低了5%。     

Eu~(3+)/TiO_2光催化剂降解罗丹明B

采用溶胶-凝胶法合成了不同Eu3+掺杂量、不同煅烧温度的Eu3+/TiO2的光催化剂,利用XRD和FT-IR对样品进行表征和分析.以罗丹明B为目标降解物,对所制样品光活性进行了研究;同时,考察了助催化剂对其光催化性能的影响.结果表明,稀土Eu3+的掺杂能细化晶粒,在500℃下煅烧,Eu3+/TiO2摩尔数比为0.05%的催化剂,加入5 mL助催化剂,三基色节能灯照射3 h,降解率可达91.8%.     

Photocatalytic degradation of benzene in gas phase by nanostructured BiPO4 catalysts

A rod-shaped BiPO4 photocatalyst was prepared by a simple hydrothermal method for light-induced catalytic degradation of stable aromatic compounds such as benzene in gas phase under ambient conditions. The samples were subjected to various technical characterizations including X-ray diffraction (XRD), transmission electron microscopy (TEM), UV/vis and FTIR spectrum, to determine the crystal structure, morphology, and optical properties of the as-prepared photocatalysts. Results indicate that BiPO4 exhibits much higher photocatalytic activity and stability under UV light irradiation than that of commercial TiO2 (Degussa P25) in the degradation of benzene to CO2. The active radical species involved in the degradation reactions over BiPO4 photocatalyst have been investigated by the spin-trapping electron paramagnetic resonance (EPR) spectra and a photoluminescence technique. Theoretical calculations reveal that BiPO4 contains highly-dispersive conduction bands, enabling high mobility of the photo-generated carries and therefore leading to fast charge transfer and separation.     

溶胶-凝胶法制备纳米TiO2/云母及光催化性能研究

文章以钛酸四丁酯为钛源,采用溶胶-凝胶法制备了云母负载纳米TiO2光催化剂(TiO2/M),通过XRD、SEM、UV等手段对所制备的催化剂进行表征,并以甲基橙为模拟污染物检测其光催化活性;讨论了催化剂焙烧温度、光催化剂添加量及重复次数对光降解甲基橙活性的影响.结果表明,在焙烧温度为400～700℃时,纳米TiO2物相为...