聚乳酸/乙烯-乙酸乙烯共聚物的共混工艺及力学性能

分别以乙烯-丙烯酸甲酯-甲基丙烯酸缩水甘油酯(E-MA-GMA)各马来酸酐接枝乙烯-乙酸乙烯酯(EVA-MAID作为增容剂,采用熔融共混的方法制备了聚乳酸(PLA)/乙烯-乙酸乙烯共聚物(EVA)/增容剂三元共混物.力学分析和扫描电镜结果表明,E-MA-GMA对PLA/EVA共混物有更好的增客效果,PLA/EVA/E-MA-GMA共混物比例为90/10/5时缺口冲击强度曩高,为最佳共混组分比例.     

增容剂mPOE含量对R-PET/LLDPE共混物结构与性能的影响

采用反应挤出加工工艺,以甲基丙烯酸环氧丙酯接枝改性乙烯-辛烯共聚物(mPOE)为增容剂,对回收聚对苯二甲酸乙二醇酯(R-PET)与线性密度聚乙烯(LLDPE)共混物进行增容增韧改性,考察了增容剂mPOE用量对R-PET/LLDPE/mPOE共混物的相结构、力学性能以及熔融、结晶行为的影响.扫描电镜(SEM)结果表明:R-PET/LLDPE/mPOE共混物中分散相的粒径和粒间距随着mPOE含量的增加而迅速减小; 而当增容剂的添加质量分数大于5%后,分散相粒径大小与粒间距的变化趋于减小.力学性能测试表明:R-PET/LLDPE/mPOE共混物的断裂伸长率和缺口冲击强度随着mPOE含量的增大先迅速增大,后变化趋缓.DSC结果表明:R-PET/LLDPE/mPOE共混物随着mPOE含量的增加,分散相粒子对R-PET结晶的成核效果降低.     

聚醚醚酮/聚酯液晶二元和三元增容共混体系的等温结晶动力学及结晶形态

采取熔融共混方法制备了聚醚醚酮（PEEK）和聚酯液晶（TLCP）二元和三元增容共混物， 用DSC和PLM对 共混物的结晶行为和结晶形态进行了研究. 结果表明， TLCP的存在使PEEK的结晶温度和结晶起始温度均略有升高， 增容剂（RCP）的加入延缓了PEEK结晶过程. 等温结晶动力学研究表明， 液晶的加入加快了聚醚醚酮的结晶速度， 但随其含量增加结晶速度降低. 与二元共混物相比， 加入增容剂后对聚醚醚酮的结晶速度基本无影响. 增容后的聚醚醚酮球晶的尺寸下降， 很难看到Maltese十字消光.     

DSC对PVC／LLDPE共混体系相容性的研究

用示差扫描量热仪对聚氯乙烯／线型低密度聚乙烯共混体系的相容性进行了研究，发现氢化后的聚丁二烯－ｂ－甲基丙烯酸甲酯共聚物在共混体系中可以起到很好的增容作用。共聚物增容剂使ＰＶＣ的玻璃化转变温度区域加宽，同时降低了ＬＬＤＰＥ组分的熔融热。共混体系中ＬＬＤＰＥ结晶动力学的测定结果表明，增容剂阻碍了ＬＬＤＰＥ相的结晶，使其结晶速度下降。动力学结果还表明，ＬＬＤＰＥ中不同结构的晶型分别按不同的Ａｖｒａｍｉ方     

聚苯乙烯与聚烯烃共混物的增容研究进展

聚苯乙烯（PS）作为四大通用塑料之一,在生产和生活中有十分广泛的用途,采用与聚烯烃（PO）共混是最常用来改善其韧性的方法。为了改善PS与PO之间的相容性,必须对PS/PO共混物进行增容改性。在各种增容方法中,添加增容剂是对不相容PS/聚烯烃共混物进行增容改性最常用的方法。本文综述了常见的非反应性增容和反应性增容方法。     

聚醚砜与聚碳酸酯增容共混物及性能

以双酚-S-型聚芳酯为增容剂,对聚醚砜/聚碳酸酯（PES/PC）共混体系的形态结构及力学性能进行了研究,结果表明,双酚-S型聚芳酯可有效地增加两相间的界面黏结性,显著降低PES/PC共混物中PC分散区的尺寸,改善两组分间的相容性.SEM分析表明,增容剂的加入,使共混体系形成双连续相的互锁结构,这种结构有利于提高共混体系的力学性能.     

增容PP/回收PET共混物的非等温结晶和熔融行为研究

双螺杆挤出机制备了相容剂PP-g-MA或PP-g-GMA增容PP/回收PET(r-PET)(质量比为80/20)共混物,DSC研究了相容剂含量、熔融温度与时间以及降温速率对共混物非等温结晶与熔融行为的影响。加入PP-g-MA或PP-g-GMA对PP结晶温度影响不明显或使其有所降低,与相容剂种类及其用量有关。PP-g-MA增容共混物中r-PET熔点比PP-g-GMA增容的低,表明相容剂PP-g-MA与共混物中r-PET的作用比PP-g-GMA的明显。熔融温度提高,共混物中PP结晶和熔点降低,r-PET熔融峰形和熔点取决于熔融温度。     

PVC/低熔点尼龙6共混物力学性能的研究

采用(苯乙烯/马来酸酐)无规共聚物(R-SMA)为增容剂制备低熔点尼龙6(uPA6)与PVC共混材料,研究了SMA和uPA6的加入量对PVC/uPA6共混物力学性能的影响。结果表明,SMA是PVC/uPA6体系的有效增容剂,SMA的加入能使uPA6在PVC中的分散相尺寸降低,大幅度提高PVC/uPA6的力学性能。     

CPE／P（AA-HEMA）吸水膨胀弹性体力学性能的研究

采用机械共混将氯化聚乙烯（CPE）与自制的吸水树脂丙烯酸-甲基丙烯酸-β羟乙酯共聚物[P（AA-HEMA）]共混,并讨论了吸水树脂以及增容剂对共混试样的力学性能的影响,研究表明简单共混时随吸水树脂量增大,共混试样的力学性能降低,CPE-g-HEMA的加入改善了试样的力学性能;但当其用量过饱和后,共混体系的反而力学性能下降,以加入3phr的CPE-g-HEMA的增容效果最为明显。     

PC—g—PS增容PPO／PET共混体系的研究

研究了聚苯醚／聚对苯二甲酸乙二醇酯共混体系的热行为，相形态及拉伸行为，结果表明，ＰＰＯ／ＰＥＴ共混物是一个高度不相容的体系，体系中存在分散相相区尺寸很大的两相结构，其宏观力学性能呈特征的脆性断裂，加了聚碳酸酯、聚苯乙烯的辐射接枝共聚物ＰＣ－ｇ－ＰＳ以作为增容剂后，共混物的相容性明显改善，分散相相区尺寸减小，共混物的拉伸行为呈韧性断裂。     

EVA增容PVC／SBS共混体系的研究

本文通过冲击实验，拉伸实验，动态力学分析及扫描电镜的观察，研究了ＥＶＡ增容的ＰＶＣ／ＳＢＳ共混体系的形态结构的关系。研究结果表明，ＥＶＡ对ＰＶＣ／ＳＢＳ有良好的增容作用，并且与ＳＢＳ一起对ＰＶＣ有协同增韧效果。     

PVC／NBR／SBS三元共混物的形态结构与性能

本文通过冲击试验、动态力学分析（ＭＭＡ）、透射电镜（ＴＥＭ）和扫描电镜（ＳＥＭ）观察，研究了聚氯乙烯／丁腈橡胶／苯乙烯。丁二烯。苯乙烯嵌段共聚物（ＰＶＣ／ＮＢＲ／ＳＢＳ）三元共混物的形态结构和性能，并且讨论了两者之间的关系。ＮＢＲ－２９对ＰＶＣ和ＳＢＳ有较好的增容作用，与ＳＢＳ一起对ＰＶＣ有协同增韧效应。     

尼龙6/乙烯-1-辛烯共聚物接枝马来酸酐共混体系的亚微相态与性能

采用熔融挤出法制备了ＰＡ６／ＰＯＥ和ＰＡ６／ＰＯＥｇＭＡＨ共混合金,借助于力学试验机、ＴＥＭ、ＳＥＭ、Ｍｏｌａｕ实验和毛细管流变仪测定了共混合金的力学性能、亚微相态、冲击断口形貌和流变性能,系统地研究了ＰＯＥｇＭＡＨ对ＰＡ６的增容增韧作用。结果表明,ＰＯＥ与ＰＡ６是不相容体系,经ＭＡＨ接枝改性后的ＰＯＥ与ＰＡ６发生化学反应,生成的ＰＯＥｇＰＡ６共聚物起到了原位增容作用,细化了分散相尺寸,有效地改善了合金的力学性能,ＰＡ６／ＰＯＥｇＭＡＨ共混合金的缺口冲击强度是ＰＡ６的１２倍。     

STUDIES ON THE COMPATIBILITY OF PPO MULTI-COMPONENT BLENDS

The compatibility and phase morphology of poly (phenylcne oxide) (PPO) multi-componenet blends with poly (ethylene terephthalate) (PET) and polystyrene (PS) were studied using differentialscanning calorimetry (DSC), dynamic mechanical analysis (DMA) and scanning electron microsopy (SEM) methods. The effect of glycidyl methacrylate-styrene copolymer (GMS), as a compatibilizer, on the morphology of the PPO blends has also been studied in detail. The influence of the moiecular weight of PET and the synergetic effect of the compatibilizers of GMS and phenoxy on the morphology were examined. The DSC and DMA results show that there are two distinct glass transitions correspondinig to PET and PPO existed, however, the Tg of PPO shifts toward lower temperature region due to the addition of GMS and PS. The SEM results reveal that PET component is as dispersed phases in the PPO matrix, part of which is located at the interfaces due to the interaction with GMS while PS is miscible in the PPO matrix. A significant     

不同增容剂对动态固化PP/EPDM/EP 共混物结构与性能的影响

将动态硫化技术应用于环氧树脂(EP)增强聚丙烯(PP)/三元乙丙橡胶(EPDM)体系中,研究了不同增容剂对动态固化共混物结构与性能的影响.实验结果表明,马来酸酐接枝PP(PP-g-MAH)增容的动态固化PP/EPDM/EP共混物是三相结构,即EPDM分散相、EP颗粒分散相和PP连续相.共混物具有较高的拉伸强度和弯曲模量,冲击强度变化不大.马来酸酐接枝EPDM(EPDM-g-MAH)增容的动态固化共混物是“核-壳”复合分散相和PP连续相结构,其中EP颗粒为核,外面包覆着EPDM-g-MAH和EPDM.这种“核-壳”结构变相地提高了EPDM橡胶的体积分数,使得共混物具有较高的冲击强度,同时保持一定的强度和模量.     

超支化聚(酰胺-酯)/聚丙烯/聚氯乙烯共混体系的相容性研究

用扫描电子显微镜(SEM),X射线能谱仪(EDS)对聚丙烯/聚氯乙烯(m(PP):m(PVC)=80:20)二元体系和超支化聚(酰胺-酯)/聚丙烯/聚氯乙烯(HBP/PP/PVC)三元体系的相容性进行了研究.通过X射线能谱微区分析得到了共混物中氯元素面分布图,对氯元素面分布进行了粒径分布统计和平均粒径计算.实验结果表明:在PP/PVC(质量比为80:20)共混物中加入3份HBP,增容的效果最好;当HBP达到4份时, PP/PVC(质量比为80:20)的相容性反而降低.     

ACS树脂改性PVC的研究

将丙烯腈(AN)、苯乙烯(St)在氯化聚乙烯(CPE)存在下进行悬浮接枝共聚,获得了ACS树脂.研究了不同用量ACS树脂对PVC流变行为、力学性能、热性能的影响,用SEM观察其拉伸断面.结果表明,ACS树脂的加入改善了PVC的流动性,其效果比抗冲型ACR好.当ACS加入量为25%时,抗冲强度可提高2～3倍,而抗拉强度变化不大,同时热性能也有所提高.     

提高聚氯乙烯与丁苯橡胶共混相容性的研究

通过加入各种增容剂（Ｃｏｍｐａｔｉｂｉｌｉｚｅｒ）和采用粉末丁苯橡胶（ＰＳＢＲ）及经接枝、交联改性的粉末丁苯橡胶（ＰＭＳＢＲ），研究了提高聚氯乙烯／丁苯橡胶（ＰＶＣ／ＳＢＲ）共混相容性的途径。物理机械性能测试结果表明：五种增容剂对软质ＰＶＣ／ＳＢＲ共混物的改性效果以粉末丁腈Ｐ８３和丁腈－２６（ＮＢＲ－２６）最佳；粉末橡胶对ＰＶＣ的改性效果优于块状橡胶，ＰＭＳＢＲ对软质ＰＶＣ的改性效果优于以ＮＢＲ－２６作增容剂的块状ＳＢＲ和ＰＳＢＲ；用不同改性方法制得的四种ＰＭＳＢＲ中，以多层乳液接枝改性的ＰＭＳＢＲ－４对ＰＶＣ的改性效果最佳，用它改性硬质ＰＶＣ的缺口抗冲击强度和软质ＰＶＣ的耐寒性，效果皆超过粉末丁腈Ｐ８３。扫描电镜、透射电镜和动态力学谱分析表明：ＰＶＣ／ＰＭＳＢＲ－４共混材料呈良好的韧性断裂，橡胶粒子分散较均匀，相界面模糊，低温Ｔｇ升高，说明ＰＶＣ／ＳＢＲ的相容性获得显著提高     

增容对回收PET/PP共混物的结晶与熔融行为的影响

制备了不同相容剂增容回收PET/PP共混物,用DSC方法研究了相容剂对r-PET结晶与熔融行为的影响,r-PET对PP结晶与熔融行为的影响和相容剂对r-PET/PP共混物结晶与熔融行为的影响,观察到PP结晶温度随着r-PET含量增加而提高,r-PET结晶温度随着PP含量增加而降低,相容剂加入明显降低共混物中r-PET结晶温度,但不同相容剂对共混物中r-PET结晶与熔融行为影响不大,共混物中PP结晶性能与相容剂的大分子链有关。     

PVC/超支化聚(胺-酯)共混物的冲击与流变性能研究

研究了超支化聚(胺-酯)的代数和用量对PVC/超支化聚(胺-酯)共混体系冲击性能和流变性能的影响,利用扫描电镜对共混体系的冲击断面形态结构进行分析.结果表明:超支化聚(胺-酯)的代数和用量均对共混体系的冲击强度有影响,当加入质量分数为5%的第3代超支化聚(胺-酯)时,共混体系的冲击强度达到42.5 kJ/m2,加入超支化聚(胺-酯)能有效降低共混体系的粘度,并且随着超支化聚(胺-酯)加入量的增多,共混体系流动行为逐渐向牛顿型流体转变,使得PVC的加工可以在较低的温度下进行,从而避免高温引起PVC降解.