Cu-45% Ni合金基带强立方织构的形成研究

采用X射线四环衍射技术研究了大应变量冷轧Cu-45%Ni(原子百分含量)合金基带冷轧织构的形成、低温回复以及再结晶过程中织构的演变行为。结果表明:Cu-45%Ni合金经大应变量冷轧后形成以S取向、Copper取向和Brass取向含量为主的Copper型轧制织构;在低温回复过程,仍为Copper型轧制织构,并且其轧制织构的强度有所增强;在再结晶过程,立方取向的含量迅速增加,各轧制取向含量均迅速减少,表明S取向、Copper取向和Brass取向在再结晶过程中均被逐渐长大的立方晶粒所吞并。在此基础上,采用背散射电子衍射技术表征其高温下强立方织构的形成过程,Cu-45%Ni合金基带经1 000℃保温1h后,其立方织构含量高达98.6%(10°),大角度晶界的含量仅为13.6%,其中包含约5%的Σ3晶界。     

Cu-45%Ni合金基带强立方织构的形成研究简

采用X射线四环衍射技术研究了大应变量冷轧Cu-45％Ni （原子百分含量）合金基带冷轧织构的形成、低温回复以及再结晶过程中织构的演变行为。结果表明：Cu-45％Ni合金经大应变量冷轧后形成以S取向、Copper取向和Brass取向含量为主的Copper型轧制织构;在低温回复过程,仍为Copper型轧制织构,并且其轧制织构的强度有所增强;在再结晶过程,立方取向的含量迅速增加,各轧制取向含量均迅速减少,表明S取向、Copper取向和Brass取向在再结晶过程中均被逐渐长大的立方晶粒所吞并。在此基础上,采用背散射电子衍射技术表征其高温下强立方织构的形成过程,Cu-45％Ni合金基带经1000℃保温1 h后,其立方织构含量高达98．6％（＜10°）,大角度晶界的含量仅为13．6％,其中包含约5％的Σ3晶界。     

3004铝合金在轧制及退火过程中织构的演变

应用取向分布函数(ODF)研究和分析了热轧、冷轧及退火对3004铝合金织构的影响·结果表明,热轧后织构类型为(100)[uvw],且(100)[011]旋转立方织构为最强;在冷轧过程中,所有样品的冷轧织构表现为典型的铜式织构特征,随形变量的增加,织构由弱到强,最后稳定在铜织构、黄铜织构和S织构3个织构组分;冷轧样品退火后,退火织构主要由立方织构、退火R/S织构和铜织构组成,其中在300℃和400℃的退火样品中存在强度较高的再结晶立方织构{001}〈100〉,100℃和200℃的退火样品中再结晶立方织构{001}〈1...     

不同取向条件下Al-Mg-Sc合金薄板的组织与性能

采用室温拉伸性能测试、金相组织观察、透射电子显微分析以及取向分布函数(ODF)测定研究冷轧态、冷轧-退火态Al-Mg-Sc合金(俄罗斯牌号01570)薄板在不同取向条件下的显微组织和力学性能.研究结果表明:合金薄板在横向、纵向和与纵向成30°方向的强度比45°和60°方向上的强度高,横向力学性能优于纵向力学性能,在45°方向的屈服强度最低,伸长率最高;冷轧态铝合金薄板具有明显的Brass织构{110}<112>,Copper织构{112}<111>和S织构{123} <634>,经350℃退火1h后板材的织构组态变化不大.合金板材中弥散析出的Al3(Sc,Zr)粒子会促进{011}<112>变形织构的形成与稳定,阻止立方织构{100}<001>的形成;不同取向条件下Al-Mg-Mn-Sc-Zr合金薄板的平面各向异性与合金的晶粒结构及晶体学织构密切相关.     

5052铝合金轧制织构演变的定量分析

采用X射线衍射仪研究了5052铝合金在冷轧过程中织构的演变规律,建立了织构体积分数与轧制真应变的数学关系式。结果表明,在冷轧过程中初始的cube织构逐渐转化为纤维轧制织构,随冷轧压下量的增加,cube、r-cube、remainder和r-Goss组分的体积分数减少,而纤维组分的体积分数增加;织构体积分数与轧制真应变的数学关系式能很好地模拟铝合金轧制过程中织构的演变;分析了轧制过程中不同织构组分的演变速率,发现随轧制真应变的增加,纤维组分的形成速率先增加而后降低。     

异步轧制对高压电解电容器用铝箔织构的影响

利用异步轧制技术对高压电解电容器用高纯铝进行冷轧,研究了异步轧制参数对铝箔冷轧织构的影响.结果表明:异步轧制的搓轧区效应,可使铝箔形成不同于同步轧制的6种主要织构的含量与分布.慢辊侧的织构总体含量高于快辊侧总体含量;S{123}(634)织构、C{112}(111)织构的变化趋势相同,立方织构{001}(100)、旋转...     

异步轧制无取向硅钢的再结晶织构演变

在无取向硅钢冷轧过程中采用同步轧制和速比为1.06,1.125,1.19的异步轧制,以考察异步轧制对冷轧和再结晶织构的影响.研究发现,异步轧制减弱冷轧织构中{001}～{112}〈110〉组分,增强{111}〈112〉并减弱{111}〈110〉组分.{111}〈112〉和{111}～{225}〈110〉形变晶粒内剪切带处分别形成η(〈001〉∥RD)及偏离其15°的η′(Ψ=75°,θ=0～45°,φ=0°)再结晶晶粒,η′因晶核尺寸优势发展成为主要织构组分.异步轧制下形变织构的变化有利于改善再结晶织构特征及性能,其影响随速比增大而增强.     

异步轧制对IF钢冷轧及再结晶织构的影响

研究了异步轧制对IF钢的冷轧及再结晶织构的影响,并且将模拟的剪切应变随辊速比的变化规律应用到以Taylor模型为基础的织构模拟中,分析了剪切应变εxz值对形变织构的影响.结果表明:随着异步轧制速比的增加,冷轧的α纤维织构组分逐渐减少,γ纤维织构组分稍有增加.异步轧制时,附加的切应变是造成这种变化的主要原因;{111}〈uvw〉再结晶晶核的形成与{001}〈110〉织构组分无关.异步轧再结晶{111}〈112〉织构组分体积分数明显多于同步轧,这是由于在冷变形状态下,{111}〈112〉织构组分就明显高于同步轧制条件.     

3%Si无取向硅钢异步轧制织构的演变

对无取向硅钢常化态板材经过异步轧制,轧制速比为1.06,经过一次冷轧到0.5 mm厚,压下率为77.3%,并在保护气氛下进行再结晶退火,考察了异步冷轧织构和再结晶织构形成及演变.常化态板材的初始织构组分以{110}和{113}织构为主,异步冷轧织构主要是由α织构和γ织构组成,快慢辊侧的织构类型没有变化,但慢辊侧α织构和γ织构的取向密度明显高于快辊侧;再结晶退火后α织构取向密度明显减弱,而γ织构的变化主要是{111}〈110〉织构组分的取向密度减弱,{111}〈112〉织构组分的取向密度加强.     

高纯电子铝箔立方织构形成的微观过程

采用EBSD微取向分析方法,通过分析高纯铝箔冷轧后退火的再结晶初期立方取向晶核的形成过程及立方取向晶粒的长大行为,探讨了高纯铝箔中立方织构形成的微观过程.结果表明,在高纯铝箔轧制基体上没有发现立方取向{001}<100>的晶核优先形成,但是再结晶完成以后却会出现较强的立方织构,因此高纯铝箔立方织构的形成主要是借助于立方取向晶粒的取向生长机制实现的.立方取向晶核容易在S取向{123}<634>的形变晶粒之间产生.     

Mechanism of surface texture evolution in pure copper strips subjected to double rolling

Developing ultra-thin copper foils with different surface roughness and microstructure has important significance for improving the service performance and reducing the production cost of high-end circuit boards. In this paper,pure copper strips with initial cube texture were subjected to a double rolling process(deformation amount ranges from 50% to 95%),and the surface textures evolution law and mechanism of doublerolled strips were studied by an X-ray diffraction technique. The results show that when a deformation amount increased from 50% to 70%,the grains of two surfaces rotate away from the cube orientation,and the formed textures of two surfaces mainly consisted of C,S and B orientation components. The orientation density values for these three components on bright surface only had slight difference; the orientation density values for C and S components were much larger than that for B components on a matt surface. When the deformation amount increased to 90%,the increase extents of orientation density values for C and S components were obviously larger than that for B components on a bright surface; the increase extents of orientation density values for these three components were almost the same on the matt surface. It has been found that when deformation amount reaches 95%,the grains orientation of bright surface were relatively concentrated,and the orientation density value for C texture obviously increased to 11.68 and that for B texture was only 3.15; the grains orientation of matt surface were relatively dispersed,and the orientation density value for C texture increased to 9.26 and that for B texture obviously increased to 6.35,and the density values of these two textures had less difference. For the condition of strong compressive and shear stress on the bright surface,grains were mainly rotating to C texture orientation; compared with the bright surface,"semi-free" deformation condition on the matt surface is beneficial to promote much more grains to rotate to the B texture orientation.     

Cu对高压电解电容器阳极铝箔再结晶织构的影响

采用织构定量检测等方法研究了铜元素对高压电解电容器阳极铝箔立方织构的影响, 讨论了相关的影响原理.结果表明, 微量铜元素的变化会改变其在位错附近的偏聚状态, 进而影响轧制铝箔的塑性变形过程和取向分布状态, 因此铜元素会影响其再结晶行为和退火铝箔的立方织构量.较低的铜含量和较高的晶粒长大温度有利于立方织构占有率的提高.     

二步冷轧对铁素体不锈钢深冲性能和织构的影响

比较了一步冷轧和二步冷轧对铁素体不锈钢深冲性能和织构的影响.结果显示,采用一步冷轧(冷轧压下率90%)后,获得了高的平均r值(rm=1.92),且45°方向的r值要大于轧向和横向的r值,导致了材料的Δr呈负值(Δr=-0.31);在总压下率一定的情况下,采用二步冷轧后,薄板的平均r值变化不大(rm=1.90),但材料的平面各向异性很小(Δr=0.14).对两种工艺的再结晶织构分析表明,一步冷轧后薄板生成了强烈的γ织构,但是织构的峰值明显偏离了{111}轴,位于{223}〈582〉处;二步冷轧后薄板则生成了均匀的γ再结晶织构.     

微观组织和织构对H65黄铜带材折弯性能的影响

电子产品关键部件小型化对黄铜合金带材折弯性能提出了更高的要求。研究了微观组织和织构对H65黄铜带材折弯性能的影响规律和影响机制。结果表明：带材平行于轧向折弯较垂直于轧向折弯更易于产生表面褶皱和裂纹,且随着折弯半径的减小,折弯性能降低。折弯变形过程中带材外表面易形成剪切带,所产生的剪切变形是造成表面褶皱和开裂的主要原因。微观组织不均匀、较强的Brass织构易导致带材折弯过程中产生剪切变形,造成带材折弯性能下降。通过调控热处理工艺来调整带材织构,减少或抑制剪切带的产生,能够提升带材的折弯性能。     

工业纯钛板材冷轧及退火微观组织和织构演变规律

采用先进电子背散射衍射（EBSD）技术,深入研究了冷轧工艺变化和道次间退火处理对工业纯钛板材微观组织和织构演变的影响规律。通过对比不同一次冷轧变形量样品经退火和二次冷轧加工后的EBSD取向分布图、取向差角分布图和极图得知,一次冷轧产生的孪晶对退火再结晶晶粒尺寸及晶粒取向（织构）产生重要的影响,进而又影响二次冷轧的变形组织和织构特征,使二次冷轧变形孪晶的生成受到一定程度的抑制,孪晶分数随着轧制变形量的提高呈现先升高后降低的规律,同时会降低二次冷轧组织中{0001}基面织构组分。     

Influence of intermediate annealing on the microstructure and texture of Ni-9.3at%W substrates

The effects of intermediate annealing (IA) on the microstructure and texture of Ni-9.3at%W substrates have been investigated by using electron backscattering diffraction and X-ray diffraction. Results suggest that IA can optimize the homogeneity of deformation microstructure. Higher IA temperatures (without undergoing recrystallization during IA) will increase the copper-type components of deformation texture and improve the content of cube texture after recrystallization. Sharp cube texture (97.2%) can be obtained at the optimum IA temperature of 650℃. The mechanism underlying the transition of deformation texture can be interpreted as that IA increases the dislocation slipping ability and suppresses the twinning deformation of Copper orientation in the subsequent rolling process. The observed strengthening of cube texture as a result of IA treatment is presumably attributed to the reduction of noncube nucleation and the optimization of preferential growth surrounding the cube nuclei.     

异步轧制下无取向硅钢的冷轧织构

研究了同步和异步轧制下无取向硅钢的冷轧织构及其沿层厚的分布特征.不同轧制方式下冷轧织构均主要由以{001}〈110〉为强点的α织构和强度相对较弱的γ织构组成,但异步轧制显著影响冷轧织构强度及其沿层厚的分布.异步轧制对表层和中间层织构强度的影响较1/4层大;异步轧制总体上减少α和γ织构,但增加{111}〈112〉组分.这表明冷轧过程引入异步轧制可为无取向硅钢的织构控制与优化开辟新的途径.     

超纯铁素体不锈钢的组织、织构及深拉伸性能

重点研究了冷轧压下率对冷轧、再结晶织构的影响.结果表明:当终轧温度为750℃时,热轧带退火后以{111}再结晶织构为主.随着冷轧压下量的增加,γ织构减弱,α织构增强,{111}再结晶织构明显增强.当冷轧压下率为84%时,{111}再结晶组分的体积分数达到64.5%,退火板的平均塑性应变比(-R)高达1.69,平面各向异性(ΔR)仅为-0.17,深拉伸性能优良.