高品质GCr15轴承钢二次精炼过程中夹杂物的演变规律

采用FE-SEM/EDS研究了转炉流程生产的GCr15轴承钢LF、RH精炼过程中夹杂物的演变规律,分析了其演变机理。结果表明:钢中复合夹杂物的演变规律可归纳为:Al2O3→MgO·Al2O3→(CaO-MgO-Al2O3-(CaS))复合氧化物夹杂和Al2O3→(Al2O3-MnS)→(Al2O3-MnS-Ti(C,N))复合氧硫碳氮物夹杂2种方式。LF精炼过程脱硫作用明显,钢中的硫化物夹杂数量大幅减少。LF精炼初期钢中主要是MnS、Al2O3、TiN的单相夹杂物。LF精炼结束后钢中的夹杂物演变为Al2O3为核心外包氧化物及MnS、TiN、Ti(C,N)、CaS的复合夹杂物。精炼渣中的CaO和耐火材料中的MgO经还原后与钢中溶解氧反应导致LF精炼结束时D类夹杂物增加。RH及软吹处理进一步强化了去除钢中的硫化物,但D类及其与A、T类复合的夹杂物含量增加。在LF阶段,夹杂物尺寸主要集中在1~3μm范围内,到RH阶段,夹杂物尺寸则主要集中分布在小于1μm的粒度范围。最大夹杂物尺寸由10.79μm降到5.68μm,单位面积夹杂个数由372个/mm2降到258个/mm2。RH及软吹处理有效地降低了钢中大于3μm的夹杂物。     

Cleaning IF molten steel with dispersed in-situ heterophases induced by the composite sphere explosive reaction in RH ladles

A novel fine inclusion removal technology was put forward with dispersed in-situ heterophases induced by the composite sphere explosive reaction. A composite sphere with this function was designed and prepared using a laboratory scale batch-type balling disc (at 12 r/min), and the composite sphere was fed at the end of the RH refining process. The results indicate that inclusions in the IF molten steel can be removed effectively by feeding composite spheres in RH ladle. Compared with conventional inclusion removal technology, using this novel technology, the amount of oxide inclusions can be decreased to a lower level and the inclusion size becomes finer, the total oxygen content in the as-cast slab can approach 5×10?6, and the cost per ton of steel produced can be reduced by 5-12 Yuan RMB.     

Variation and optimization of acid-dissolved aluminum content in stainless steel

As a key step in secondary refining, the deoxidation process in clean stainless steel production is widely researched by many scholars. In this study, vacuum oxygen decarburization (VOD) deoxidation refining in a 40-t electric arc furnace + VOD + ingot casting process was analyzed and optimized on the basis of Al deoxidation of stainless steel and thermodynamic equilibrium reactions between the slag and steel. Under good stirring conditions in VOD, the deoxidation reaction reaches equilibrium rapidly, and the oxygen activity in the bulk steel is controlled by the slag composition and Al content. A basicity of 3–5 and an Al content greater than 0.015wt% in the melt resulted in an oxygen content less than 0.0006wt%. In addition, the dissolved oxygen content decreased slightly when the Al content in the steel was greater than 0.02wt%. Because of the equilibrium of the Si–O reaction between the slag and steel, the activity of SiO₂ will increase while the Si content increases; thus, the Si content should be lowered to enable the formation of a high-basicity slag. A high-basicity, low-Al₂O₃ slag and an increased Si content will reduce the Al consumption caused by SiO₂ reduction.     

钢液精炼和连铸过程中物理去除夹杂物现状及展望

夹杂物去除是钢液精炼的重要任务之一。目前与去除夹杂物相关的工艺方法主要有:钢包-电磁搅拌和钢包底吹氩;RH及RH侧底复吹;中间包-控流装置、气幕挡墙和通道电磁感应加热;结晶器电磁搅拌与电磁制动和水口吹氩。本文总结了钢水精炼中各个反应器去除夹杂物的方法和机理,并分析了影响夹杂物去除效率的主要因素,为钢水二次精炼的夹杂物去除工艺优化提供理论依据和参考。     

精炼渣碱度对304不锈钢中夹杂物的影响

实验室条件下模拟304不锈钢冶炼中的AOD工位,采用硅铁做终脱氧剂,选择CaO-SiO2-Al2O3-MgO-CaF2五元渣系,考察了精炼渣碱度对304不锈钢中夹杂物的影响.实验中发现,随精炼渣碱度的增大,钢中全氧质量分数降低,夹杂物的总数、总面积和平均半径减小,说明高碱度渣对304不锈钢中的脱氧产物吸附以及对细小夹杂物的生成有利;碱度大于2的精炼渣处理效果明显优于碱度为1.5的实验渣系,建议现场采用碱度大于2的渣系处理钢液.     

VHD过程脱氧制度的研究

为确定电弧炉-VHD 过程的脱氧制度,本文论述了在该工艺过程取样分析的基础上,运用热力学理论,数理统计及计算机数据处理方法,确定出电弧炉粗炼钢液的残铝量与VHD 过程精炼后钢液残铝量,以及终渣成分、精炼时间等工艺参数,因而获得良好的精炼效果。     

RH脱碳过程中极低氧钢水的碳氧反应机理

BOF+LF+RH+CC工艺路线生产IF钢,在RH脱碳前,钢水经脱氧和LF精炼后,钢中自由氧达到极低水平.根据表观脱碳速率常数的不同,这种极低氧钢水的RH脱碳可以划分为四个阶段.与传统三个阶段的RH脱碳不同的是在低速脱碳阶段和快速脱碳阶段存在一个脱碳速率介于两者之间的过渡阶段.在正规溶液模型的基础上,建立了能够准确预报钢液氧含量及顶渣FeO含量的RH脱碳模型.结果表明:在RH吹氧前,极低氧含量的钢液与顶渣之间基本不传氧;吹氧之后,钢液氧含量呈线性增加,当钢液氧势大于顶渣氧势后,钢液向顶渣传氧,渣中FeO含量上升;RH处理结束FeO含量较处理初始有所回升,但是仍处于极低水平,能够有效降低顶渣对钢液的二次氧化.     

Cleaning IF molten steel with dispersed <Emphasis Type="Italic">in-situ</Emphasis> heterophases induced by the composite sphere explosive reaction in RH ladles

A novel fine inclusion removal technology was put forward with dispersed in-situ heterophases induced by the composite sphere explosive reaction. A composite sphere with this function was designed and prepared using a laboratory scale batch-type balling disc (at 12 r/min), and the composite sphere was fed at the end of the RH refining process. The results indicate that inclusions in the IF molten steel can be removed effectively by feeding composite spheres in RH ladle. Compared with conventional inclusion removal technology, using this novel technology, the amount of oxide inclusions can be decreased to a lower level and the inclusion size becomes finer, the total oxygen content in the as-cast slab can approach 5×10⁻⁶, and the cost per ton of steel produced can be reduced by 5–12 Yuan RMB.     

304奥氏体不锈钢夹杂物的冶金行为

根据热力学计算,结合生产过程实际,研究了Si脱氧条件下304奥氏体不锈钢在LF精炼、连铸过程夹杂物的变化规律.结果表明,钢水中主要形成CaO-Al2O3-SiO2类复合夹杂物,钢水中Al含量随Si含量的降低逐渐减小.当精炼渣碱度R=1.5时,随精炼、连铸过程的进行,复合夹杂物中Al2O3含量逐渐减少,CaO,SiO2含量逐渐增加.终点铸坯夹杂物成分为30%～35%CaO,20%～27%Al2O3,25%～30%SiO2,其他成分含量较少.终点铸坯夹杂物略显碱性,变形能力稍弱.     

IF钢生产过程非金属夹杂物的演变行为

在DS-LD-RH-CC工艺IF钢工业生产过程系统取样和全氧含量、氮含量、非金属夹杂物形貌和化学成分检测的基础上,结合热力学分析,研究了非金属夹杂物含量、形貌与成分的演变过程.结果表明,冶炼过程钢中全氧含量逐渐降低,但需控制钢包渣氧化性以进一步降低铸坯中全氧含量;在浇铸过程中发生明显的增氮现象,应进一步加强保护浇铸,控制浇铸过程钢水增氮;在RH精炼过程中,脱氧后主要生成团簇状单一Al2O3夹杂物,Ti合金化后生成球形Al-Ti-O和内外分层的Al-Ti-Ca-Mg-O复合夹杂物;在钢水凝固过程中,生成了内层为Ti-Al-Mn-O-S、外层为TiN和AlN的复合夹杂物.在铸坯中还存在由结晶器卷渣导致的含有K,Na成分的Ti-Al-Ca-Si-Mn-O大型复合夹杂物.     

BOF--LF--CC生产SWRH82 B硬线钢的洁净度研究

采用系统取样与实验室综合分析,对BOF-LF-CC工艺生产的SWRH82B钢洁净度衍变规律进行研究。结果表明,钙处理后钢中T[ O]和显微夹杂物数量显著下降,轻微增氮;浇铸过程增氧增氮严重;铸坯中<5μm显微夹杂占97%,主要是棱角分明的纯Al2 O3夹杂,球状复合氧化物与CaS和MnS的复合夹杂,简单氧化物或氮化物与MnS的复合夹杂;LF精炼后钙处理,脱氧显著,但使得铸坯中出现很多Al2 O3硬性夹杂,对SWRH82B盘条质量造成严重的危害;中间包结构不合理,卷渣、内衬侵蚀和二次氧化严重,连铸过程钢液洁净度下降。     

TP347H精炼渣二次氧化控制及夹杂物变性处理

研究了采用EF+VOD+IC工艺流程生产TP347H不锈钢时由于精炼渣成分产生的二次氧化及其氧化夹杂物的变性处理过程.试验中VOD精炼过程中采用Al进行终脱氧，降低精炼渣中FeO、SiO2含量，精炼渣四元碱度控制在1.3以上，保证钢中全氧质量分数小于0.003%.脱氧后使用喂Ca-Si线及钢包软吹的精炼手段，可将硬质Al2 O3及MgAl2 O4转变为CaO-Al2 O3夹杂，减少硬质MgAl2 O4夹杂总量并使夹杂物熔点低于1500益.此类夹杂在炼钢温度下呈液态且更易于聚集与上浮，而在后续轧制、锻造过程中低熔点夹杂随基体发生形变，减少钢材裂纹的产生.     

RH生产超低碳钢的工艺优化

通过建立ＲＨ真空处理脱碳数学模，研究了「Ｃ」０、「Ｏ」０、吹氩流量、浸入管内径对脱碳效果的影响，模型计算结果表明，针对某厂ＲＨ处理工艺，若适当提高转炉出钢「Ｃ」，降低出钢「Ｏ」，即可满足钢中「Ｃ」的要求，又可降低脱碳终点「Ｏ」从而减少脱氧合金的消耗。     

超低碳铝镇静钢冶炼过程氮含量的控制

针对企业冶炼超低碳铝镇静钢过程中增氮量高、波动大及控制不稳定的问题,采用工艺数据统计和现场取样的手段,系统梳理了冶炼过程钢液脱氮和增氮的主要环节和影响因素.转炉脱碳期和真空处理是脱氮的主要环节,碳氧期的总脱碳量高则终点氮含量低;转炉底吹N2/Ar切换点在吹炼70%以前对终点氮含量影响不大;VD在无氧条件下脱氮有利,RH则在有氧条件下脱氮有利.控制钢中溶解氧>200×10-6则出钢过程增氮可控制在5×10-6以下;炉料的氮带入是真空精炼环节增氮的重要因素,最高达11×10-6;采用密封垫+吹Ar的保护方式,增氮量最低为1×10-6.     

KR-BOF-LF-CC生产汽车大梁钢LG510L洁净度的研究

通过氧氮分析、金相分析、大样电解法、扫描电镜及能谱分析等,研究采用KR-BOF-LF-CC工艺生产的汽车大梁钢LG510L的洁净度。结果表明,铸坯中平均T[O]和氮含量分别为29.20×10-6和38.80×10-6;钢中显微夹杂物和大型夹杂物数量都随着各工序的不断进行大体呈递减趋势;钙处理前主要显微夹杂物为Al2O3,经过钙处理后,夹杂物发生变性,主要为CaO-Al2O3;铸坯中大型夹杂物主要是SiO2和硅铝酸盐,来源于脱氧产物及其与耐火材料或炉渣反应的产物。     

应用镁蒸气对模具钢中夹杂物变性的研究

D2冷作模具钢最常见的失效形式为磨损失效,改善夹杂物的数量、形态和分布能降低钢的磨损率.利用颗粒镁在高温下生成镁蒸气,并通过高纯氩气携带通入钢液中,考察了镁对钢中非金属夹杂物的变性效果.实验结果表明,镁蒸气通入钢液后,钢中非金属夹杂物尺寸明显变得细小,夹杂物的成分从单纯的Al2O3和Al2O3与Cr,Mo和V等合金氧化物的复合产物向富MgO的MgO和Al2O3复合夹杂物转变.铸态组织的观察结果表明细小夹杂物在钢液中的残存对于凝固和相变过程中钢的晶粒细化有利.     

GCr15轴承钢中MnS-Al_2O_3复合夹杂物析出行为

对于钢液铝脱氧精炼过程产生的Al_2O_3夹杂物严重影响钢的性能,而在钢液凝固过程中MnS夹杂物容易包裹着Al_2O_3夹杂物形成复合夹杂物,这种复合夹杂物改善钢材的性能有重要意义。通过场发射扫描电镜和能谱对国内某钢厂连铸坯中夹杂物形貌以及组成进行观察与分析,发现大量MnS包裹Al_2O_3复合夹杂物。同时通过理论热力学阐述MnS包裹Al_2O_3复合夹杂物的析出机理,计算得出:Al_2O_3夹杂物在钢液中形成,Mn S夹杂物在钢液凝固过程中形成,由于Al_2O_3夹杂物先析出,Mn S夹杂物可以在先析出的Al_2O_3夹杂物进行形核与长大,为钢中MnS包裹Al_2O_3复合夹杂物生成提供了理论依据。     

帘线钢中氧化物夹杂控制技术在生产中的应用

在帘线钢冶炼过程中,通过采用炉后弱脱氧、防止钢液污染,以及控制精炼顶渣碱度指数和Al2O3含量指数等措施,使钢中夹杂物向低熔点区域转变,促进钢中夹杂物上浮、排出钢液,同时也使钢中残留氧化物夹杂具有良好的变形性能.实践表明,通过采用上述工艺措施,帘线钢中夹杂物成分、尺寸和变形性得到了有效控制.     

超低氧钢熔炼过程中炉衬与钢液的相互作用

研究高温下耐火材料的相对稳定性及在真空熔炼超低氧钢过程中炉衬材料向钢液供氧的热力学条件和动力学规律。结果表明，在真空感应熔炼过程中，通过透气砖向熔池吹氩，可以实现在较低的真空度下熔炼超低氧钢，以及有效去除钢中的氧化物夹杂物颗粒。     

IF钢生产过程非金属夹杂物行为研究

对首钢京唐生产IF钢的同一浇次前2炉的RH精炼、镇静和中间包浇铸过程进行了系统取样,并利用Aspex自动扫描电子显微镜分析统计了钢中夹杂物的成分、尺寸等信息.研究发现,Al2O3-TixO复合夹杂物在Ti合金化和二次氧化的情况下都会生成,并随着精炼的进行逐渐转变为Al2O3,这与热力学计算的结果一致;而Al2O3可以作为Al2O3-TixO的形核核心,形成Al2O3-TixO包裹Al2O3的夹杂物,并且在Al2O3-TixO转变为Al2O3的过程中会导致钢滴进入夹杂物内部,从而形成Al2O3包裹钢滴的夹杂物.