苯并三氮唑衍生物的缓蚀性能研究

以苯并三氮唑（BTA）为原料合成1-羟甲基苯并三氮唑,将其与乙二胺按一定比例混合,通过挂片、电极化曲线以及交流阻抗等实验方法对其缓蚀性能进行了测定.证明该缓蚀剂在质量分数为3%的NaCl溶液中10mg/L的质量浓度下对黄铜的缓蚀率达到90%,比BTA有更好的缓蚀性能.电化学测量表明,新缓蚀剂的加入使铜的自腐蚀电位负移,增强了阴极极化的抑制作用,提高了铜电极表面的电荷转移电阻,从而具有教好的缓蚀效果.     

苯并三氮唑在金属清洗剂中缓蚀性研究

本文研究了苯并三氮唑在金属清洗剂中的缓蚀作用,用电化学法比较研究了苯并三氮唑(BTA)、硅酸钠、硝酸钠在10%NaCl溶液中对铜的缓蚀性能;在原电池中探讨苯并三氮唑与硅酸钠、硝酸钠协同对铜的缓蚀作用。实验结果表明,苯并三氮唑本身具有缓蚀性,缓蚀率为54.5%,加入助溶剂硅酸钠后缓蚀率由54.5%增加到84.5%;硅酸钠、苯并三氮唑复配后在油酸三乙醇胺金属清洗剂中对铜的缓蚀率可达97.6%;浓度为0.0008mol/L苯并三氮唑在时间达3h时缓蚀作用最强,且硅酸钠(0.004mol/L)、苯并三氮唑(0.0008mol/L)和油酸三乙醇胺三者复配对铜的缓蚀作用最好。苯并三氮唑对铝基本无缓蚀作用。     

钨酸盐与苯并三氮唑协同缓蚀机理的探讨

采用静态挂片法研究了钨酸钠与苯并三氮唑 ( BTA)对碳钢的协同缓蚀作用。实验发现 ,在氯离子浓度为 1 .4× 1 0 -3mol/L的水中 ,钨酸钠与苯并三氮唑对碳钢没有明显的协同缓蚀作用 ;在同样氯离子浓度的水中投加 6.2× 1 0 -5mol/L锌离子后 ,钨酸钠与苯并三氮唑总浓度为 1× 1 0 -3mol/L、Na2 WO4 ∶BTA=8∶ 2 (摩尔比 )时 ,碳钢的腐蚀速率比单独使用 Na2 WO4 或 BTA时有所降低 ,表明两者间有协同作用。利用 BTA溶液的紫外 -可见吸收光谱解释了锌离子的作用 ,根据极化曲线测定及碳钢表面膜的分析结果 ,对 Na2 WO4 - BTA-锌离子的协同缓蚀机理进行了探讨     

苯并三氮唑和4-羧基苯并三氮唑对铜缓蚀作用的光电化学比较

采用光电化学方法和交流阻抗方法将不同浓度的ＢＴＡ（苯并三氮唑）和４ＣＢＴＡ（４－羧基苯并三氮唑）在硼砂缓冲溶液（ｐＨ９．２）中对铜电极的缓蚀性能作了比较。发现在阳性向电位扫描中,一定农度的ＢＴＡ作用下,铜电极光响应由ｐ型转化为ｎ型,并可依此判断缓蚀剂的缓蚀性能。ｎ型光响应越大,缓蚀剂的缓蚀性能越好;而在４ＣＢＴＡ作用下,铜电极光响应保持ｐ型,然其阴极向扫描中最大光电汉变化明显,并可据此判断缓蚀剂诉     

苯并三氮唑在铁电极上的光谱电化学研究

苯并三氮唑在硫酸溶液中吸附在铁电极上的极化曲线和表面拉曼光谱研究结果表 明：苯并三氮唑同时抑制了铁的阳极溶解反应和阴极析氢反应;当电位负于腐蚀电位时,苯并三 氮唑以分子或质子化的形式吸附于电极表面．     

钼酸锂与苯并三氮唑对碳钢在溴化锂溶液中缓蚀作用的协同效应

通过静态挂片法研究了钼酸锂与苯并三氮唑对碳钢在溴化锂溶液中缓蚀作用的协同效应，并通过极化曲线评价了钼酸锂与苯并三氮唑复配的缓蚀作用，实验表明钼酸锂与苯并三氮唑对碳钢在溴化锂溶液中的缓蚀作用有一定的协同效应，添加0．02mol／L钼酸锂和0．02mol／L苯并三氮唑能显著抑制溴化锂溶液对碳钢的腐蚀。通过分析极化曲线、俄歇能谱及扫描电镜，可能的缓蚀机理是在碳钢表面形成一层钼酸锂、三氧化钼、铁-苯并三氮唑和三氧化二铁等组成的钝化膜，阻滞阳极反应从而起到缓蚀作用。     

苯并三氮唑和磷酸钠对锌的协同缓蚀

采用静态失重法、动电位极化曲线法、电化学交流阻抗法、扫描电镜和X射线光电子能谱等方法,研究了在质量分数为17%(0.534mol/L)的四丁基溴化铵(TBAB)溶液中,苯并三氮唑(BTA)和Na3PO4(SP)单独和复配使用对锌腐蚀的抑制作用.结果表明,BTA和Na3PO4及其复配物对TBAB溶液中的锌具有缓蚀作用,B...     

防冻液中苯并三氮唑与苯甲酸钠对多种金属的缓蚀作用

采用电化学阻抗谱研究了苯并三氮唑与苯甲酸钠对防冻液中多种金属的防腐性能.研究结果表明,在碱性条件下,苯并三氮唑和苯甲酸钠单独作为缓蚀剂时,对多种金属均能起到缓蚀作用,将苯并三氮唑和苯甲酸钠进行复配,缓蚀效果更加明显,具有协同缓蚀作用.     

利用比浊法进行铜和苯并三氮唑的相互测定

根据苯并三氮唑和铜（Ⅱ）能生成沉淀化合物的反应,分别研究了用苯并三氮唑和铜作沉淀剂,利用比浊法进行铜（Ⅱ）和苯并三氮唑的相互测定,测定线性范围分别为０．２～１．２ｍｇ／Ｌ和２．４～２１．６ｍｇ／Ｌ。该法所用仪器简单,操作简便,适宜于生产厂和应用单位使用。用该方法测定了内燃机车冷却水中的苯并三氮唑和糖精钠厂排放的废水中铜的含量,结果与电位滴定法及原子吸收法相吻合。     

高分子担载苯并三氮唑及其铜配合物的合成及表征

在相转移催化下，将苯并三氮唑以共价键担载于氯甲基化交联聚苯乙烯，采用元素分析及红外光谱对其结构进行了表征．合成了高分子担载苯并三氮唑与铜（Ⅱ）的配合物．初步考察了其催化氧化性能     

苯并三唑衍生物的缓蚀作用及PPP量子化学研究

通过挂片失重法和电化学极化曲线研究了苯并三唑,１－氯苯并三唑,５－硝基苯并三唑和５－氨基苯并三唑四种苯并三唑衍生物在ＮａＣｌ溶液中对铜的缓蚀作用。用ＰＰＰ－ＳＣＦ半经验量子化学方法对它们的结构参数进行计算,分析表明ＢＴＡ优良的缓蚀作用主要来自它对一价了了的促钝化作用,苯并三唑衍生物在铜表面的吸附是通过整个环上的π电子与铜相互作用实现的,π电子的化学吸附作用对其缓蚀性能有一定的影响。     

2－十一烷基－1－（双硫脲）乙基－咪唑啉在铜表面上的成膜作用

研究了２－十一－烷基－１－（双硫脲）乙基咪唑啉（简称ＳＭ－２）在盐酸介质中对７０－１铜的缓蚀作用及其在黄铜和紫铜管表面上的成膜性能。结果表明，它优于ＢＴＡ或ＭＢＴ。     

Influence of pH,immersion time,and benzotriazole concentration on copper corrosion in citric acid based slurries

Copper corrosion in citric acid based slurries with or without benzotriazole (BTA) was investigated as a function of the slurry pH,immersion time and BTA concentration by static etching and electrochemical experiments.The chemical composition of the corroded surface was determined using X-ray photoelectron spectroscopy (XPS).The static etching rate of copper in a H2O2 +citric acid+BTA slurry was lower than that in a H2O2 +citric acid slurry at pH 4.4-8.When the pH of the slurry was >8 or <4.4,the results were reversed and the static etching rate of copper increased when BTA was added to the H2O2 +citric acid slurry.The inhibitory effect of BTA in the H2O2 +citric acid slurry at pH 6 increased with the increasing immersion time of the copper.The corrosion current density of copper gradually decreased with increasing BTA concentration in slurry.     

Preparation and characterization of a chitosan-based low-pH-sensitive intelligent corrosion inhibitor

A chitosan (CS)-based low-pH-sensitive intelligent corrosion inhibitor was prepared by loading a pH-sensitive hydrogel with benzotriazole (BTA); the pH-sensitive hydrogel was synthetized by crosslinking CS with glutaraldehyde (GTA). Analysis by Fourier- transform infrared (FT–IR) spectroscopy showed that Schiff reactions occurred between amino and aldehyde groups. The swelling ability of the hydrogel was investigated using a mass method, and it was observed to swell more in an acidic environment than in an alkaline environment. The hydrogel’s loading capacity of BTA was approximately 0.377 g·g-1, and its release speed was faster in an acidic environment than in an alkaline environment because of its swelling behavior. The corrosion inhibition ability of the intelligent inhibitor was tested by immersion and electrochemical methods. The results showed that after 4 h of immersion, the polarization resistance (R4) value of copper with the intelligent inhibitor was approximately twice of that of copper with BTA, indicating that the intelligent inhibitor could effectively prevent copper from corroding.     

Synergistic Effect of Tungstate and Benzotriazole on Corrosion Inhibition of Carbon Steel in Solutions Containing Cl^-

The corrosion inhibition of tungstate, benzotriazole (BTA) and their combination in solutions containing Cl^- was studied by electrochemical techniques. The results indicated that the inhibition efficiency of tungstate was higher than that of BTA. The efficiency increased with increasing concentration of tungstate or BTA. In the studies of synergistic effect of tungstate and BTA, it had been found that in pH 9.0 solution, the largest Rt could be obtained with the concentration ratio of tungstate / BTA being 1 : 1. Lowering the pH value of solution would reduce the efficiency of inhibitors, especially in binary inhibitors. Increasing the concentration of Cl^- accelerated the corrosion of carbon steel in the solutions with various inhibitors, but the influence of Cl^- on corroding rate in binary inhibitors was not so strong as in single component. The results ofsurface analysis showed that W, C, N, O and Fe elements existed in the protecting film formed with binary inhibitors. The thickness of the film was about 12-15 nm.     

提高化学镀铜层表面性能的方法探讨

用化学氧化及苯并三氮唑（ＢＴＡ）钝化处理的方法来提高化学镀铜层的表面抗氧化、耐腐蚀和耐磨性能。并与铬酸盐钝化处理方法进行了对比，得出ＢＴＡ可取代铬酸盐的钝化处理方法；化学氧化处理略逊于ＢＴＡ或铬酸盐钝化处理方法。此外，对化学氧化和ＢＴＡ钝化处理方法的机理也进行了探讨。     

模拟海水中铜腐蚀及缓蚀的光电化学研究

用光电化学方法现场测量铜电极的开路光电压,用开路光电压的变化来反映铜的腐蚀行为及缓蚀剂ＢＴＡ的缓蚀行为。实验发现开路光电压由正变负即光响应由Ｐ型光响应转变为Ｎ型光响应表明铜电极受到Ｃｌ－的侵蚀,在铜板电极表面形成了含有ＣｕＣｌ在内的复杂相。在本文条件下从ｗ（缓蚀剂ＢＴＡ）为５×１０－６％时开始产生缓蚀作用,随着ｗ（缓蚀剂）的增加,ＣｕＢＴＡ膜变得越致密越厚,缓蚀作用越好,表现为开路光电压越来越小。并用表面电子能谱技术测试结果佐证     

电沉积壳聚糖-镝复合涂层缓蚀性的研究

以壳聚糖和镝为原料,利用电沉积技术在铜片上形成新型的壳聚糖-镝复合涂层.涂层的耐腐蚀性采用电子扫描显微镜（SEM）、X射线能谱（EDS）、动电位极化测量（TAFEL曲线）和电化学交流阻抗（EIS）进行研究.试验结果表明,在电压为5V,沉积时间为5min,溶液pH=3.8的室温条件下可以在铜表面形成稳定、均匀的壳聚糖-镝复合涂层,该涂层能够显著提高铜片在酸性体系中的缓蚀性.     

2-己基咪唑作为铜的盐酸酸洗缓蚀剂作用机理的研究

通过失重法研究了2-己基咪唑 (2-HeIM )在5%盐酸中对铜的酸洗缓蚀性能。探讨了温度和 2-HeIM浓度对缓蚀效果的影响，从中得出了 2-HeIM在铜表面的吸附等温式，计算了吸附热及 2-HeIM的加入对铜在盐酸中腐蚀反应活化能的影响，进而探讨了 2-HeIM对铜的缓蚀作用机理。结果表明，30℃下，在 5%盐酸中，当 2-HeIM的浓度在 6mmol/L以下缓蚀率随 2-HeIM浓度的增加而增加 ,当浓度达到 6mmol/L时 ,缓蚀率趋于定值。在 2mmol/L到 6mmol/L浓度范围内吸附在铜表面的 2-HeIM分子间的作用力整体表现为引力；2-HeIM在铜表面的吸附是吸热反应；2-HeIM的加入降低了铜的腐蚀反应活化能。     

卤素离子与苯骈三氮唑协同成膜动力学的体声波传感技术研究

采用体声波传感技术就卤素离子与铜缓蚀剂——苯骈三氮唑( BTA)协同成膜的动力学及相应复合膜的稳定性进行了研究 .结果表明 ,卤素离子 ( F- ,Cl- ,Br- ,I- )中仅 I- 与 BTA具有协同效应 ,能有效地提高BTA的缓蚀效果和膜层稳定性 ,同时 ,对 BTA的成膜动力学有明显影响