表面重熔加工对材料耐空泡腐蚀的影响

采用TIG(钨极惰性气体保护焊)表面重熔工艺对表面耐空泡腐蚀堆焊材料进行改性加工,与磨削表面加工对比研究了TIG表面重熔对空泡腐蚀的影响.结果表明:在45 h空泡腐蚀试验后,磨削试样的累积失重量是TIG表面重熔试样的1.59倍;相变产生的马氏体剥落是质量损失的主要形式,而TIG表面重熔工艺延迟了奥氏体到马氏体的相变,降低了质量损失;大量裂纹沿着马氏体片层发展,而TIG重熔表面抑制了裂纹发展,避免了大的物质剥落.     

激光表面处理灰铁的工艺实验研究

本文探讨了激光表面处理灰铁的工艺。运用1.2kW CO_2激光加工机重熔普通灰铸铁表面并进行合金化处理。结果表明,激光表面处理时白口深度的大小与激光器工艺参数P/(Dv)~2/1成线性关系,且受表面涂料的影响;白口层深度与熔区表面硬度成指数关系,白口深度越大,则硬度值越高。激光表面处理后,试样自表层起可划分为3个区域,即:熔化区,组织为莱氏体;热影响区,组织为针片状马氏体和隐晶马氏体;基体区,组织为珠光体。     

激光冲击处理不锈钢慢应变速率拉伸应力腐蚀性能

利用激光冲击处理技术对304不锈钢片试样进行激光冲击处理。采用慢应变速率拉伸实验方法评价304不锈钢激光冲击处理前后在80℃时、质量分数为3.5%Na Cl溶液中的应力腐蚀开裂敏感性。通过金相显微镜(OM)和扫描电子显微镜(SEM)分析激光冲击处理后表面强化层的晶粒细化程度。采用显微硬度计测定了表面显微硬度分布及影响层深度。实验结果表明,激光冲击处理未能显著细化试样表层晶粒,但可以提高显微硬度。随着冲击次数增加,表面显微硬度值也增加,影响层厚度提高。慢应变速率拉伸应力腐蚀试验结果表明激光冲击处理可以降低不锈钢应力腐蚀开裂敏感性,且双面冲击处理比单面冲击处理效果更好。     

热浸镀铝球墨铸铁氩弧重熔工艺

为强化热浸镀铝层的耐磨性能,将球墨铸铁经780℃热浸镀铝后进行氩弧重熔处理,分析重熔工艺参数对重熔层性能的影响,利用扫描电镜对热浸镀铝层和氩弧重熔层组织进行了观察。结果表明:热浸镀铝层经氩弧重熔处理后,组织改善,由原来富铝层和扩散层转变为重熔层和过渡层。氩弧重熔工艺参数对重熔组织裂纹率、熔深、表面硬度影响较大,重熔电流增大或电弧扫描速度减小时,重熔层裂纹率下降,熔深增加,硬度升高。在重熔电流为70～120 A时,重熔层和过渡层硬度最高可达8.430和8.820 GPa。氩弧重熔处理能明显提高热浸镀铝层的显微硬度。     

铝合金激光熔覆的最佳能量密度选择

铝合金密度小、熔点低、为了把较高熔点的耐磨合金层熔覆到其表面上，而又不让界面上的熔铝上浮以损害涂层强度，激光重熔的能量密度选择十分重要，这里用一系列能量密度进行了重熔试验，对其重熔层的性能，组织，成份及表面状况进行测试和分析，研究了铝合金基体上熔覆Ｎｉ－Ｃｒ层时激光能量密度对熔覆层质量的影响。     

激光相变硬化对轴承钢组织与性能的影响研究

本文对低温回火态Gcr15轴承钢的激光相变硬化处理进行了研究.试验了激光处理的工艺参数对硬化过程的显微组织、淬硬层的硬度变化、残余应力分布、残留奥氏体形貌与数量以及耐磨性能等的影响.结果表明:经激光相变硬化处理后,Gcr15钢的表面硬度可达HV1000以上,硬化层的显微组织为缺陷密度高的隐针马氏体,晶粒度为ASTM 14级,残留奥氏体约达20%,呈膜态分布于马氏体条片之间及碳化物周围,超细的碳化物非常弥散地分布着,表面层保持较大的压应力而耐磨性能明显提高.据此,可以认为激光相变硬化的强韧化机制是:晶粒细化强化、亚结构强化,弥散析出强化以及残留奥氏体强化等的综合贡献.     

40CrNiMoA激光宽带相变硬化处理

研究了40CrNiMoA钢在激光宽带相变硬化处理各工艺参数对合金显微硬度的影响.实验结果表明:40CrNiMoA激光宽带相变硬化处理搭接量的选择范围为14%~18%,激光宽带相变硬化处理后合金组织明显细化导致表面强化,淬层硬度可达到700HV以上,并且沿激光作用区横向硬度呈明显规律分布;探讨了40CrNiMoA激光宽带相变硬化相应机制.     

灰铸铁HT200脉冲激光表面重熔

文章报道了用千瓦级N d:YAG脉冲激光器对灰铸铁HT 200进行表面重熔的实验.对激光参数与重熔层熔池形貌、表面粗糙度、显微硬度及结构的关系进行了分析,并提出迅速有效地获得最佳激光加工工艺参数的方法.     

激光表面硬化对球墨铸铁的组织与滑动磨损性能的影响

将一种铜钼球墨铸铁经正火及经633K等温淬火后，研究了激光表面硬化对它们的组织与滑员性能的影响。滑动磨损试验方法为在接触应力下与经热处理到HRC62－64的GCr15钢对磨。结果显示对于等温淬火球铁，激光硬化层中马氏体片的尺寸与基体奥氏体－贝氏体中的铁素体板条尺寸相近，认为这是一种组织遗传现象，研究结果还表明奥贝球铁的耐磨性优于珠光体球铁，而激光表面硬化可以进一步提高两种基体铸铁的磨损性能。     

MoCu球铁激光淬火过程温度场的数值计算

根据激光淬火过程的特点及复杂性，提出用有限元方法计算激光淬火过程中温度场及组织分布的传热学数学模型；在计算中对热物性值随温度的变化进行了分段线性回归处理；激光淬火属快速加热范畴，奥氏体化点相应提高．相变潜热则根据相变量的多少以温升、温降的形式加以处理．以ＭｏＣｕ球铁为例对不同激光处理参数下的温度场及组织分布进行了计算及实验验证．     

Effect of scanning speed during PTA remelting treatment on the microstructure and wear resistance of nodular cast iron

The surface of nodular cast iron (NCI) with a ferrite substrate was rapidly remelted and solidified by plasma transferred arc (PTA) to induce a chilled structure with high hardness and favorable wear resistance. The effect of scanning speed on the microstructure, microhardness distribution, and wear properties of PTA-remelted specimens was systematically investigated. Microstructural characterization indicated that the PTA remelting treatment could dissolve most graphite nodules and that the crystallized primary austenite dendrites were transformed into cementite, martensite, an interdendritic network of ledeburite eutectic, and certain residual austenite during rapid solidification. The dimensions of the remelted zone and its dendrites increase with decreased scanning speed. The microhardness of the remelted zone varied in the range of 650 HV_0.2 to 820 HV_0.2, which is approximately 2.3–3.1 times higher than the hardness of the substrate. The wear resistance of NCI was also significantly improved after the PTA remelting treatment.     

机床导轨表面激光硬化处理及其耐磨性试验研究

本文利用大功率CO_2激光器对机床滑动导轨表面进行激光相变硬化处理和研究分析;并通过耐磨性试验研究,获得了相应的磨损曲线和寿命指标。同时,本文对这种表面新技术的实际应用进行了工业试验分析。     

宽带激光处理铸铁组织与强韧性的研究

采用宽光束ＣＯ２ 激光,对灰铸铁进行相变硬化和熔凝强化处理,分析了两种工艺条件下铸铁组织强韧化机理．结果表明,相变硬化马氏体形态主要为针状,组织内存在微细孪晶结构;熔凝形成的莱氏体组织内弥散分布着未熔Ｆｅ３Ｃ及新生相Ｆｅ７Ｃ３ ．声发射试验表明,灰铸铁经相变硬化处理,其强韧性稍优于熔凝处理的结果．结合激光形成的温度场特点,对试验结果进行了讨论．研究方法包括透射电子显微镜、Ｘ射线衍射、声发射试验等．     

含As、Sn、Pb、Ti球墨铸铁的热处理

探讨了１０种热处理工艺对含Ａｓ、Ｓｎ、Ｐｂ、Ｔｉ球墨铸铁试样抗拉强度及延伸率的影响．结果表明：含Ａｓ、Ｓｎ、Ｐｂ、Ｔｉ球墨铸铁采用低温部分奥氏体化正火处理,可以获得较佳的综合力学性能;高温退火有利于其综合力学性能的提高;在共析转变温度上、下波动加热－－冷却的珠光体球化处理是改善其韧性的有效措施．     

灰铸铁激光重熔的正交设计

报道了千瓦级NdYAG脉冲激光表面重熔的工艺参数探索中采用正交实验设计的方法,可以迅速有效地获得最佳激光加工工艺参数,为激光加工技术在工业生产中的应用提供了一个有效的方法.     

9SiCr工具钢表面激光熔覆合金的组织与性能

使用CO2激光器对9SiCr工具钢表面进行Co基和Ni基合金熔覆处理,X射线衍射仪、扫描电子显微镜分析了激光合金熔覆层的相组成和显微组织;显微硬度计对合金熔覆区的显微硬度进行测量·结果表明,合金熔覆层在微观结构上存在熔覆区、结合区和基体热影响3个区域·Co基合金熔覆区相组成为奥氏体+铁素体+碳化物,Ni基合金熔覆区相组成为奥氏体+铁素体+碳化物+金属间化合物·Ni基合金熔覆层的显微硬度约为Co基的2倍     

石墨和碳化物形态对高镍奥氏体球铁抗热冲击性能的影响

本文论述了合金元素Si,Cr,Mo对含Ni20％的高镍奥氏体球墨铸铁抗热冲击性能的影响,揭示了石墨和碳化物形态与热冲击疲劳裂纹扩展方式和扩展速率之间的关系。发现石墨呈球状时热冲击疲劳裂纹为晶界型裂纹,抗热冲击性能最好;呈片状时为穿晶型裂纹,抗热冲击性能最差,呈枝晶状时为(晶界加穿晶)混合型裂纹,抗热冲击性能介于前二者之间.加入适量的Cr,Mo,Si可显著地提高抗热冲击性能。     

球墨形貌的非规则维初探

本文基于广义非规则维模型,提出了一种对球墨三维形貌进行定量描述的方法。用该法对Sb-Mg球铁的断口石墨形貌进行研究,结果表明利用非规则维恒权均值(FD)、FD直方图和FD值图象,可以定量地描述石墨表面的起伏程度,各类起伏的频率及其空间分布特征,从而客观地反映Sb对Mg蚌铁中球墨三维形貔的影响。