TiC在Ti2CS上形核生长的电镜观察及其取向关系的测定

为探讨与控制薄板坯连铸连轧工艺条件下碳化钛在钢中的析出行为,应用透射电子显微术(TEM)研究了纳米尺度TiC和Ti2CS析出相的结构及取向关系.结果表明,实验钢中Ti2CS的析出温度较TiC的高,先析出的Ti2CS可作为TiC的非自发形核地点.实验观察到细小TiC粒子在Ti2CS上生长的现象.电子衍射和X射线能谱(EDS)分析表明:TiC和Ti2CS之间的取向关系为{001}Ti2CS∥{111}TiC,〈100〉Ti2CS∥〈011-〉TiC.在TEM下还观察到以孪晶形式存在的TiC,孪晶面为(1-11-)面.总之,在钢中先行析出的Ti2CS和TiC粒子都可能成为新生成TiC的非自发形核地点,孪生和外延生长是TiC沉淀的两种重要机制.     

冷轧低合金高强钢再结晶和析出行为研究

利用热模拟试验机研究了冷轧低合金高强钢的再结晶动力学规律,并基于JMAK方程建立了再结晶动力学模型,为退火过程中铁素体再结晶和析出行为的控制提供了理论依据.结果表明,随退火温度升高,铁素体达到完全再结晶时所用时间大大缩短;冷轧压下量相同时,初始贝氏体组织具有更高的位错密度和储存能;80℃/s快速加热条件下,回复和再结晶过程相应同步提前,且再结晶发生前的剩余变形储能增大,从而使铁素体再结晶快速完成.同时新工艺下实验钢析出粒子尺寸更均匀,体积分数更高,析出强化贡献更明显.     

CSP低碳微皿钢中Ti（C，N）的析出行为

通过实验观察及热力学计算，研究了CSP低碳微Ti钢中的Ti（C，N）析出．实验观察到大量15～30nm的Ti（C，N）第二相粒子，它们在铸坯均热保温和前两道次的热轧中析出并长大充分；均热前CSP铸坯中只有很少量尺寸约大于50nm的TiN粒子析出，铸坯中观察不到微米级的大块TiN夹杂．研究结果表明，CSP工艺下粒子析出行为同传统工艺相比发生了变化，所以微量Ti在钢中的作用也有很大不同．     

薄板坯连铸连轧流程试制含钒钛取向硅钢中氮化物析出相

通过热力学计算与模拟试验研究了含钒钛取向硅钢中氮化物析出相的析出规律与析出行为,并探讨了含钒钛元素的氮化物析出相作为薄板坯连铸连轧流程制备取向硅钢中辅助抑制剂的可行性.研究表明,在所冶炼的含钒钛取向硅钢的成分范围内,Ti N在钢液凝固末期便具备析出的热力学条件,而Al N与VN只可能在凝固后的α+γ或α+Fe3C两相区内析出.含钒钛取向硅钢中氮化物析出相以成分复杂的复合析出相为主,且随着钒钛加入量的增加,钢中抑制剂析出相总的分布密度由于含钒钛元素的氮化物析出相的增加而明显提高,使抑制剂抑制初次再结晶晶粒正常长大的能力得以加强,最终成品的磁感应强度值B8由1.857 T提升至1.898 T.同时,加入不高于0.007%的Ti与不高于0.005%的V不会影响中间脱碳退火工序的脱碳效果以及高温退火净化阶段硫、氮的脱除效果,其形成的含钒钛元素的纳米级氮化物析出相适合作为薄板坯连铸连轧流程制备取向硅钢的辅助抑制剂.     

含铜无取向电工钢中析出相及其析出机理

研究了含铜低碳低硅无取向电工钢中的析出相及其析出机理.由能谱(EDS)及选区电子衍射(SAED)分析可知,铁素体基体上存在的大量弥散分布的等轴状析出相为类B2结构的铜.这些铜析出相的析出机理可以是一般析出、位错析出、台阶机理相间析出和弓出机理相间析出:一般析出在550、650和750℃三个等温温度均可发生;位错析出只发生在较低的等温温度(550℃),此时析出相呈特殊的平行短列状;台阶机理相间析出也可在上述三个等温温度下发生,但650℃等温时最有利于台阶机理相间析出,此时析出相平直列状分布;弓出机理相间析出只发生在较高的等温温度(750℃),析出相弯曲列状分布.     

X100管线钢的组织性能

利用金相显微镜、扫描电镜、透射电镜等研究了X100管线钢的力学性能、显微组织、晶粒取向及析出物.实验结果表明,采用控轧控冷两阶段轧制工艺轧制出实验钢平均屈服强度达到724 MPa,屈强比0.87,夏比冲击功在-60℃仍有255J,韧脆转变温度在-60℃以下.平均有效晶粒尺寸为2.43μm,大角度晶界占78.8%,尺寸在10 nm左右的析出物与位错相互缠结起到了良好的析出强化作用.     

含铌TRIP钢连续退火后的组织性能及强化机理

在实验室模拟了含铌与无铌TRIP钢的连续退火工艺过程,通过金相显微技术(OM)、扫描电镜(SEM)、透射电镜(TEM)、背散射电子衍射技术(EBSD)、X射线衍射(XRD)和拉伸实验等检测手段研究了TRIP钢的组织性能,分析了TRIP钢中残余奥氏体稳定性的影响因素及强化机理.结果表明:在连续退火工艺条件下,Nb的存在细化了TRIP钢的微观组织,与未添加Nb的钢相比,添加Nb可以提高TRIP钢中残余奥氏体含量和残余奥氏体碳含量.含铌TRIP钢中残余奥氏体主要以团块状或薄膜状分布于铁素体与贝氏体晶界,极少部分以细小球状分布于铁素体晶内.含铌TRIP钢热轧后的主要析出物为Fe3C和(Nb,Ti)(C,N),退火后的主要析出物为(Nb,Ti)(C,N).细小含铌析出物的析出强化导致了随着退火温度的升高,屈服强度和抗拉强度升高.     

600 MPa级钛微合金化高强钢的组织与性能研究

采用光学显微镜、透射电镜以及能谱分析等对转炉CSP流程600 MPa级钛微合金化高强钢的组织及性能进行研究.结果表明,试验钢具有良好的综合力学性能,其典型组织为多边形铁素体加粒状贝氏体;位错和位错胞的强化作用成为钛微合金钢的主要强化机制之一;钢中M/A岛在增加试验钢强度的同时并未明显降低其韧性和塑性;试验钢中存在TiN、TiC和TiS等析出物,为钢的细晶强化和析出强化提供了保证;试验钢中存在大量纳米级铁碳析出物,其沉淀强化作用不容忽视.     

含Nb-Ti低碳微合金钢纳米碳化物析出行为

采用热膨胀仪、显微硬度计和透射电镜研究了等温温度对Nb-Ti微合金钢组织性能及析出行为的影响规律.结果表明,在不同温度下等温淬火均得到铁素体与马氏体的双相组织,且随着等温温度的降低,铁素体的体积分数逐渐增大.实验钢中存在两种主要的析出形态,分别为相间析出和弥散析出,且随着等温温度的降低,析出形态逐渐从相间析出向弥散析出转变.通过HRTEM确定相间析出碳化物具有Na Cl型晶体结构,晶格常数为0.432 nm,且与铁素体基体满足Baker-Nutting(B-N)关系.铁素体相的维氏硬度随着等温温度的降低而逐渐增大.     

含硼微合金钢中硼氮化物形成的热力学分析

应用合金元素在奥氏体中的固溶度积公式,对含硼铝镇静钢,Ti-B和Ti-Nb-V-B系微合金钢中各种析出相的析出关系和析出量及其对奥氏体中固溶硼质量分数的影响进行了热力学分析.结果表明:含硼铝镇静钢中BN的析出优先于Al N的析出,使增加奥氏体稳定性的B的有效质量分数减少;提高含硼钢中的固溶B质量分数的有效方法是加入比B与N的结合力强的Ti;复合微合金钢中Nb,V的质量分数对固溶B的质量分数几乎没有影响,只与钢中加入Ti的质量分数有关,Ti-B和Ti-Nb-V-B系微合金钢中Ti的质量分数最少为钢中N质量分数的3.4~3.8倍.     

Microstructure and strengthening parameters of ultra-thin hot strip of low carbon steel

The microstructure and precipitation mechanism of ultra-thinhot strip produced by CSP technology were analyzed by electron back scattered diffraction (EBSD), H-800 transmission electron microscope (TEM) and thermodynamics theory. The EBSD results show that the finishing hot rolling microstructures are mixture of recrystallized and deformed austenite. After phase transformation, ferrite grains embody substructures and dislocations that led ultra-thin hot strip high strength and relatively low elongation rate. TEM observations show that there are a lot of fine and dispersive precipitates in microstructures. Most of aluminium nitrides are in grains, while coexisted precipitates of MnS along grain boundaries. Coexisted precipitates compose cation-vacancy type oxides such as Al₂O₃ in the core, while MnS at the fringe of surface. At the same time, reasons for microstructure refinement and strengthening effect were investigated.     

电铸Cu的显微组织、晶粒取向和晶界结构

采用SEM,TEM和EBSD研究了电铸Cu的微观组织形貌、晶粒取向和晶界特征.SEM观察表明,沿沉积方向,组织由细小等轴晶区、等轴晶和柱状晶的混合晶区转变为粗大柱状晶区.EBSD分析表明,对于所有晶区,小角度晶界(15°)的分布频率较小,大角度(≥15°)晶界为电铸Cu组织的主要晶界.在大角度晶界中,CSL晶界占有很大比例,其中Σ3的分布频率较大.柱状晶由平行分布的层状孪晶构成,近似垂直于沉积厚度方向,层间孪晶界为Σ3类型,TEM的观察也显示了孪晶的存在.细等轴晶区晶粒的择优取向不明显,混合晶区和粗柱状晶区有明显的〈111〉和〈101〉择优取向.在粗柱状晶区,平行于沉积厚度方向,具有较强的〈111〉择优取向,表明大多数{111}孪晶面垂直于沉积厚度方向.     

Effect of nano-sized precipitates on the crystallography of ferrite in high-strength strip steel

For strip steel with the thickness of 1.6 mm, the yield and tensile strengths as high as 760 and 850 MPa, respectively, were achieved using the compact strip production technology. Precipitates in the steel were characterized by scanning and transmission electron microscopy to elucidate the strengthening mechanism. In addition, intragranular misorientation, Kernel average misorientation, and stored energy were measured using electron backscatter diffraction for crystallographic analysis of ferrite grains containing precipitates and their neighbors without precipitates. It is found that precipitates in specimens primarily consist of TiC and Ti₄C₂S₂. Ferrite grains containing precipitates exhibit the high Taylor factor as well as the crystallographic orientations with {012}, {011}, {112}, or {221} plane parallel to the rolling plane. Compared with the intragranular orientation of adjoining grains, the intragranular misorientation of grains containing precipitates fluctuates more frequently and more mildly as a function of distance. Moreover, the precipitates can induce ferrite grains to store a relatively large amount of energy. These results suggest that a correlation exists between precipitation in ferrite grains and grain crystallographic properties.     

双辊薄带连铸1.2%Si无取向电工钢组织和析出物

研究了双辊薄带连铸条件下,1.2%Si无取向电工钢初始组织和析出物形貌及分布规律.结果表明,在1 550℃浇注条件下,铸带经过空冷后以粗大的原始铸态铁素体组织为主,也有一部分相变产生的细小晶粒,晶粒尺寸范围为50~400μm.铸带中析出物为AlN和MnS,其中AlN析出分为高温析出和相变析出两种,高温析出AlN尺寸在0.5μm左右,相变析出AlN尺寸则在100 nm左右,二者对再结晶组织影响不大.MnS在铸带成型和成品退火过程中都有析出,尺寸范围为30~40nm.     

取向硅钢常化过程析出物和组织演变规律

使用透射电镜(TEM)和电子背散射衍射技术(EBSD)对取向硅钢热轧板常化过程中析出物和组织的变化进行了研究。结果表明,热轧及常化过程中都有大量细小的析出物析出,其中热轧板中主要是MnS和少量MnS与AlN的复合析出物;常化板中主要是AlN和少量MnS与AlN的复合析出物;且常化板中析出物数量比热轧板中析出物的数量高1~2个数量级,平均尺寸减小约16nm。热轧板的组织沿着厚度方向存在较大不均匀性,高斯织构主要存在于热轧板次表层的变形组织中,且强度约为2;常化热处理后试样厚度方向组织的均匀性变大且次表层可以得到细小均匀的晶粒组织,高斯织构依然存在于试样次表层但强度减小约为0.8。     

Effect of hot rolling on the microstructure and impact absorbed energy of the strip steel by CSP

The microstructures and impact absorbed energies at various temperatures were investigated for steel strips hot rolled to thickness reductions of 95.5%, 96.0%, 96.5%, 97.0%, and 97.5%. Results indicate that grain refinement can be realized with an increase in hot rolling reduction. Besides, finer precipitates can be achieved with an increase in hot rolling reduction from 95.5% to 97.0%. The impact absorbed energy decreases with a decrease in testing temperature for steel strips hot rolled to 95.5%, 96.0%, and 96.5% reductions in thickness. However, in the case of steel strips hot rolled to 97.0% and 97.5% reductions in thickness, the impact absorbed energy remained almost constant with a decrease in testing temperature.     

热轧态与回火态 AH80 DB 低碳贝氏体钢组织与冲击韧性

采用光学显微镜、扫描电子显微镜和透射电子显微镜对热轧态和回火态AH80DB低碳贝氏体钢的显微组织、马氏体/奥氏体( M/A)岛、第二相的析出行为以及晶界取向差、有效晶粒尺寸进行研究,揭示回火后低碳贝氏体钢冲击韧性得到改善的原因.结果表明：两种试样的组织均由板条状贝氏体、粒状贝氏体和针状铁素体组成,其中回火态试样中针状铁素体组织较多.热轧态钢中存在较大尺寸M/A岛且呈方向性分布,大角度晶界比例占17.33%,有效晶粒尺寸为3.57μm;而回火态钢中M/A岛的尺寸较小,大角度晶界比例增加3.43%,有效晶粒尺寸减小0.56μm.热轧态钢中析出相主要是( Nb,Ti) C,尺寸在50~150 nm之间,回火态试样中析出较多细小的球状( Nb,Ti) C析出相,尺寸在10 nm左右.     

Effect of micro-alloying Ca on microstructure,texture and mechanical properties of Mg-Zn-Y-Ce alloys

Microstructure,texture and mechanical properties of Mg-5 Zn-0.3 Y-0.2 Ce alloys with the addition of trace xCa(x=0,0.3,0.6 wt%) were systematically investigated in this work.The results revealed that more secondary eutectic phases and smaller grain size of as-cast microstructure could be found with increasing Ca content.After hot extrusion,the Ca-free alloy showed a uniformly recrystallized grain structure,while the Ca-containing alloys possessed a bimodal grain structure composed of fine dynamic recrystallized(DRXed) grains with a size of several microns and un-recrystallized coarse grains.EBSD analysis showed that the three extruded alloys had a fiber texture of(0001) basal plane aligned with the extrusion direction.Texture intensity of the DRXed region was weaker than the deformed region.The extruded alloy with the addition of 0.6 wt% Ca exhibited the highest yield strength of 321 MPa due to the smallest DRXed grain size,the deformed region with strong basal texture and dense nanosized precipitates.     

轧制退火316奥氏体不锈钢的晶界特征分布

利用EBSD技术对不同形变量冷轧并退火处理的316奥氏体不锈钢的晶界特征分布进行了研究．结果发现,小变形轧制经退火处理后,试样晶粒尺寸明显长大的同时∑3^n（n=1,2,3）晶界（也称特殊晶界）比例不断提高．晶粒取向分析表明,合金中高斯（Goss）、黄铜（Brass）、铜型（Cop—per）和立方（Cube）取向（包括其几何变体）的择优长大是特殊晶界比例提高的重要原因．     

IF钢生产过程中的织构演变

对IF钢生产过程中热轧、冷轧及退火试样的织构演变进行研究.分别借助EBSD和XRD测定和计算了热轧、退火及冷轧试样的取向分布函数及相关织构组分的体积分数.结果发现,热轧板在变形过程中发生了动态再结晶,晶粒为细小的等轴晶,为后续组织发展提供了基础;热轧后试样中的织构很弱,不会影响冷轧织构组分及含量.冷轧过程是织构形成的主要过程,试样中含有4种主要的织构组分:{001}〈110〉、{111｝〈110〉、{111}〈112〉和{112}〈110〉.退火过程中发生再结晶,4种冷轧织构组分在退火过程中均分别转变为{111｝面织构.