Effect of La0.8Sr0.2Co0.2Fe0.8O3-δ
morphology on the performance of composite cathodes |
| |
作者姓名: | Erqing Zhao Xiaotian Liu Lianbao Liu Hua Huo Yueping Xiong |
| |
作者单位: | School of Chemical Engineering and Technology,Harbin Institute of Technology |
| |
基金项目: | the National Natural Science Foundation (No. 51072040);National Program on Key Basic Research Project (973 Program no. 2012CB215400) |
| |
摘 要: | In the present work,one dimensional La0.8Sr0.2Co0.2Fe0.8O3 δ(LSCF) nanofibers with the mean diameter of about 100 nm prepared by electrospinning were deposited on Gd0.2Ce0.8O1.9(GDC) electrolyte followed by sintering to form one dimensional LSCF nanofiber cathode. And LSCF/GDC composite cathodes were formed by introducing GDC phases into LSCF nanofiber scaffold using infiltration method. The polarization resistances for the composite cathode with an optimal LSCF/GDC mass ratio of 1/0.56 are 0.27,0.14 and 0.07 Ω cm2at 650,700 and750 1C,respectively,which are obviously smaller than 2.26,0.78 and 0.29 Ω cm2of pure LSCF nanofiber cathode. And the activation energy is1.194 eV,which is much lower than that of pure LSCF nanofiber cathode(1.684 eV). These results demonstrate that the infiltration of GDC into LSCF nanofiber scaffold is an effective approach to achieve high performance cathode for solid oxide fuel cells(SOFCs). In addition,the performance of composite cathode in this work was also compared with that of our previous nanorod structured LSCF/GDC composite cathode.
|
关 键 词: | La0.8Sr0.2Co0.2Fe0.8O3-δ Composite cathode Electrospinning Infiltration |
收稿时间: | 26 September 2013 |
本文献已被 CNKI 维普 ScienceDirect 等数据库收录! |
| 点击此处可从《自然科学进展(英文版)》浏览原始摘要信息 |
| 点击此处可从《自然科学进展(英文版)》下载免费的PDF全文 |