Effect of Al on microstructure and mechanical properties of as-extruded Mg–1Mn alloy sheet

The effect of Al addition on microstructure and mechanical properties of hot extruded Mg–1 Mn alloy sheet was investigated. The results revealed that the dynamic recrystallization was promoted by increasing Al content. The ultimate tensile strength and yield strength of the alloy increased with the increase of Al content. The Mg–9 Al–1 Mn alloy exhibited the highest strength, with tensile strength of 308 MPa, 307 MPa, 319 MPa, yield strength of 199 MPa, 207 MPa, 220 MPa and the elongation of 20.9%, 20.1%, 19.2% in 0°, 45°, 90°, respectively.The high strength was mainly attributed to the formation of fine dynamically recrystallized grains and large amounts of the second phase. The strengthening mechanism of the alloys was explained.     

Microstructure,mechanical properties and wear resistance of an Al–Mg–Si alloy produced by equal channel angular pressing

Microstructure, mechanical properties and wear resistance in an ultrafine-grained Al–Mg–Si alloy fabricated utilizing a combination of equal channel angular pressing (ECAP) and dynamic aging were investigated in this paper. The results indicated that the grain size of the ECAP alloy was significantly refined, i.e., to ~239 nm after three ECAP passes. Meanwhile, the yield and tensile strength of the ECAPed material reached 340 MPa and 445 MPa, respectively, while maintaining a significant uniform elongation of 14%. Wear resistance results demonstrated that the wear rate, wear depth and width of the ECAPed material decreased in comparison with the solution-treated (SST) and peak-aged (T6) conditions under a load range of 5–25 N. The adhesive wear that occurs in the undeformed specimens at 10 N does not appear in the ECAPed specimen at the same load, indicating that the ECAPed specimen delay the appearance of more serious wear mechanisms under certain loads. The cooperative interaction of high density nano-scale β" precipitates and dislocations resulted in a combination of super-high strength and good work hardening ability which suppressed the extension of cracks between the friction layer and the plastic deformation zone. As a consequence, the combination of ECAP and dynamic aging brings a significant improvement for antifriction performance of the 6061 aluminum alloy.     

金属间化合物(Mg,Zn)_(12)Ce与(Mg,Zn)_(11)Ce的研究

对300℃时Mg-Zn-Ce系富镁侧化合物的成分特征、结构和相平衡关系进行了研究.结果表明,Mg-Zn-Ce富镁角存在一个Mg12Ce的二元置换固溶体(Mg,Zn)12Ce,还存在一个三元线性化合物(Mg,Zn)11Ce(τ相).(Mg,Zn)12Ce中Zn的范围为0~7.3%(原子分数),其晶体结构为体心四方晶格.三元线性化合物τ相含Zn为8.5%~43.5%(原子分数),其晶体结构为C底心正交晶格.(Mg,Zn)12Ce和τ相均与α(Mg)存在稳定的两相平衡,且在Mg-Zn-Ce系富镁角还存在三相平衡Mg+(Mg,Zn)12Ce+τ.     

铝合金变形抗力的实验研究

采用恒应变速率凸轮式形变压缩试验机试验了四种铝合金材料的变形抗力 ,分析了应变率和应变速率对变形抗力的影响 ,结果表明随应变的增加 ,变形抗力以近似幂函数关系增加 ,在此基础上建立了简单、适用的变形抗力计算模型     

激光辐照Fe81.5P18.4Yb0.1非晶合金的晶化特征

本文用扫描电镜（ＳＥＭ）和示差扫描量热法（ＤＳＣ）研究了ＸｅＣｌ准分子激光辐照Ｆｅ＿（８１．５）Ｐ＿（１８．４）Ｙｂ＿（０．１）非晶合金的晶化特征。结果发现，辐照样品的断面上有类冲击波纹样的层状规则的晶粒分布，其晶粒尺寸由辐照表面向样品内部逐渐减小，最后是近纳米尺度的微晶排布，样品的热稳定性也明显改善。     

镁改型蛭石对铵离子的交换性能

对经人工改型所得的镁型蛭石进行了铵离子交换性能的研究．在不同pH值下测定了镁型蛭石对NHr的全交换容量，在不同温度下测定了样品的平衡等温线．结果表明，镁型蛭石对NH4^ 的交换总量随pH值的变化而波动，在pH值为7时其交换总量为59．32mmol／100g，其选择性随温度的降低而升高，这为蛭石作为一种新型填料提供了一定的理论依据。     

化学配比对TiAl有序合金微观组织和变形特性的影响

本研究用三点弯曲实验测定了铝含量为43at·％～56at·％的Ti-Al二元合金的力学性能;利用光学显微镜、X射线衍射仪和透射电子显微镜研究了不同成分合金的微观组织和变形亚结构。实验结果表明:根据不同成分合金的微观组织可将其分成三类,即:γ-TiAl单相组织(52at·％～56at·％Al);双态组织(46at·％～50at·％Al)和全片层结构晶粒组织(43at·％～46at·％Al),其中以具有细晶双态组织的合金具有较好的塑性变形能力。本文从微观组织结构和变形位错组态的变化,探讨了合金成分对TiAl基有序合金塑性变形的影响机制。     

NiAl基复合材料的研究进展

为了提高NiAl合金强度，改善NiAl合金塑性，在制备NiAl复合材料时，用不同的制备方法在NiAl合金中加入增强剂，如陶瓷或金属颗粒、晶须、短纤维和长纤维等制成复合材料，以不同的增强剂为基础总结了NiAl基复合材料研究在制备、结构、性能及机理等方面的最新进展。     

Improvement in hydrogen storage performance of Mg by mechanical grinding with molten salt etching Ti3C2Clx

Mg-based materials are currently a hot research topic as hydrogen storage materials due to their considerable theoretical hydrogen storage capacity. However, the kinetic performance of hydrogen absorption and desorption of Mg is too slow and requires high temperature, which seriously hinders the application of this material. MXene is a new type of two-dimensional material with significant role in improving thermodynamics and kinetics. In this experiment, a two-dimensional layered MXene containing Cl functional group was prepared by molten salt etching using the Ti-containing MAX phase as the raw material. Then different ratios of Ti₃C₂Cl_x were uniformly dispersed onto the surface of Mg by high energy ball milling. The samples were characterized by hydrogen absorption and desorption kinetics, SEM, XRD, XPS, and DSC to investigate the effect of Ti₃C₂Cl_x on the hydrogen absorption and desorption performance of Mg. The onset hydrogen absorption temperature can be reduced to room temperature and the hydrogen release temperature is reduced by 200 ​°C by doping Ti₃C₂Cl_x. And there is also 5.4 ​wt% hydrogen storage in the isothermal hydrogen absorption test at 400 ​°C. The results of DSC demonstrate that the E_a of Mg+15 ​wt% Ti₃C₂Cl_x was reduced by 12.6% compared to pristine Mg. The ΔH is almost invariable. The results of XPS show that the presence of multivalent Ti promotes electron transfer and thus improves the conversion between Mg²⁺/Mg and H⁻/H. This study provides a guideline for further improving the hydrogen absorption and desorption performance of Mg-based hydrogen storage materials.     

C对Fe—20%Cr合金抗氧化性的影响

本文对不同含碳量的 Fe-20%Cr 合金进行了900℃静止大气气氛下的抗氧化实验,并测定了在此温度下的氧化动力学曲线.通过结合氧化膜表面微观形貌对氧化动力学曲线的分析,以及氧化膜下表层的微观分析等,指出随含碳量增加,氧化过程由良性的外部氧化转向恶性的内部氧化的过程及原因,并分析了合金中存在的两种主要类型的碳化物对氧化过程的影响.为高温磨损工况下材料的选择提供了一定的理论依椐.