Effect of Al on microstructure and mechanical properties of as-extruded Mg–1Mn alloy sheet

The effect of Al addition on microstructure and mechanical properties of hot extruded Mg–1 Mn alloy sheet was investigated. The results revealed that the dynamic recrystallization was promoted by increasing Al content. The ultimate tensile strength and yield strength of the alloy increased with the increase of Al content. The Mg–9 Al–1 Mn alloy exhibited the highest strength, with tensile strength of 308 MPa, 307 MPa, 319 MPa, yield strength of 199 MPa, 207 MPa, 220 MPa and the elongation of 20.9%, 20.1%, 19.2% in 0°, 45°, 90°, respectively.The high strength was mainly attributed to the formation of fine dynamically recrystallized grains and large amounts of the second phase. The strengthening mechanism of the alloys was explained.

Effect of Al on microstructure and mechanical properties of as-extruded Mg–1Mn alloy sheet

The effect of Al addition on microstructure and mechanical properties of hot extruded Mg–1Mn alloy sheet was investigated. The results revealed that the dynamic recrystallization was promoted by increasing Al content. The ultimate tensile strength and yield strength of the alloy increased with the increase of Al content. The Mg–9Al–1Mn alloy exhibited the highest strength, with tensile strength of 308 MPa, 307 MPa, 319 MPa, yield strength of 199 MPa, 207 MPa, 220 MPa and the elongation of 20.9%, 20.1%, 19.2% in 0°, 45°, 90°, respectively. The high strength was mainly attributed to the formation of fine dynamically recrystallized grains and large amounts of the second phase. The strengthening mechanism of the alloys was explained.