Zn-Cr水滑石的合成及其衍生双金属氧化物催化活性研究

用低饱和共沉淀法合成了不同原子Zn-Cr比的水滑石类化合物，采用XRD，IR，DTA－TG，分光光度法对其结构进行了表征，并以其为前体，350℃、450℃灼烧处理得双金属氧化物催化剂，以乙醇脱水、脱氢为探针反应，用脉冲反应法对比研究了其催化活性。     

氮氧自由基光阻聚剂的研究

文中简单地介绍了新型光阻聚剂-4-羟基-2,2,6,6-四甲基哌啶氮氧自由基的特点、合成路线、结构测试以及阻聚原理。     

钙钛矿型(ABO_3)化合物的光催化活性及其影响因素

:ABO3钙钛矿型复合氧化物具有光催化活性 .其光催化活性与 A- O、B- O的电负性差值、B离子的 d电子结构以及适当掺杂有关     

A new acid pickling process for copper alloys

The cleaning process of removing oxides on the surface of copper alloy sheets was investigated systematically. Through optimizing, a perfect process was selected that is fit for removing oxides on the surface. By acid pickling, all kinds of copper oxides are removed completely, furthermore, no poisonous gases are given out and a smooth and clean surface of copper alloys is obtained. At present, the process is applied successfully in the copper-processing industry.     

小分子有机酸对铁(氢)氧化物表面吸附的砷酸盐的解吸作用研究

采用等温解吸热力学的方法,结合X射线衍射(XRD)与比表面积分析,研究了柠檬酸、草酸和NaCl溶液在pH 6.5环境下对水铁矿、针铁矿和赤铁矿表面吸附砷酸盐的解吸特性。实验结果表明,柠檬酸的解吸能力最强,草酸次之,NaCl最差。这主要是由于柠檬酸和草酸可通过配位交换和诱导配体溶解来解吸砷。但由于柠檬酸分子中可配位-OH多于草酸,因而其解吸能力强于草酸。赤铁矿吸附的砷酸盐最易解吸,而水铁矿吸附的砷酸盐则最难解吸,这与水铁矿具有较大的比表面积和较高的表面活性有关。     

空气电极催化剂La2-xSrxCuO4+λ在氧还原反应中的催化活性研究

合成了La2-xSrxCuO4+λ(0≤x≤1)系列类钙钛矿复合氧化物,并作为催化层电极材料制备了空气电极,在碱性介质中以Hg/HgO为参比电极测量了电极的极化曲线、循环伏安和交流阻抗,考察了组成对催化剂的电催化活性的影响.研究发现La2-xSrxCuO4+λ型类钙钛矿复合氧化物电极材料催化活性较高,并且活性随Sr掺杂量的不同活性也有所变化.EIS测试结果表明不同配比的La2-xSrxCuO4+λ型类钙钛矿复合氧化物电极阻抗谱均由一个半圆和一个拖尾直线组成,并提出了空气电极的等效模拟电路,得到了模拟值,对拟合的动力学参数进行了解释.     

化学发光法氮氧化物分析仪故障分析及解决方案

在对空气自动监测站仪器的10年维护过程中,遇到很多仪器故障和技术问题,通过对仪器的探索和实践,整理了化学发光法氮氧化物分析仪常见故障分析和解决办法,并着重于实际条件,总结出主要依靠自身来排除故障的方案,希望对仪器的正常运行提供一些有益的参考.     

水滑石的合成及其对催化丙酮合成异佛尔酮的影响

用共沉淀法合成铁铝水滑石,焙烧制得镁铝复合氧化物催化剂．采用连续微反装置,以丙酮缩合生成异佛尔酮为探针反应,探讨了镁铝水滑石的合成对镁铝复合氧化物催化性能的影响,采用．XRD、TG—DTA等分析手段对催化利前体镁铝水滑石进行表征．结果表明,镁铝水滑石的合成工艺对水滑石的微观晶体结构有较大影响,镁铝比是较为重要的影响因素...     

传统加热和微波加热下氧化锰矿的碳热还原行为研究

For the purpose of exploring a potential process to produce FeMn, the effects of microwave heating on the carbothermal reduction characteristics of oxidized Mn ore was investigated. The microwave heating curve of the mixture of oxidized Mn ore and coke was analyzed in association with the characterization of dielectric properties. The comparative experiments were conducted on the carbothermal reductions through conventional and microwave heatings at temperatures ranging from 973 to 1373 K. The thermogravimetric analysis showed that carbothermal reactions under microwave heating proceeded to a greater extent and at a faster pace compared with those under conventional heating. The metal phases were observed in the microstructures only under microwave heating. The carbothermal reduction process under microwave heating was discussed. The electric and magnetic susceptibility differences were introduced into the thermodynamics analysis for the formation of metal Mn. The developed thermodynamics considered that microwave heating could make the reduction of MnO to Mn more accessible and increase the reduction extent.     

双钙钛矿Sr2-xKxCOSbO6(0≤x≤0.4)系列氧化物结构及电学性质

采用传统的固相反应法合成了系列多晶样品Sr2-xKxCoSbO6(0≤x≤0.4),利用粉末X线衍射(XRD)和红外光谱对系列氧化物的晶体结构进行了表征,它们都属于单斜晶系,空间群为P21/n.通过标准的四引线法测量了材料的电性能,在300～473 K温度内样品呈现典型的半导体性质,进一步研究了样品的导电机制.