掺杂C60的聚乙烯基咔唑光导光膜的光电子能谱

采用Ｘ－射线光电子能谱表面分析技术并通过变温手段研究了聚乙烯基咔唑（ＰＶＫ）与Ｃ６０的作用形态，结果表明，ＰＶＫ与Ｃ６０可以形成电荷转移络合物，并且它的形成和解离随着温度的变化是可逆的。ＰＶＫ与Ｃ６０的电荷转移络合物的形成可能是改善ＰＶＫ光电性能的关键所在。     

室温基底溅射沉积c轴取向ZnO薄膜

c轴取向氧化锌(ZnO)薄膜具有较强的压电和压光效应,常常用于声电、声光装置。在体声波(BAW)方面,如用于超声显微镜和薄膜谐振器等;在声表面波(SAW)方面,作为一种传输和相干材枓,它用作滤波器、卷积器、放大器、图象扫描以及谐振器;在导向光波(GOW)中,ZnO薄膜也广泛应用于声光和电光装置和二次谐波发生器等。     

等效粒子模型在氢气氛下ZnO脱硫研究中的应用

本文用热重法研究了球形及圆柱体T305脱硫剂在氢气氛下脱除COS反应的宏观动力学。实验表明,该反应对COS为一级反应。在240～390℃的温度范围内,就粒子上的反应而言,反应初期受反应本身控制,中后期转移到颗粒扩散控制。反应活化能及产物层扩散活化能分别为19.097 kJ/mol和46.438 kJ/mol.用等效粒子模型描述动力学行为,给出了该模型的各参数估值,讨论了有氢及无氢气氛下模型参数的差异及其原因。     

纳米ZnO的表面改性研究

研究了纳米ZnO表面改性的影响因素，确定了最优改性剂和改性条件。通过正交实验以月桂酸钠为改性剂、用量为15％、pH值为6、改性时间为1．5h时，改性后的纳米ZnO的亲油化度达到79．2%，能较好地分散于甲醇和二甲苯中。     

Structure and electrical characteristics of Nb-doped SrTiO3 substrates

Strontium titanate (SrTiO3) has been widely used as substrates for growing perovskite oxides thin films be- cause SrTiO3 is chemically and compositionally stable, and has small lattice mismatch with many perovskite oxides[1―3]. It is known that SrTiO3 it…     

Sm3+掺杂碱锌硼硅酸盐玻璃的稳定性

为了实现纳米半导体微晶在稀土Sm^3 掺杂碱锌硼硅酸盐基础玻璃中的受控成核、生长,系统研究了基础玻璃的SiO2与B2O3摩尔比以及BaO、ZnO、La2O3、Y2O3、Nb2O5等不同的网络中间体对玻璃稳定性的影响。研究表明：控制SiO2与B2O3摩尔比以及BaO、La2O3、Y2O3、Nb2O5在玻璃中的掺入量均能提高玻璃的形成能力,增加玻璃的稳定性;不同的组分对于玻璃稳定性的改善也具有不同的机制,但是并不影响玻璃的析晶产物。     

Undoped semi-insulating indium phosphide (InP) and its applications

During the past several years, the research and development of InP material has made great progress due to serving as the substrate for most optoelectronic devices operating at the communications wavelength of 1.31 and 1.55 μm. At present, InP has become an important semiconductor material together with Si and GaAs. When compared to GaAs, InP has higher electron velocity, higher radiation hardness and better heat-conducting property. The advantage of InP crystal material allows higher frequency operation and lower power requirements. Therefore, InP is widely being used for the manufacture of microwave devices, high-frequency devices and optoelectronic integrated circuits (OEICs) which are indispensable for wireless technology, satellite communications^[1—3]. Although n-type and p-type InP can meet actual needs, semi-insulating InP substrates remain to be improved due to their poor uniformity and consistency. For this reason, several possible approaches have been reported to the preparation of SI InP by wafer annealing under different conditions^[4—9].     

[CrMo_6O_(24)H_6]~(3-)掺杂聚苯胺材料的制备及荧光性质

在盐酸介质中,以(NH4)2S2O8为氧化剂,杂多阴离子[CrMo6O24H6]3-为掺杂剂合成出了聚苯胺掺杂材料,用FT-IR,XRD进行了表征,测定了该材料的电导率、常见溶剂中的溶解度及其荧光性质.该材料的电导率为1.4×10-2S·cm-1,最高溶解度可达到0.60mg·mL-1,在以260nm和332nm为激发波长,可分别在425nm和567nm处得到荧光发射峰。     

纳米FePt薄膜材料的研究进展

Ll_0FePt（001）薄膜由于具有较高的磁各向异性和较高的矫顽力在磁记录介质材料方面具有潜在的应用前景,本文从衬底选择、元素掺杂和制备工艺三个方面介绍了FePt薄膜的研究近况。     

新型N-TiO2亚甲基蓝的可见光催化脱色研究

以纳米管钛酸为前驱体, 在氨气气氛中600℃热处理, 制备得到新型氮掺杂TiO₂. 这种二氧化钛具有明显的可见光吸收, 晶型为锐钛矿. 实验表明, 对亚甲基蓝的可见光脱色性能比相同条件下处理P25-TiO₂得到的氮掺杂TiO₂高. ESR结果表明, NO修饰的束缚单电子氧空位(V_O·-8226;-NO-Ti)的生成, 是氮掺杂TiO₂具有可见光催化活性的原因.