不同CO_2压力下形成的N80钢腐蚀产物膜特征

对N80钢在不同CO2压力下进行高温、高压腐蚀实验,根据失重法计算N80钢的腐蚀速率,利用扫描电镜观察腐蚀产物膜的微观形态,分析腐蚀产物膜的厚度和Ca元素含量,利用电化学阻抗谱和极化曲线法测试了腐蚀产物膜的电化学性能,并对腐蚀产物膜与基体间的剪切强度进行了测试.结果表明,随CO2压力增加,N80钢腐蚀速率增大;腐蚀产物膜晶粒尺寸基本不变,膜中微观缺陷数量逐渐增多;腐蚀产物膜电阻和反应电阻呈逐渐增加的趋势;腐蚀产物膜与N80钢基体结合的剪切强度下降,促进了N80钢的腐蚀.     

CO2分压对N80钢腐蚀产物膜保护性能的影响

利用高温高压釜对N80钢进行了两种温度、不同CO2分压下的腐蚀实验.测量了腐蚀速率,观察了腐蚀产物膜的宏观形貌及去除腐蚀产物膜后金属基体的表面状态,用扫描电镜(SEM)观察了腐蚀产物膜的微观形貌并测量了膜的厚度,对在不同条件下成膜的N80钢进行了电化学极化曲线与交流阻抗谱(EIS)分析.结果表明:CO2分压升高,腐蚀产物膜保护性能提高,但由于介质的腐蚀性增强,腐蚀速率上升;膜局部缺陷是导致金属基体表面点蚀的主要诱因,CO2分压升高有利于减少65℃时膜表面的局部缺陷;在90℃下腐蚀产物膜的保护性能比65℃下对CO2分压的变化更为敏感.     

油套管用钢P110的CO_2腐蚀动力学研究

利用高温高压腐蚀试验及电化学原位测量技术,并辅以SEM、EDS和XRD等微观分析手段研究了油套管用钢P110在CO2分压为2 MPa、温度为100℃的3.5%NaCl水溶液中的腐蚀失重、界面反应电化学特性、腐蚀产物膜的微观形貌、成分和结构特征,探讨了油套管用钢CO2腐蚀动力学.研究结果表明:油套管用钢P110的CO2腐蚀产物为FeCO3;随腐蚀时间的延长及腐蚀产物膜的形成,平均腐蚀速率逐渐降低、趋势变缓,产物膜生长满足抛物线生长规律;腐蚀产物晶粒逐渐长大并堆垛紧密,逐渐成膜覆盖于金属表面,膜厚先增加后逐渐趋于稳定,对基体保护能力增强;不同腐蚀时间交流阻抗图谱(EIS)的拟合结果表明,极化电阻随着腐蚀时间增加逐渐增大,电极反应由最初的活化控制变为扩散控制.     

3Cr低合金管线钢及焊接接头的CO_2腐蚀行为

采用高温、高压反应釜和电化学技术对3Cr低合金管线钢及焊接接头的CO2腐蚀行为进行研究.结果表明,3Cr低合金管线钢在高温、高压CO2腐蚀环境中表面生成致密的富Cr腐蚀产物膜,这是其抗CO2腐蚀性能优于X65钢的主要原因.3Cr低合金管线钢焊接接头中母材、热影响区和焊缝的腐蚀产物膜特征相似,结构致密,均存在Cr元素的富集.与X65钢相比,3Cr低合金管线钢的自腐蚀电位较正,自腐蚀电流密度较低.在CO2腐蚀介质中,3Cr低合金管线钢焊接接头的母材区域作为阳极首先发生腐蚀,焊缝和热影响区作为阴极受到保护.     

新型2Cr1Mo2Ni钢在含二氧化碳油田采出液中的腐蚀行为

为弄清Mo和Ni元素在低Cr钢耐蚀方面所起的作用,炼制了新型2Cr1Mo2Ni钢,研究其在模拟油田采出液中的腐蚀行为,实验条件为80℃,0.8MPa CO2分压.利用扫描电镜和能谱分析研究了2Cr1Mo2Ni钢和3Cr钢的腐蚀产物膜微观形貌和成分,测试了高温高压极化曲线和电化学阻抗谱,分析了腐蚀产物膜的生长过程.实验结果表明,Mo和Ni元素在提高抗CO2腐蚀性能方面的作用不及Cr元素.2Cr1Mo2Ni钢腐蚀164h后,中低频感抗弧消失,腐蚀产物膜开始完全覆盖基体表面;腐蚀240h后,生成的腐蚀产物膜具有较好的保护性.     

20钢和16Mn钢在模拟CO2驱环境的腐蚀电化学行为

为提供CO2驱油环境中地面管线钢的选材依据,本文通过动电位极化曲线和交流阻抗谱研究了20、16Mn钢在模拟CO2驱溶液中的腐蚀电化学行为,并对数据进行了拟合分析。结果表明：在饱和CO2条件下,20钢在低温阶段易形成具有保护性的产物膜,而随着温度逐渐升高,产物膜变的疏松,腐蚀加剧;16Mn钢在中低温阶段,随着温度的升高,腐蚀加剧,饱和的CO2极大的促进了腐蚀的发生。     

X70钢在含SO2的弱酸性溶液中的腐蚀行为的电化学研究

用动电位扫描法和交流阻抗法研究了弱酸性溶液中SO2的存在、溶液酸度、温度、浸泡时间和极化电位对X70钢腐蚀行为的影响.结果表明,X70钢在含有SO2的弱酸性溶液中的腐蚀反应过程是受阳极控制的;SO2的存在促进了X70钢腐蚀反应阳极过程的进行;增加酸度和提高温度,主要促进了X70钢腐蚀反应的阴极过程;随着浸泡时间的延长和极化电位的增大,X70钢腐蚀反应的阻抗的模值逐渐减小,高频端相角最大处逐渐向高频方向漂移,相角最大值不断减小.     

海水中硫酸盐还原菌对09Cr2AlMoRE钢的腐蚀行为

采用动极化曲线、电化学交流阻抗谱(EIS)等电化学测试技术和化学浸泡法研究海水中硫酸盐还原菌(SRB)对09-Cr2AlMoRE钢的腐蚀行为.结果表明,SRB新陈代谢产物S2-与腐蚀产物Fe2+反应生成硫化铁,促进了09Cr2AlMoRE钢的阳极活性溶解.09Cr2AlMoRE钢的腐蚀产物呈絮状,颗粒粗大、疏松,分布不连续;杆状硫酸盐还原菌在钢表面局部富集、附着,细菌通过细胞外高聚物被腐蚀产物所包裹.09-Cr2AlMoRE钢在接菌海水中的腐蚀产物由FeS构成,其中硫元素含量高达8.29%.膜沉积处的FeS与附近的09-Cr2AlMoRE钢表面组成腐蚀电偶电池,而SRB的作用在于不断提供H2S以维持FeS的电化学活性,从而加速腐蚀.     

NaCl对N80钢在含CO2溶液中的电化学腐蚀影响的研究

用电化学阻抗谱(EIS)和极化测量，研究了在含CO2的溶液中NaCl含量对N80钢的电化学腐蚀行为的影响．结果表明，随着NaCI含量的增大，N80钢的腐蚀电位正移，抑制了腐蚀过程的阴阳极反应，降低了N80钢的腐蚀速率．分析表明,Cl-在N80钢表面的吸附为Temkin等温吸附．     

大牛地奥陶系马五段硫化氢腐蚀机理与影响因素

为了解决大牛地气田硫化氢腐蚀严重问题,分析了硫化氢腐蚀机理以及影响腐蚀程度的因素。结合大牛地奥陶系马家沟组马五段地质条件以及硫化氢赋存条件确定该区域硫化氢形成的机理,为硫酸盐热化学还原反应;且该区域存在的大量石膏层为含硫化氢气体提供了良好的圈闭条件。硫化氢腐蚀模拟试验模拟了马五段地层水环境对N80钢和P110钢的腐蚀程度,P110钢的腐蚀程度较N80钢轻微,两者均属于极严重腐蚀。结合腐蚀表面微观形貌观测与腐蚀产物能谱分析得出:大牛地奥陶系马家沟组马五段硫化氢腐蚀机理为高温高压下CO2/H2S电化学腐蚀为主;并伴随有高Cl-破坏腐蚀产物膜加速腐蚀。硫化氢腐蚀影响因素分析得出温度和CO2含量增加会加速硫化氢腐蚀。     

Corrosion behavior and characteristics of the product film of API X100 steel in acidic simulated soil solution

The short-term corrosion behavior of API X100 steel in an acidic simulated soil was investigated by electrochemical measurements and soaking experiments, followed by corrosion morphology observations and X-ray photoelectron spectroscopy analyses. The results show that X100 steel exhibits an obvious pitting susceptibility in an acidic soil environment. Pits nucleate after approximately 10 h of immersion. Along with the nucleation and growth of the pits, the charge-transfer resistance and open-circuit potential first increase sharply, then decrease slowly, and eventually reach a steady state. The maxima of the charge-transfer resistance and open-circuit potential are attained at approximately 10 h. The evolution of the electrochemical process is confirmed by the analysis of the product film. The product film exhibits a porous and loose structure and could not protect the substrate well. The product film is primarily composed of ferrous carbonate and ferrous hydroxide (Fe(OH)₂). The concentration of Fe(OH)₂ in the product film increases from the inside to the outside layer.     

温度对L80碳钢在含CO2天然海水中腐蚀行为的影响

 通过高温高压试验和电化学技术研究了温度对L80碳钢在含CO₂天然海水中腐蚀行为的影响,并用扫描电子显微镜(SEM)、能量弥散X射线谱(EDS)和X射线衍射(XRD)对腐蚀产物膜进行了表征。结果表明,随着温度的升高,L80碳钢在液相条件下的腐蚀速率呈先增大后减小的趋势,在90℃达到最大值;而在气相条件下呈现与液相条件下完全相反的趋势。腐蚀产物膜的主要成分为FeCO₃,FeCO₃膜层的阴离子选择透过性以及Cl^-在L80碳钢表面的吸附促进了CO₂腐蚀,在90℃的气相和液相中所形成的腐蚀产物膜的电化学特征进一步验证了高温高压试验结果。     

新型耐蚀低合金钢筋腐蚀行为

 应用动电位极化、电化学阻抗谱、周浸腐蚀试验的方法,研究了HRB400 碳钢钢筋和两种Cr 合金化的低合金钢筋在0.01mol/L NaHSO₃溶液中的腐蚀行为。结果表明,相比HRB400 钢筋,Cr 合金化钢筋的开路电位明显正移,Cr 元素提高了钢的热力学稳定性;随着Cr 元素质量分数的增加,钢筋的自腐蚀电流密度减小,极化电阻增大,Cr 合金化的钢筋具有相对较小的电化学腐蚀速率;周浸加速腐蚀72 h 后,HRB400 钢筋和Cr 合金化的钢筋均以均匀腐蚀为主,添加Cr 元素可以显著降低钢筋的均匀腐蚀速率。     

在混凝土模拟孔隙液中癸二酸二异辛酯的缓蚀特性研究

采用动电位极化曲线和电化学阻抗谱研究了癸二酸二异辛酯在模拟混凝土孔隙液中对钢筋的保护作用.癸二酸二异辛酯的加入导致混凝土钢筋的腐蚀电位正移,对钢筋的阳极电化学过程有抑制作用.其缓蚀效果随癸二酸二异辛酯浓度增加而增加,当癸二酸二异辛酯的浓度为2%时,对含有400mg/LCl-的混凝土模拟液中钢筋电极的缓蚀效率为78.5%.氯离子含量是影响钢筋腐蚀性能和癸二酸二异辛酯阻锈剂作用的重要因素.癸二酸二异辛酯能够在钢筋表面形成沉淀性保护膜.     

咪唑啉季铵盐缓蚀剂的合成及应用性能评价

以腐蚀速率为评价指标,以原料配比、反应时间、催化剂加量为考察因素,采用正交实验设计,得到了咪唑啉季铵盐缓蚀剂的最佳合成条件:苯甲酸与三乙烯四胺物质的量比为2∶1,先在140～160℃经缩合脱水反应2 h,再升温至220～250℃环化脱水反应2 h,得到咪唑啉中间体;然后使中间体与氯化苄在90℃左右反应4 h,得到咪唑啉季铵盐缓蚀剂主剂.将主剂与表面活性剂和溶剂复配,得到酸化缓蚀剂.采用静态挂片失重法和电化学方法考察了该缓蚀剂的缓蚀性能.结果显示:缓蚀剂质量分数为1%时,N80钢在90℃体积分数为15%的HCl介质中,缓蚀率为97%;缓蚀剂是以抑制阳极为主的混合型缓蚀剂.     

纳米TiO2对丙烯酸酯聚氨酯涂层/碳钢界面的初期失效行为的影响

采用激光电子散斑干涉技术、电化学阻抗技术和扫描电化学显微镜技术实时、动态和原位观测了涂覆丙烯酸聚氨酯涂层的碳钢在质量分数为3.5%的NaCl溶液中浸泡初期的界面腐蚀行为,并对比了纳米TiO2的添加对界面腐蚀行为的影响.在浸泡初期无宏观缺陷存在时,激光电子散斑干涉技术成功检测到涂层界面的微小变化,电化学阻抗技术显示不同涂层低频阻抗膜值的变化情况,均与扫描电化学显微镜技术获得的腐蚀电化学形貌结果一致,即在浸泡初期,未添加纳米TiO2的涂层其界面变化速度(即锈蚀萌生速度)较添加涂层明显得多,表明纳米TiO2可延缓涂层/碳钢的界面失效.     

一种席夫碱在酸性介质中对N80钢的缓蚀机理研究

以苯甲醛、水合肼为原料合成一种席夫碱,研究了其在5%的HCl中的缓蚀性能及缓蚀机理,并计算了相应的热力学数据.研究表明:该席夫碱是以抑制阳极腐蚀过程为主的混合型缓蚀剂,它在N80钢表面的吸附过程是吸热过程,其吸附行为符合Langmuir吸附等温式.     

外加电位对X80管线钢模拟海岸土壤腐蚀的影响

为探究双相X80管线钢在沿海土壤模拟溶液环境中的腐蚀机理，采用极化曲线、慢应变速率拉伸试验(SSRT)和交流阻抗(EIS)法对不同外加电位(-750,-900和-1 050 mV vs.饱和甘汞电极(SCE))下双相X80管线钢的应力腐蚀和电化学腐蚀行为进行研究。结果表明，双相X80管线钢在-1 050 mV电位下对应力腐蚀(SCC)最为敏感。慢应变拉伸呈现为脆性断裂，断口可见铁素体区域圆形或椭圆形的凹坑，这是由于过度阴极反应产生的氢原子扩散进入到钢中在铁素体晶界聚集，氢气析出产生的较高氢压超过材料的强度产生圆形孔洞，在拉伸应力作用下变为椭圆形。在此电位下EIS模拟电阻最小，耐腐蚀性最差。-750 mV的外加电位可起到一定的电化学保护作用，但不足以防止X80管线钢应力腐蚀的发生。-900 mV的外加电位可有效抑制X80管线钢的阳极溶解，SSRT的强度和延展性均高于0 mV电位试样，表现出韧性断裂特征，EIS模拟电阻最高，因此双相X80管线钢在模拟海岸土壤环境下最佳的阴极保护电位约为-900 mV vs. SCE。双相X80管线钢在沿海土壤模拟环境中的应力腐蚀行为的研究可对其在实际使用过...