蔡家营铅锌银矿床中的钾质白云母研究

钾质白云母是铅锌银矿床中的主要热液蚀变矿物,通常表现为白云母化、绢云母化、伊利石化。系统地研究了钾质白云母化的矿物组成,采用了电子探针、差热分析、X射线分析等技术方法,探讨了钾质白云母的结构特征和形成的地质环境及找矿意义。     

广东韶关高岭土的矿物特性

采用X射线荧光光谱分析（XRF）、化学分析、X射线衍射分析（XRD）、扫描电镜（SEM）、电子探针（EPMA）及激光粒度分析等方法,综合研究了广东韶关高岭土的化学组成、矿物组成、矿物形貌、粒度分布及铁、钛染色物质的赋存状态.结果表明：广东韶关高岭土是一种富钾高岭土,90%的颗粒粒径小于25.86μm,主要矿物为高岭石（约90%）、长石（约5%）、伊利石（约3%）、石英（约1%）、云母（约1%）,此外含有少量的赤铁矿、褐铁矿、黄铁矿、锐钛矿,其中高岭石呈微鳞片层状.     

陕西汉中南郑蛇纹石玉的矿物学研究

目的 研究南郑蛇纹石玉的矿物学特征及其颜色成因.方法 通过对南郑蛇纹石玉进行野外调研,并结合镜下观察、扫描电镜、X荧光光谱分析、X射线衍射、红外光谱等现代分析手段对南郑蛇纹石玉进行矿物学综合研究.结果 南郑蛇纹石玉主要矿物成分为利蛇纹石,呈隐晶质、毛毡状交织结构.玉石中出现少量Fe,Ti,Mn离子替代Mg,占居八面体位置,Al替代部分Si,占居四面体位置,还有部分O被OH取代.结论 南郑蛇纹石玉致色因素有多种,主要与过渡金属离子Fe~(3+)的d-d跃迁以及Mn的含量有关.     

氧化铜对高胶凝性熟料矿物形成及固溶的影响

借助化学分析法测定了水泥熟料中C4A3S矿物的含量和Cu2 离子在熟料中的浸出率,用X射线内标法测定了水泥熟料中C3S含量;用X射线衍射和差热分析研究了矿物形成过程;并采用扫描电镜和透射电镜分别研究矿物形貌和C3S晶体结构.研究结果表明:生料中掺入一定量的CuO,能降低水泥熟料的烧成温度,促进C3S和C4A3S两种矿物相互共存.过高的CuO亦会降低C4A3S矿物的分解温度.     

滁州绢云母XRD和红外分析的研究

绢云母具有广阔的应用前景与市场潜力,蒙脱石(间层)具有膨胀性会对绢云母在涂料中的使用产生影响。本文通过对滁州产出的绢云母分别进行了X射线衍射、化学成分、红外吸收光谱等分析,滁州绢云母具有结晶度较高,水化程度较低的特征,它的10与5衍射峰的半高宽W1和W2基本相等,表明滁州的绢云母中不含有蒙脱石(间层)。     

含硼铁精矿工艺矿物学研究

采用传统工艺矿物学研究方法,结合X射线衍射、化学分析、MLA等分析手段对含硼铁精矿的化学组成、矿物组成、矿物嵌布特征进行了详细研究.结果表明:含硼铁精矿中的硼、铁分别主要赋存于硼镁石及磁铁矿中;主要脉石矿物为蛇纹石、云母及碳酸盐矿物;矿石中矿物连晶复杂、共生关系密切,磁铁矿、硼镁石、硼镁铁矿紧密共生,与蛇纹石、云母等密切连生,多呈犬牙交错状或不规则状接触;此研究结果对含硼铁精矿的合理综合利用具有一定的指导意义.     

吉林哈福瓷石矿矿物岩石特征的研究

本文采用系统的实验资料,较详细研究了吉林哈福瓷石矿的矿物岩石特征,其中包括差热及热失重特征,X射线衍射特征,红外吸收光谱特征,电子探针及电镜特征等。研究结果表明:矿石主要由水云母(含少量绢云母)、石英及少量蒙脱石组成,其中水云母占30-50％,石英占50-70％;化学成分与南方瓷石相比,具有SiO_2偏高,AiO_3、K_2O偏低的特点;它是在相对封闭的系统中,在中性到弱碱性的中低温热液条件下,由集细斑岩蚀变而成,并测得矿石包体平均均一温度为138℃,包体气液的PH值约等于7。因此,哈福瓷石是一种独具特色的岩石——水云母绢英岩;矿石可作为腊质代用原料和日用、工业陶瓷的原料及釉面砖原料。     

树瘤状ZnO-Bi2O3复合氧化物微晶的生长及光学特性

利用超声液相掺杂法合成具有三级分型结构的Bi₂O₃-ZnO纳米复合氧化物.用粉末X射线衍射（XRD）和X射线光电子能谱（XPS）对产物的物相和组成进行分析.扫描电镜观察结果表明,超声时间和掺杂氧化铋摩尔分数是控制产物形貌的关键因素.同时探讨树瘤状晶体形成机理.紫外-可见（UV-Vis）和荧光光谱（PL）显示所合成的产品具有光学性质.     

矿渣胶凝材料固结尾砂的微观实验

用X射线衍射、扫描电镜和热重!差示扫描量热方法表征了矿渣胶凝材料的水化产物和微观结构,研究了矿渣胶凝材料对尾砂固结过程的影响.微观实验结果表明:矿渣胶凝材料的水化产物主要为水化硅酸钙凝胶(C—S—H)、钙矾石(AFt)及少量的帕水钙石(Ca2Al4Si4O15(OH)2.4H2O)和沸石类矿物,随着养护时间的延长,矿渣胶凝材料在水化过程中发生晶体结构重组和重排;尾砂中的方英石、云母和碳酸盐类矿物(方解石、白云石等)是尾砂固结过程中的活性成分,能生成其他晶体矿物和胶凝状矿物,这是导致固结体微观结构不同的主要原因.     

青田石主要品种的宝石学特征研究

青田石是我国重要的玉石种类之一,选取青田石的几个主要品种,对其进行常规宝石学特征以及大型仪器测试,结果表明:所选青田石样品结构细腻,主要组成矿物均为显微鳞片状集合体。所选样品中封门黄、红花冻的主要矿物成分为叶蜡石;紫檀冻主要由叶蜡石和绢云母组成;蓝星的主要组成矿物为叶蜡石和伊利石;山炮绿的矿物成分主要为绢云母;珍珠冻的主要矿物组成为红柱石和叶腊石。     

一个翡翠新品种的发现

在缅甸发现一个翡翠新品种——榴辉翠,其主要组成矿物为石榴石和绿辉石,是绿辉石质翡翠类的新成员,也是榴辉岩的新类型。它呈深绿色,有淡黄绿色斑点,其他宝石学特征与绿辉石质翡翠相似。用电子探针、X射线粉晶分析、红外光谱等测试手段对榴辉翠进行了详细研究。     

SiC对不锈钢的摩擦磨损特性

在室温、无润滑的条件下,利用销盘式摩擦磨损实验考察了SiC与不锈钢(1Cr18Ni9Ti)组成摩擦副的摩擦磨损特性,SiC在5 N和20 N载荷作用下磨损机制为脆性分层磨损.SiC随载荷增加摩擦系数减少,但磨损率随载荷增加而增加.结果表明,SiC与不锈钢对磨时,磨损率达10-4mm3/(N.m)-1数量级,属磨损剧烈,不适合组成摩擦副.     

微乳体系相图及超微CuI晶体的合成与研究

考察了W([H2O]/[SDS])、T(温度)对SDS/正丁醇/环己烷/水四元微乳液体系相图的影响,并在T=60℃时利用此体系合成了超微的碘化亚铜晶体。用XRD、IR、TEM对产物进行了表征。结果表明:当W([H2O]/[SDS])=20、T=60℃时所得到的碘化亚铜晶体是粒径在100nm左右的块状立方晶体。     

Nano Cr Interlayered CrN Coatings on Steels

CrN coated steels assisted with a nano Cr interlayer were investigated. The Cr nano-interlayers were prepared by sputter deposition with a thickness about 70-100 nm. CrN coatings were also prepared by sputter deposition on the Cr nano-interlayers. The crystal structures, microhardness, and scratch resistance of CrN/Cr coatings were determined. Results show that the Cr nano-interlayers improve scratch resistance and the microhardness of CrN coated steels. A rapid heat treatment with infrared （IR） was performed for coated specimens in the attempt to improve bonding, With IR heat treatments, the beneficial effect of the Cr nano-interlayers was clearly observed. Without the Cr nano-interlayers, severe cracks on the surface of coatings were observed after IR heat treatment. However, with a Cr interlayer, no cracks on the surface of CrN coatings were observed after the heat treatment. The scratch resistance of coatings was also affected by the Cr nano-interlayers. The scratch track was clean and showed significantly smaller amount of scratch debris for CrN coatings with Cr interlayers than those without the Cr nano-interlayers. The microhardness of coatings with the Cr nano-interlayers is higher than those without the Cr nano-interlayers after IR heat treatment. The Cr and CrN phase have been identified with X-ray diffraction analysis, and the results show that the higher the nitrogen content in the sputtering gas, the stronger the CrN peaks observed in the diffraction patterns are.     

珠江广州段微表层和次表层水中重金属分布与风险的初步评价

2009年2月至7月对珠江广州段4个站位的微表层与次表层水中As、Cd、Cr、Cu、Zn和Pb的质量浓度进行调查研究,并对健康风险作了初步评价.结果表明:珠江广州段水体均不同程度地受到6种重金属的污染;除Zn以外,微表层对其余5种重金属均具有较强的富集作用;通过饮水途径所致健康风险中,微表层平均总致癌风险为1.7×10-4.a-1,是次表层平均总致癌风险1.5×10-4.a-1的1.1倍,是国际辐射防护委员会(ICRP)推荐的最大可接受风险水平5.0×10-5.a-1的3.4倍;总致癌风险(As、Cd和Cr)约占总风险的99.8%,远高于总非致癌风险(Cu、Zn和Pb)的0.2%,控制含Cr和As废水的排放是降低该河段重金属污染物健康风险的有效途径.     

X射线荧光光谱测定铝矿石中主次量元素含量

用熔融玻璃片制样,用理论a系数和基本参数次法校正元素间的效应,用X射线光谱仪对铝矿石样品中的Al2O3、SiO2、Fe2O3、TiO2、K2O、Na2O、CaO、MgO、P2O5、MnO、S、Pb、Zn、Sr、Sc Zr、V、Ga、Cr等19种组分进行测定。结果表明,各组分的RSD均小于9.80%,除个别组分元素的含量在检测限附近误差较大,其余组分元素含量与标准值基本吻合。该测定方法的精密度和准确度可与化学法相媲美。     

翡翠中绿辉石的矿物学特征

本文对翡翠中主要组成矿物绿辉石的矿物学特征进行了探讨。研究表明绿辉石的主要化学成份为ＳｉＯ２、Ａｌ２Ｏ３、Ｎａ２Ｏ,含有少量ＴＦｅＯ、ＭｇＯ、ＣａＯ、Ｃｒ２Ｏ３、ＭｎＯ、ＴｉＯ２、Ｋ２Ｏ。其绿辉石的化学成份介于硬玉与透辉石的二元混溶系列的中间态,具有Ｐ２或Ｐ２／ｎ型结构绿辉石的特征,这也得到了绿辉石的Ｘ射线粉晶衍射分析的证实。     

哈尔滨大气PM2.5中人为源元素化学组成特征及来源

应用场发射扫描电镜(FESEM)和电感藕合等离子(ICP-MS)技术对2007年哈尔滨市市区四季所采集的PM2.5样品进行了研究。图像分析和粒度分析表明:PM2.5的颗粒类型主要为矿物颗粒、飞灰颗粒和烟尘集合体,数量—粒度呈双峰分布,峰值出现在0.2～0.5μm和1.0～2.5μm之间。其中飞灰颗粒的数量占总颗粒数量的26%,体积只占颗粒总体积的3%,即PM2.5中细颗粒主要为飞灰颗粒。元素分析和富集因子分析表明,颗粒中所测的58种元素中有Cd、Sn、Tl、Te、Bi、V、Pb、Sb、Zn、As、Ag、In、Mo、Cu、Ga、Cr、W 17种元素在颗粒中得到富集,来自人为源,且燃煤源为主要贡献者。因子分析显示冶金排放、垃圾焚烧、汽车尾气源及动力与机电工业排放源也是明显的贡献者。     

鳞片石墨在水中的聚团行为

鳞片石墨在水中表现出强疏水性,易形成疏水聚团,其聚团行为影响分选过程的选择性和加工利用过程的分散性。通过对鳞片石墨粉体颗粒的润湿接触角、润湿热、ξ电位的测量及真空浮选实验,研究了鳞片石墨在水中的聚团行为。结果表明:鳞片石墨粉体颗粒的接触角接近90°,疏水性强;不同粒级的鳞片石墨被水润湿呈现出放热和吸热两个过程,且不能自发进行;接触角越大,Zeta电位越小,颗粒越易聚团。石墨颗粒在水面上以大鳞片为中心形成片状聚结,随着颗粒浓度的增多,相互叠加形成远大于颗粒尺度的聚团。鳞片石墨在水中的聚团行为符合扩展的DLVO理论,颗粒间的疏水作用力是聚团形成的根本原因。     