膨润土的改性实验及表征

为提高膨润土对低浓度瓦斯的吸附性能,用质量分数3%的硫酸溶液和正二十四烷通过化学浸渍法对膨润土原土进行改性实验。对硫酸改性膨润土、正二十四烷改性膨润土、膨润土原土进行N2的吸附、比表面积、孔容和孔径测试。通过改性前后数据对比可知,改性后膨润土的吸附量、比表面积、孔容相应的增大,且硫酸改性膨润土的性能优于正二十四烷改性膨润土。改性后膨润土对CH4的最大吸附量为5.36 mmol/g,比改性前增加了3.72 mmol/g,增量明显。     

改性膨润土对水中敌百虫和敌敌畏的吸附性能研究

研究了用季铵盐阳离子表面活性剂四甲基氯化铵（TMAC）、四乙基氯化铵（TEAC）和十六烷基三甲基溴化铵（CTMAB）改性的膨润土对有机磷农药敌百虫和敌敌畏的吸附性能。结果表明，用阳离子表面活性剂改性的膨润土的层间距和有机碳含量与改性时所用表面活性剂种类有关；改性膨润土对水中敌百虫和敌敌畏的吸附能力优于原土，并且吸附量随阳离子表面活性剂碳链的增长而增大；同一长链阳离子表面活性剂改性的膨润土对敌敌畏的吸附能力大于敌百虫；温度升高不利于敌百虫和敌敌畏在改性膨润土上的吸附。     

硅溶胶处理剂改善膨润土吸附性

通过测定分析硅溶胶、膨润土对金属阳离子吸附能力，对硅溶胶处理膨润土进行研究。实验证明用硅溶胶处理后膨润土吸附能力提高１０－１７％。     

表面活性剂改性膨润土吸附Cr(VI)的研究

研究了膨润土原土及2种经不同表面活性剂改性的膨润土在不同的pH值、不同的用量等条件下对Cr(VI)的吸附情况,以及3种土达到吸附平衡所需的时间.还研究了3种土对Cr(VI)的等温吸附.结果表明,1827改性的膨润土吸附效果好,平均去除率为93%,且几乎不受pH值和时间的影响.其中2种改性膨润土对Cr(VI)的吸附为Freundlich吸附.     

膨润土改性与印染废水脱色研究

试验分别采用焙烧法、酸浸法(HCl)、盐浸法(NaCl)对辽宁钙基膨润土进行了改性处理,并利用改性膨润土对印染废水进行吸附脱色性能的研究。结果表明:改性膨润土的吸附性能优于天然钙基膨润土,其中500℃焙烧后改性的膨润土吸附效果最佳。最佳脱色工艺条件为:体系pH值1～3、搅拌时间20 min、改性土用量30 g/200 mL。经过处理的废水水样,色度去除率达到99.0%以上,化学需氧量(CODcr)为92.16 mg/L,达到了国家一级排放标准(GB8978-1996)。     

壳聚糖改性膨润土的制备及其对活性嫩黄的吸附性能研究

通过对壳聚糖(CTS)改性膨润土的制备(改性土)及对活性嫩黄印染废水吸附性能研究,探讨了壳聚糖量、醋酸体积分数等因素,制得改性土以及改性土用量、染料质量浓度、介质的pH等对吸附性能的影响.结果表明:随着壳聚糖量的增加,吸附量逐渐增大,达到最大值后逐渐减小;醋酸体积分数为1%时制备的壳聚糖改性土吸附效果最好.随着改性土用量的增大,吸附量逐渐减小;吸附量随活性嫩黄染料质量浓度的增加而增加.壳聚糖量为0.089g、醋酸体积分数1%、改性土用量0.600g,吸附效果最好.吸附试验符合Arrhenius方程模型,并通过XRD分析结果证实了改性土的制备.     

膨润土改性天然粘土防渗材料的研究

膨润土具有很好的防渗和吸附性能．在华北黄土和华南红土中加入一定量的膨润土，以增强衬层材料的防渗性能．研究了膨润土加入量对土样抗压强度和压实土样渗透系数的影响，压实含水率、压实干密度等因素对压实粘土渗透性能的影响．实验原理为Darcy定理．实验结果表明：对于黄土，膨润土合量为6％—7％时，抗压强度最大．选择大于强度最优含水率2％的压实含水率有利于提高黄土及其改性粘土的防渗功能．对于红土，加入8％的膨润土对其抗压强度有很大的改善，抗渗性能有着较大的提高，渗透系数只相当于原土的1／30．选用24％左右的压实含水率可以使红土(及其改性粘土)的抗压性能与防渗性能同时优化．     

改性膨润土对废水中硫化物的吸附及再生研究

采用微波辐射技术和盐酸对膨润土进行活化改性处理,研究了改性膨润土对废水中硫化物的吸附性能.实验结果表明,改性膨润土对硫化物的吸附能力明显增强.吸附时间、温度、pH值和膨润土用量是影响吸附的主要因素.改性膨润土对硫化物的吸附规律较好地符合Freundlich吸附等温式.采用30%双氧水作为膨润土的再生剂,可使其再生重复使用.     

壳聚糖改性膨润土对酸性红吸附性能的研究

探索壳聚糖与膨润土的质量比与反应介质酸度对制备壳聚糖改性膨润土的影响并以改性土为吸附剂探讨了改性土质量、吸附温度、吸附时间、介质的pH值及酸性红溶液质量浓度对酸性红吸附性能的影响.结果表明:制备的改性土随着壳聚糖质量的增加吸附量先增大后减小、随着反应介质的酸度增强,改性土的吸附能力增加;随着改性土质量的增加吸附量先增大后减小;随着反应温度上升改性土吸附能力先增大后减小;随着酸性红染料质量浓度的增加吸附能力增加;随着反应pH值的增大吸附能力先增大后减少.质量比为1∶125,冰醋酸体积分数为1%为最佳制备条件,改性土质量为0.6g,温度温度为25℃,吸附时间为70min,介质pH为7左右时是最佳吸附条件.且其吸附行为满足Langmuir等温式.     

有机改性膨润土对氧化乐果的吸附作用

以钙基膨润土为原料,经提纯钠化后用十二烷基三甲基溴化铵进行有机改性.探讨了有机膨润土对有机磷农药氧化乐果的吸附性能,考察了pH、温度、吸附时间以及有机膨润土用量对吸附效果的影响.结果表明,改性膨润土对水中氧化乐果的去除能力优于原土,对50 mL浓度为0.8 g/L的氧化乐果溶液,在pH值为7.0、温度25℃、吸附时间30 min、有机膨润土投加量10 g/L条件下,对氧化乐果的去除率可达80.6%.     

水分散性纳米SiO2的制备、表面修饰及性能

以硅粉为主要原料，在碱催化下制备出了高固含量、低成本的纳米SiO2水分散液。采用聚醋酸乙烯对纳米SiO2进行了表面修饰，并对其机理进行了探讨。研究了反应奈件和表面修饰条件等对水分散性纳米SiO2性能的影响，得到了适宜的工艺条件。     

改性微粒硅溶胶的研制及应用机理研究

The preparation and their application in papermaking of aluminium modified silica sol (AMS) and boron modified silica sol (BMS) were first investigated in China. At the same time the structures and configurations of AMS and BMS were first time authenticated. The modified silica sol microparticle system was detailedly and systemically studied with colloid charge titration. On the research of flocculation mechanism the laser sizer was also first time used to determine the floc size. Results showed that sodium silicate was treated and acidification was carried out by means of strongly acid cation exchange resins and obtained almost sodium free acid sols. The acid sol obtained after acidification was then made alkaline.     

APPLICATION OF BORON MODIFIED SILICA SOL ON RETENTION AND DRAINAGE

INTRODUCTIONRecently with the high speed, large-scale develop-ment of papermaking, in the manufacture of paper and paperboard conventional single and dual reten-tion and drainage systems cannot obtain satisfying re-tention and drainage. So in 1980 microparticulate systems appeared. Because of its superiority such as good retention effectiveness on fine and chemicals, improving drainage and paper formation, reducing waste water and enhancing the concentration of white water for good recover…     

壳聚糖季铵盐改性膨润土的制备及其对印染废水处理

 以膨润土为原料,利用壳聚糖季铵盐为改性剂,探讨制备壳聚糖季铵盐改性膨润土的最佳条件。结果表明,土液比为50g·L-1,原土粒度为0.150mm,壳聚糖季铵盐溶液的质量浓度为1.5g·L-1,微波加热时间7min,浸泡时间30min条件下制备的改性膨润对模拟印染废水脱色率较好,通过正交实验,确定了改性膨润土处理模拟印染废水的最优条件为：pH值为3.0,投土量为14g·L-1,搅拌速度为150r·min-1,搅拌时间为20min,离心时间为8min。对直接耐晒翠兰和酸性橙红的脱色率分别高达94.6%和80.3%,改性土对直接耐晒翠兰的脱色效果优于对酸性橙红的脱色效果。     

KH-550改性纳米二氧化硅的研究

用硅烷偶联剂KH-550对纳米SiO2样品表面进行改性,测定了改性SiO2样品的亲油化度,并用羟基紫外线吸收法测试了改性效果,对所得纳米SiO2样品的改性效果进行了评价,探讨了纳米级SiO2的改性机理.结果表明,改性剂用量、改性温度、改性时间明显地影响改性效果.通过对改性工艺条件的合理调控,实现了用硅烷偶联剂KH-550改性纳米SiO2样品,找到了合适的改性工艺与条件,所得改性纳米SiO2样品具有较高的疏水性.     

白炭黑的表面改性和性能研究

为提高白炭黑对有机高分子的亲和性,利用偶联剂同时拥有亲油基和亲水基的结构特性,对白炭黑颗粒表面进行改性.考察了改性时间、温度、pH和偶联剂与白炭黑的质量比对白炭黑表面改性情况的影响.通过红外光谱、热失重、氮气吸脱附、接触角、活化度及沉降体积测试等手段对改性前后白炭黑结构及改性效果进行表征.结果表明,γ-甲基丙烯酰氧基丙基三甲氧基硅烷(KH570)的改性效果明显优于γ-巯丙基乙氧基双(丙烷基-六乙氧基-硅氧烷)(Si747)和双-(γ-三乙氧基硅基丙基)四硫化物(Si69).以无水乙醇为改性剂,当KH570与白炭黑的质量比为14%、改性温度为50℃、pH为7、改性反应6 h时,活化度达到最大.改性后偶联剂接枝在白炭黑表面,亲水性降低、分散性提高,表面浸润性得到明显改善,拓宽了白炭黑在工业中的应用范围.     

透水铺装改性基层对典型径流污染物动态除污实验研究

为提高透水铺装对雨水径流的净化作用,通过优选骨料和掺入添加剂的方法对透水铺装基层进行改性,制备了沸石基层、陶粒基层、掺粉煤灰砾石基层和掺膨润土砾石基层;同时制备一组传统砾石基层作为参照对比基层;并将改性后的基层和参照基层对雨水径流典型污染物COD、TP、TN、Cu~(2+)的削减作用进行了过滤吸附实验。实验结果表明,4种改性基层对污染物去除能力整体上较传统砾石基层均有一定程度的提高;但不同改性方法对污染物的去除效果差异较大。整体来看,掺膨润土砾石基层对污染物COD、TP、Cu~(2+)的去除效果最好;但在去除TN的实验中,除沸石基层外,其他基层对TN的去除效果皆不理想。研究结果表明,过滤除污实验中,掺入添加剂方面改性,掺膨润改性基层对于污染物削减效果最好;而掺入骨料方面,沸石改性基层去除效果最佳。建议将沸石作为骨料,膨润土作为添加剂制成改性基层,以最大化实现去除污染物的作用。     

大豆分离蛋白/二氧化硅改性水性聚氨酯膜性能的研究

采用溶胶-凝胶法制备了大豆分离蛋白/二氧化硅杂化溶胶,并应用于水性聚氨酯的改性.采用流延法制备大豆分离蛋白/二氧化硅/水性聚氨酯共混膜,红外光谱研究表明大豆分离蛋白、二氧化硅和水性聚氨酯间发生了多层次的氢键作用,以膜的拉伸强度、断裂伸长率和溶失率为指标,研究了各组分混配比例对共混膜力学性能及耐溶剂性能的影响.通过接触角、热重分析、扫描电镜和原子力显微镜分析讨论了共混膜的亲水亲油性、耐热性能,以及膜表面的形态形貌.结果表明,大豆分离蛋白/二氧化硅添加量为6％（质量分数）、两者之间质量比为1∶1时,改性膜的力学性能最优,耐溶剂性随添加量增加而改善.