SBR/PAANa遇水膨胀橡胶的力学及膨胀性能研究

研究了SBR/PAANa混炼型遇水膨胀橡胶的力学及遇水膨胀性性能.结果表明,PAANa含量越高,SBR/PAANa膨胀性能和压缩永久变形性越高,但拉伸强度逐渐降低;相对于在去离子水中,增加金属离子浓度或者金属离子电荷都会使SBR/PAANa膨胀性能下降.     

ABS/硅橡胶共混物的阻燃性能研究

研究了十溴联苯醚/三氧化二锑(DBDPO/Sb2O3)、有机硅橡胶/含氟聚合物、有机硅橡胶/硬脂酸镁、二盐基亚磷酸铅、滑石粉对ABS燃烧性能的影响.研究结果表明:DBDPO/Sb2O3阻燃体系配合含氟聚合物对ABS/硅橡胶共混物的阻燃是有效的.当硅橡胶2PHR、含氟聚合物1PHR、添加剂DBDPO/Sb2O320PHR时,ABS的氧指数达27;二盐基亚磷酸铅对硅橡胶/硬脂酸镁阻燃ABS有较强的助阻燃作用.     

顺丁橡胶/丙烯酸酯橡胶/甲基乙烯基硅橡胶共混材料制备及性能

用顺丁橡胶(BR)、丙烯酸酯橡胶(ACM)和甲基乙烯基硅橡胶(MVQ)共混的方法,研制具有优异力学性能和耐热性能的共混材料.通过样品力学性能及热老化性能的测定,确定共混的最佳配比和制备工艺;采用傅里叶变换红外光谱分析(FT-IR)和差示扫描量热仪分析(DSC)测试手段,研究了并用胶的表面形貌和化学组成.结果表明:BR/ACM/MVQ并用胶的相容性好于ACM/MVQ的相容性,BR能够与ACM和MVQ形成交联网络.BR的加入改善了ACM/MVQ的相容性,增大的相界面积和分子链段的运动,降低了BR/ACM/MVQ的玻璃化温度(t_g),同时,力学性能及耐热性能明显改善.     

Oil Gels Based on Styrene Butadiene Rubber

Four oil absorbents based on styrene butadiene (SBR), i.e., pure SBR (PS), 4. tert-butylstyrene-SBR (PBS), EPDM-SBR network (PES) and 4.tert-butylstyrene-EPDMSBR (PBES), were produced from crosslinking polymerization of uncured styrene butadiene rubber (SBR), 4-tert-butylstyrene (tBS) and ethylene-propylenc-diene terpolymer (EPDM). The reaction took place in toluene using benzoyl peroxide (BPO) as an initiator. Uncured SBR was used as both a pre-polymer and a crosslink agent in this work, and the crosslinked polymer was identified by IR spectroscopy. The oil absorbency of the crosslinked polymer was evaluated with the method ASTM (F726-81). The order of maximum oil absorbency was PBES>PBS>PES>PS. The maximum values of oil absorbency of PBES and PBS were 74.0g/g and 69.5g/g, respectively. Gel fractions and swelling kinetic constants, however, had the opposite sequences. The swelling kinetic constant of PS evaluated by an experimental equation was 49. 97×10~(-2)h~(-1).     

丁基橡胶/聚(苯乙烯-甲基丙烯酸甲酯)互穿聚合物网络的结构与阻尼性能

为提高材料的阻尼性能,采用分步方法,以丁基橡胶(IIR)为聚合物网络Ⅰ,聚(苯乙烯-甲基丙烯酸甲酯)[P(St-MMA)]为聚合物网络Ⅱ,制备了丁基橡胶/聚(苯乙烯-甲基丙烯酸甲酯)互穿聚合物网络[IIR/P(St-MMA)IPN].采用红外光谱、动态力学分析等检测手段研究了反应时间、IIR/P(St-MMA)质量比、交联剂用量、丙烯酸丁酯(BMA)的含量等因素对IPN材料阻尼性能的影响.实验结果表明:适量极性单体的加入有利于提高IPN的阻尼性能;添加交联剂和单体BMA可明显提高IPN的阻尼性能.     

橡胶力学状态方程的非高斯链校正

橡胶状态方程是描述轻度交联橡胶应力应变曲线的基本方程,然而该方程与实际拉伸过程所反映的应力应变曲线有较大的误差,仅在拉伸比小于1.5时才吻合.该文采用统计与等效自由旋转链相结合的方法对橡胶拉伸后偏离高斯链进行校正,得到了非高斯链校正因子,从而获得了在较广的拉伸比范围内均与橡胶实际拉伸曲线相吻合的理论方程.     

聚氨酯橡胶和丁腈橡胶-镍基喷焊层摩擦副湿磨粒磨损试验研究

对聚氨酯橡胶(UR)丁腈橡胶(NBR)与Ni基喷焊层摩擦副湿磨粒磨损进行了试验研究。研究结果表明,摩擦副具有较强的抗磨性,聚氨酯橡胶(UR)较丁腈橡胶(NBR)具有更高的抗磨性。高聚物的磨损量随比压和相对速度的增加而增大,摩擦系数随相对速度的增加而增大,随比压的增加而减少。本试验结果对石油钻井机械中,摩擦副在磨粒、腐蚀介质中的选材有参考价值。     

天然橡胶对聚乳酸的改性研究

为了更好地将聚乳酸(PLA)这种可以完全降解的环境友好型高分子材料应用在环保塑料这个领域中，并克服其固有的脆性.选用具有良好的韧性、生物相容性以及低成本可再生的天然橡胶(NR)来对PLA进行改性.采用动态硫化熔融加工的方法制备不同NR质量分数(5%～15%)的NR-PLA复合材料.通过机械性能测试发现，加入10%NR后，断裂伸长率由7.3%(PLA)升高到41.1%，表明NR对PLA具有显著增韧的效果；并且通过SEM发现两者之间相容性较好.本研究对进一步更好地应用PLA具有推进作用.     

多壁碳纳米管/硅橡胶复合材料压敏元件特性

为研究碳纳米管填充聚合物复合材料的压力敏感特性,将硅橡胶为基体、多壁碳纳米管为填料的复合材料涂覆在印制板基底上,经溶剂挥发成膜,制备出柔顺式复合材料压敏元件。对碳纳米管质量分数1.6%、4.3%、9.3%的元件进行压阻特性测试,在单轴步进压力下实时检测压力和元件电阻。结果表明,压敏元件在0～110N单轴步进压力下表现出正压阻效应,特性曲线的变化区间与碳纳米管质量分数相互对应。提出压阻效应的机理是元件在压力作用下产生变形,导致碳纳米管导电网络发生破坏与重构。扫描电镜分析表明,碳纳米管随机取向分散于硅橡胶基体中,形成1-3型复合结构。该新型复合材料压敏元件可用于开发柔顺式力传感器。     

Thermal properties study on the ablation materials of inorganic silicon compound from organosilicone in high percent conversion

The new type of silicone rubber prepared by organosilicon polymer containing special groups presents the tensile strength of 3.92 MPa and the elongation at break of 285%. Compared with Sylgard~184 sili-cone rubber (Dow Corning Corporation),it has better high temperature resistance and almost no weightlessness from room temperature to 430℃. Thermogravimetric analysis was conducted to re-search the thermal degradation at different temperatures and the heat pyrolysis products were trace determined by FT-IR. The results show that with the increase of temperature,the organic groups of products are gradually decomposed. Organosilicon rubber is gradually changed into the typical inor-ganic SiCO compounds in the process of pyrolysis. Elemental analysis and X-ray photoelectron spec-troscopy results show that the pyrolyzates are mainly composed of Si,C and O elements above 1050℃. X-ray diffraction analysis showes that partial β-SiC crystal structure is brought about gradually from the pyrolysis products at 1050℃ to 1500℃ under nitrogen atmosphere. With the treatment temperature rising,the crystallinity of SiC and cristobalite obviously increases.     

在干摩擦和边界润滑条件下丁苯橡胶对20#钢的磨损机理研究

用扫描电子显微镜 (SEM)和X射线光电子能谱仪 (XPS)分析了磨损表面的形貌、元素含量及金属表面元素化学状态的变化 ,用镜面全反射傅立叶红外光谱仪 (FT IR)分析了橡胶表面官能团的变化。结果表明 ,2 0 # 钢被磨损的物理过程为磨粒磨损 (微切削 )。 2 0 # 钢被磨损的化学机制包括 :①金属及其氧化物与丁苯橡胶大分子自由基的反应 ;金属与具有含氧基团的丁苯橡胶分子链间的反应 ;②金属与矿物油烷烃链间及金属与氧化的矿物油烷烃链间的反应 ,主要反应产物为含有Fe C的金属聚合物及含有Fe O的聚合物 ;③金属本身的氧化 ,主要反应产物为Fe2 O3 ,FeO和Fe3 O4,在边界润滑条件下的金属磨损表面的氧化最明显     

深部调驱缓膨高强度颗粒的制备及其性能评价

为了减缓聚丙烯酰胺体膨颗粒遇水膨胀速率,满足非均质性地层深部调驱的需要,采用乳液聚合技术,以丙烯酰胺、天然胶乳为主要原料,制备了缓慢膨胀的高强度油田堵水调剖颗粒.分别对天然胶乳、交联剂、引发剂以及膨润土的加入量对产品膨胀性能的影响进行了实验研究,确定了实验的最佳配比:水600 g、丙烯酰胺150 g、交联剂0.45 g、引发剂0.4 g、膨润土55 g、天然胶乳190 g,制备的堵水颗粒浸水110 h后开始缓慢膨胀,10 d吸水倍率50 g/g,耐温83.1℃,封堵率98.4%.实验结果表明,在聚合体系中加入天然乳胶与丙烯酰胺共聚能够极大地减缓堵水颗粒浸水初期的膨胀速率,增大体膨后颗粒强度,适合深部储层调驱.     

橡胶衬层硬度和厚度对水润滑轴承系统跳动量的影响

根据舰船推进装置对水润滑轴承系统的运行精度要求,通过建立水润滑橡胶轴承系统有限元接触模型,研究不同橡胶硬度、厚度对直槽和螺旋槽水润滑橡胶轴承系统跳动量的影响规律,提出水润滑轴承系统跳动量控制方法。研究结果表明,水润滑橡胶轴承系统跳动量随橡胶硬度增大而减小,随橡胶厚度增大而增大。当橡胶硬度在85~95Shore A时,轴承系统主轴跳动量较小。在保证沟槽尺寸的前提下,尽量设计成较薄的橡胶厚度。相比直槽结构,螺旋槽水润滑橡胶轴承系统跳动量更小。因此,科学合理地设计水润滑橡胶轴承橡胶衬层材料硬度和几何结构,能显著减小轴承系统的跳动量,提高运行精度。     

共轭三组分互穿聚合物网络的力学性能和形态——聚氨酯/聚甲基丙烯酸甲酯/废胶粉体系

基于共轭三组分互穿聚合物网络 (CTC_IPN)和界面共轭互穿这两个新概念 ,通过互穿聚合物网络技术成功地制备了聚氧化丙烯二元醇聚氨酯 /聚 (甲基丙烯酸甲酯 共 三烯丙基异氰脲酸酯 ) /废胶粉CTC_IPN(PU/P(MMA_co_TAIC) /SRP_CTC_IPN ) ,研究了这种材料以及PU/SRP共混物的力学性能 .结果表明 ,PU /P(MMA_co_TAIC) /SRP_CTC_IPN由于含公共网络P(MMA_co_TAIC) ,其性能明显优于PU/SRP共混物 .用扫描电子显微镜 (SEM )和透射电子显微镜(TEM )研究了PU/P(MMA_co_TAIC) /SRP_CTC_IPN和PU/SRP共混物的断面形貌 ,结果表明 ,两者具有完全不同的断裂机理 .TEM结果表明 ,P(MMA_co_TAIC)网络能分别与PU及SRP网络互穿 ,从而改善了两者之间的界面结合     

不同基准混凝土强度橡胶混凝土力学性能

为了探讨不同基准混凝土强度(C60,C40和C20)下,橡胶粉体积取代率和橡胶粉粒径对混凝土力学性能的影响,采用混凝土常规力学性能试验方法进行了橡胶混凝土和易性、抗压强度以及弹性模量试验。试验结果表明:橡胶混凝土立方体抗压强度、坍落度和弹性模量均随体积取代率的增加、橡胶粉粒径的增大而降低;橡胶粉体积取代率与强度降低系数之间存在较好的线性关系,回归分析的橡胶混凝土抗压强度方程形式简单,具有较理想的精度。     

废聚苯乙烯泡沫塑料综合利用研究进展

聚苯乙烯泡沫具有质量轻、表观密度低、不易分解、廉价等优点，是当下应用最广泛的塑料制品之一。同时其废弃物的丢弃量也越来越大，这种聚苯乙烯泡沫废弃物在大自然中难以降解，燃烧还会产生有毒物质，导致回收处理难度较大，给环境带来了很多问题。如果将废聚苯乙烯泡沫塑料（WFPS）进行回收或者资源化利用，不仅能改善环境问题，而且符合“低碳”理念。对WFPS的回收包括溶剂回收、热解回收等方法进行了详细地介绍，重点综述了WFPS在能源领域、建筑领域和环境保护领域的资源化再利用的研究现状。结合中国WFPS的回收现状对其今后回收与再利用技术研究前景作出了展望：1）兼顾经济与环保的规模化溶剂回收技术的开发；2）催化裂解回收单体的高效催化剂的研发；3）聚焦高附加值的WFPS资源化利用技术研究。     

氯化丁基橡胶复合阻尼材料的制备及表征

为了使氯化丁基橡胶(CIIR)的阻尼功能区向高温区拓展,制备宽温宽频阻尼材料,将氯化丁基橡胶与聚丙烯酸酯(PMAc)共混制备了互贯聚合物网络(IPN)复合阻尼材料。动态力学性能分析表明：复合阻尼材料有效地实现了阻尼功能区向高温区拓展,其中,CIIR/PEA IPN具有较高的阻尼值,但阻尼温区较窄,而CIIR/PBMA IPN同时具有较高的阻尼值和较宽的有效阻尼温区,耗散系数大于0.3的有效功能区可从-50℃持续至60℃。采用傅立叶红外光谱、固体核磁共振谱及透射电镜对IPN的微观结构分析表明：IPN中CIIR和PMAc形成了双相连续、物理互锁的微观相态结构。     

含铜感压导电橡胶的研究

本文探讨了在含铜感压导电橡胶的制备过程中,铜粉粒径、铜粉含量橡胶片厚度和它与两电极板的接触方式对感压导电橡胶的感压导电灵敏性的影响,实验结果表明:通过混合粒径为75-125μm的铜粉250-450(重量),硅橡胶100份,硫化剂5份,然后硫化成0.4的薄片,可以制备出具有较高灵敏性的感压导电橡胶。此种弹性材料可用作开关。     

软皮辊纺纱工艺的生产实践

本文针对软胶辊纺纱工艺进行了生产实践和分析，为纺织厂的工艺参数优化提供参考依据。     

锡偶联型高乙烯基SSBR/BR/NR共混性能研究

该文研究了高乙烯基锡偶联型SSBR、NR、BR3种胶料的相容性及共混硫化胶的性能。结果表明：SSBR、NR及BR在一定的比例下，具有较好的相容性，DMA曲线上只有1个玻璃化转变，当SSBR／BR／NR的比例为20：30：50时，共混硫化胶的 M300、断裂伸长率和断裂时的拉伸疲劳次数最大，力争陛能较好。SSBR／BR／NR3种胶料共混有效地改善了NR的耐磨耗性能和抗湿滑性能，而对滚动阻力影响不大。