以溶胶-凝胶法制得AgNO3掺杂的TiO2溶胶,选用铝合金为载体,采用提拉法制得Ag-Ti-O复合膜.以亚甲基蓝为目标降解物,评价了膜片的可见光光催化性能.用XRD、FT-IR、SEM等方法对膜片的理化性能进行表征.结果表明:Ag-Ti-O复合膜对亚甲基蓝的可见光光催化降解表现出优异的活性,在AgNO3的添加量为8×10-2mol/L和拉膜次数为3次的条件下,对亚甲基蓝的脱色率可达98%;膜片重复使用8次,活性持续保持良好.     

掺铅TiO2薄膜的制备及光催化性能

以钛酸四丁酯为前驱体,采用溶胶-凝胶法在玻璃板表面制得均匀的TiO2,并利用浸渍法镀pb2 得到掺铅的TiO2,用紫外漫反射、荧光光谱分析等手段对其进行了表征.研究结果表明,掺杂铅离子使TiO2的荧光峰明显增强,吸收带边发生红移,在紫外光区和可见光区的吸收明显增强.以紫外灯为光源,通过对甲基橙的光催化降解研究,发现掺铅TiO2薄膜的光催化活性明显大于掺Ag,Bi及纯TiO2薄膜,这是提高TiO2光催化活性的有效方法.     

纳米TiO2光催化降解甲基橙的研究

用XRD表征了TiO2的晶体形态,并用紫外可见光广度计研究了其对紫外光的吸收.通过研究TiO2的添加量和甲基橙的初始浓度对甲基橙的降解速率的影响,得出最佳实验条件为TiO2的添加量2.5g/L,甲基橙的初始浓度12.25mg/L.用光还原法在TiO2上沉积Ag后,催化剂的光催化活性大大提高.     

CuO/ TiO2H2O2光催化体系中亚甲基蓝脱色机理

采用水解法制备了具可见光响应能力的CuO/TiO2光催化剂.通过对不同光源和pH条件下体系中·OH存在量和脱色率的考察,提出了亚甲基蓝光催化脱色的机理.紫外光照射时,酸性条件下体系中有大量·OH生成,·OH扩散至液相中起主要脱色作用;碱性条件下·OH生成量较少,·OH通过与吸附于催化剂表面的亚甲基蓝作用来实现脱色;中性时两者协同作用.该3种条件下脱色率均远高于弱酸和弱碱时.光源为可见光时,光催化体系中电子传递产生回路,各种PH条件下体系中均只有少量·OH生成.酸性和中性条件下·OH必须扩散至液相中与亚甲基蓝反应,脱色率极低;碱性条件下亚甲基蓝被吸附于催化剂表面,·OH利用效率提高,同时由于光敏化作用的存在,使得脱色率极高.     

金属离子掺杂对TiO2光催化性能影响分析

TiO2光催化剂可有效去除水中有机污染物。本文采用溶胶—凝胶法(Sol—gel)制备了掺杂不同含量金属离子的复合型TiO2光催化剂，光催化降解甲基橙溶液实验结果表明：掺杂Cr^3 的TiO2光催化活性明显高于单一TiO2和其他几种掺杂催化剂的光催化活性；当Cr^3 的掺入比例约为1．0％时，其光催化活性最高，紫外光照4h甲基橙的降解率达到90％以上，可见光照射6h甲基橙的降解率达85％以上。可望将掺杂金属离子的纳米TiO2作为一种有效的光催化剂，广泛应用于被污染水体的净化处理。     

Ag/TiO2薄膜光催化性能的研究

用含有AgNO3的复合溶胶凝胶制备Ag/TiO2薄膜,然后对其进行了SEM,XRD,RBS研究,以甲基橙为反应物检验了含有不同n(Ag)/n(Ti)的Ag/TiO2薄膜在365nm紫外光作用下的光催化降解效率.具有最佳光催化降解效率的是溶胶中n(Ag)/n(Ti)=0.064的Ag/TiO2薄膜,与未掺银TiO2薄膜相比,效率提高了73%.     

纳米TiO2光催化降解亚甲基蓝的研究

在封闭的光催化反应器中，以紫外光为光源，γ-Al2O3为载体，纳米TiO2为催化剂，进行了亚甲基蓝溶液降解脱色研究，分别从催化剂用量、反应初始浓度、光源强度及H2O2的添加量等方面考查了亚甲基蓝的降解率。结果表明，能够有效地完成亚甲基蓝等有机物降解脱色和降解，降解率可达95％以上。     

Fe，Gd共掺杂改性TiO2的可见光光催化活性

采用溶胶-凝胶法制备了铁和钆共掺杂纳米TiO2粉体材料,研究了共掺杂粉末在可见光下的光催化性能.紫外可见吸收光谱分析显示:共掺杂粉末在可见光区有较强吸收,共掺杂离子以协同作用拓展TiO2光谱响应.光催化降解实验表明,共掺杂TiO2粉体有很高的可见光光催化活性,以550 ℃热处理的同时掺杂质量分数为0.05%Fe和0.05%Gd的TiO2粉体光催化效果最好,在可见光下对甲基橙的降解率为79.6%.     

纳米TiO2/玻璃薄膜光催化降解亚甲基蓝的研究

用溶胶 -凝胶法在玻璃表面制备了均匀透明的纳米TiO2 薄膜 .采用高压汞灯为光源 ,敞口固定床反应器对水中染料亚甲基蓝进行了光催化氧化实验 .实验结果表明 :随着涂膜次数的增加 ,薄膜TiO2 负载量增加 ,锐钛矿晶相粒径增大 .TiO2 薄膜对亚甲基蓝氧化降解具有较高的光催化活性 ,降解反应符合一级速率方程 .对亚甲基蓝的暗态吸附及光催化降解机理作了初步探讨     

溶胶-凝胶法制备La3+、碳纳米管掺杂纳米TiO2及光催化性能

采用溶胶-凝胶法,分别制备了不同掺杂量的La3 掺杂TiO2、多壁碳纳米管掺杂TiO2及La3 与碳纳米管共掺杂纳米TiO2粒子.通过紫外光照射甲基橙溶液的光催化降解实验,研究了掺杂对TiO2光催化活性的影响.实验表明,适量的La3 掺杂可以提高TiO2的光催化活性,最佳掺杂浓度为La3 摩尔分数等于0.08%,碳纳米管掺杂也可以提高TiO2的光催化活性,La3 与碳纳米管共掺杂TiO2具有最高的光催化活性.10%(碳原子的摩尔分数)碳纳米管、0.08%La3 (摩尔分数)共掺杂TiO2在1 h内对甲基橙溶液的降解率达到84%,而纯TiO2在1 h内对甲基橙溶液的降解率只有约53%.X衍射图谱和透射电镜分析表明,制得的TiO2均为锐钛矿型,晶粒直径约为8～25 nm.     

離子交換法制備載銀沸石抗菌劑及其性能研究

以酸活化沸石為載體,AgNO3為反應液,通過離子交換法制備載銀沸石抗菌劑.采取正交試驗法研究了制備工藝對抗菌劑載銀量及抗菌性能的影響.結果發現沸石的酸化是重要的影響因素,其次是AgNO3的濃度、反應溫度和時間.試驗表明,最佳的制備工藝條件為:活化酸度(HCl)1.5 mol/L,AgNO3濃度0.5 mol/L,反應溫度50℃,反應時間2 h.通過最佳的制備工藝條件制備載銀沸石抗菌劑的載銀量為2.40%,這種抗菌劑具有良好的抗菌性能.     

反应条件对银胶体粒径及分布的影响

重点考察了利用液相化学还原法制备银胶体时温度、浓度和加料方式对粒径分布的影响。以PVP(聚乙烯吡咯烷酮)和六偏磷酸钠为稳定剂,以次亚磷酸钠为还原剂液相还原硝酸银,制备出有不同粒径和分布的银胶体。利用激光衍射粒度分析仪、UV-vis分光光度计和透射电镜(TEM)确定胶体的粒径、分布和形态。研究结果表明:一次性加料获得的粒径和分布较小,硝酸银浓度和温度影响聚并和生长,从而对粒径分布产生复杂影响。     

MCM-22分子筛对水溶性染料的吸附作用

采用呲啶吸附FT-IR、NH3-TPD、低温N2吸附等表征了所合成的MCM-22分子筛的酸性和孔结构,并考察了吸附时间、吸附剂用量、染料初始浓度、溶液pH及重复利用次数等对甲基橙(MO)和亚甲基蓝(MB)吸附性能的影响.结果表明:MCM-22分子筛对甲基橙和亚甲基蓝均有较好的吸附效果.对浓度为1×10-4mol·L-1...     

Loading and releasing behavior of carboxymethyl cellulose and chitosan complex beads

The complex beads of carboxymethyl cellulose (CMC) and chitosan (CHI) that are fabricated by interfacial complexation have a core-shell structure composed of a thin skin layer and a 3D entangled internal structure, which endows the beads with adsorption possibilities toward anionic and cationic molecules via electrostatic interaction. However, the loading and releasing behavior of such a system is essential and fundamental for their application yet has not been studied systematically. In this work, the influences of beads physical state, adsorbent dosage, agitation speed, solution pH and temperature on the loading behavior were investigated. The CMC@CHI beads demonstrated different loading efficiency to three typical dyes of methylene blue (MB), acid blue-113 (AB), and methyl orange (MO) with different charge status. The adsorption rate followed an order of MB ? AB ? MO, giving 97.4%, 73.3% and 20.2%, respectively. The releasing of three dyes from CMC@CHI beads also exhibited different rates, and MB release was found to be prolonged compared to AB and MO. The loading mechanism of dyes was further investigated via X-ray photoelectron spectroscopy. These CMC@CHI beads may have possible applications in mixed dye removal as well as encapsulating systems of drugs or sensitive chemicals with different charges.     

多金属氧酸盐/亚甲基蓝多层膜的制备及性质研究

我们采用层接层自组装技术将多金属氧酸盐H3PW12O40(PW12)和小分子有机染料亚甲基蓝(MB)组装成多层复合膜,并将此复合膜通过X射线光电子能谱、红外和循环伏安进行表征。紫外可见光谱表明,PW12与MB通过静电吸引,可以很好的自组装成均匀的多层膜,并且比较了复合膜与PW12/MB混合水溶液的区别。     

氧化硅基底负载TiO2薄膜的制备及其光催化应用研究

以钛酸丁酯为钛源，乙酰丙酮和冰醋酸为水解抑制剂，聚乙二醇为致孔剂，制备了一种稳定的TiO₂水溶胶。采用浸渍提拉法将TiO₂溶胶负载到活化的载玻片上，再经180℃水热或500℃煅烧得到TiO₂薄膜催化剂。采用扫描电子显微镜（SEM）、原子力显微镜（AFM）、透射电子显微镜（TEM）、X射线晶体衍射（XRD）和Raman光谱等分析手段对样品进行了表征，结果表明：TiO₂薄膜是由粒径为8~12 nm的球形颗粒组成的多孔结构，其晶型为结晶度良好的锐钛矿。以甲基橙为光降解物，在紫外灯下测试薄膜的光催化性能，结果显示煅烧处理的TiO₂薄膜催化剂的光催化活性优于水热处理，对低浓度甲基橙的降解效率达90%以上，并且多次重复使用后光催化活性基本保持不变。     

银锌复合透明抗菌薄膜的制备及其性能研究

采用sol—gel法，以正硅酸乙酯（Si（OC2H5）4）作为反应的前驱体，硝酸锌、硝酸银为抗菌活性成分，柠檬酸为配合剂，无水乙醇为溶剂，HNO3为催化剂，通过浸渍提拉法在普通的玻璃基片上制备银锌复合薄膜，用扫描电镜（SEM）和紫外可见光谱（UV-Vis）对薄膜进行了表征，抑菌圈法评价银锌复合薄膜的抗菌性能，结果表明：透明的银锌复合薄膜具有优良的抗菌性能。     

超声协同作用下亚微米掺铝氧化锌催化降解亚甲基蓝的研究

通过溶液直接沉淀法制备了掺Al3+的亚微米氧化锌Zn(Al)O,利用XRD和SEM确定其晶体结构和形貌大小.采用Fenton/Co2+体系,在掺铝氧化锌存在和超声协同下进行降解亚甲基蓝的实验,研究溶液初始pH、H2O2浓度、反应温度、Zn(Al)O投加量、Co2+浓度、亚甲基蓝(MB)浓度等实验条件对MB降解率的影响,并对4种降解方法的效果进行比较. 结果表明:采用Fenton/Co2++Zn(Al)O+超声体系,在H2O2浓度为100 mmol/L,pH5～9,温度30～50C,Co2+浓度0.1～0.3 mmol/L,Zn(Al)O投加量1.0 g/L的条件下降解初始质量浓度达80 mg/L的MB溶液,自然光下超声1h后降解率高达72%. 对其降解机理进行了初步讨论.对掺铝氧化锌循环使用的研究发现,循环1次后降解率为68%, 2次下降到48%.在自然光下降解,该文合成的Zn(Al)O的降解率是P25（降解率约40%）的1.8倍.     

大麻杆活性炭对染料吸附性能的研究

以天然大麻杆为原料,采用磷酸活化法制备大麻杆活性炭。利用低温氮吸附对样品的比表面积与孔结构进行了表征,并利用亚甲基蓝与甲基橙两种染料对活性炭在液相中的吸附行为进行了研究。结果表明,样品的比表面积与中孔孔容随着活化温度的升高而增大,在500℃时达到最大值1325.73m2/g,随后由于磷酸过度活化导致结构坍塌致使各参数有所降低;在25℃下,大麻杆活性炭对亚甲基蓝与甲基橙的吸附等温线均遵循Langmu ir方程,单层吸附量分别达到471.698mg/g和363.64mg/g,吸附量主要受微孔孔容、染料分子尺寸及染料分子与活性炭表面作用力三者的共同影响。吸附动力学能够很好的符合准二级动力学方程,且亚甲基蓝的吸附速率高于甲基橙。     

脉冲放电等离子体技术处理偶氮染料废水

为有效处理染料废水,以甲基橙和刚果红溶液为例研究高压脉冲放电等离子体技术的脱色效果.通过测定脉冲放电处理前后甲基橙和刚果红溶液的紫外-可见吸收光谱来计算脱色率,考察放电参数、添加剂对染料脱色率的影响.实验结果表明,脉冲放电对甲基橙和刚果红溶液脱色效果显著,且相同条件下甲基橙(单偶氮)比刚果红(双偶氮)脱色率高.两者脱色率均随峰值电压、脉冲频率的增大而提高,随溶液电导率的增大而降低,随H2O2的加入而提高.当电极间距由15 mm增大到25 mm时,放电形式也由火花放电逐渐向电晕放电转变,溶液的脱色率由90%降到44%.