Effect of MWCNT reinforcement on the precipitation-hardening behavior of AA2219

Aluminum alloy matrix composites have found a predominant place in research, and their applications are explored in almost all industries. The aerospace industry has been using precipitation-hardenable alloys in structural applications. However, insufficient literature is available on the influence of multiwalled carbon nanotubes (MWCNTs) on precipitation-hardenable alloy composite materials; thus, this work was designed to elucidate the effect on MWCNT reinforcement on AA2219 with and without precipitation hardening. Reinforcement with MWCNTs has been reported to accelerate precipitation and to achieve greater hardness within a much shorter time. The addition of 0.75wt% MWCNTs resulted in maximal hardness at 90 min, which is approximately 27% of improvement over the maximum hardness achieved by the corresponding monolithic alloy after 10 h of aging. The sample reinforced with 0.75wt% MWCNTs showed an improvement of 82% in hardness by solutionizing and aging compared to that achieved by sintering.     

羟基磷灰石/碳纳米管复合生物材料的制备与表征

为了赋予碳纳米管(CNTs)表面良好的生物性能,拓展CNTs在硬组织生物材料及组织工程支架材料中的应用,采用化学共沉淀和水热后处理法宏量制备了羟基磷灰石(HA)/多壁碳纳米管(MWCNTs)复合材料,通过调节制备过程中浓硝酸纯化的MWCNTs加入量,考察不同MWCNTs含量的HA/MWCNTs复合材料的结合形式.扫描电子显微镜(SEM)和透射电镜(TEM)表征结果表明,当ω(MWCNTs)＝15%时,MWCNTs表面均匀地包覆了一层由纳米HA晶粒紧密相连的膜层,在此情况下MWCNTs与纳米HA形成最佳结合状态.体外细胞培养实验表明,制备的HA/MWCNTs复合材料具有良好的生物相容性.     

新型TiO2纳米管透析膜与传统透析膜对细胞生长状态的影响

 研究采用阳极氧化法制备新型高强度的TiO₂纳米管阵列薄膜, 通过对纳米管底部进行腐蚀获得两端通透的TiO₂纳米管阵列薄膜.在纳米管阵列薄膜表面和高分子透析膜表面种植HK-2细胞和HUVEC细胞, 成功制备具有生理功能的生物膜材料.采用MTT方法对比研究了TiO₂纳米管阵列薄膜、聚醚砜(PES)、混合纤维素以及再生纤维素4种薄膜材料黏附细胞的活性;利用荧光显微镜观察4种材料对两种细胞黏附的影响;同时使用扫描电镜观察细胞在4种薄膜材料上的生长形态.结果表明, TiO₂纳米管阵列薄膜最有利于细胞的黏附及增殖, 且细胞活性最高, PES薄膜的效果次之, 再生纤维素薄膜最不适合细胞的增殖及黏附;荧光显微镜观察证实TiO₂纳米管阵列薄膜相比高分子薄膜更能促进细胞的黏附及生长, 证实所制备的TiO₂纳米管阵列薄膜能够很好地与两种细胞相容, 克服了传统透析材料的不足, 改善了细胞与材料的黏附, 是用于生物人工肾研究较为理想的候选材料.     

修饰碳纳米管对硼酚醛树脂摩擦性能的影响

采用共价接枝法制备了羧基化碳纳米管(MWCNTs -COOH)、二氨基二苯基甲烷修饰碳纳米管( MWCNTs -DDM)、硼酸化碳纳米管(MWCNTs- Borate)修饰碳纳米管(MWCNTs).通过原位聚合的方法制备了修饰碳纳米管/硼酚醛树脂.使用3种碳纳米管改性的树脂制备了摩擦材料并研究了其摩擦性能.结果表明,修饰碳纳米管的加入,有助于提高摩擦材料摩擦系数的稳定性,减小磨损率,改善热衰退性.其中添加质量分数为1％的MWCNTs- Borate的情况改善最大,磨损率减小43.2％,摩擦系数和磨损率衰退率仅为10.3％和28.6％,摩擦表面保持完好.     

N/C对碳氮膜修饰的多壁碳纳米管细胞相容性的影响

为改善碳纳米管的细胞相容性,通过离子束辅助沉积方法在由化学气相沉淀法制备的多壁碳纳米管表面沉积纳米厚度的碳氮膜以进行表面修饰.通过观察L929小鼠肺部成纤维细胞、EAHY926人内皮细胞和兔血红细胞在修饰前后的碳纳米管表面的黏附和生长状态可知,沉积CNx膜的多壁碳纳米管的细胞相容性优于沉积前,表现出良好的生命活性和增殖状态,同时,较高的N/C比有利于细胞在沉积CNx膜碳纳米管表面的增殖和生长以及细胞形态的伸展.     

多壁碳纳米管-神经生长因子复合物的制备及生物活性测定

为探讨采用羧基化多壁碳纳米管（MWCNTs—COOH）非共价接枝神经生长因子（NGF）制备碳纳米管神经生长因子（MWCNTsNGF）复合物,考察复合物的生物活性。采用透射电子显微镜（TEM）表征MWCNTs—NGF复合物的微观形貌,酶联免疫吸附法（ELISA法）测定MWCNTs—NGF复合物载带NGF的量,MTT法测定了MWCNTs—NGF复合物的对嗜铬细胞瘤细胞（PCI2细胞）的毒性,PCI2细胞培养法评价复合物的生物活性,TEM表征复合物与细胞的分布情况。结果：TEM图像表明NGF连接到了MWCNT上,EI．ISA法测得MWCNTsNGF复合物载带NGF的量为797．63pg／mg,MWCNTs—NGF复合物对PCI2细胞有一定的毒性,生物活性试验表明NGF浓度相同的情况下,MwCNTs—NGF复合物组PCI2细胞的分化率明显高于NGF组。TEM图像表明碳纳米管能进入细胞。结论：碳纳米管能载带NGF进入细胞,使NGF能更好的表达生物活性。     

P3HT-MWCNTs光敏性复合薄膜的制备和性能

采用化学氧化法,合成一种聚(3 - 己基噻吩),即P3HT,将之与多壁碳纳米管(MWCNTs)有效复合,最后形成一种透明的电子给体--受体异质结型P3HT - MWCNTs光敏性纳米复合薄膜.采用核磁共振、红外光谱、紫外-可见光谱和透射电镜等测试手段,对合成产物进行表征和分析.研究表明,己基的引入使得聚噻吩的溶解性能明显改善,同时通过对碳纳米管的表面修饰和改性,碳纳米管与P3HT具有较好的相容性.紫外-可见光吸收光谱显示,P3HT薄膜比其相应的溶液具有更高的电子共轭效应,随着氧化剂用量的提高,有助于提高其电子共轭效应.在一定范围内,随着MWCNTs含量的增加,P3HT - MWCNTs光敏薄膜发生红移,提高了对太阳能的利用率.     

十六烷基胺-多壁碳纳米管复合物的制备及NO吸附性能

为制备在室温下对NO吸附性能优异的材料,采用十六烷基胺并通过化学缩合的方法对多壁碳纳米管进行了修饰,制备了十六烷基胺-多壁碳纳米管复合物,并分别采用TG-DSC,XRD,FT-IR,Raman,SEM等技术对所制备的复合物进行了表征.研究表明:十六烷基胺通过酰胺键修饰在多壁碳纳米管表面,经十六烷基胺修饰的碳纳米管结构基本没有发生变化.原位TG-MS结果表明:在室温下,经十六烷基胺修饰的多壁碳纳米管的NO吸附量是纯碳纳米管的8.58倍,其选择性吸附NO能力较纯碳纳米管明显提高.原因是十六烷基胺修饰的多壁碳纳米管n型电导能力增强,而使受电子体NO分子易与修饰的碳纳米管作用并发生化学吸附.     

多壁碳纳米管及其对H_2吸附体系的Raman光谱

利用原位和非原位紫外 Raman谱法 ,对以 CH4 为碳源 ,由催化法制备的多壁碳纳米管( MWCNTs) ,K -修饰的该类 MWCNTs,以及它们对 H2 的吸附体系进行了 Raman谱表征 ,观测到可分别归属于类石墨结构的基频模 D和 G以及它们的三阶组合频 ,表面 C-H3基和 C-H2 基等的特征Raman峰 ;H2 在这类碳纳米管上的吸附态包括解离吸附生成表面 C-H3和非解离吸附分子氢 H2 ( a) ;在相同实验条件下 ,K -修饰体系上这两类氢吸附物种的表面浓度都比未经 K -修饰的相应体系高 .     

NaCl 对海藻酸钠/多壁碳纳米管复合溶液流变性能的影响

本文研究了不同氯化钠（NaCl）浓度,不同温度下的海藻酸钠（SA）及其与多壁碳纳米管（MWCNTs）复合溶液的流变行为。利用 Ostwald’s 和 Arrhenius 方程计算得出溶液的非牛顿指数和粘流活化能。结果表明,纺丝溶液属于非牛顿流体,溶液的零剪切粘度随着NaCl浓度的增加逐渐增加,非牛顿指数却逐渐降低。MWCNTs 的加入使得SA溶液的粘流活化能降低,说明 MWCNTs 的加入增加了溶液的流动性。     

A novel monoclinic manganite/multi-walled carbon nanotubes composite as a cathode material of lithium-air batteries

A novel composite of monoclinic manganite/ multi-walled carbon nanotubes （γ-MnOOH/MWCNTs） composite as a cathode material of lithium-air batteries was successfully synthesized by a simple one-step hydrothermal method. Owing to the unique three-dimensional network of γ-MnOOH embedded in the porous structure of MWCNTs, the γ-MnOOH/MWCNTs composite could have an advantage of high electrocatalytic activities over those of two other kinds of cathode materials （MWCNTs and y-MnOOH/MWCNTs mixture）. The results of charge- discharge tests showed that the γ-MnOOH/MWCNTs composite as a cathode material of lithium-air batteries could effectively enhance the catalytic activity for the oxygen evolution reduction （OER） process. The lithium-air battery based on y-MnOOH/MWCNTs composite exhibits low charge potential and high discharge capacity.     

干湿交替对砂岩断裂特性影响试验研究

周期性的水岩相互作用对岩石的物理力学性能有较大的影响,被认为是影响岩土工程安全稳定性的重要因素之一。以典型的均质青砂岩为试验对象,利用中心裂纹圆盘试件开展了砂岩I~II复合型断裂试验,研究了干湿交替作用对砂岩I~II复合型断裂特性的影响;通过观测干湿交替后砂岩微观结构的变化特征,探讨了干湿交替作用的劣化机理;并结合复合型断裂则对试验结果进行了有效评估。研究表明,砂岩的纯I型,纯II型以及I~II复合型断裂韧度均随着干湿交替次数的增加而逐渐减小;其劣化趋势基本一致,但劣化程度略有不同。当加载角较大或II型分量主导时,干湿交替作用对砂岩断裂韧度的劣化影响更为显著。考虑了T应力影响的广义最大周向应变准则和广义最大周向应力准则都能对试验结果进行很好的预测。在纯II型时,基于广义最大周向应变准则的理论预测值比基于广义最大周向应力准则的理论值更接近试验值。     

TaC及Ta2O5涂覆纳米碳管的制备与表征

以纳米碳管为反应性模板、金属钽粉为金属源,采用熔盐法在纳米碳管表面反应原位生成TaC涂层,在混合空气下将TaC涂层于不同温度氧化转化为Ta2O5涂层,并运用XRD和SEM对生成产物的晶体组成和形貌进行表征。结果表明,采用熔盐反应法可在纳米碳管表面生成较为均匀的TaC涂层,经不同温度氧化后生成Ta2O5涂覆纳米碳管复合材料,在较高温度下其仍能保持纳米碳管原有的形貌。     

基于木质素和多巴胺改性的MWCNTs水相分散

为解决碳纳米管材料的团聚问题,对多壁碳纳米管(multi-walled carbon nanotubes,MWCNTs)进行多巴胺改性所形成的表面聚多巴胺层,增强了MWCNTs与木质素的结合力,从而最终实现以木质素为分散剂的水相MWCNTs稳定分散。采用傅里叶变换红外光谱和透射电镜对改性MWCNTs的表面化学结构和分散形态进行表征,应用紫外分光光度计定量评价pH值、木质素质量浓度及改性MWCNTs质量浓度对MWCNTs分散效果的影响。结果表明:经多巴胺改性的MWCNTs在木质素分散下可实现高达95.65%的分散度;中性、碱性条件有利于提高分散稳定性;木质素质量浓度为改性MWCNTs质量浓度的5倍时,MWCNTs分散效果最佳;木质素最多能均匀分散其2.5倍质量浓度的改性MWCNTs。     

Cu修饰碳纳米管基复合材料的高效合成及其催化应用研究

报道了一类壳聚糖预修饰的多壁碳纳米管(MWCNTs)在温和条件下自发还原Cu离子制备Cu修饰碳纳米管基复合材料的新合成路线.联合谱学表征(XRD,SEM,HRTEM,UV-vis)研究表明,平均粒径约为2nm的超小Cu粒子均匀地分散在MWCNTs的表面;氨水是引发自发还原反应的关键因素;Cu修饰碳纳米管基复合材料能高效催化还原对硝基苯酚.     

碳纳米管场发射显示屏栅极工艺的研究

利用优质云母板作为栅极结构基底材料，结合简单的丝网印刷工艺将导电银浆制作成条状栅极，制作了新型的栅极结构；采用高温分解方法制备了碳纳米管薄膜阴极，制作了三极结构碳纳米管阴极平板显示屏样品。该样品具有良好的场致发射特性以及栅极控制能力。利用这种新型的栅极结构，能够克服整体器件高温封装所带来的技术困难，避免碳纳米管阴极和阳极荧光粉的损伤，实现了稳定可靠的高温封装，具备了制作大面积场致发射器件的潜力。     

掺杂磺酸聚苯胺/碳纳米管复合膜电极制备及其应用

采用共聚法制备了掺杂磺酸的聚苯胺/多壁碳纳米管复合薄膜,并用其对铂电极进行表面修饰而制备出复合膜电极;通过扫描电子显微镜和红外光谱仪对复合膜电极表面的形态和组分进行表征,并采用电化学方法对其导电性和电催化活性进行测试.结果表明:与聚苯胺电极相比,掺杂磺酸的聚苯胺/多壁碳纳米管复合膜电极的表面形态更均匀致密,导电性能显著提高,响应峰电流从145μA增加到1.61mA,表面电荷密度提高了12.1倍,且稳定性也相应提高;复合膜电极具有较高电催化活性,在草酸环境中对抗坏血酸(AA)的线性响应不受干扰,其线性相关系数为0.996 0,灵敏度为9.09A/(mol·cm2),氧化峰的电位差达到340mV,能够明显区分其混合物.     

DOPO-HQ改性碳纳米管/EP复合材料的制备及性能

采用混酸氧化多壁碳纳米管(MWCNTs),然后与含磷化合物2–(6,H–二苯并–5–氧杂–6–膦酰杂–6–苯基)–1,4–对苯二酚(DOPO-HQ)反应,对MWCNTs进行功能化修饰,并用功能化的碳纳米管(MWCNTs-P)对环氧树脂进行改性.对比了MWCNTs与MWCNTs-P对环氧树脂力学性能和阻燃性的影响,结果表明,MWCNTs与MWCNTs-P的加入均能提高环氧树脂的力学性能,MWCNTs-P改性效果更好.当MWCNTs-P添加量为0.5%时,环氧树脂的冲击强度提高了232%;SEM结果显示,加入碳纳米管使环氧树脂复合材料的韧性有一定程度的提高.MWCNTs-P的添加量为1.0%时,复合材料的拉伸性能和弯曲性能最好.极限氧指数(LOI)测试结果表明,MWCNTs-P提高了环氧树脂的阻燃性,MWCNTs-P的添加量为0.5%时,复合材料的LOI达到30.2%.     

化学镀法制备多壁碳纳米管负载非晶态镍-磷纳米粒子催化剂的性能及其苯加氢催化活性研究

通过化学镀工艺,采用以次磷酸钠为还原剂的镀液将镍-磷（Ni-P）纳米粒子负载于多壁碳纳米管（MWCNTs）表面。通过场发射扫描电子显微镜（FE-SEM）、高分辨透射电镜（HR-TEM）、X射线衍射仪（XRD）、选区电子衍射仪（SAED）、电感耦合等离子体质谱（ICP-MS）、傅里叶变换红外光谱仪（FT-IR）、差示热分析仪（DTA）、X射线光电子能谱仪（XPS）等测试手段对催化剂的物理化学性能进行了表征,分析结果表明：Ni-P纳米粒子化学组成为Ni_73.8P_26.2,为非晶态结构实心圆球体,均匀分散负载于MWCNTs外壁,平均尺寸约100 nm,粒度分布窄,镍元素与磷元素之间无明显电子转移,催化剂在350℃以下结构和热稳定性较强。通过催化剂对于苯加氢反应的研究评价了其催化性能,结果表明在Ni-P/MWCNTs催化剂作用下,苯全部选择性地转化为环己烷,催化剂显示出较好的催化活性（71.2%）和高选择性（100%）。     

Highly stretchable and sensitive strain sensor based on silver nanowires/carbon nanotubes on hair band for human motion detection

In this work, a highly stretchable and sensitive strain sensor using silver nanowires(Ag NWs)/multi-walled carbon nanotubes(MWCNTs) on hair band is proposed. The fabrication process of such sensors enabled scalable and facile production with low cost by dipping hair band into Ag NWs/MWCNTs composites suspension. The sensing performance of the sensors was optimized by tuning the Ag NWs/MWCNTs mass ratio. The hair band based strain sensor with Ag NWs/MWCNTs mass ratio of 30 exhibited the best performance with high sensitivity of 416.0 and good stretchability up to 70%. Moreover, great repeatability and long-term stability could be achieved over 7500 cycles of stretch-release. This Ag NWs/MWCNTs-hair band sensor can be used for monitoring human motions and swallowing action.