Fe，Gd共掺杂改性TiO2的可见光光催化活性

采用溶胶-凝胶法制备了铁和钆共掺杂纳米TiO2粉体材料,研究了共掺杂粉末在可见光下的光催化性能.紫外可见吸收光谱分析显示:共掺杂粉末在可见光区有较强吸收,共掺杂离子以协同作用拓展TiO2光谱响应.光催化降解实验表明,共掺杂TiO2粉体有很高的可见光光催化活性,以550 ℃热处理的同时掺杂质量分数为0.05%Fe和0.05%Gd的TiO2粉体光催化效果最好,在可见光下对甲基橙的降解率为79.6%.     

纳米TiO_2光催化改性研究

研究了不同类型(非金属、稀土金属、过渡金属)的掺杂元素对TiO2在可见光下的光催化活性的影响。采用XRD对其结构进行表征,以结晶紫为目标降解物,使用紫外-可见分光光度计测试了不同掺杂TiO2在可见光下的光催化性能。     

畅晓钰1 李 帅1 苏耀东2 姚鸿飞2 陈玉静2

通过溶胶凝胶法,以硝酸铁为铁源、尿素为氮源,分别制备了铁掺杂、氮掺杂、铁氮共掺杂二氧化钛粉末。采用X射线衍射仪,紫外-可见光谱仪等对样品进行表征和分析。并以亚甲基蓝作为目标降解物,来评价样品的光催化性能。结果表明,500℃下制备的催化剂均为锐钛矿相,结晶性较好,掺杂使材料的吸收光谱发生红移,掺铁5%,掺氮12%时对可见光的吸收效果最好。光催化6h对亚甲基蓝的降解效果效果Fe-N-TiO2＞Fe-TiO2＞N-TiO2＞纯TiO2。Fe、N共掺杂产生协同作用,使TiO2的光催化性能明显优于单掺杂样品和纯TiO2。     

水解沉淀法制备氮掺杂TiO_2可见光光催化剂

为拓展TiO2可见光的响应范围,以氨水为氮源,在常温条件下采用水解沉淀法制备了氮掺杂TiO2粉末。以X射线衍射、紫外-可见漫反射吸收光谱和X射线光电子能谱等对TiO2进行了表征。对可见光照射下的光催化活性进行了测试,并考察了煅烧温度及掺杂量等对光催化活性的影响。结果表明:氮掺杂致使TiO2吸收边带向可见光区偏移,在降解亚甲基蓝的实验中表现出良好的可见光催化活性;随煅烧温度的增加,氮摩尔分数增加,晶粒增大,可见光催化活性减弱;煅烧温度为400℃,氮的摩尔分数为2%时制备样品的光催化活性最高。     

N掺杂TiO2的制备、表征及其光催化性能

采用水热法制备了N掺杂TiO2光催化剂,并用X衍射、X光电子能谱和紫外-可见吸收光谱进行了表征,测定了其光催化氧化甲基橙的催化性能.结果表明,与未掺杂TiO2相比,N掺杂TiO2在可见光区有更大的吸收,N的掺杂还明显提高了TiO2光催化氧化甲基橙的性能.     

La-CdS/TiO2光催化剂的制备及表征

 采用金属掺杂和半导体复合两种方法结合制备La3+掺杂、CdS复合TiO2光催化剂。通过SEM、XRD和UV-DRS等对样品形貌、结构及光吸收性能进行了表征,并以甲基橙溶液为目标降解物考察了改性TiO2的光催化性能。结果表明,La-CdS/TiO2光催化剂在可见光区的吸收能力显著提高,光吸收发生明显红移,吸收边波长为452 nm;La3+掺杂降低了光生电子-空穴对的复合率,CdS复合扩展了光谱响应范围,光催化活性明显提高,光照15 min后,La-CdS/TiO2对甲基橙的降解率高达99%。     

铁掺杂纳米TiO2的可见光催化性能

为了提高纳米TiO2催化剂的光催化氧化性能,采用溶胶-凝胶法,以酞酸丁酯为原料制备铁掺杂纳米TiO2光催化剂(Fe-TiO2).分别采用X射线衍射和紫外-可见光漫反射对其晶相和光催化活性进行表征.以偶氮结构的弱酸性染料溶液为目标降解物,研究在可见光照射下Fe-TiO2的光催化性能.结果表明,Fe-TiO2光催化剂的晶相为单一锐钛矿相,粒径为17.7nm;吸收边带红移至500nm,禁带宽度减小到2.48eV.在可见光下光催化反应180min,Fe-TiO2光催化剂对弱酸性染料的降解率达99.86%.     

La掺杂对纳米TiO2薄膜晶体结构和光催化性能的影响

采用溶胶一凝胶法在玻璃表面制备La掺杂纳米TiO2薄膜;利用X射线衍射仪(XRD)和原子力显微镜(AFM)对其结构和形貌进行表征;通过对紫外光照射下亚甲基蓝溶液的光催化降解率评价其光催化性能;研究不同掺杂量、热处理温度以及pH值对La掺杂纳米TiO2薄膜光催化性能的影响,并对其光催化的影响机制进行探讨.研究结果表明:适量La掺杂能抑制TiO2由锐钛矿相向金红石相的转变,引起晶格膨胀,导致晶格畸变;La掺杂使TiO2的吸收光谱发生红移,扩展TiO2的光谱吸收范围,有效地提高纳米TiO2薄膜的光催化性能,且光催化反应符合一级动力学方程:La掺杂量(摩尔分数)为0.5%的纳米TiO2薄膜在400℃热处理2 h后具有最大的光催化效率98.2%,其光催化效率比纯TiO2薄膜的光催化效率提高约40%.     

铜钕共掺杂纳米Ti02光催化降解偏二甲肼废水

以钛酸四丁酯为原料,采用溶胶-凝胶法制备纯纳米TiO2和铜掺杂、钕掺杂、铜钕共掺杂TiO2,用X射线衍射、傅里叶红外光谱对其进行表征,用15W紫外灯作光源,20mg/L的偏二甲肼污水作为光催化反应模型污染物,研究TiO2的光催化性能,考察掺杂量对降解率的影响,结果表明,掺杂改变了TiO2的晶胞参数,提高了TiO2的光催化活性,共掺杂具有协同效应,共掺杂样品中铜离子摩尔分数为2.0%,钕离子摩尔分数为1.5%时其光催化性能最好.在25℃下,偏二甲肼废水质量浓度为20mg/L,加入催化剂质量浓度为0.6g/L,降解60min时,偏二甲肼废水的降解率达到93.4%.     

稀土离子Gd3+掺杂TiO2光催化剂的制备及其对碱性品红降解性能的研究

采用溶胶-凝胶法制备了Gd3+掺杂TiO2光催化剂,利用紫外-可见漫反射光谱对样品进行了表征.考察了纯TiO2和 Gd3+掺杂TiO2对碱性品红染料降解性能的影响.结果发现Gd3+的掺入抑制了TiO2由锐钛矿相向金红石相的转变,与纯TiO2相比,Gd3+掺杂TiO2催化剂在可见光区的吸收能力增强,该催化剂光催化降解碱性品红的活性提高了20%左右.实验表明,掺杂Gd3+ 1%(质量分数),温度为25 ℃,底物浓度为20 mg·L-1时对碱性品红染料降解的效果较好.     

LaVO4/TiO2在分解甲基橙中的光催化性能研究

光催化剂TiO₂在污水有机物降解中有着巨大优势,但由于对光的利用率过低,需要在TiO₂的基础上进行掺杂来改善其光催化性能。本研究利用稀土镧元素对TiO₂进行了掺杂分别制备了LaVO₄/TiO₂和La(NO₃)₃/TiO₂复合光催化剂,并将它们应用于甲基橙的光催化降解反应,证实了LaVO₄对TiO₂的光催化效果有较明显的增强作用。另外还研究了不同pH条件制备和不同掺杂比例的LaVO₄/TiO₂光催化效果,pH在10.56左右制备出的LaVO₄和掺杂比例为5%的LaVO₄制得的LaVO₄/TiO₂复合光催化剂效果较好。     

稀土氧化物掺杂对TiO2/沸石光催化性能的影响

以钛酸丁酯和稀土氧化物为原料, 采用溶胶 凝胶法制备了镧、 钕和镱稀土离子掺杂TiO₂/沸石光催化剂. 通过XRD和IR方法对样品进行表征, 研究了不同沸石粒径及不同稀土氧化物掺杂量(质量分数)对农药敌敌畏光催化降解性能的影响. 结果表明, 当沸石最佳粒径为0.15 mm, La³⁺掺杂量质量分数为3.0%时（以TiO₂质量计）, 稀土离子的掺杂可显著提高TiO₂//沸石的光催化降解性能.     

Preparation, characterization and photocatalytic activity of N-doped TiO2 nanocrystals

N-doped TiO₂ nanocrystals were prepared using titanium alkoxide as precipitant with different proportional materials. The products were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and UV-vis diffuse reflectance spectra. It is confirmed experimentally that the photocatalytic activity of N-doped TiO₂ is much higher than that of Degussa P25, when used for the degradation of crystal violet. The degradation kinetics follows an apparent first-order reaction, which is consistent with a generally observed Langmuir-Hinshelwood mechanism. The doping of TiO₂ with nitrogen significantly increases the absorption in the region of visible light. The energy of the band gap of N-doped TiO₂ is 2.92 eV. The better performance of N-doped TiO₂ can be explained by the fact that it is also excited with longer-wavelength light.     

I-doping of anodized TiO<Subscript>2</Subscript> nanotubes using an electrochemical method

In order to obtain TiO2 with high photocatalytic activity, a cathode reduction was used to dope I⁷⁺ and I⁵⁺ into TiO₂ nanotubes of anodized Ti in C₂H₂O₄•2H₂O + NH₄F electrolyte. SEM images show that the anodization method integrated the preparation with the doping process, which for nonmetals-doping is advantageous to maintain the morphological integrity of TiO₂ nanotubes. I⁷⁺-I⁵⁺-doping enhances the UV response of TiO₂ and result in a red-shift. Under UV/visible irradiation, a I⁷⁺-I⁵⁺-doped sample (400°C) showed the highest I_ph and photocatalytic efficiency. A part of I^– in the I⁷⁺-I⁵⁺-doped sample is involved in the UV response, the red-shift and the higher I_ph.     

Fe_2O_3/TiO_2复合纳米管阵列的制备及其可见光催化性能研究

在氟化铵-乙二醇体系中,采用阳极氧化法在铁基体上制备Fe_2O_3纳米管阵列,然后以氟钛酸铵为钛源,利用水热法在Fe_2O_3纳米管阵列上负载TiO_2纳米片,制得Fe_2O_3/TiO_2复合纳米管阵列,利用SEM、EDS、XRD、TEM、UV-Vis等手段,对所制Fe_2O_3/TiO_2纳米管阵列的表面形貌、物相结构及光催化性能进行表征,并分析Fe_2O_3/TiO_2纳米结构对亚甲基蓝的可见光降解能力。结果表明,Fe_2O_3/TiO_2复合纳米管阵列具有良好的可见光响应;NH_4F浓度为0.4%、水热反应3h制备的Fe_2O_3/TiO_2复合结构具有最佳的光催化性能,对亚甲基蓝的降解率可达90%。     

CdS光化学修饰介孔TiO2及其增强的可见光催化活性

[目的]提高介孔TiO₂材料的光催化活性。[方法]采用蒸发诱导自组装法(EISA),以四氯化钛和钛酸丁酯为钛源,嵌段共聚物P123(EO₂₀PO₇₀EO₂₀)为模板剂,制备介孔TiO₂。用光化学修饰法将CdS掺进介孔TiO₂中,合成对可见光有较好响应的复合材料,并利用X射线衍射(XRD)、透射电镜(TEM)、原子吸收分光光度法(AAS)和光催化等手段对样品进行表征。[结果]XRD和TEM结果表明成功合成有序的六方介孔材料;AAS确定复合材料中Cd的含量为0.96mg/g;光催化于500 W氙灯下以2×10^-5mol/L次甲基蓝(MB)为模型污染物,结果显示CdS/TiO₂复合材料的可见光催化活性明显提高。[结论]光化学修饰法制备的介孔CdS/TiO₂复合材料可增强其可见光催化活性。     

Preparation and photocatalytic activity of Cu-doped TiO2/SiO2

Cu²⁺-doped nanostructured TiO₂-coated SiO₂ (TiO₂/SiO₂) particles were prepared by the layer-by-layer assembly technique and their photocatalytic property was studied. TiO₂ colloids were synthesized by the sol-gel method using TiOSO₄ as a precursor. The experimental results showed that TiO₂ nanopowders on the surface of SiO₂ particles were well distributed and compact. The amount of TiO₂ increased with the increase in coating layers. The shell structure appeared to be composed of anatase titania nanocrystals at 550°C. The 2-layer coated TiO₂ particles on the surface showed a higher degradation rate compared with all the different-layer samples. The photocatalytic activity of Cu²⁺-doped TiO₂/SiO₂ was higher than that of undoped TiO₂/SiO₂. The optimum dopant content was about 0.10wt%.     

TiO2/SiO2复合光催化剂制备工艺参数优化及其表征

先以无机钛盐、硅酸盐为原料制取聚合硅酸硫酸钛,再通过液相水解法制得TiO2/SiO2复合光催化剂,并用SEM、XRD、BET和甲基橙脱色率对复合光催化剂进行表征。结果表明,TiO2/SiO2复合光催化剂制备优化工艺参数为:Ti(SO4)2作钛源、Ti/Si摩尔比为12∶1、水解反应pH值为6、煅烧温度为650℃,以此条件制备的复合光催化剂对甲基橙脱色率可达98.6%以上;TiO2/SiO2复合光催化剂为一种分散均匀的纳米级球形颗粒,其成分为以锐钛矿为主的TiO2,SiO2的复合有效抑制了TiO2晶粒的生长,同时提高了TiO2的热稳定性。     

二氧化钛-硫化镉/氧化石墨烯复合材料光催化降解废水中有机物的研究

本论文采用溶剂热法制备出TiO₂-CdS/rGO三元复合光催化材料,并对其降解亚甲基蓝、罗丹明B的光催化活性进行研究,发现TiO₂-CdS/rGO对于亚甲基蓝、罗丹明B的光催化降解活性优于TiO₂-CdS,催化效率明显提高,降解时间大大缩短;在可见光照射下,以TiO₂-CdS/rGO为光催化剂,光反应时间40 min,亚甲基蓝、罗丹明B的降解率可达100%。本文还研究了催化材料的稳定性、催化剂用量对光催化降解效果的影响。     

二氧化钛-硫化镉/还原氧化石墨烯复合材料光催化降解废水中有机物的研究

采用溶剂热法制备出二氧化钛-硫化镉/还原氧化石墨烯(TiO_2-CdS/rGO)三元复合光催化材料,研究其对亚甲基蓝、罗丹明B的光催化降解效果.结果表明,TiO_2-CdS/rGO对亚甲基蓝、罗丹明B的光催化降解效果优于TiO_2-CdS的,催化效率得到明显提高,降解时间大大缩短.在可见光照射下,以TiO_2-CdS/rGO为光催化剂,当光反应时间为40min时,亚甲基蓝、罗丹明B的降解率可达100%.