热致相法制备聚丙烯—聚乳酸共混中空纤维膜及其性能测试

采用热致相分离法制备了等规聚丙烯(iPP)-聚乳酸(PLA)共混中空纤维膜,并在碱性条件下水解膜表面的聚乳酸而产生亲水性基团,从而提高共混膜的表面亲水性.讨论了热致相法制膜中稀释剂配比对于共混膜的力学性能以及气体渗透性能的影响,表征了水解前后膜的接触角变化.电镜结果表明,聚乳酸颗粒呈10~20μm多孔状球状粒子均匀分散于共混膜的内部和表面,两种高分子组分表现为部分相容.此外力学性能结果发现共混膜的断裂伸长率高于iPP膜,而气体渗透性能结果证明稀释剂配比为5∶5时通量最佳.最后接触角测试表明,共混膜水解后亲水性获得大幅度提高.     

聚乳酸的合成和改性研究进展

聚乳酸类材料是一种用途广泛的生物降解高分子材料,已经成为生物医用材料中最受重视的材料之一.乳酸均聚物的合成主要有两种方法:丙交酯开环聚合法和直接缩聚法.直接缩聚法包括溶液缩聚和熔融缩聚;按照反应机制,开环聚合法包含阴离子型开环聚合、阳离子型开环聚合和配位开环聚合.本文讨论了各种聚合方法的机制和研究进展.由于乳酸均聚物合成的成本高,产物分子量低及其疏水性、脆性等性能缺陷,限制了其应用范围,目前对聚乳酸的研究主要集中在改性上,本文详细介绍了共聚、交联、表面修饰等化学改性方法和共混、增塑、纤维复合等物理改性方法的最新研究进展.并对聚乳酸的合成及改性的研究方向进行了展望,改进聚乳酸的合成工艺条件,使用无毒或低残留量的催化剂;用新材料对聚乳酸进行改性.在克服原有缺点的基础上开发出新用途的聚乳酸材料.     

聚乳酸微球的制备

利用聚乙烯醇和阿拉伯胶作为修饰剂, 采用溶剂挥发法制备聚乳酸微球, 通过正交实验设计研究了不同的修饰剂、 有机溶剂、 聚乳酸浓度、 表面活性剂、 搅拌速度等因素对微球粒径的影响, 并对制备的微球粉体学性质进行了初步研究. 结果表明, 在本文的工艺流程下制备的微球具有较均一的粒径, 平均粒径为2.0～3.0 μm, 微球表面平滑, 呈球形.     

CdTe/聚乳酸荧光膜的制备与研究

采用丙交酯开环聚合制备高纯度的聚乳酸,以十二胺为相转移剂,将一锅法合成的巯基CdTe量子点转移到三氯甲烷中,采用共聚的方法,合成了CdTe/聚乳酸(CdTe/PLA)纳米掺杂杂化材料及荧光膜的制备.通过紫外-可见光谱仪(UV-vis)、荧光(PL)等表征方法考察合成的CdTe量子点的光学性能,通过扫描电镜(SEM)、XRD及拉伸试验机系统研究了改性后的荧光膜的力学性能和纳米材料在聚乳酸膜中的分散情况.结果表明:CdTe量子点在聚乳酸中分散程度很好,并且保留了PLA膜的力学性能,所制备的复合膜具有优越的荧光性能.     

乳酸膨润土及其在聚乳酸材料中的应用

为扩展聚乳酸的应用范围,用乳酸与碱性钙基膨润土反应制备出剥离型乳酸膨润土,并用该材料与聚乳酸通过氯仿溶液铸膜法制备出聚乳酸/乳酸膨润土复合膜.用扫描电镜(SEM)观察膜的形态,万能力学试验机测定膜的拉伸强度和断裂伸长率,差示扫描量热法(DSC)和热重分析(TGA)研究膜的热性能.测试结果表明,添加1％的乳酸膨润土以剥离...     

用于食品保鲜包装的聚乳酸透气膜研究

制备了聚乳酸透气膜,并研究了其用于猪肉包装的保鲜效果.采用非溶剂致相分离法制备聚乳酸膜,通过添加N-甲基吡咯烷酮,使得薄膜具备多孔结构.对薄膜的透光率进行了测试,利用扫描电镜和红外光谱仪对薄膜的微观结构和基团组成进行了表征.实验发现,聚乳酸多孔膜扫描电镜图与聚乳酸纯膜相比,薄膜内部具有均匀的多孔结构.从红外光谱图中可以看出,添加了N-甲基吡咯烷酮的薄膜与聚乳酸纯膜的吸收峰没有明显的差别,说明N-甲基吡咯烷酮在后续操作中从薄膜中分离出来,形成孔洞后并不会影响聚乳酸膜本身结构.在薄膜用于新鲜猪肉的包装中,通过聚乳酸透气膜的包装,猪肉的保质期得到了延长.与保鲜袋、保鲜膜、聚乳酸纯膜包装的猪肉相比,聚乳酸透气膜能有效延长猪肉保质期2～3 d.     

生物降解高分子--聚乳酸的合成

以天然矿石--改性片麻岩为聚合反应的催化剂,通过直接缩聚方法制备了不同分子量的聚乳酸.并应用FTIR,^1H-NMR,DSC等测试手段对两种不同催化剂制备的聚乳酸的结构进行对比研究.同时也研究了反应时间对聚合产物分子量的影响.     

聚乳酸降温膜的研究

用L-丙交酯单体,在催化剂作用下开环聚合,得到聚乳酸,采用己内酯做改性剂,得到复合材料,并制备出聚乳酸基复合膜,聚合物采用核磁(H NMR)进行结构鉴定,利用凝胶色谱仪(GPC)测试聚合物的分子量,采用DSC对薄膜进行结晶度测定.并将该膜应用到加热不燃烧卷烟领域,实验结果表明,聚乳酸用于烟棒具有较好的降温效果.     

木质素接枝右旋聚乳酸的结晶行为及对左旋聚乳酸的结晶促进作用

木质素（lignin）作为仅次于纤维素的第二大可再生生物质资源,近年来受到广泛关注并已被应用于高分子材料的改性。本文在对碱木质素烷基化修饰的基础上,利用其丰富的羟基对右旋丙交酯进行开环聚合,制备了一系列不同分子量的烷基化木质素接枝右旋聚乳酸（LGPD）。通过对LGPD自身结晶行为的研究表明,木质素的存在能够促进右旋聚乳酸（PDLA）的结晶,提高其吸收紫外线的能力。相对于4臂右旋聚乳酸（4a-PDLA）,将LGPD作为添加剂加入到左旋聚乳酸（PLLA）后更有利于立构复合晶的形成,从而进一步提高了共混材料的结晶能力。     

聚乳酸微球制备的初步研究

聚乳酸PLA(polylactide)是一种无毒、可生物降解的聚合物,它具有良好的生物相容性,在医药上有广泛的应用.通过实验研究了聚乳酸浓度,表面活性剂浓度以及两者的配料比对溶媒挥发法制备聚乳酸微球及微球粒经的影响.实验为进一步制备医用聚乳酸微球和类似的医用药剂做了有益的探索.     

聚己二酸乙二酯的合成及其与聚乳酸的共混研究

分别采用对甲苯磺酸与钛酸丁酯两种催化剂,通过缩聚反应制备了脂肪族聚酯——聚己二酸乙二酯(PEA)。研究了催化剂的种类和用量对PEA分子量的影响,考察了PEA样品对聚乳酸力学性能的改性效果。结果表明,两种催化剂用量相同时,钛酸丁酯的催化效率高;用钛酸丁酯做催化剂时,最佳用量为酸的摩尔量的1‰;用对甲苯磺酸做催化剂时,最佳用量为酸的摩尔量的5‰;不同分子量的PEA对PLA改性效果不同,采用较高分子量的PEA与聚乳酸(PLA)共混,在PEA含量达到10%之后,可以取得较好的改性效果。     

环糊精接枝聚乳酸的初步研究

以偶联法合成了环湖精(CD)接枝聚乳酸(PLA)共聚物CD＿g＿PLA,即先合成PLA支链,再将PLA末端羧基转变为高反应活性的酰氯,然后通过PLA末端的酰氯与CD上羟基反应,将PLA支链偶联到CD上,得到CD＿g＿PLA共聚物,对共聚物进行了红外等初步表征。与PLA均聚物相比,接枝共聚物的亲水性有明显的改善。CD＿g＿PLA的合成提供了一种新型完全可生物降解的缓释药物载体。     

聚乳酸在医学领域应用研究进展

 聚乳酸是一种具有良好的生物相容性、可生物降解性和生物吸收性的脂肪族聚酯类高分子材料,主要原料乳酸来源于玉米等天然材料,其无刺激性、无毒副作用,对人体高度安全,对环境友好,可塑性好,易于加工成型,被公认为新世纪最有前途的生物医用材料和新型包装材料。通过改性后的聚乳酸类材料在力学性能、热性能及降解性能等方面均有改善,更加符合现代医药学材料的要求,近几年已经广泛应用于医用生物材料中。本文详述了聚乳酸类材料在医用手术缝合线、牙科材料、眼科植入材料、骨折固定材料、组织工程支架、药物缓释材料及临床应用等医药学领域中的研究进展,展望了未来聚乳酸类材料的研究及应用方向,为在克服聚乳酸材料原有缺陷的基础上开发出新用途的医药学类材料提供有效的资料依据。     

Mechanical and Thermal Properties of Apocynum and Ramie Fiber Mat Reinforced Polylactic Acid Composites

With the increasing awareness of environmental protection and rational utilization of resources, natural fiber reinforced composites have shown broad development prospects. Apocynum fiber, known as the "king of wild fiber", not only has moisture absorption, air permeability, and good mechanical properties but also has many health-related advantages such as antibacterial properties. In this study, four types of needle-punched Apocynum fiber and ramie fiber mat reinforced polylactic acid(PLA) composites were fabricated. Mechanical and thermal properties of the composites were tested and analyzed. The results showed that compared with those of the ramie fiber finish needle-punched mat reinforced composites, the tensile strength and the tensile modulus of Apocynum fiber finish needle-punched mat reinforced composites had increased by 15.3% and 60.1%, respectively. In comparison, the bending strength and the bending modulus were decreased by 21.8% and 7.6%, respectively. Moreover, compared with the Apocynum fiber finish needled-punched mat reinforced composites and the ramie fiber finish needle-punched mat reinforced composites, the Apocynum 50/ramie 50 finish needle-punched mat reinforced composites had the best tensile and bending properties. The after-fracture morphology was detected by a scanning electron microscope(SEM). The thermal properties of the composites were also characterized. It was found that the thermal properties of the four types of composites showed very similar behaviors.     

生物医用聚乳酸纤维增强壳聚糖棒材

利用原位沉析法制备了聚乳酸纤维/壳聚糖复合棒材,对复合棒材的微观形貌、力学性能进行了表征.有机聚乳酸纤维和有机壳聚糖基体具有良好的相容性,纤维表面还会因氢键等作用和基体产生物理吸附及一定的分子链缠结,SEM结果表明,纤维与基体间形成了良好的界面作用.复合棒材因聚乳酸纤维的加入有效地提高了弯曲强度和模量.当添加8%(质量分数)11 mm长的纤维时,复合材料弯曲强度达到108.9 MPa,比壳聚糖提高了54.9%,复合棒材弯曲模量达到4.74 GPa,比壳聚糖提高了170.9%.聚乳酸纤维和壳聚糖均具有良好的生物相容性和可降解性,这种复合材料在可吸收内固定材料方面将具有广阔的用途.     

乳酸和聚乳酸的研究进展

从环境与可持续发展的角度,概述了乳酸和聚乳酸的研究现状与发展方向。     

电纺聚-L-乳酸/β-磷酸三钙复合物纳米纤维膜

利用静电纺丝法制备了生物可吸收聚-L-乳酸(PLLA)/β-磷酸三钙(β-TCP)复合物纳米纤维膜.采用扫描电子显微镜(SEM)、场发射扫描电子显微镜(FESEM)等手段研究了复合物纳米纤维膜的结构和形态,详细探讨电纺工艺条件对制备PLLA/β-TCP复合物纳米纤维的形态影响.通过拉伸力学测试、噻唑蓝比色法(MTT)对复合物纳米纤维膜的力学性能和体外细胞相容性作了进一步研究.结果表明,PLLA/β-TCP复合物纳米纤维的几何结构与电纺条件有关,随着聚合物溶液浓度增加、溶液流速增大,纤维直径有不同程度的增大;复合物纳米纤维膜的拉伸强度和杨氏模量随β-TCP的含量增加而下降;复合物纳米纤维膜对L-929细胞系无细胞毒性,显示良好的细胞相容性.     

绿色塑料聚乳酸的关键技术研发与产业化应用

聚乳酸(PLA)作为一种新型生物基绿色塑料,能够广泛应用于多种领域,为解决环境污染和石油依赖等问题提供有力的材料支撑。中国科学院长春应用化学研究所针对当前聚乳酸产业化存在的关键科学和技术性难题,开展了生物基聚乳酸绿色塑料产业化关键技术的创新性研发及应用推广项目,从L-乳酸出发,突破了乳酸低聚、裂解、丙交酯精制和开环聚合等一系列关键技术问题,取得了一系列创新性成果,在世界上继美国Nature Works后第二个实现了PLA规模化生产和应用,加速推动了以聚乳酸为龙头的生物可降解塑料行业的发展。本文综述了聚乳酸关键技术研发与产业化项目的重要意义,已取得的阶段性成果,并针对聚乳酸产业化在我国的发展提出了许多对策建议。     

Dexamethasone-Loaded PLGA Microspheres Incorporated PLLA/PLGA/PCL Composite Scaffold for Bone Tissue Engineering

The combination of micro-carriers and polymer scaffolds as promising bone grafts have attracted considerable interest in recent decades.The poly(L-lactic acid)/poly(lactic-co-glycolic acid)/polycaprolactone(PLLA/PLGA/PCL)composite scaffold with porous structure was fabricated by thermally induced phase separation(TIPS).Dexamethasone(DEX)was incorporated into PLGA microspheres and then loaded on the PLLA/PLGA/PCL scaffoldtopreparethedesiredcompositescaffold.The physicochemical properties of the prepared composite scaffold were characterized.The morphology of rat bone marrow mesenchymal stem cells(BMSCs)grown on scaffolds was observed using scanning electron microscope(SEM)and fluorescence microscope.The resultsshowedthatthePLLA/PLGA/PCLscaffoldhad interconnected macropores and biomimetic nanofibrous structure.In addition,DEX can be released from scaffold in a sustained manner.More importantly,DEX loaded composite scaffold can effectively support the proliferation of BMSCs as indicated by fluorescence observation and cell proliferation assay.The results suggested that the prepared PLLA/PLGA/PCL composite scaffold incorporating drug-loaded PLGA microspheres could hold great potential for bone tissue engineering applications.     

聚乳酸/聚环氧乙烷纳米纤维膜的结构与性能表征

采用静电纺丝方法制备了聚乳酸(PLLA)/聚环氧乙烷(PEO)纳米纤维膜,利用扫描电子显微镜(SEM)、差示扫描量热(DSC)、X-射线衍射(XRD)和拉伸测试,对PLLA/PEO纳米纤维膜的形貌、结构、结晶行为和力学性能进行了表征,探究了PEO的质量分数对PLLA/PEO纳米纤维膜的结构、结晶行为和力学性能的影响。结果表明,PEO的加入,降低了PLLA/PEO纳米纤维膜的平均直径和直径分布宽度,提高了纤维的结晶速度、结晶度及断裂伸长率;PEO分子可提高聚乳酸分子链的运动能力和降低纤维的取向度,从而降低因取向引起的中间相含量,提高结晶相含量,进而改善聚乳酸纤维的结晶性能和韧性。