钢表面激光熔覆TiC_P/Fe基合金复合耐磨涂层

在２０钢表面用激光束熔覆了ＴｉＣ颗粒与Ｆｅ基自熔合金复合耐磨涂层。对涂层的组织、化学成分、硬度及耐磨性进行了分析。结果表明，熔覆层主要由γ－Ｆｅ，α－Ｆｅ（马氏体）和ＴｉＣ颗粒组成。为获得平整而无裂纹的表面复合涂层，随预涂覆层的ＴｉＣ量的增加，所需激光能量密度提高，复合涂层的硬度及耐磨性也随之增加。     

镍基自熔合金激光熔敷层的组织和干摩擦磨损特性

研究了几种不同成份的Ｎｉ基自熔合金激光熔敷层的组织和干摩擦磨损性能。结果表明,熔敷层的耐磨性远高于淬火态ＧＣｒ１５钢,其中以Ｎｉ２１＋ＷＣ＋ＣｅＯ２合金熔敷层的耐磨性最好,磨损机制主要是磨粒磨损和部分粘着磨损。     

感应熔敷WC/Ni基复合涂层的组织和性能

采用高频感应熔敷技术，以Ni60A自熔合金粉末、微纳米碳化钨粉末为原料，在16Mn钢表面制备出以微纳米WC颗粒为增强相的Ni基金属陶瓷涂层，并测试了涂层的显微硬度。利用磨擦磨损试验机，以45#钢为对磨偶件，评价了涂层的滑动干磨擦性能。实验结果表明：涂层的硬度为890～910,磨擦系数为0．3-0．4，耐磨性比16Mn钢提高4倍以上。     

抽油机光杆激光熔覆表面耐磨损性能研究

以抽油机光杆常用20CrMo钢为基体材料,选择Co基、Ni基和Fe基合金粉末为熔覆材料,使用HGL 9450-000型5 kW横流CO2激光器,采用同步送粉方式进行激光熔覆加工,获得了组织致密无宏观缺陷的激光熔覆层.利用硬度计和MPX-2000型盘销式摩擦磨损试验机对20CrMo钢及三种自熔合金涂层试样进行耐磨损性能研究.     

自熔合金氧乙炔焰喷熔层可靠性分析

进行了自熔合金氧乙炔火焰喷熔层的腐蚀、磨粒磨损和摩擦磨损行为对比的试验研究，对喷熔层与母材之间的结合性能及喷熔层孔隙进行了测试分析．试验结果表明：自熔合金喷熔层可以在高负荷环境及非氧化性酸腐蚀的严重的工作环境中服役．     

真空熔烧Ni基合金涂层的力学性能研究

为了得到Ｎｉ基合金涂层抗拉性能,对采用不同温度制备的真空熔烧Ｎｉ基合金涂层进行了抗弯性能试验。通过测量和计算,取得了Ｎｉ基合金涂层的抗弯强度及其随熔烧温度提高而变化的规律。由钢基体和Ｎｉ基合金涂层组成的弯曲试样实质上是复合材料。根据对Ｎｉ基合金涂层杨氏弹性模量的测定,按复合材料模型计算了抗弯强度。试验结果表明,真空熔烧Ｎｉ基合金涂层具有相当好的弯曲强度。     

激光溶覆用复合粉混料方法的研究

采用不同混料方式在Ｃｏ－０１钴基自熔合金粉末基础上添加钼元素。研究了各种混料方式对混料后粉末形貌、混料成分均匀性以及复合粉的激光熔覆性能的影响，对适合于激光熔覆用复合粉末生产的混料方法进行了初步探讨。     

镍基碳化钨高温磨损特性的研究

本文用不同碳化钨含量的镍基自熔合金粉末喷焊层的试样,进行扫描电镜形貌观察和X光衍射分析,同时进行了高温磨粒磨损试验,试验结果发现粉末中碳化钨的含量对喷焊层的磨损特性及组织结构有重要的影响,其中以35%碳化钨喷焊层的高温耐磨性最佳.     

镍基激光熔覆层腐蚀磨损交互作用

采用CO2激光器在5Cr21Mn9Ni4N不锈钢表面制备了含CeO2的镍基激光熔覆层,并对不同成分的激光熔覆层进行动态腐蚀试验、动态磨损试验和腐蚀磨损双重影响试验.分析讨论CeO2、冲击速度、硫酸介质浓度和石英砂浆对镍基激光熔覆层动态腐蚀速率、动态磨损速率和腐蚀磨损速率作用的影响.在腐蚀磨损中,腐蚀和磨损共同作用、相互增强,熔覆层的抗腐蚀磨损作用的性能与熔覆层的耐磨性、耐蚀性的综合性能相关.     

原位生成TaB_2颗粒增强镍基复合涂层的组织与耐磨性

以Ta粉、B粉和Ni60A粉为原料,利用氩弧熔覆技术在Q235钢基体表面制备原位生成TaB_2颗粒以增强Ni基复合涂层。通过金相显微镜、扫描电镜、X射线衍射仪、显微硬度计以及摩擦磨损试验机对复合涂层的显微组织、物相、显微硬度以及涂层耐磨性进行分析研究。结果表明,镍基复合涂层形成良好,没有气孔和裂纹等缺陷,涂层与基体呈现良好的冶金结合。熔覆层由原位生成的TaB_2颗粒相、Fe-Cr相及Cr_7C_3相组成。TaB_2颗粒弥散分布在基体上,氩弧熔覆涂层的平均显微硬度达到11.50 GPa,比基体Q235钢提高约4倍。在室温干滑动磨损条件下,该熔覆涂层的耐磨性比基体提高约12倍。     

二氧化钛涂层/钢的摩擦磨损性能

在室温下对二氧化钛涂层/GCr15钢、20Cr钢/GCr15钢进行了油润滑情况下的球盘式摩擦磨损试验.研究了速度、载荷等外部因素对摩擦系数、磨损率等的影响.结果表明,涂层的显微硬度(HV)基本维持在685,气孔率很低,具有较高的致密性和较好的加工性能,可以更好地满足耐磨工艺的需要;TiO2涂层/GCr15钢摩擦副在试验条件下抗磨损性能优于20Cr钢/GCr15钢.     

几种合金粉末喷涂层的摩擦磨损特性

通过扫描电于显微镜观察、Ｘ射线能谱分析、显微硬度测定和干摩擦磨损试验，本文研究了Ｍｉ＋４Ｂ微晶粉末、Ｇ３０２铁基喷涂粉末和Ｍ＿８０Ｓ＿２０铁基非晶自熔合金粉末喷涂层的组织和耐磨性．结果表明，Ｍ＿８０Ｓ＿２０ｓ喷涂层内仍保留一定数量的高硬度的合金非晶质点，粉末颗粒塑性变形大，层状结构明显，结合充分；Ｍ＿２十４Ｂ喷涂层仍保持粉末高速钢的组织特性，粉末颗粒塑性变形最小，层内有较多的孔洞和空隙；Ｇ３０２喷层的结合情况介于两者之间。三种合金喷涂层均具有比ＧＣｒ１５钢高得多的耐磨性。     

碳纤维/石墨-铜基自润滑耐磨复合涂层的摩擦学性能

为提高45~#钢的摩擦学性能,采用热压烧结技术,在45~#钢表面制备了以Ni为中间连接层的铜基自润滑耐磨复合涂层。采用扫描电镜和能谱仪对涂层表面及截面的微结构进行了分析;采用球-盘式摩擦磨损试验机与GCr15球配副,在不同载荷和速度下,研究了铜基自润滑耐磨复合涂层和基体的干摩擦学性能,并分析了磨损机理。结果表明:在所有试验条件下,含4wt%碳纤维和2wt%石墨样品的摩擦系数和磨损率均比45~#钢低,且在15 N载荷、500 r/min转速下显示出最优的摩擦学性能。     

Tribological behaviors of some polymeric materials in sea water

Ocean tribology, a new research field of tribology, is being established and developing. The investigation on the tribology in sea water has important significance to ocean exploitation. In this paper, the tribological behaviors of UHMWPE, PTFE as well as Ekonol/PTFE, graphite/PTFE and CF/PTFE sliding against GCr15 steel and Ni-Cr-WC alloy in sea water were investigated, and compared with those in pure water. Results show that the main factors that affect the tribological behaviors of five polymeric materials in sea water are the corrosive effect and lubricating effect of sea water. When polymeric materials sliding against GCr15 in sea water, owing to serious corrosion of counterface by sea water, the surface roughness of the counterface increases largely. As a result, the lubricating effect of medium decreases sharply and the plowing effect of counterface increases greatly. So the friction coefficients and wear rates of five materials sliding against GCr15 in sea water are much larger than those under other conditions. Such wear model, depending on the corrosion of counterface by medium, can be called indirect corrosive wear. Under other three conditions, owing to the more superior lubricating effect of sea water than pure water and the better wettability of Ni-Cr-WC than GCr15, the friction coefficients and wear rates of five materials increase in the following order： sliding against Ni-Cr-WC in sea water 〈 sliding against Ni-Cr-WC in pure water 〈 sliding against GCr15 in pure water. Moreover, compared with other materials, CF/PTFE is the one with more superior plowing and wear resistance in pure and sea water, which is a potential frictional material well suitable for pure and sea water lubrication.     

工具钢表面激光熔覆耐磨性试验研究

使用5kWCO2激光器对9SiCr工具钢表面进行Co基和Ni基合金熔覆处理·利用销盘式摩擦试验机对激光熔覆表面和Q235配副进行干摩擦和油润滑试验,通过扫描电镜研究了熔覆层表面磨损形貌并分析了干摩擦和润滑条件下磨损机理·试验结果表明,熔覆区磨损形式主要是磨粒、粘着磨损·干摩擦时,Ni合金熔覆层比Co合金耐磨性要好;润滑条件下,两种合金的耐磨性比干摩擦时都有很大提高     

奥贝球铁的无润滑滑动磨损机制

研究了一种铜钼奥贝球铁在按触应力下与GCr15钢对磨时的无润滑滑动磨损。结果表明当载荷小于98N时,奥贝球铁比GCr15耐磨。磨损过程中的形变诱发马氏体相变是这种材料具有良好耐磨性的重要原因。观察到了轻微磨损向剧烈磨损的转化。轻微磨损的机制是氧化磨损与分层机制;而脱层与分层机制则为造成剧烈磨损的原因。     

M_2十4B喷涂层及激光涂覆层的组织与磨损特性

本文对Ｍ２十４Ｂ微晶粉末的喷涂层和激光涂覆层的组织与耐磨性进行了研究．结果表明，喷涂层和激光涂覆展均有各自独特的组织特征，两者的耐磨性均为ＧＣｒ１５钢的６．５倍以上．     

55%铝—锌—1.6%硅合金镀层的耐蚀性能

在盐雾试验（ＮＳＳ、ＡＳＳ）、曝气试验、浸泡试验和缝隙腐蚀试验的基础上,通过与锌镀层和铝镀层的对比,研究了５５％Ａｌ－Ｚｎ－１．６％Ｓｉ合金镀层的耐蚀性能．镀层中富锌相的存在,导致缝隙腐蚀中的自催化酸化闭塞电池难以形成,因而该镀层的耐缝隙腐蚀性能优于铝镀层;在其他试验条件下,由于镀层表面富铝相占较大面积,使得镀层的耐蚀性高于锌镀层,接近于铝镀层．钝化处理后各镀层耐蚀性均有显著提高．     

铸钢轧辊电火花沉积YG8涂层的组织结构和性能

采用新型电火花沉积设备,把YG8电极材料沉积在铸钢轧辊材料上,制备了WC沉积涂层,研究了其微观组织及耐磨性能. 结果表明:沉积层主要由Fe3W3C、Co3W3C、W2C和Fe7W6C等相组成;沉积层与基体冶金结合,具有纳米颗粒尺寸的Fe7W6、W2C等硬质相弥散分布于沉积层中;沉积层的平均硬度为1 331 HV;沉积层较铸钢轧辊的磨损性能提高了2.3倍;沉积层的磨损机理以疲劳磨损为主,细小的弥散分布的硬质相是沉积层硬度及耐磨性提高的主要因素.