TiO2/SiO2复合光催化剂制备工艺参数优化及其表征

先以无机钛盐、硅酸盐为原料制取聚合硅酸硫酸钛,再通过液相水解法制得TiO2/SiO2复合光催化剂,并用SEM、XRD、BET和甲基橙脱色率对复合光催化剂进行表征。结果表明,TiO2/SiO2复合光催化剂制备优化工艺参数为:Ti(SO4)2作钛源、Ti/Si摩尔比为12∶1、水解反应pH值为6、煅烧温度为650℃,以此条件制备的复合光催化剂对甲基橙脱色率可达98.6%以上;TiO2/SiO2复合光催化剂为一种分散均匀的纳米级球形颗粒,其成分为以锐钛矿为主的TiO2,SiO2的复合有效抑制了TiO2晶粒的生长,同时提高了TiO2的热稳定性。     

TiO2/SiO2复合光催化剂制备工艺参数优化及其表征

先以无机钛盐、硅酸盐为原料制取聚合硅酸硫酸钛,再通过液相水解法制得TiO2/SiO2复合光催化剂,并用SEM、XRD、BET和甲基橙脱色率对复合光催化剂进行表征.结果表明,TiO2/SiO2复合光催化剂制备优化工艺参数为:Ti(SO4)2作钛源、Ti/Si摩尔比为12∶1、水解反应pH值为6、煅烧温度为650℃,以此条件制备的复合光催化剂对甲基橙脱色率可达98.6％以上；TiO2/SiO2复合光催化剂为一种分散均匀的纳米级球形颗粒,其成分为以锐钛矿为主的TiO2,SiO2的复合有效抑制了TiO2晶粒的生长,同时提高了TiO2的热稳定性.     

介孔TiO2及Fex/TiO2纤维光催化降解酸性橙Ⅱ的性能研究

以胶原纤维为模板分别负载钛(Ti4+)或钛(Ti4+)和铁(Fe3+),在高温下煅烧制得介孔TiO2和Fex/TiO2纤维.以酸性橙Ⅱ为模型分子,研究了介孔TiO2和Fex/TiO2纤维在可见光照射下对酸性橙Ⅱ的降解特性.研究表明,通过掺杂Fe3+能有效地提高介孔TiO2纤维的光催化活性,在本实验条件下,最佳的Fe/Ti摩尔比为0.01,最佳的煅烧温度为600℃.在酸性橙Ⅱ初始pH值为3～6,初始浓度为0.1 mmol.L-1,介孔Fe0.01/TiO2纤维用量为1 g.L-1,可见光照射下反应4 h后,酸性橙Ⅱ的脱色率和矿化率达到99%和46%以上.光催化活性的稳定性研究表明,介孔Fe0.01/TiO2纤维具有良好的光催化活性的稳定性,能多次重复使用.     

磁性纳米TiO2/Fe3O4的制备及光催化去除甲基紫的研究

采用溶胶-凝胶法,在磁性纳米Fe3O4表面包覆TiO2制备磁性纳米TiO2/Fe3O4复合光催化剂.用XRD、SEM、FTIR对其表面结构进行表征,结果显示Fe3O4表面被锐钛型的TiO2包覆,该磁性纳米光催化剂颗粒分布均匀,平均粒径为80～100 nm.将纳米TiO2/Fe304用着光催化剂去除水中的甲基紫染料,在紫...     

TiO2/Y2O3/海泡石复合体的制备及光催化降解甲基橙的研究

以TiCl4和Y2O3为原料,海泡石为载体,采用过氧化氢络合物热分解法制备了复合TiO2/Y2O3/海泡石光催化剂.以甲基橙为目标降解物.进行正交试验,得出制备的最佳条件.研究了对甲基橙溶液的降解率的影响因素。     

磁性纳米复合光催化剂Bi2O3/Fe3O4的制备及其光催化活性研究

以纳米Fe3O4磁粉为载体,采用溶胶－沉淀法成功地制备了Bi2O3/Fe3O4磁性纳米复合光催化剂.用SEM和XRD对其形貌和结构进行表征,并以偶氮染料甲基橙溶液的光催化降解,来评价Bi2O3/Fe3O4磁性纳米复合光催化剂的光催化活性.结果表明,Bi2O3比较均匀地包覆在Fe3O4粒子的表面,在合成过程中Fe3O4的结构和大小几乎没有发生变化.该复合光催化剂具有较高的光催化活性,在500 W Xe灯照射60 min后,使甲基橙的降解率达到91.5%,并具有可利用其磁性回收重用的特点,应用前景广泛.     

CeO2-TiO2/[CoW12O40]5--HTLC的制备及光催化性能

为了克服杂多酸易溶于极性溶剂,较难回收重复使用的缺点,采用共沉淀法制备了镁铝水滑石;并以硝酸根型水滑石作为前体,通过插层组装合成了杂多阴离子[CoW12O40]5--HTLC;再采用微乳液法将CeO2掺杂的TiO2负载到[CoW12O40]5--HTLC上,焙烧后得到CeO2-TiO2/[CoW12O40]5--HTLC光催化剂。采用XRD、FT-IR、SEM-EDS和UV-Vis漫反射光谱等手段对催化剂进行了表征;以甲基橙为模拟污染物,考察了催化剂样品的光催化性能。实验结果表明:CeO2掺杂TiO2复合粒子在可见光区吸光性能高于TiO2;CeO2掺杂TiO2与杂多阴离子[CoW12O40]5-有协同光催化作用,CeO2-TiO2/[CoW12O40]5--HTLC光催化剂对可见光的吸收大大增强。经模拟日光照射2 h,15%(CeO2-TiO2)/5%[CoW12O40]5--HTLC催化剂对甲基橙的脱色率达到93%。     

Ti掺杂Bi2O3的光催化性能

采用溶胶—活性炭浸渍法制备了掺杂不同比例Ti的Bi2O3粉体光催化剂,并利用X射线衍射分析(XRD)、BET比表面积测试法(BET)、扫描电镜分析(SEM)、紫外—可见光漫反射谱(UV-Vis DRS)等技术对其进行了表征。表征结果显示,掺Ti的Bi2O3样品在紫外区有比纯Bi2O3更强的吸光性能。通过对甲基橙在紫外光(λmax=365 nm)下的降解实验评价光催化剂的光催化活性,考察不同钛掺杂量及不同焙烧温度对光催化性能的影响。结果表明,当光催化剂中钛掺杂摩尔百分含量为3%,焙烧温度为300℃,其光催化活性最好。当催化剂用量为2 g/L时,在120 min内,对浓度为20 mg/L的甲基橙溶液进行光催化降解,其降解率达96.4%。     

溶胶-凝胶法制备TiO_2/MCM-41负载型光催化剂及其性能表征

以钛酸丁酯为钛源、MCM-41分子筛为载体,采用溶胶-凝胶法制备TiO2/MCM-41负载型光催化剂,并通过XRD、BET、TEM、XPS对最佳条件下制备的光催化剂进行表征。结果表明,所制光催化剂是一种具有均匀规则孔道结构的介孔材料,其粉体比表面积高达358.8m2/g;经700℃煅烧,催化剂主要晶相为锐钛矿相。光催化剂中的Ti以+4价存在,TiO2表面羟基氧所占比率为38.0%。以水中甲基橙为模拟污染物,TiO2/MCM-41光催化剂对浓度为25mg/L的甲基橙溶液降解0.5h后,其脱色率为93.7%。     

微乳液制备粉煤灰微珠负载型La~(3+)、Fe~(3+)共掺杂TiO_2光催化剂

以粉煤灰微珠为载体,采用微乳液法制备La3+、Fe3+共掺杂TiO2光催化剂.并用透射电镜、扫描电镜对复合粒子的形貌进行观察;X射线衍射对煅烧后复合粒子中的组分进行分析;分光光度法测得TiO2在粉煤灰微珠表面的包覆率;分光光度计测定催化剂甲基橙的脱色率.实验结果表明:采用微乳液法制备的负载型Fe3+、La3+共掺杂TiO2尺寸均匀,分散度较好,包覆率达到35.67%,甲基橙的脱色率为48%,催化剂可再生5次.Fe3+、La3+共掺杂的协同作用使催化剂活性更高,Fe3+、La3+的最佳掺杂量分别为0.3%、1.0%.     

纳米Fe2O3-Al2O3复合材料的制备

采用溶胶-凝胶表面包覆法制备了纳米Fe₂O₃-Al₂ O₃复合材料, 利用X射线衍射和透射电镜对样品的物相、 粒度和形貌进行了研 究. 结果表明, α-Fe₂O₃掺杂降低了Al₂O₃相变温度, 在900 ℃可以得到稳定的α-Al₂O₃相.     

纳米Al2O3颗粒对Cu-Al2O3性能的影响

采用溶胶-凝胶法制备纳米Al₂O₃颗粒,通过粉末冶金法制备氧化铝铜（Cu-Al₂O₃）。采用X射线光电子能谱仪、扫描电子显微镜、洛氏硬度仪和涡流计分别测试了Cu-Al₂O₃的结合能、微观组织、硬度和导电率。结果表明：随Al₂O₃颗粒含量的增加,Cu-Al₂O₃的硬度先升高后降低,当Al₂O₃颗粒的质量分数达到0.084%时,Cu-Al₂O₃的硬度达到最大值75.73（HRB）。Cu-Al₂O₃的导电率随着Al₂O₃颗粒含量的增加逐渐下降。Al₂O₃颗粒的质量分数为0.084%时为最佳值,Cu-Al₂O₃的硬度达到最大值,导电率达到69.1% IACS。     

Preparation and photocatalytic activity of Cu-doped TiO2/SiO2

Cu²⁺-doped nanostructured TiO₂-coated SiO₂ (TiO₂/SiO₂) particles were prepared by the layer-by-layer assembly technique and their photocatalytic property was studied. TiO₂ colloids were synthesized by the sol-gel method using TiOSO₄ as a precursor. The experimental results showed that TiO₂ nanopowders on the surface of SiO₂ particles were well distributed and compact. The amount of TiO₂ increased with the increase in coating layers. The shell structure appeared to be composed of anatase titania nanocrystals at 550°C. The 2-layer coated TiO₂ particles on the surface showed a higher degradation rate compared with all the different-layer samples. The photocatalytic activity of Cu²⁺-doped TiO₂/SiO₂ was higher than that of undoped TiO₂/SiO₂. The optimum dopant content was about 0.10wt%.     

TiO2微粉对Al2O3-MgO-Cr2O3浇注料性能的影响

马克思的市民社会决定国家理论的形成,经历了一个思想交锋、自我批判、绵延提升直至最终导出唯物史观之创建的逻辑进程。马克思立足于《莱茵报》时期的感性经历,先后运用哲学、历史学和政治经济学的方法和知识对黑格尔理性国家观进行系统的理论清算,纠正了黑格尔的市民社会与国家关系的“历史错位”,首次确立了“社会本体论”原则。市民社会决定国家理论的形成是标志着唯物史观开始诞生的第一命题。分析马克思市民社会决定国家理论的发展脉络和演进逻辑,有利于澄清马克思市民社会理论与唯物史观的内在关联,科学评价市民社会理论在历史唯物主义中的历史地位。     

K2CO3活化合成的甘蔗渣衍生多孔碳用于CO2吸附

环境中化石燃料的大量使用导致CO₂浓度不断增加,这是全球变暖的主要原因。为了解决这一问题,开发一种高效廉价的吸附材料至关重要。以甘蔗渣为碳源,尿素为N源,通过碳化和K₂CO₃活化制备出N掺杂多孔碳。多孔碳的物理化学性质用N₂解吸等温线、傅里叶红外光谱、元素分析、扫描电子显微镜观察和X射线衍射等方法进行表征。结果表明：该材料具有高度发达的孔隙、较高的N含量和较高的石墨化程度。当尿素与甘蔗渣混合比是2、碳化温度是800℃、K₂CO₃浸渍比是3时,多孔碳的比表面积高达2 486.67 m²·g^-1,同时CO₂吸附量高达250.73 mg·g^-1。由此可见以廉价的甘蔗渣制备N掺杂的多孔碳用于吸附CO₂具有广阔的应用前景。     

Al2O3/WO3/ZrO2催化剂的制备及在酯交换反应中的研究

以松木为模板,采用模板法将不同含量的Al₂O₃添加到WO₃/ZrO₂复合氧化物中,采用X射线衍射、BET比表面积分析、拉曼光谱和NH₃等温吸附测试等手段对其进行表征,以评估其改进结果。将Al₂O₃/WO₃/ZrO₂催化剂应用到甲醇与乌桕油（非食用油）的酯交换反应中,在其他反应条件相同,Al₂O₃质量分数为3%时,生物柴油最高产率达到83.1%。结果表明：添加Al₂O₃稳定了ZrO₂的四方相结构,使得催化剂比表面积更大、孔数量增加;模板法制备的催化剂孔径分布均匀,WO₃呈高度分散无定型状态;引入Al₂O₃增加了WO₃/ZrO₂催化剂的中强酸性,对弱酸性和强酸性无明显改变。     

稀土Sm_2O_3对Mo_2NiB_2基金属陶瓷微观组织和力学性能的影响

以NiB、Mo、Cr、V、Ni等几种粉末为基本原料,并以稀土Sm_2O_3为添加剂,采用真空液相烧结法制备Mo_2NiB_2基金属陶瓷。利用XRD、SEM、EDS、洛氏硬度计和电子万能试验机等研究添加Sm_2O_3对Mo_2NiB_2基金属陶瓷微观组织和力学性能的影响。结果表明,添加0.3%~0.9%的Sm_2O_3后,金属陶瓷晶粒明显细化,组织分布更加均匀,材料的硬度和抗弯强度也得到提高。当Sm_2O_3添加量为0.6%时,所得试样的晶粒最为细小,晶粒尺寸大致在0.8~3.0μm,材料的力学性能最佳,其硬度和抗弯强度分别达到HRA88.7和1550 MPa。     

BiFeO3掺杂Pb（In1/2Nb1/2）O3-Pb（Mg1/3Nb2/3）O3-PbTiO3陶瓷的制备与磁电性能研究

以固相合成法制备了铁酸铋（BiFeO₃,简称BFO）掺杂的铌铟酸铅-铌镁酸铅-钛酸铅（Pb（In_1/2Nb_1/2）O₃-Pb（Mg_1/3Nb_2/3）O₃-PbTiO₃,简称PIN-PMN-PT）多铁性陶瓷材料,X射线衍射（XRD）测试结果表明：样品具有钙钛矿结构,电滞回线显示其铁电性良好,剩余极化值（P_r）可达18 μC·cm^-2.由于BiFeO₃掺杂后,样品电矩减小,氧空位增多,使其铁电畴翻转困难,样品的电性能略有下降,但是其磁性能随BiFeO₃掺入量的增加而逐渐增强,且样品居里温度（T_m）为200℃左右.该材料在电磁学领域有望成为具有应用前景的多铁性材料.     

O3/H2O2工艺控制太湖原水中致嗅氨基酸

针对太湖原水中氨基酸氯化消毒后可能引发的嗅味问题,采用太湖某水厂滤后水为研究对象,考察了O₃/H₂O₂深度处理工艺对水中致嗅氨基酸的去除效果及影响因素。结果表明滤后水中致嗅氨基酸占总游离氨基酸的81.6%,采用O₃/H₂O₂工艺降解致嗅氨基酸的最佳投量为1.5 mg·L^-1 O₃和0.06 mM H₂O₂,去除率91.28%,致嗅氨基酸浓度降至484.62 ng·L^-1,加氯消毒后几乎没有致嗅风险。水温10~30℃范围内,O₃/H₂O₂对致嗅氨基酸的去除率随温度升高而增大;pH=6~8范围内,去除率随pH的升高而增大。另外,该组合工艺较单独O₃/H₂O₂对溴酸盐的生成也有明显抑制作用。     

Fe_2O_3/TiO_2复合纳米管阵列的制备及其可见光催化性能研究

在氟化铵-乙二醇体系中,采用阳极氧化法在铁基体上制备Fe_2O_3纳米管阵列,然后以氟钛酸铵为钛源,利用水热法在Fe_2O_3纳米管阵列上负载TiO_2纳米片,制得Fe_2O_3/TiO_2复合纳米管阵列,利用SEM、EDS、XRD、TEM、UV-Vis等手段,对所制Fe_2O_3/TiO_2纳米管阵列的表面形貌、物相结构及光催化性能进行表征,并分析Fe_2O_3/TiO_2纳米结构对亚甲基蓝的可见光降解能力。结果表明,Fe_2O_3/TiO_2复合纳米管阵列具有良好的可见光响应;NH_4F浓度为0.4%、水热反应3h制备的Fe_2O_3/TiO_2复合结构具有最佳的光催化性能,对亚甲基蓝的降解率可达90%。