Al-Cu-Fe-Mg,Al-Cu-Fe-Zn和Al-Cu-Fe-Zn-Mg系准晶的形成规律研究

著者采用快速凝固方法制备了Al-Cu-Fe-Mg,Al-Cu-Fe-Zn和Al-Cu-Fe-Mg-Zn系合金粉末,这些快冷合金粉末在室温下为晶态相或晶态相与准晶相共存结构,把粉末加热到773～873K时,晶态相开始转变为准晶相,在1000～1073K时晶态相基本上完全转变为准晶相,继续提高加热温度,准晶相重新变为晶态相。本文对三种合金系列的加热相变规律,准晶相形成规律和准晶相的成分范围进行了详细的研究。     

Al-Cu-Fe-Zn系准晶的形成规律研究

本文通过快速冷凝方法制得了Al-Cu-Fe-Zn系合金粉末。这种快冷合金粉末在室温下为准晶相和晶态相共存结构,当把粉末加热到773K左右时,晶态相开始消失并且转变为准晶相,加热到1000K晶态相基本上完全转变为准晶相,继续升温准晶相又逐渐减少,晶态相重新产生和增加。本文对Al-Cu-Fe-Zn系快冷合金粉末的加热相变、准晶形成规律、准晶的成分范围进行了详细的研究。     

Al-Cr和Al-Cr-Mn合金系准晶粉末的制备和研究

文中给出了Al-Cr和Al-Cr-Mn合金系准晶粉末的制取方法,同时对准晶粉末的形貌、成分、衍射特征和热稳定性能进行了研究,并且采用计算机对高温衍射数据进行了处理,绘制了准晶动态相变图。结果表明,在Al-Cr和Al-Cr-Mn合金系列之中,合金成分和冷却速度对二十面体相的形成有很大影响,Al_(82)Cr_(18)和Al_(82)(Mn,Cr)_(18)在10~5～10~6K/s的冷却速度下,能够得到几乎完全的二十面体的准晶粉末。在Al-Cr合金中,随着Cr含量的增加,提高了准晶相的热稳定性,添加第三组元Mn,也能提高准晶相的热稳定性。     

大块准晶材料的制备

给出了一种大块准晶材料的制取方法,并且对所得材料的性能进行了研究。采用快速凝固制取几乎完全为二十面体相的准晶粉末,通过爆炸成形得到大块准晶材料。研究结果表明,在Al-Mn,Al-Cr和Al-Mn-Cr合金系列中,调整合金成分和冷却速度能够制得几乎完全为二十面体相的Al_(77.5)Mn_(22.5),Al_(82)Cr_(18)和Al_(78)Mn_(18)Cr_4准晶粉末,经爆炸成形后,所得的大块准晶材料仍然保持其二十面体相结构。     

Al-Mn-Si系合金准晶的研究

本文系统研究了Al-Mn-Si系合金中准晶的形成规律和稳定性。准晶I相在Al20Mn6Si合金附近还为最佳成分区,该区合金成分的准晶I相形成能力最大,稳定性最强。而准晶I相在Al20Mn15Si合金附近,形成能力最小,稳定性最弱。通过对准晶I相晶化温度的分析指出,α(Al)相能降低准晶I相的稳定性。准晶I相存在类似非晶态的驰豫现象,驰豫之后稳定性提高。本文还给出了部分合金准晶I相晶化激活能数据。     

铝基多元系准晶合金形成规律的研究

本文是关于铝基多元系准晶合金形成规律的研究．在研究中采用了著者提出的加和原则对多元系铝基准晶的形成规律进行了解析．结果表明，某些准晶态合金可以按一定成分范围相互加和，通过快速凝固和普通熔铸等方法制备新的多元系准晶合金，同样根据准晶的加和原则，可以从某些多元系准晶预测新的基本准晶．     

Al-Mn准晶粉末的制取和研究

本文给出了Al-Mn准晶粉末的制取方法,并且对准晶粉末的形貌、成分、衍射特征和热稳定性能进行了研究。在Al-Mn合金系列中,合金成分和冷却速度对二十面体相的形成有很大影响,并且Mn含量在一定范围内增加,提高了二十面体相的热稳定性。实验结果表明,Al_(77.5)Mn_(22.5)合金在10~5～10~6K/s的冷却速度下,能够得到几乎完全的二十面体相的准晶粉末,这种粉末在673K下加热基本保持其亚稳结构。     

Al63-xCu25Fe12Yx稀土准晶组织性能研究

研究了在雾化制备Al63-xCu25Fe12Yx稀土准晶粉末,结果表明制备的准晶粉末细小且近似球形,添加少量稀土的准晶粉末更细小;850 ℃×4小时热压后准晶中除少量Y的稀土化合物相外,基本上是准晶相;添加少量的稀土后,准晶的硬度和耐磨性均有一定程度提高.     

快速冷凝Al47Cu25Fe8Fe8Mg20合金粉末的TEM研究

本文用透射电子显微镜研究了快速凝Ａｌ４７Ｃｕ２５Ｆｅ８Ｍｇ２０合金粉末，在淬火态粉末中，发现并确定了四个晶体相，在８００℃热处理的粉末中，观察了Ｆ型二十面体准晶相。     

压力和温度对Al－Cu－Fe系准晶合金相变的影响

采用Ｘ射线衍射、透射电镜等手段研究了高压下Ａｌ６５Ｃｕ２０Ｆｅ１５等快速凝固粉末中准晶及晶体相的相变问题，在８００℃，６ＧＰａ条件下，准晶粉末中的晶体相基本上转变为二十面体准晶相。在常压下，准晶相在高温转变为晶体相．压力对相变热力学有显著影响。     

机械合金化法制备Cu-Ti-Zr基非晶合金

采用机械合金化法成功制备Cu40Ti60-xZr(x=0,10,30,50)非晶合金.研究Cu-Ti-Zr合金粉末由晶态向非晶态转变过程中的组织结构变化,探讨非晶合金的形成机制,以及非晶合金的热稳定性和晶化产物.结果表明,非晶合金直接从初始元素得到,在反应过程中没有金属间化合物出现,非晶化过程可以由间隙扩散模型来解释.Cu40TixZry非晶粉末的DSC分析表明,随着Ti含量的降低和Zr含量的升高,非晶粉末的晶化温度Tx逐渐升高,对非晶粉末在相应的Tx温度附近退火15min后发现,Cu40Ti30Zr30合金没有析出相,Cu40Ti1Zr50析出了Zr2Cu,Cu4Ti和少量的一些未知相.     

A Study of Making Iron Aluminide Alloy Powders with New Rotating Electrode Technology

A new process was used for producing FeAl alloy pow de rs with double consumable rotating electrodes and the powders made in this appar atus were analyzed. In this new technology, tungsten rod serves as a cathode ele ctrode, while the alloy rod as an anode electrode. The conventional rotating ele ctrode process must have an anode with pre-melting alloys; however, in this new process, using pure iron as cathode electrode and pure aluminum as anode electr ode can eliminate the step of pre-melting. The e...     

Structure and corrosion resistance of Al–Cu–Fe alloys

The microstructure and electrochemical properties of Al–Cu–Fe alloys with the atomic compositions of Al_(65)Cu_(20)Fe_(15),Al_(78)Cu_7Fe_(15)and Al_(80)Cu_5Fe_(14)Si_1have been studied.The alloys were produced by induction melting of pure elements with copper mold casting.The microstructure of the alloys was analyzed by X-ray diffraction and high-resolution transmission electron microscopy.The formation of quasicrystalline phases in the Al–Cu–Fe alloys was confirmed.The presence of intermetallic phases was observed in the alloys after crystallization in a form of ingots and plates.The electrochemical measurements were conducted in 3.5%NaCl solution.The electronic structure of the alloys was determined by X-ray photoelectron spectroscopy.The post corrosion surface of the samples was checked using a scanning electron microscope equipped with the energydispersive X-ray detector.It was observed that the Al_(65)Cu_(20)Fe_(15)alloy had the highest corrosion resistance.The improved corrosion resistance parameters were noted for the plate samples rather than those in the as-cast state.And the hardness of the Al_(65)Cu_(20)Fe_(15)alloy was significantly higher than the other alloy samples.     

晶粒细化对Cu-20Ag-30Cr合金在HCl溶液中腐蚀电化学行为的影响

采用机械合金化通过控制球磨时间制备不同晶粒尺寸的三元合金粉末,然后分别以真空热压工艺制备常规晶粒尺寸和纳米晶粒尺寸的Cu-20Ag-30Cr合金块状合金。并且利用PARM273A和M5210电化学综合测试系统对两种合金进行电化学腐蚀测试,通过测定电化学极化曲线和交流阻抗谱研究了常规晶粒尺寸和纳米晶粒尺寸的Cu-20Ag-30Cr合金在不同浓度HCl溶液中的腐蚀电化学行为。结果表明随着HCl浓度的增加,腐蚀电流密度随之持续增大,自腐蚀电位持续负移,传递电阻持续减小,表明合金的腐蚀程度加剧,合金的耐腐蚀性能减弱;在相同浓度的HCl溶液中,纳米晶粒尺寸的Cu-20Ag-30Cr合金的腐蚀电流密度明显高于高于Cu-20Ag-30Cr合金,表明经过晶粒细化合金腐蚀速度加快,其耐腐蚀性能下降。     

Microstructure and mechanical properties of spark plasma sintered Ti-Mo alloys for dental applications

Ti-Mo alloys with various Mo contents from 6wt% to 14wt% were processed by spark plasma sintering based on elemental powders. The influence of sintering temperature and Mo content on the microstructure and mechanical properties of the resulting alloys were investigated. For each Mo concentration, the optimum sintering temperature was determined, resulting in a fully dense and uniform microstructure of the alloy. The optimized sintering temperature gradually increases in the range of 1100–1300℃ with the increase in Mo content. The microstructure of the Ti-(6–12)Mo alloy consists of acicular α phase surrounded by equiaxed grains of β phase, while the Ti-14Mo alloy only contains single β phase. A small amount of fine α lath precipitated from β phase contributes to the improvement in strength and hardness of the alloys. Under the sintering condition at 1250℃, the Ti-12Mo alloy is found to possess superior mechanical properties with the Vickers hardness of Hv 472, the compressive yield strength of 2182 MPa, the compression rate of 32.7%, and the elastic modulus of 72.1 GPa. These results demonstrate that Ti-Mo alloys fabricated via spark plasma sintering are indeed a perspective candidate alloy for dental applications.     

富Zr相对NdFeB合金HDDR粉末磁各向异性的影响

研究了添加Ｚｒ的ＮｄＦｅＢ合金中富Ｚｒ相的形成对ＨＤＤＲ粉末磁各向异性的影响．结果表明，ＮｄＦｅＺｒＢ合金的ＨＤＤＲ粉末基本上是磁各向同性的，但是ＮｄＦｅ－ＣｏＺｒＢ合金的ＨＤＤＲ粉末却显示出很强的磁各向异性特征．显微组织的观察发现，两种合金中富Ｚｒ相的种类、数量和化学成分存在明显的差别，其中Ｃｏ和Ｚｒ的复合添加对富Ｚｒ相的形成具有抑制作用，这是相应ＨＤＤＲ粉末具有显著磁各向异性的主要原因     

影响高比重合金性能的主要因素探讨

本文研究了有关因素对高比重合金性能的影响,结果表明,当合金的钨含量高于95％时,则主要因素即成形压力对合金的最终性能有较大的影响,其影响规律对高比重合金的研究与生产均有一定的指导意义.     

高温合金GH4169与GH4202在富氧气氛中的燃烧行为

采用富氧燃烧实验方法,通过光学显微镜、扫描电子显微镜和能谱仪等手段对GH4169和GH4202高温合金燃烧试样进行分析,建立合金燃烧质量、热量和氧传输模型,探究两种合金的富氧燃烧机理并提出提高新型高温合金抗燃烧性能的措施。结果表明：GH4202与GH4169合金在富氧条件下均发生燃烧,GH4202抗燃烧性能优于GH4169；两种合金以液相进行燃烧,在合金燃烧前沿存在由未完全燃烧的金属颗粒和氧化物组成“燃烧层”,燃烧层中合金元素的燃烧行为是决定合金整体燃烧的关键性因素；合金元素在燃烧前沿呈现“选择性燃烧”规律,Nb、Ti、Al、Cr等元素易于与氧发生燃烧,Ni滞后燃烧且燃烧热低,起到良好的抗燃烧作用。